TU Berlin UniBw München The Use of Silica-Fume and PEG The Use of Silica-Fume and PEG to Enhance Sintering of LLDPE to Enhance Sintering of LLDPE Powders in Powders in Rotomolding Process Rotomolding Process

Rotational molding

Embed Size (px)

DESCRIPTION

 

Citation preview

Page 1: Rotational molding

TU Berlin UniBw München

The Use of Silica-Fume and PEG to The Use of Silica-Fume and PEG to Enhance Sintering of LLDPE Powders inEnhance Sintering of LLDPE Powders in

Rotomolding ProcessRotomolding Process

Page 2: Rotational molding

What is ROTATIONAL MOLDING

?

Page 3: Rotational molding

a technology for manufacturing hollow seamless articles

a technology for manufacturing hollow seamless articles

Page 4: Rotational molding

by heating, melting,

sintering

by heating, melting,

sintering

Page 5: Rotational molding

of powderof powder

Page 6: Rotational molding

1 mm1 mm

raw reactor powder of LLDPEraw reactor powder of LLDPE

Page 7: Rotational molding

ProblemsProblems

Page 8: Rotational molding

many bubbles

many bubbles

Page 9: Rotational molding

crack resistance

is lowis low

Page 10: Rotational molding

overheating overheating

Page 11: Rotational molding
Page 12: Rotational molding
Page 13: Rotational molding

to

Page 14: Rotational molding

ExperimentalExperimental

RESULTSRESULTS

Page 15: Rotational molding

Set-up forSet-up for

blendingblending

Page 16: Rotational molding

Set-up forSet-up for

sinteringsintering

Page 17: Rotational molding

Uniaxial Uniaxial

RotomoldingRotomolding

Page 18: Rotational molding

PE powderPE powder

1 mm1 mm

Page 19: Rotational molding

after 10 min of heatingafter 10 min of heating

1 mm1 mm

Page 20: Rotational molding

If melt is in diffusion equilibrium with atmosphere gas in the bubble tend to flow outwards because of pressure difference ΔP until radius r of the bubble diminishes to zero.

PiPi

ΔP = Pi - Patm = 2T/rΔP = Pi - Patm = 2T/r

PatmPatm

Dissolving the bubblesDissolving the bubbles

Page 21: Rotational molding

PE powder+

SF (800 ppm)

PE powder+

SF (800 ppm)

1 mm1 mm

Page 22: Rotational molding

after 10 min of heatingafter 10 min of heating

1 mm1 mm

Page 23: Rotational molding

PE powder + SF (800 ppm): PE powder + SF (800 ppm): very good free-flowvery good free-flow

PE powder + SF (800 ppm): PE powder + SF (800 ppm): very good free-flowvery good free-flow

42.5o42.5o

Page 24: Rotational molding

PE powder: good free-flowPE powder: good free-flowPE powder: good free-flowPE powder: good free-flow

45o45o

Page 25: Rotational molding

Example of Gas Permeable Polymers:

Example of Gas Permeable Polymers:

Silicone Rubber: high flexibility of the silicon-oxygen chain in siloxane provides “openings” which are freevolume and permit gas diffusion, see Zhang and Cloud (2006).

Silicone Rubber: high flexibility of the silicon-oxygen chain in siloxane provides “openings” which are freevolume and permit gas diffusion, see Zhang and Cloud (2006).

Page 26: Rotational molding

Gas Permeation Gas Permeation

Page 27: Rotational molding

Siloxane – high flexible chainSiloxane – high flexible chain (Si-O-Si bond)

PEG – high flexible chainPEG – high flexible chain (C-O-C bond)

Page 28: Rotational molding

Gas Permeation of Polymers, BarrerGas Permeation of Polymers, Barrer

1

10

100

1000

10000

100000

1000000

LDPE Silicone PEG est.

N2

O2

CO2

H2O

Page 29: Rotational molding

PE powder+

PEG (0.4%)

PE powder+

PEG (0.4%)

1 mm1 mm

Page 30: Rotational molding

PEG beadsafter 10 min of heating

PEG beadsafter 10 min of heating

1 mm1 mm

Page 31: Rotational molding

PE powder + PEG (0.4%) PE powder + PEG (0.4%) at 72at 72ooC: no free-flowC: no free-flow

PE powder + PEG (0.4%) PE powder + PEG (0.4%) at 72at 72ooC: no free-flowC: no free-flow

70o70o

Page 32: Rotational molding

PEG + Silica FumePEG + Silica FumePEG + Silica FumePEG + Silica Fume

Page 33: Rotational molding

PE powder+

PEG (0.4 %)+

SF(800 ppm)

PE powder+

PEG (0.4 %)+

SF(800 ppm)

1 mm1 mm

Page 34: Rotational molding

after 10 min of heating

after 10 min of heating

1 mm1 mm

Page 35: Rotational molding

PE + PEG(0.4%) + SF(800ppm)PE + PEG(0.4%) + SF(800ppm)at 72at 72ooC: free-flow properties C: free-flow properties

