MEHANSKE LASTNOSTI LESA

MEHANSKE LASTNOSTI LESA

Interno gradivo!V učne namene zbrala in uredila Gabi Dolenšek

Natančni viri niso navedeni; na napake me opozorite!

MEHANSKE LASTNOSTI LESA

TRDOTA LESA

TRDNOST LESA

JE ODPOR LESAPROTI PRODIRANJU

TRŠEGA TELESA VANJ

JE SPOSOBNOST, DA SE UPIRA SPREMEMBIOBLIKE IN PORUŠITVI ZARADI DELOVANJA

ZUNANJIH SIL

JE NAJVEČJA NAPETOST,KI NASTANE V TELESU OB

PORUŠITVI

TRDOTA LESA

JE ODPOR LESAPROTI PRODIRANJU

TRŠEGA TELESA VANJ•NA PREČNEMPREREZU TRŠI LES

KOT NA R ALI T

•VEČJA GOSTOTA – VEČJA TRDOTA

•KASNI LES – TRŠI OD RANEGA

•BOLJ SUH LES – TRŠI

•VEČ LIGNINA - TRŠI

DOLOČANJE TRDOTE

PO BRINELLU

TRDI LESOVImacesen

javorjesenhrasthreh

bukevbeli gaber

gvajak

MEHKI LESOVIjelka

smrekatopol

kostanjlipa

brezajelšabalza

HB=F/SHB – trdota N/mm2

F – silaS – površina odtisa

kroglice

ODPOR LESAPROTI OBRABI

(stopnice, pragovi, parket,..)•gost les•suh les

•prečni prerez.

• metoda po Brinellu • Jekleno kroglico s premerom 10 mm vtisnemo v les s

konstantno silo: pri mehkih lesov s silo100 N, pri srednje trdih lesovih 500 N in pri zelo trdih lesovih s silo 1000 N. Brinellska trdota je razmerje med uporabljeno silo in površino odtiska HB = F/A v N/mm2.

• metoda po Janki.• Jekleno kroglico s premerom 11,3 mm vtisnemo v les do

ekvatorja. Površina odtiska je tedaj 1 cm2. Trdota je definirana kot sila, ki je potrebna za vtiskanje kroglice do ekvatorja ali kot razmerje med silo in površine vtiska.

• Trdota je odvisna od smeri preskušanja: pri anizotropnem lesu je trdota prečne površine 1,5 - 2,5 x večja od trdote trangencialne ali radialne površine. Tangencialna površina je nekoliko trša od radialne površine .

Brinell Hardness Test

• The Brinell test was devised by a Swedish researcher at the beginning of the 20th century.

• The test comprises forcing a hardened steel ball indentor into the surface of the sample using a standard load as shown in Fig.1(a). The diameter/load ratio is selected to provide an impression of an acceptable diameter. The ball may be 10, 5 or 1mm in diameter, the load may be 3000, 750 or 30kgf, The load, P, is related to the diameter, D by the relationship P/D 2 and this ratio has been standardised for different metals in order that test results are accurate and reproducible. For steel the ratio is 30:1 - for example a 10mm ball can be used with a 3000kgf load or a 1mm ball with a 30kgf load. For aluminium alloys the ratio is 5:1. The load is applied for a fixed length of time, usually 30 seconds. When the indentor is retracted two diameters of the impression, d 1 and d 2 , are measured using a microscope with a calibrated graticule.and then averaged as shown in Fig.1(b).

Janka Steel Ball Hardness Test For Wood

• The Janka Hardwood Scale was invented in 1906 by Gabriel Janka {1864 - 1932}, an Austrian wood researcher and is an adaptation of the Brinell Hardness Test for metals. The American Society for Testing and Materials {ASTM} standardized the test in 1927.

• The Janka Hardness Test measures how hard wood is. It measures the pounds of force (lbf) required to drive in a steel ball with a diameter of 11.28 millimeters {0.444 inches} into the wood to half its diameter. The higher the number the harder the wood. This procedure was chosen so that the result would leave an indention of exactly 100 square millimeters {0.16 square inches} in size.

• It is one of the best ways to determine how easily a particular wood species will dent, ding, scratch and wear. It also suggests how difficult a species will be to saw, plane, route, sand, nail and work in general.

• The hardness of wood usually varies with the direction of the wood grain. When testing is done on the surface of a plank, perpendicular to the grain, the test is said to be of side hardness. Any particular wood species will deviate in hardness from one piece of lumber to another. The below numbers are an average side hardness with the wood at 12% moisture content. Most pieces of wood in the same specie will be plus or minus 10% of the below numbers.

