nd

an

iver

f T

acul

Julianalaan 136, 2628 BL Delft, The Netherlands

past few years in terms of hurdles that still stand in the way of the successful implementation of zeolite membrane reactors in industry.

instance in catalysis, heat integration, product purication Although the concept of membrane reactors has alreadybeen introduced in the 1950s, it was only with the advent ofnew inorganic materials and high-temperature membranesystems [2,3] in the last 30 years that considerable growthin the research and development of membrane reactor tech-nology has been achieved. The signicant interest in the

* Corresponding author. Address: Reactor and Catalysis Engineering,DelftChemTech, Faculty of Applied Sciences, Delft University of Tech-nology, Julianalaan 136, 2628 BL Delft, The Netherlands.

E-mail address: Koos.Jansen@tnw.tudelft.nl (J.C. Jansen).

Microporous and Mesoporous Mate 2005 Elsevier Inc. All rights reserved.

Keywords: Catalytic membranes; Catalytic membrane reactors; Zeolites; Zeolite membranes

1. Introduction

Increasingly stringent market and environmentaldemands, such as the minimization of energy consumptionand ever-greater emphasis on process safety and superiorproduct quality, mandate major revision of plant congu-rations. The manufacturing of fuel and chemicals hasindeed been subject to large technological improvementsduring the past century. Headway has been made for

and euent clean-up. The new millennium, however, stillneeds further improvements in processes and catalysts aswell as novel manufacturing technologies. Membrane reac-tors are one of such evolving technologies that have hugepromise to deliver processes that are more compact, lesscapital intensive, oer improved conversion for equilibriumlimited reactions, allow controlled operation and have sub-stantial savings in energy and resultant costs due to feed/product separation at elevated process temperatures [1].Received 15 August 2005; received in revised form 9 October 2005; accepted 14 October 2005

Dedicated to the late Denise Barthomeuf, George Kokotailo and Sergey P. Zhdanov in appreciation of their outstanding contributions to zeolite science

Abstract

The integration of reaction and separation in catalytic membrane reactors has received increasing attention during the past 30 years.The combination promises to deliver more compact and less capital-intensive processes with substantial savings in energy consumption.With the advent of new inorganic materials and processing techniques, there has been renewed interest in exploiting the benets of mem-branes in many industrial applications. Zeolite membranes, however, have only recently been considered for catalytic membrane reactorapplications. Despite the signicant recent interest in these types of membranes there are relatively few reports of the application of suchmembranes in high-temperature catalytic membrane reactor applications. This can be attributed to a number of limitations that still needto be addressed such as the relatively high price of membrane units, the diculty of controlling the membrane thickness, permeance,high-temperature sealing, reproducibility and the dilemma of upscaling. A number of research eorts, with some degree of success havebeen directed to nding solutions to the remaining challenges. This review makes a critical assessment of what has been achieved in theZeolite based lms, membraProgress an

E.E. McLeary a, J.C. Ja Department of Chemistry and Polymer Science, Un

b Ceramic Membrane Centre, The Pore, Delft University oc Reactor and Catalysis Engineering, DelftChemTech, F1387-1811/$ - see front matter 2005 Elsevier Inc. All rights reserved.doi:10.1016/j.micromeso.2005.10.050es and membrane reactors:prospects

sen a,b,*, F. Kapteijn c

sity of Stellenbosch, Stellenbosch 7602, South Africa

echnology, Julianalaan 136, 2628 BL Delft, The Netherlands

ty of Applied Sciences, Delft University of Technology,

www.elsevier.com/locate/micromeso

rials 90 (2006) 198220

Meeld is demonstrated by more than a 100 scientic publica-tions (Fig. 1) on the subject per annum as well as severalpatents dealing with membrane reactors that have already

19951996

19971998

19992000

20012002

20032004

050

100

150

200

250

300

350

400

Num

ber o

f Pub

licat

ions

Year

Articleson M

embrane Reactors

Articleson Zeolite M

embranes

Articleson Zeolite M

embrane

Reactors

Membrane Reactor Patents

Zeolite Membrane

Patents

Zeolite Membrane

Reactor Patents

Fig. 1. Scientic publications on membrane reactors and zeolite mem-brane reactors, respectively (Scinder search).

E.E. McLeary et al. / Microporous andbeen led [4,5].Most publications highlight the remarkable potential of

membrane reactors such as the ability to shift the overallconversion beyond thermodynamic equilibrium by selec-tive product removal, improvement in selectivity by distrib-uted addition of reactants alongside the reactor and safetyimprovement through controlled reactant contact [6,7](Table 1).

