    FindPrecasters or Suppliers that provide products, equipment and services to make precast

    concrete.

    FIND PRECAST PRODUCTS NOW

    National Precast Concrete Association> Precast Magazines> Safety/Tech Archive - 1997-2003> Using

    Fly Ash in Concrete

    Using Fly Ash in Concrete

    May 8, 2010

    Safety/Tech Archive - 1997-2003

    6 Comments

    What to look for when using fly ash in precast products.

    By Arnie Rosenberg

    Dr. ArnieRosenberg is a former research director at Grace Construction Products and now a guest

    researcher at the National Institute for Standards and Testing, working on the characterization of fly

    ash.

    All precast concrete producers can now use a group of materials called fly ash to improve the quality and

    durability of their products.Fly ash improves concretes workability, pumpability, cohesiveness, finish,

    ultimate strength, and durability as well as solves many problems experienced with concrete todayand all for

    less cost. Fly ash, however, must be used with care. Without adequate knowledge of its use and taking

    proper precautions, problems can result in mixing, setting time, strength development, and durability.

    What Is Fly Ash?

    Fly ash is a group of materials that can vary significantly in composition. It is residue left from burning coal,which is collected on an electrostatic precipitator or in a baghouse. It mixes with flue gases that result when

    powdered coal is used to produce electric power. Since the oil crisis of the 1970s, the use of coal has

    increased. In 1992, 460 million metric tons of coal ash were produced worldwide. About 10 percent of this

    was produced as fly ash in the United States. In 1996, more than 7 million metric tons were used in concrete

    http://precast.org/precast-magazines/safety-tech-1997-2003/http://precast.org/2010/05/using-fly-ash-in-concrete/http://precast.org/2010/05/using-fly-ash-in-concrete/http://precast.org/2010/05/using-fly-ash-in-concrete/http://precast.org/2010/05/using-fly-ash-in-concrete/http://precast.org/bookstore/http://precast.org/meetings/http://precast.org/education/http://precast.org/precast-possibilities/http://precast.org/http://precast.org/http://precast.org/http://precast.org/precast-magazines/safety-tech-1997-2003/http://precast.org/2010/05/using-fly-ash-in-concrete/http://precast.org/precast-magazines/safety-tech-1997-2003/http://precast.org/precast-magazines/http://precast.org/http://precast.org/find/http://precast.org/contact/http://precast.org/bookstore/http://precast.org/foundationhttp://precast.org/meetings/https://portal.precast.org/http://precast.org/education/http://precast.org/npcaservices/http://precast.org/precast-possibilities/http://www.facebook.com/nationalprecasthttp://www.twitter.com/nationalprecasthttp://www.linkedin.com/company/1029550http://www.youtube.com/nationalprecasthttp://www.flickr.com/photos/nationalprecast/collections/http://precast.org/feedhttp://precast.org/
  • 8/13/2019 Using Fly Ash in Concrete

    2/8

    in the U.S. Economically, it makes sense to use as much of this low-cost ash as possible, especially if it can

    be used in concrete as a substitute for cement.

    Coal is the product of millions of years of decomposing vegetable matter under pressure, and its chemical

    composition is erratic. In addition, electric companies optimize power production from coal using additives

    such as flue-gas conditioners, sodium sulfate, oil, and other additives to control corrosion, emissions, and

    fouling. The resulting fly ash can have a variable composition and contain several additives as well as products

    from incomplete combustion.

    Most fly ash is pozzolanic, which means its a siliceous or siliceous-and-aluminous material that reacts with

    calcium hydroxide to form a cement. When portland cement reacts with water, it produces a hydrated

    calcium silicate (CSH) and lime. The hydrated silicate develops strength and the lime fills the voids. Properly

    selected fly ash reacts with the lime to form CSHthe same cementing product as in portland cement. This

    reaction of fly ash with lime in concrete improves strength. Typically, fly ash is added to structural concrete at

    15-35 percent by weight of the cement, but up to 70 percent is added for mass concrete used in dams,

    roller-compacted concrete pavements, and parking areas. Special care must be taken in selecting fly ash to

    ensure improved properties in concrete.

    Standards

    There are two classes of fly ash: F is made from burning anthracite and/or bituminous coal, and C is

    produced from lignite or subbituminous coal. In Canada, there is a further distinction. When the lime content

    is 8-20 percent, it is classified Cl, and when it is higher, it is class C.

    In the United States and other parts of the world where U.S. standards have been adopted, the chemical part

    of the specification requires only a combined total of silica, alumina, and iron oxide. It does not specify the

    amount of silica that reacts with lime to produce added strength. The alumina content could be high in fly ash,

    which could be detrimental because more sulfate to control its reactivity might be required. Sulfate is added tothe cement to control only the setting reactions of the aluminates and ferrites in the cement. However, the

    amount is limited because expansive reactions are possible after the concrete has set. This amount of sulfate

    does not take into account the extra aluminates that can be added when fly ash is used. Too much iron oxide

    will retard the setting time.