NAPETOSTI V LESU

LES OBREMENIMO Z ZUNANJO SILO – LES SE UPIRA SPREMEMBI –

V LESU NASTANEJO NAPETOSTI

STATIČNA OBREMENITEV DINAMIČNA OBREMENITEV

TLAČNA OBREMENITEV NATEZNA OBREMENITEV

=F/S

- NAPETOSTm2=PaN/mm2=MPa

NATEZNI PREIZKUS

-leseno palico (l) vpnemo-obremenimo na nateg v osni smeri

-palica se podaljša za raztezek, ki ga merimo-palica se DEFORMIRA

-les se upira deformacijam – v njem nastanejoNAPETOSTI

=F/S

l

l

ELASTIČNO OBMOČJEPO PRENEHANJU OBREMENITVE SE LES POVRNE V PRVOTNO OBLIKO –

ELASTIČNE DEFORMACIJE

PROPORCIONALNAMEJA

PLASTIČNO OBMOČJEV LESU NASTANEJO TRAJNE –

PLASTIČNE DEFORMACIJE

V ELASTIČNEMOBMOČJU VELJA

HOOKOVZAKON

l

l

E

HOOKOVZAKON VELJAV ELASTIČNEM

OBMOČJU

E

l

l

– ELASTIČNA NAPETOST (N/m2=Pa, N/mm2=MPa)– SPECIFIČNA deformacijaE – modul elastičnosti (N/mm2= MN/m2=MPa)

HOOKOVZAKON

Raztezek (specifična deformacija)je premosorazmeren z napetostjo.

El

l

E-mera za TOGOST materiala-odpor materiala proti elastični

deformaciji-višji E- manjša sprememba

oblike

MODUL ELASTIČNOSTI - E

JE VEČJI

KO SILA DELUJE V SMERILESNIH VLAKEN

PRI NORMALNI TEMPERATURI

ČE JE LES SUH

ČE JE RAST PRAVILNA

PRI LESU Z VIŠJO GOSTOTO

DOPUSTNA NAPETOST

Nahaja se v območju elastičnih deformacij!

V izdelkih izkoriščamo le deltrdnosti materiala!

Določajo jih predpisi instandardi!

VARNOSTNI KOLIČNIK =

Je razmerje med največjo napetostjo v materialu in dopustno napetostjo.Lesene konstrukcije od 2 do 15.

.dop

maks

LEZENJERELAKSACIJA –POPUŠČANJE

SILE NE POVEČUJEMO-DEFORMACIJA PA SES ČASOM POVEČUJE

el – elastična def..

zad -zadržana def.

vis -viskozna def.PRIMERI?

MEHANSKE LASTNOSTI LESASO

BOLJŠE:

če je les gostejši če je les bolj suh (velja v higroskopskemobmočju – do TNCS)

če je temp. normalna

v smeri lesnih vlaken

IGLAVCI – ožje branikeVENČASTO POR. LISTAVCI –

širše branikeče je les pravilno raščen, Brez napak

ODVISNOST TRDNOSTNIH LASTNOSTIOD VLAGE

TRDNOSTLESA

TLAČNA

UPOGIBNASTRIŽNA

NATEZNA

• RAZLOŽI – POJASNI!• Zgradba celične stene• Celulozno ogrodje• Snop celuloznih molekul• Urejeni deli celuloz – kristaliti• Neurejeni deli – amorfni• Higroskopnost celuloze• Nabrekanje in krčenje lesa – trdnost lesa in vezana

voda• Krčitvena anizotropija

CEPLJENJE LESAJe razdvajanje lesa v smeri

lesnih vlaken.

NAJLAŽJE SE CEPI:

-les z ravnim potekom lesnih vlaken

-manj gost les (iglavci)

-vlažen les

-v smeri trakov - radialno

PREDNOSTI?SLABOSTI?

IZDELKI?

• http://www.swst.org/teach/teach2/properties2.pdf UČNO GRADIVO V ANGLEŠČINI

• http://www.cpi.si/files/cpi/userfiles/Lesarstvo_tapetnistvo/4-LES_LASTNOSTI.pdf

• http://www.cpi.si/files/cpi/userfiles/Lesarstvo_tapetnistvo/mehanske_fizikalno_kemicne_lastnosti_lesa.pdf