The clear advantages that exist for the combination ofreaction and separation in a single unit and the multitudeof possible applications reported in the scientic literaturedoes not negate the fact that challenges remain which limitsthe large-scale industrial application of catalytic membranereactors. This is acknowledged by several authors and evi-denced by the shortage of commercialized high-tempera-ture membrane reactor based processes (Table 2).

Several review papers have already been published, deal-ing with dierent aspects and applications of membranereactors; Armor and Hsieh has published some of the ear-liest reviews in the eld [2,25] highlighting the advantagesas well as the major challenges for inorganic membranesto be used in catalytic devices. Saracco and Specchia[6,26] provided a survey on the reactions which have beenperformed in catalytic inert membrane reactors employingeither dense (metals) or porous (mainly ceramic) mem-branes and also considered the practical diculties to thecommercialization of membrane reactors. In the morerecent past, reviews on the subject were published by Sirkaret al. [27], Dixon [7], Dalmon [28] and Tsotsis et al. [2931].Dittmeyer et al. [32] emphasized the role of palladium in areview on the subject and Noack et al. [33] looked at thedevelopments in inorganic membranes and the implicationsfor their practical application. Hsieh devoted the largerportion of a book to the subject of inorganic membranereactors [34], while most recently, Marcano and Tsotsisauthored a book, encompassing a broad treatment of cat-alytic membranes and membrane reactors [35].

Due to the multidisciplinary nature of membrane reac-tor technology, it is impossible to do justice to all aspectsof the eld in a single review article. It is also not the objec-tive of the author to add to the already extensive list ofreviews in the eld but rather to focus on the progressmade and the road forward to the industrial realizationof zeolite-based, catalytic membrane reactors.

2. Zeolites applied in membrane reactor congurations

In zeolite-based membrane reactors the membranenormally consists of a thin lm of a mesoporous ormicroporous zeolite on a macroporous support, typicallya-Al2O3, stainless steel or carbon. This thin lm may simul-taneously serve (i) as both a catalyst and a permselectivemembrane, (ii) as a permselective diusion barrier or (iii)as an inert non-selective reactant distributor. Permselectiv-ity depends on the size of the permeating molecules relativeto the pore size of the membrane, the chemical nature ofthe permeating molecules and the membrane material aswell as the adsorption properties of the membranein amixture of components with dierent adsorption character-istics the stronger adsorbing compound will permeate pref-erentially [36].

The common modes of application of zeolites in mem-brane reactors is; as a catalytic membrane reactor (CMR),a packed bed membrane reactor, a catalytic non-permselec-tive membrane reactor, a non-permselective membrane anda reactant-selective packed bed reactor (RSPBR) (illus-trated in Table 3). The zeolite-based catalytic membranereactor generally consists of a supported permselective layer(membrane) that simultaneously acts as catalyst (CMR).The aforementioned catalytic membrane:

(a) could be inherently catalytic due to the presence ofcatalytic sites (Bronsted acid sites; Lewis acid sites;metal ions in cationic positions; transition metal ionsin zeolite lattice positions; extra-lattice transitionmetal compounds in channels and cavities of a zeolite,metal particles in zeolite cavities) [4,37,38]. Zhu et al.recently synthesized metal nanoparticles encapsulatedin mesoporous silicates as model porous catalysts withthe aim to improve reaction selectivity [39].

(b) could have a separate catalytic and permselectivelayer. Van der Puil reported a composite hydrogena-tion catalyst, in which the catalytic phase (TiO2-sup-

soporous Materials 90 (2006) 198220 199ported platinum) was coated with a thin continuouslayer of oriented silicalite crystals, creating separation

Table 1Applications of membrane reactor processes reported in recent literature

Reaction type Reaction Reactor cong. Operating conditions Membrane Advantages sought/obtained Ref.

Dehydrogenation Methanol oxidativedehydrogenationto formaldehyde

PBMR 200250 CFeMo oxide

Non-permselective316L stainless steel

Increased selectivity andyield due to distributed/controlled reactant addition

[8,9]

Oxidativedehydrogenation ofbutane to butadiene

CMR 550 C V/MgO Aluminaimpregnatedwith MgO

Feed congurations thatlead to a low partial pressureof oxygen also give rise toan improved selectivity

[10]

Hydrogenation CO2 hydrogenationto methanol

CMR 210230 C Pd MOR/ZSM-5/chabazite

Higher CO2 conversionand CH3OH selectivity

[11]

Oxidation Oxidation of alkanes PBMR 150450 C MFI/Al2O3,SiO2/Al2O3and AlPO4/Al2O3

AlPO4 membrane wasthe most ecient forO2 distribution

[12]