PE + PEG(0.4%) + SF(800ppm)PE + PEG(0.4%) + SF(800ppm)at 72at 72ooC: free-flow properties C: free-flow properties

60o60o

Page 36: Rotational molding

PE powder+

PEG+CA (0.4%)

PE powder+

PEG+CA (0.4%)

1 mm1 mm

Page 37: Rotational molding

after 10 min of heating

after 10 min of heating

1 mm1 mm

Page 38: Rotational molding

PE powder+

PEG+CA (0.4%)+

SF (800ppm)

PE powder+

PEG+CA (0.4%)+

SF (800ppm)

1 mm1 mm

Page 39: Rotational molding

after 10 min of heating

after 10 min of heating

1 mm1 mm

Page 40: Rotational molding
Page 41: Rotational molding

Silica Fume

Page 42: Rotational molding

Novel PPA: PEG+

Silica Fume

Page 43: Rotational molding

Silica Fume

PEG +

Carboxylic Acids+

Page 44: Rotational molding

What are micro-pellets?

• Small regular oval shaped plastic granules with a diameter between 500-600µm.

• Produced from the same base material as powder, i.e. Qenos 711UV etc.

• Differ from powder by way of the manufacturing process and particle size distribution.

Page 45: Rotational molding

Process comparison

Customer

Dust Collector

Blower

Bag

PE pellets Cyclone

Sieves

GrindingHead

OversizeParticles

Powder

85-105oC

Source: Practical Guide to Rotational Mouldingby R Crawford & M Kearns

POWDERPELLETS and

MICRO-PELLETS

Source: Gala Industries

Bag

Centrifugal Dryer

Extruder

PE Powder

Die Plate

PDVCutter

Process Water

Process WaterPump

WaterBath

190-210oC

Page 46: Rotational molding

Particle size distribution comparison.

0

10

20

30

40

50

60

70

0 50 106 150 212 250 425 500 600 710 850 1000

Particle Size, Micron

% B

y W

eig

ht

Powder MicroPellets

Ave = 300-350 µm

Ave = 550 µm

Page 47: Rotational molding

IMPROVED ECONOMICS AND MORE OPTIONS FOR THE MOULDER

What are the benefits of micro pellets?Manufacturing Process• Consistent quality and size• Less contamination• Dust free during mould filling

Shape and Particle Size Distribution• Potential for faster cook times• Potential for lower peak internal air temperature• Greater bulk density (0.51kg/m3 cf. 0.34 kg/m3)• Improved flow (10 sec cf. 32 sec)• Potential for improved mechanical properties• Improved filling and definition of difficult to fill mould areas• Moulded parts with more uniform wall thickness• Maintained / improved surface finish

Other • Cheaper raw material

Page 48: Rotational molding

Micro Pellet Tank Trial

20

25

30

35

40

45

50C

ycle

Tim

e (m

ins)

Cook Time (min) Cool Time (min)

Cool Time (min) 17 16 16 17

Cook Time (min) 28 24 25 24

Powder Tank - 1 Tank - 2 Tank - 3

Meet requirements of tank standard impact testing with no ductile or brittlefailures using a 9.06kg drop dart @ 1.4m.

Oven machine, Tank Size = 2,250L, Shot Weight = 55kgs, Wall thickness = ~5mm, Colour = Merino.

> 12%

Page 49: Rotational molding

Rotomolding PPAs:Rotomolding PPAs: Silica Fume (SF): "Free-Flow" Agent.

PEG+SF: Densification & Processing Aid (D&PA).

PEG + Carboxylic Acids (CA): Advanced D&PA.

Novel Processing Additives: PEG + CA + SF.

Silica Fume (SF): "Free-Flow" Agent.

PEG+SF: Densification & Processing Aid (D&PA).

PEG + Carboxylic Acids (CA): Advanced D&PA.

Novel Processing Additives: PEG + CA + SF.

Page 50: Rotational molding

Extrusion PPAs:Extrusion PPAs: Silica Fume (SF): Thickening Agent.

PEG+SF+Anti-Oxydants: Processing Aid (PA).

PEG + Carboxylic Acids (CA): Advanced PA.

Novel Processing Additives: PEG + CA + SF.

Silica Fume (SF): Thickening Agent.

PEG+SF+Anti-Oxydants: Processing Aid (PA).

PEG + Carboxylic Acids (CA): Advanced PA.

Novel Processing Additives: PEG + CA + SF.

Page 51: Rotational molding
Page 52: Rotational molding
Page 53: Rotational molding

Process comparison

MICRO-PELLETSWATER COOLING

Source: Gala Industries

Bag

Centrifugal Dryer

Extruder

Powder

Die Plate

PDVCutter

Process Water

Process WaterPump

WaterBath

190-210oC

Bag

Extruder

Powder

Die Plate

PDVCutter

125-135oC

Air Cooler

MICRO-PELLETSAIR COOLING

Page 54: Rotational molding

Little things can make BIG CHANGES

Page 55: Rotational molding

Cost Effectivepatent pending