    Although in ASTM C618, the loss on ignition listed in the table of requirements is less than 6 percent, a

    footnote actually allows up to 12 percent. Incomplete combustion products such as carbon, which affects air

    entrainment, water-cement ratio, set, and the concretes color, could cause this ignition loss. Fly ash is

    considered to have met C618s requirements if the 7- or 28-day strength of a sample with 20 percent fly ash

    reaches 75 percent of the control strength in an ASTM C109 test.

    Both class C fly ash and slag have about 35 percent silica and much lower calcium oxide than portland

    cement. In most cases, lower calcium oxide means better durability. In some fly ash, alumina and iron oxide

    can be quite high, leading to lower strength and unusual setting time problems. The carbon content was

    reported in some to be so high that it was beyond the special footnoted exception in ASTM C618.

    Advantages

    The advantages of using fly ash far outweigh the disadvantages. The most important benefit is reduced

    permeability to water and aggressive chemicals. Properly cured concrete made with fly ash creates a denser

    product because the size of the pores are reduced. This increases strength and reduces permeability.

    Today, there are at least two ways to make fly ash more beneficial: a dry process that involves triboelectric

    static separation and a wet process based on froth flotation. These procedures generally lower the carbon

  • 8/13/2019 Using Fly Ash in Concrete

    3/8

    content and the LOI of fly ash. The cost of an additional storage bin should be easily covered by the

    reduction in the cost of the concrete and the added benefits to the concrete. Low-carbon fly ash or the use of

    a better air-entraining agent at a higher-than-usual addition rate can control the problem of freeze-thaw

    durability.

    Advantages in Fresh Concrete

    Since fly ash particles are spherical and in the same size range as portland cement, a reduction in the amount

    of water needed for mixing and placing concrete can be obtained. In precast concrete, this can be translatedinto better workability, resulting in sharp and distinctive corners and edges with a better surface appearance.

    This also makes it easier to fill intricate shapes and patterns. Fly ash also benefits precast concrete by

    reducing permeability, which is the leading cause of premature failure. The use of fly ash can result in better

    workability, pumpability, cohesiveness, finish, ultimate strength, and durability. The fine particles in fly ash help

    to reduce bleeding and segregation and improve pumpability and finishing, especially in lean mixes.

    Advantages in Hardened Concrete

    Strength in concrete depends on many factors, the most important of which is the ratio of water to cement.

    Good quality fly ash generally improves workability or at least produces the same workability with less water.

    The reduction in water leads to improved strength. Because some fly ash contains larger or less reactive

    particles than portland cement, significant hydration can continue for six months or longer, leading to much

    higher ultimate strength than concrete without fly ash.

    There have been several cases in which the early strength of concrete was low, particularly where a significant

    portion30 percent or moreof the portland cement was replaced with fly ash. This need not be a serious

    problem today, since set time is also controlled by many other factors that can be altered to compensate for

    added fly ash, if necessary.

    The observed slow set and low early strength obtained with fly ash has caused a reduction in the amount ofthis mineral admixture used in concrete. Although some fly ash materials will reduce early strength and slow

    the setting time it does not have to be the case today. Some fly ash actually accelerates set. The addition of

    accelerators, plasticizers and/or a small amount of additional CSF, as well as the proper beneficiated fly ash,

    can mitigate this problem.

    Properly proportioned concrete containing fly ash should create a lower cost. Because of the reduced

    permeability and reduced calcium oxide in properly selected fly ash, it should be less susceptible to the alkali-

    aggregate reaction. Sulfate and other chemical attacks are reduced when fly ash is added. Fly ash, which has

    little effect on creep, has been suspected of contributing to corrosion because it reacts with the calcium

    hydroxide. Fly ash, in fact, does not materially reduce alkalinity, and the reduced permeability helps to protectthe concrete from chloride penetration, the cause of rebar corrosion (see Rosenbergs article on corrosion in

    the Fall 1999 issue of MC Magazine). A superplasticizer combined with fly ash can be used to make high-

    performance and high-strength concrete. Concrete containing fly ash generally performs better than plain

    concrete in drying shrinkage tests.

    Disadvantages

    The quality of fly ash is importantbut it can vary. Poor-quality fly ash can have a negative effect on concrete.

    The principle advantage of fly ash is reduced permeability at a low cost, but fly ash of poor quality can

    actually increase permeability. Some fly ash, such as that produced in a power plant, is compatible withconcrete. Other types of fly ash must be beneficiated, and some types cannot be improved sufficiently for use

    in concrete.

    Some concrete will set slowly when fly ash is used. Though this might be perceived as a disadvantage, it can

  • 8/13/2019 Using Fly Ash in Concrete

    4/8

    actually be a benefit by reducing thermal stress. When cement sets, it produces 100 calories per gram so that

    the temperature of a structure may rise 135 degrees. Certain fly ash can be used to keep the temperature

    from rising too high (less than 45 degrees). However, concrete with fly ash can set up normally or even

    rapidly, since many other factors control the set and strength development.

    Freeze-thaw durability may not be acceptable with the use of fly ash in concrete. The amount of air entrained

    in the concrete controls the freeze-thaw durability, and the high carbon content in certain fly ash products

    absorbs some air entraining agents, reducing the amount of air produced in the concrete, making the concretesusceptible to frost damage. High-carbon fly ash materials tend to use more water and darken the concrete as

    well. It is not recommended to use a high-carbon (greater than 5 percent) content fly ash, but if it must be

    used, the proper air content can be reached by increasing the dosage of an air-entraining agent.