Partial oxidationof ethane to syngas

CMR 800900 CLiLaNiO/c-Al2O3

Dense ceramicmembrane

Ethane conversion of100%, the selectivityof CO was higherthan 91%

[13]

Partial oxidationof methane to syngas

PBMR 875 C LiLaNiO/c-Al2O3 catalyst

Dense ceramicmembrane

94% methane conversionand higher than 95%CO selectivity

[14]

Partial oxidationof methanol

NMR FeMo oxidecatalyst bed220250 C

316L-SSmembrane

Observed increasedoperational stability

[15]

Selective oxidationof ethane to ethylene

CMR 825875 C Dense ceramicmembrane

Ethylene yield of 56%with ethylene selectivityof 80%

[16]

Selective oxidationof carbon monoxide

CMR 200250 C PtY Y-type zeolite/porous a-Al2O3

Selective oxidationof COthe CO conc.on the permeate sidedecreased below thedetection limit

[17]

Oxidation of benzeneto phenol

CMR

fun

MeTable 3Classication of membrane reactor congurations according to membrane

E.E. McLeary et al. / Microporous andselectivity and steric constraints at the zeolite/plati-num interface [40].

(c) could have zeolite crystals with catalytic abilityembedded in a matrix e.g. polymer membrane oranother mesoporous zeolite/ceramic membrane.ction and location [51,52,45,53,54]

soporous Materials 90 (2006) 198220 201Baron et al. recently investigated the use of a poly-meric membrane with dispersed zeolite crystals incap-sulating immobilized metal-complexes, acting as aninterphase contactor during alkene oxidation in aCMR [41].

MeWhen the reactor consists of a membrane that is perm-selective but not catalytic with a conventional catalyst pres-ent in the form of a packed bed of pellets/extrudates in theow stream, it is termed a packed bed membrane reactor(PBMR). Caro et al. reported the application of MFI zeo-lite membranes in the dehydrogenation of isobutane, forthe selective removal of H2, ultimately resulting in anincrease in conversion. The catalytic reaction took placein a catalytic packed bed of Cr2O3 on Al2O3 spheres onthe tube side of the membrane [42]. Although the majorityof applications of zeolite membrane reactors reported in lit-erature to date falls into the category of PBMR, more andmore researchers are exploring the use of zeolite mem-branes as catalytically active centers and with dierent,more adventurous modes of operation. Sloot et al. intro-duced a novel membrane reactor (termed a catalytic non-permselective membrane reactor, CNMR) for the catalyticoxidation of H2S to elemental sulfur, in which the mem-brane is although catalytically active, not permselective,and acts as reaction front, facilitating stoichiometrical feedrates of reactants [43]. When applied to the catalytic reduc-tion of NOx with NH3 Sloot et al. obtained high conver-sions of NOx despite uctuating reagent concentrations[44]. Wu et al. also later used a composite membrane (tita-nium silicalite-1/polydimethylsiloxane) as a catalytic inter-phase contactor in the two-phase reaction of n-hexaneoxidation by dilute aqueous hydrogen peroxide [45]. In thisreactor, the catalytic membrane was placed at the interfacebetween the H2O2 aqueous phase and the n-hexane vaporphase. The two reactants, H2O2 and n-hexane, reach thecatalyst surface by diusion through the membrane, there-after reacting with each other. After their formation, theproducts diuse out of the membrane. An additionaladvantage of using such a membrane interphase contactoris that it avoids the use of co-solvent at industrial scale. Ina non-permselective membrane reactor (NMR) themembrane does not have any catalytic activity, nor doesit have permselectivity, it simply acts as a distributor ofthe reactant. Guizard and co-workers investigated the par-tial oxidation of alkanes in a membrane reactor where themembrane (MFI) acts as a O2 distributor, allowingimproved selectivity and preventing reaction run-away[12]. Increasing attention is being paid to particle-levelmembrane reactors (PLMR) which consists of catalyst par-ticles coated with a permselective membrane layer allowingthe selective addition of reactants to the reaction zone orthe selective removal of products from the reaction zonewhen one products diusivity is much higher than thoseof the other products. The main benet arising from thisconguration is the increased membrane area per unit reac-tor volume compared to that of conventional membranereactors. This is highly advantageous considering the di-culty to achieve a large membrane area with the absence ofdefects. Nishiyama et al. prepared a silicaalumina catalystcoated with a silicalite membrane and applied it to toluene

202 E.E. McLeary et al. / Microporous anddisproportionation. Good selectivity for the p-xylene iso-mer, due to its selective removal, was achieved [46]. Nishiy-ama et al. recently demonstrated the viability of membranecoated catalyst particles as a means to achieve selectivityagain when they reported the use of spherical Pt/TiO2particles coated with a silicalite-1 for the selective hydro-genation of linear and branched alkenes. The compositesilicalite-1/Pt/TiO2 catalyst showed 1-hexene/3,3-DMBhydrogenation selectivities of 1220 at 50 C and 1830at 100 C due to the selective permeation of 1-hexenethrough the silicalite-1 layer [47].

