Presentation of the hot-dip galvanising process and of the different parameters that are important when choosing one product over another. There are two suggestions for different types of treatment lines: a fully acid line with enhanced protection for rough environments needing passivation and another line with alkaline degreasing for extremely greasy parts.
Citation preview
Ptg. de la Masìa, 13 bxos LD608349 Cabrera de Mar – Barcelona (España) Tel: +34 93 754 17 47– Fax: +34 93 754 16 52admin@angem.com
SOCOVRAI®
Protect steel & iron againstcorrosion
• A Zn layer is chemically attached to the steel surface.
• Zn corrodes slower than iron and, thus, protects
Hot-dip galvanizing
• Zn corrodes slower than iron and, thus, protects iron from corroding.
• Very strong protection against corrosion.
• Different metals (Ni, Cr…) are attached to the base metal surface.
• Used for high-gloss applications.
Electroplating
HDG is used in heavy-dutyindustries
Building & Construction
Street Furniture & Road Safety
Wire frameWire frame
Utilities & Piping
Agricultural-used steel
Transportation & Automotive
Fasteners
• Acid (cold, pre-etching)• Alkaly (warmed, needs
rinsing off)Degreasing
• Mechanic• Water-based dilution: acid or alkalyEtching
Rinsing
Rinsing
Hot-dip galvanising stages
• ZnCl2 and NH4Cl double and triple salts
• ZnCl2Flux
• Protection against corrosionGalvanising
• Protection against white corrosionPassivation
Rinsing
Drying
DEGREASING
GALVANISINGPASSIVATION
ETCHING
FLUX
ANGEM proposes the full range of products
PS series
Additives
Passivants
IC series
Additives
Additives
Salts
SOCOVRAI®PSAG
SOCOVRAI®PSJ
AcidSOCOVRAI®PSB
SOCOVRAI®PSMM
Alkaly
Degreasers
PSJ
SOCOVRAI®PS9M
PSMM
SOCOVRAI®PS198S
SOCOVRAI®PS3xE (electrolithic)
How to choose a degreaser
Dirt type
Shape and quanity of
partsAlloy type
Degreaser
Processcost
Form of application
SOCOVRAI®IC111
SOCOVRAI®IC115
Corrosioninhibitor
SOCOVRAI®AF132
SOCOVRAI®AH131N
Additives
Etching
IC115
SOCOVRAI®IC33
SOCOVRAI®IC120
AH131N
• Higher temperature• Higher HCl
concentration
Difficult to control the acid attack on the metal
Optimum etching requires a balance between HCl y Fe
concentration
• Higher Fe concentration
Etchingspeed
Reduce bath activity
Decapado óptimo en HCl a 20ºC
200
250
300
Co
nc.
de H
ierr
o /
(g
/L)
Exhausted bath Renovate bath
A CI enlarges the margin of etching
0
50
100
150
0 50 100 150 200 250Conc. HCl / (g/L)
Co
nc.
de H
ierr
o /
(g
/L)
Tiempos mayores Óptima Saturación
HCl attacks base metal
A corrosion inhibitor enlarges margins
No
No VOCs
Low toxicity
No
SOCOVRAI ® IC120: environmentally friendly
SOCOVRAI®IC 120
No APEs
No ADR
Environmentally-friendly
Has alcoxylated alcohol and phosphonatedderivatives
PASSIVATION
High-protection acid line
DEGREASING
SOCOVRAI®
ETCHING FLUX
GALVANIZING
SOCOVRAI®
PSAG
80 – 130 g/l25ºCYearlycleaning
SOCOVRAI®
IC120 (0,3%) + AH131N (2 l/m3)
HCl] >100 g/L, [Fe3+]<140 g/LT: 25 ºC
Sel double + SOCOVRAI®
AF132 (5 g/l) + ATH3 (0,5%)
D: 1,2 – 1,26 g/l65 -70ºC
SOCOVRAI®
AR32
450ºC
DE-ZINC
SOCOVRAI®
IC 33
ADL 3P
50-70ºC
Line with alkaly degreaser
DEGREASING
SOCOVRAI®
ETCHING FLUX
GALVANIZING
RINSING
SOCOVRAI®
PSB
7 -20 %55 - 60ºCCleaningevery 6 moths
SOCOVRAI®
IC120 (0,3%) + AH131N (2 l/m3)
HCl] >100 g/L, [Fe3+]<140 g/LT: 25 ºC
Sel double + SOCOVRAI®
AF132 (5 g/l) + ATH3 (0,5%)
D: 1,2 – 1,26 g/l65 -70ºC
SOCOVRAI®
AR32
450ºC
DE-ZINC
SOCOVRAI®
IC 33