    Slow set and low early strength need not be consequences of using fly ash. Most of the time, high- fineness

    and low-carbon fly ash will result in high early strength. Sometimes, additional lime, an accelerator or a

    superplasticizer will be needed. Fly ash also can be mixed with a small amount of condensed silica fume

    (CSF) to improve set or early-strength properties. Certainly, careful attention to the mix design and water

    content is always necessary to obtain proper set and early strength development.

    Precasters should try to obtain fly ash with as high a silica content as possible. Silica reacts with lime from

    cement to produce strength and reduce permeability (class F fly ash should have 50 percent silica content;

    class C should have 35 percent silica content).

    Ask that the water requirement be less than the control, that the color, density and fineness have a minimum

    variation (

  • 8/13/2019 Using Fly Ash in Concrete

    5/8

    Dear Sir or Madam,

    I was wondering if you could help me for finding out a recipe of

    concrete that use for wall precast semi-wet. I would like to

    fabricate wall panel (L=3.7 m * Depth =9 cm * Width =60cm)

    for using it in house. I would like to obtain the recipe for Cubic

    Meter .

    all the best

    Reply

    Raul Bernal on February 19, 2013 at 10:51 pmsaid:

    very informative thanks

    Reply

    Rajendra Sonvane on March 10, 2013 at 7:04 amsaid:

    The such information related fly ash is very useful for my carrier,

    Please send me info how much qty of cement with replace fly ashfor making 1 cub. concrete .

    Reply

    Praveen Davis on November 9, 2013 at 12:59 pmsaid:

    Hi,

    I use fly ash from a near by company which uses coal fired boiler.

    The ash is tan in color and I doubt that I could not replace

    cement. Please advice on this. Is tan color flyash is good or not?

    Reply

    Mason Nicholson November 11, 2013 at 10:39 amsaid:

    http://www.precast.org/http://precast.org/2010/05/using-fly-ash-in-concrete/?replytocom=25252#sfw-respondhttp://precast.org/2010/05/using-fly-ash-in-concrete/?replytocom=24842#sfw-respondhttp://precast.org/2010/05/using-fly-ash-in-concrete/?replytocom=24833#sfw-respondhttp://precast.org/2010/05/using-fly-ash-in-concrete/?replytocom=24815#sfw-respond
  • 8/13/2019 Using Fly Ash in Concrete

    6/8

    *

    *

    Leave a Reply

    Your email address will not be published. Required fields are marked *

    Name

    Email

    Website

    pNeMxcWZixvT * Copy This Password *

    * Type Or Paste Password Here *

    Comment

    You may use these HTML tags and attributes:

  • 8/13/2019 Using Fly Ash in Concrete

    7/8

    Privacy & Terms

    cite="">

    Post Comment

    Precast Inc. Magazine(298)

    Precast Solutions Magazine(227)

    Archive - 2004-2008(264)

    Safety/Tech Archive - 1997-2003(12)

    Visit the NPCA Bookstore to find many more resources on precast concrete.

    Visit the Bookstore

    Copyright & Privacy NoticeSitemap

    Follow

    15

    Sponsor Links

    2013 NPCA - 1320 City Center Dr., Suite 200 - Carmel, IN 46032 - (800) 366-7731

    Type the text

    92Like

    http://www.cna.com/portal/site/cna/menuitem.489f2511a757a1a1df88e0f2a86631a0/?vgnextoid=ae6a2d7254354210VgnVCM200000751e0c0aRCRDhttp://www.predlsystems.com/http://www.press-seal.com/http://www.stackit.net/http://www.qmccranes.com/http://www.gkservices.com/http://www.bhs-sonthofen.com/http://www.ejco.com/http://www.conshield.com/http://www.titaniisoftware.com/http://www.tekamixers.com/http://www.conacweb.com/http://www.spillmanform.com/http://www.wphilts.com/http://www.skako.com/http://www.xypex.com/http://www.polylok.com/http://www.easiset.com/http://precast.org/sitemap/http://precast.org/copyright/http://precast.org/bookstorehttp://precast.org/precast-magazines/safety-tech-1997-2003/http://precast.org/precast-magazines/archive-2004-2008/http://precast.org/precast-magazines/precast-solutions/http://precast.org/precast-magazines/precast-inc/https://twitter.com/intent/follow?original_referer=http%3A%2F%2Fprecast.org%2F2010%2F05%2Fusing-fly-ash-in-concrete%2F&region=follow_link&screen_name=nationalprecast&tw_p=followbutton&variant=2.0http://www.google.com/intl/en/policies/
  • 8/13/2019 Using Fly Ash in Concrete

    8/8

    http://www.facebook.com/nationalprecasthttp://www.twitter.com/nationalprecasthttp://www.linkedin.com/company/1029550http://www.youtube.com/nationalprecasthttp://www.flickr.com/photos/nationalprecast/collections/http://precast.org/feed