Marcano and Tsotsis [35], Perez et al. [48,49], Falconeret al. [50] as well as Coronas and Santamaria [49] intro-duced similar acronyms for ease of reference to the dier-ent membrane reactor types.

3. Progress in zeolite membrane synthesis for membrane

reactor applications

Polymeric membranes allow both high permselectivityand fast permeation, well-developed technology to producethin polymeric membranes already exists and are alsorelatively cheap, yet these membranes have importantdrawbacks that limit their use in membrane reactors. Theshortcomings, namely their limited resistance to tem-perature, solvents and corrosive environments, limits theapplication of polymeric membranes to bioreactor andliquid-phase reaction systems [55]. Inorganic membranes,such as ceramics and metals however, do promise signi-cant payo in chemical processing, owing to their superiorcharacteristics of thermal, mechanical and structural stabil-ities as well as chemical and solvent resistance. Inorganicmembranes also allow regeneration through the oxidativeremoval of carbonaceous species at 400500 C and there-fore have longer life expectancies than their polymericcounterparts.

Inorganic membranes can be classied into two types:non-porous (dense) and porous membranes. Dense mem-branes prepared from palladium or perovskites only allowcertain gases (such as H2 or O2) to permeate via mecha-nisms such as solutiondiusion or solid-state ionic con-duction. Such non-porous systems exhibit extremely highselectivities but have limited permeabilities, although here,substantial research eort during the last decade have pro-duced uxes within reach of targets [56]. These membranesfurther require high capital investment due to the use ofprecious metals and/or extreme synthesis and operatingconditions [57] and may be mechanically unstable [58]. Incontrast, microporous silica membranes have proven tobe promising for molecular sieving applications. Precisepore size control (0.30.4 nm in diameter) to allow forseparation on the basis of size by molecular ltration orsieving has however not yet been achieved for amorphousinorganic membranes and they are also chemically,mechanically and thermally less robust [59] than zeolitemembranes.

Zeolite membranes form one of the newest branches of

soporous Materials 90 (2006) 198220the inorganic membrane eld. Unlike the most micropo-rous metal oxides (e.g., SiO2, Al2O3 and TiO2) that have

tortuous pore channels, zeolites are microporous alumino-silicate materials that have a well-dened, uniform poresystem of molecular dimensions (enabling shape or sizeselective catalysis or separation) due to their porous crys-talline structure. Zeolites are relatively stable at hightemperatures, can be acidic or basic in nature and can exhi-bit hydrophilic or organophilic properties. These molecularsieves can be tailor made for a specic application throughion exchange, dealuminationrealumination, isomorphoussubstitution and insertion of catalytically active guests suchas transition-metal ions, complexes, basic alkali metal ormetal oxide clusters. The molecular sieving abilities,Fig. 2, and selective sorption properties in combinationwith their catalytic activity, in addition to their thermaland chemical stability, make zeolites ideally suited for thecombination of separation and reaction under processconditions.

Total selectivity, or sieving, results when the size of thepore apertures is similar to the dimensions of the gas mol-ecules. Even the very critical separation of propanepro-pene is possible in this way [60]. However very high

papers on the subject and literature abounds with reviewson zeolite membranes (van de Graaf et al. [65], Caroet al. [33,66], Tsapatsis et al. [67] and Lin et al. who recentlysummarized the signicant progress made in the synthesisof microporous membranes [68]).

MFI zeolite membranes (silicalite-1, ZSM-5), on at ortubular supports, have been investigated extensively forapplication in gas separation, catalytic reactors and per-vaporation. Silicalite-1 has for instance been applied inthe separation of n-hexane from its branched isomers in ahydroisomerization membrane reactor [69]. The linear alk-anes are preferentially adsorbed by the zeolite and suppliedto a packed bed of catalyst. The control of the feed compo-sition to the reaction resulted in an increased selectivity andconversion. Zeolite A membranes have often been the tar-get of investigations because their small pore size would inprinciple exclude molecules with a size larger than 4.1 Athereby opening the eld to highly selective separations inthe gas and liquid-phases [70]. Other zeolite membranesthat have been reported include FAU [71], MOR [72,73],FER [74], GIS(P) [75], SAPO-34 [76], zeolite T [77,78],

CHA (SAPO-34)

eti0

E.E. McLeary et al. / Microporous and Mesoporous Materials 90 (2006) 198220 203selectivity is also possible with mixtures of gases whenthe zeolite pore sizes are signicantly larger than the mole-cules, due to adsorption selectivities and/or the dierencesin diusivities of the various components in the mixture[61,62].

A great deal of progress in the science of zeolite mem-brane synthesis has been made since the rst preparationsof zeolite membranes by Suzuki in 1987 [37] the stand-alone, mechanically unstable membrane by Haag and Tsi-koyiannis of Mobil in 1991 [4,63] and the rst supportedsilicalite-1 membrane reported in literature by Geus et al.[64]. Since then there has been an exponential growth in

NH3

CO2

n-alkanes

double branched alkanes

single branched alkanes

o/m-xylene

1,3,5-TIPBN(C4F9)3N(C4F9)3

Kin0.0 0.2

HeH2O

H2

O2

N2CO

C3H6C2H4CH4

H2S

SF6benzene p-xylene Fig. 2. Comparison between the eective pore sizes of dierent zeolites and tmembrane reactor applications.BEA [51] and mesoporous UTD-1 [79]. The hydrophilicLTA zeolitic membrane has been the rst to nd industrialapplication. The rst large-scale pervaporation plant,which produces 530 l/h of solvents (EtOH, IPA, MtOH,etc.) at less than 0.2 wt.% of water from 90 wt.% solventat 120 C, has been put into industrial operation recentlyby Mitsui Engineering and Shipbuilding Co. Ltd. [80].The plant is equipped with 16 modules, each of whichconsists of 125 pieces of NaA zeolite membrane tubes.The excellent water separation is however based onthe strong hydrophilic nature of the LTA membrane andnot on molecular sieving [81]. Few reports exist for the

NaA

FERM

FI

MO

RFAU

GIS

BEA

c diameter / pore size [nm].4 0.6 0.8 1.0he kinetic diameters of gas molecules featured in reports on zeolite-based

Mesuccessful application of zeolite A membranes to gas sepa-ration. Most authors report selectivities similar to thoseexpected for Knudsen ow through the membraneanindication of the presence of intercrystalline pores.

Despite the measurable success achieved in supportedzeolite membranes during the past decade, few reports onthe practical application of such membranes in high-temperature catalytic membrane reactors exist. To somerespect this can be contributed to the diminishing interestof industry in novel catalytic and separation materialsand processes that provide only moderate performanceimprovements to established processes. The current eco-nomic climate and the fact that material uncertaintiesand associated development costs rarely counterbalancepotential benets fuel this somewhat discouraging viewof industry. However, the lack of implementation of zeo-lite membrane reactor technology cannot solely be blamedon industrial scepticism. In order to bring zeolite mem-brane reactors to commercial applications, there are anumber of criteria that still have to be met and/or furtherexplored:

1. The synthesis of membranes with high permeability andselectivity, i.e. oriented, thin layers i.e. small eectivethicknesses are required which must be highly uniformand free of defects. Optimal membrane reactor opera-tion requires the membrane ux to be in balance withthe reaction rate [82].

2. Reproducibility and long-term stability of membraneperformance. Coke deposition, triggered to a largeextent by the acidic nature of the zeolite framework,necessitates the possibility of repeated membrane re-generation and a technology for repairing defectivemembranes.

3. Ultramicroporous membranes, i.e. those with su-ciently small pores (3 A) to allow separation on thebasis of size exclusion, and without intercrystallinepores. The majority of the membranes synthesized sofar are MFI-type zeolite membranes that have porediameters (5 A), which are still too big to selectivelyseparate small gaseous molecules.

4. The sealing of the membranes at high-temperatures(>250 C) and pressures.

5. Scaling-up of membrane modules, requiring the abilityto prepare large defect-free membranes at reasonablecosts.

6. Cost of membranes and membrane modules.7. Clarication of multicomponent transport and separa-

tion behaviour through zeolitic and non-zeolitic path-ways in the membranes at industrially relevantoperating conditions.

Recent research eorts have therefore been directed tonding solutions to the above challenges. For this reasonthe advances made in the eld of membrane reactors mir-

204 E.E. McLeary et al. / Microporous andror the advances made in the production of new andimproved membranes.3.1. The synthesis of high-ux, selective membranes

The quality of zeolite membranes is determined by inter-crystalline porosity (defects) [83], the crystal orientationrelative to the membrane layer [84], size of the crystals[85] and the thickness and uniformity of the zeolite layer[86]. In recent years, several groups have reported prepara-tions of high quality zeolite membranes: MFI [87,88],mordenite [89,90], Y-type [91], A-type [92] and ferrierite[93]. A variety of methods for the fabrication of zeolite thinlms exists which includes dip coating, spin coating, sput-tering, chemical vapour deposition (CVD) and laserablation [94]. The three most common methods used toproduce membranes for gas separation have been (a) theformation of a composite, by embedding zeolite crystalsin a matrix, such as a polymer, (b) in situ crystallizationin the presence of a substrate, such as a porous ceramic,to give a supported zeolite membrane and (c) the morerecently developed secondary growth process whichinvolves the deposition of colloidal zeolite crystals on amacroporous support followed by hydrothermal synthesis.

Most papers written on zeolite membranes, and mostdevelopment in the eld have been targeted at MFI typemolecular sieves. Table 4 gives a summary of recent pro-gress made in the synthesis of silicalite-1 membranes.

In order to control and direct the synthesis of thin, ori-ented, selective zeolite membranes, crucial to the success ofmembrane reactors, a fundamental understanding of themechanism of zeolite crystallization and membrane growthneeds to be gained. The preparation of zeolite membranesis still often conducted in conditions similar to zeolitepowder synthesis, which are not optimized for membraneformation. Finding the proper conditions to prepare adesired zeolite membrane is often largely based on trialand error, limiting the reproducibility of membrane prepa-ration. As a result, substantial eort has recently been putinto the elucidation of the mechanism of crystal growth[104] and zeolite lm formation [105107], as well as therole of structure directing agents (SDAs) in the assemblyof long-range ordered materials. More importantly the cor-relation between the mechanism, the membrane synthesisprocedure and composition and the resulting zeolite lmhas been investigated. De Moor et al. [108], using a combi-nation of in situ SAXS, USAXS and WAXS (ultrasmalland wide-angle X-ray scattering), found the nucleation ofSi-TPA MFI to be a two-step process: rst nutrients mustassemble into composite species (2.8 nm). Aggregation ofthese nanometer-scale primary units to 1015-nm-sizedparticles is found to be an essential step in nucleation ofthe zeolite since it enhances the nucleation rate. By varyingthe alkalinity, it was found that 2.8 nm particles werealways present unlike their aggregates which were notformed at high alkalinities (Si/OH ratio > 2.65) [109].Although the size of the primary units for MFI was shownto be independent of the structure-directing agent used

soporous Materials 90 (2006) 198220(a dimer of TPA, a trimer of TPA or trimethylene-bis(N-hexyl,N-methyl-piperidium)), the organic species does have

Table 4Overview of synthesis for thin, high ux, oriented silicalite-1 membranes

Ref. OH/Si Na+/TPA+ Synthesistemp. (C)

Synthesis method Support Membranethickness (lm)

CrystalOrientation

Membrane performance

[95] 0.32 0.00 165 In situ, hydrothermal, horizontalplacement of support at bottom ofautoclave, clear solution

SS 304 plates 1 b-Oriented Flux and selectivity not given

[95] 0.50 0.00 165 In situ, hydrothermal, horizontalplacement of support at bottom ofautoclave, clear solution

SS 304 plates 0.6 b-Oriented Flux and selectivity not given

[96] 0.32 0.00 165 In situ, hydrothermal, horizontalplacement of support at bottom ofautoclave, clear solution

SS 304Aluminium alloy

Mea pronounced inuence on the crystal growth step and,therefore, on the crystal growth rate, size, and morphology[110]. The suggested growth mechanism agrees with a mech-anism proposed earlier by Schoeman et al. [111] essentiallythe same growth mechanism was also suggested by denExter et al. [112].

Although most of the earlier molecular sieve membranesprepared were freestanding, the vast majority of zeolitemembranes prepared today are supported, owing to theirgreater structural stability and reduced mass-transfer resis-tance. Two critical stages can be distinguished during theformation of supported zeolite membranes, namely nucle-ation on the support followed by crystal growth to forma continuous zeolite lm covering the support. Nucleationand crystal growth processes during zeolite membrane syn-thesis are very sensitive to experimental conditions such assynthesis solution/gel composition (which Wang et al.proved can be manipulated to control the crystal growthorientation [95]), pH, temperature, chemical and structuralnature of the support [113], support position [75,114],structure directing agents (SDAs) [99] used to assemblelong-range ordered materials and even nutrient sources[115,116].

Synthesis of zeolite membranes or thin lms on a sup-port can broadly be classied as either in situ, a one-stephydrothermal synthesis where the support is placed indirect contact with the alkaline precursor solution, or sec-ondary (seeded) growth in which an existing zeolite phase(seed crystals), is attached to the support followed byhydrothermal growth of the applied seeds to a continuouslayer. In essence both these techniques involve nucleationand crystal growth steps, although nucleation sites are cre-ated and applied separately and with more control to thesurface of the support during secondary synthesis. Sincesecondary growth techniques enable improved control ofnucleation site location and density, it renders the natureof the support less important for membrane growth withgrowth proceeding from a layer of seed crystals coveringthe support [117]. Nevertheless good adherence of the zeo-lite seed crystals (nucleation sites), as well as the zeolite lmto the support is still as important as is the case for in situsynthesis in order to guarantee the mechanical, thermaland chemical stability of the composite membrane.

The above constitutes the main dierence between zeo-lite powder and zeolite membrane synthesis as well asone of the diculties inherent to the preparation of zeolitemembranes, namely the existence of an additional parame-ter, the substrate and the linking of zeolite crystals to thatsubstrate so as to obtain a continuous thin composite zeo-lite membrane. Various techniques have been developed tofacilitate nucleation and crystal growth on the substrateand to tailor the interaction between the zeolite layer andthe substrate.

It has been well established that the quality of the under-lying support determines, to a high degree, the quality of

206 E.E. McLeary et al. / Microporous andthe selective membrane layer on top. A thin zeolite lm isless likely to adhere in a continuous fashion to a roughor large-pore substrate, therefore whenever attempting toprepare a supported zeolite membrane; one of the rststeps taken is to ensure that the substrate surface issmooth. Smooth porous surfaces for deposition of a zeolitelayer could be created in its simplest form by mechanicalpolishing of the substrate [84,118]. However this methodis tedious and repetitive while more importantly, the pol-ishing of tubular support interiors are unfeasible. Morerecently the deposition of a thin meso-/micro-porous lmon the support have been used to create a smooth surfacefor zeolite lm growth. The layer has the additional benetof serving as a diusion barrier, preventing the zeolite layerfrom penetrating the support, which would result in alonger eective diusion path, whilst also protecting thesupport against possible leaching [64]. Lai et al. [99] dip-coated an a-alumina support with a mesoporous silicalayer according to the method developed by Tsai et al.[119] to improve the surface nish of the substrate for seedcrystal deposition. They reported not only and improvedux due to a shorter eective diusion path, but alsoincreased selectivity partly due to the elimination ofstress-induced crack formation during calcinations. A p-xylene/o-xylene selectivity as high as 400 at a p-xylenepermeance of 3 107 mol/(m2 s Pa) with an essentiallyb-oriented MFI lm of 1 lm was obtained.

Hedlund et al. [103,120] reported what they termed atwo-step support masking technique to prevent supportinvasion and leaching. They applied a coating of PMMAon the surface of the support and plugged the pores ofthe support with a polyethylene wax. The PMMA layerwas removed by rinsing in acetone for a week while thepolyethylene wax was later removed during calcination.A monolayer of colloidal nucleation seeds was adsorbedelectrostatically on the support, followed by hydrothermalgrowth, producing a defect-free lm, although grainboundaries are still clearly visible, with a thickness of0.5 lm. High-pressure xylene separation tests were carriedout at 400 C at 100 kPa hydrocarbon partial pressure(200 kPa total pressure). The p-xylene/m-xylene selectivitywas 13 at a p-xylene permeance of 1.1 107 mol/(m2 s Pa).

One of the challenges faced during in situ synthesis isensuring a high nucleation site density on the support,often giving rise to higher lm thickness than desired toclose all defects. Techniques that have been used to ensurethat nucleation takes place on the support are multitude.

The adherence of the zeolite crystals to the support sur-face is to a large extent determined by the hydrophilicity ofthe support surface, e.g. the number of OH-groups pernm2. Treatment of the support with NaOH in order toincrease the number of surface hydroxyl groups wouldtherefore impart the support with more nucleation pointsas well as sights where crystals could adhere by means ofVan der Waals interactions and H-bonding. Kim et al.reported treatment of the support with trimethylchlorosi-

soporous Materials 90 (2006) 198220lane to create SiCl bonds on the surface of the supportin order to enhance adhesion of a mesoporous layer to

Methe support [121]. Pretreatment of the support surface byimpregnation or spin-coating with the appropriate tem-plate was also shown to direct the formation of crystalliteson the support. Chau et al. found that a coating of a metaloxide (e.g. Fe2O3) on the support surface provided a simpletechnique to control the number and type of nucleationsites available on the support surface [117]. Their resultsindicated that there was a direct correlation between thenumber of nucleation sites and the amount of iron(III)ox-ide present on the surface of the support and allowed thesynthesis of a more complete and uniform zeolite lm. Syn-thesis conditions, such as a highly alkaline synthesismixture, have also been shown to favor a high nucleationdensity [118,122]. In a more recent report of Van den Berget al. UV-radiation was used to increase the number ofdefect sites and hydroxyl groups to promote the hydrophi-licity of a TiO2-coated support. The authors reported anincreased nucleation and the resultant formation of a uni-form, monolithic zeolite A lm, well attached to the sup-port [123,124].

Other approaches that rely on limiting/directing nutri-ent sources or other conditions necessary for synthesis, tothe surface of the support have also been examined. Elec-trophoretic deposition can be used to coat substrates withcharged particles from colloidal suspension. Zeolite parti-cles formed during hydrothermal synthesis assume a nega-tive/positive charge due to electrical double layer eects.These charged zeolite particle would be attracted to a sup-port to which an opposite charge is applied. Oonkhanondet al. made use of this principal to attract ZSM-5 particlesto the surface of a porous alumina tube in order to obtain a1015 lm thick, continuous layer [125]. Mohammadi andPak synthesized a zeolite A membrane from Kaolin thatwas electrophoretically deposited on a cylindrical anodeand treated hydrothermally [126]. Heating only the supportwhile the rest of the synthesis solution is cooled would ruleout nutrient depletion by competing nuclei and crystalgrowth in the bulk solution and result in crystallizationbeing limited to the support surface. Yamazaki and Tsuts-umi used a plate heater to apply heat to the substrate areaalone with a static solution, as well as a circulated solutionsystem [127]. In both scenarios zeolite membrane forma-tion was not accompanied by powder formation in the bulksolution. Deposition of lms within a substrate can beachieved by using the countercurrent reactor conguration,where each reagent enters from the opposite side of thesubstrate. This method would eectively eliminate nucle-ation and growth from occurring outside the support[128]. The vapor phase transfer synthesis method is a vari-ation of the in situ synthesis method, developed by Xu et al.that consists of two steps: covering the support with a syn-thesis gel and crystallization of the dried gel under autoge-neous pressure. Since one of the nutrient sources is limitedto the support surface, zeolite membrane formation wouldalso be limited to the support surface [129,130].

E.E. McLeary et al. / Microporous andSeeded synthesis tends to produce continuous lms a lotmore readily and with better reproducibility due to bettercontrol over nucleation site density. One of the determiningfactors for the successful synthesis of a thin, defect-freezeolite lm on the support with this two-stage method, isthe application of a thin, uniform and continuous layerof seed crystals to the support. The simplest and often usedmethod is to apply seed crystals to the substrate withmechanical rubbing [130,92]. This method is not ideal how-ever since it is quite dicult to obtain a continuous andeven seed layer. Several authors applied seed crystals tothe support by dipcoating the substrate in a suspensionof zeolite particles, followed by drying at room tempera-ture and calcination in order to x the crystals to the sup-port surface. This process is often repeated a few times inorder to ensure a suciently high coverage of the supportwith zeolite seed crystals [84,131,132]. Electrostatic attrac-tion could be used to limit the number of times the dipco-ating procedure has to be repeated. This involves chargemodication of the substrate surface by adsorption of ananionic or cationic polymer, which would then eect theelectrostatic attraction of colloidal zeolite particles insuspension to the surface of the support [115]. Theelectrostatic deposition process generally achieves a highcoverage of the substrate with well-adhered particles andis one of the most-eective techniques developed to datefor seed crystal deposition. Electrophoretic deposition(EPD) oers a way to coat a substrate uniformly with avariety of charged particles without the need to pretreatthe substrate. Seike et al. [133] prepared a zeolite Y mem-brane through EPD of NaY zeolite seed crystals on astainless steel support. Shan et al. [134] were recently ableto prepare zeolite lms through electrophoretic deposi-tion in a non-aqueous medium, allowing the applicationof a higher voltage and better control over the thicknessand density of the prepared lms. The self-assembly ofmicrometer-sized zeolite crystals on supports via covalentlinkers has received increasing attention during the lastve years. This method of preparation, although promis-ing for yielding well-oriented monolayers, is howeverrather complicated and to date no membrane suitablefor gas separation has been obtained [135,136]. Othermethods that have been investigated for the deposition oforiented monolayers of zeolite seed crystals include Lang-muirBlodgett deposition [137] and pulsed laser ablation[79].

The MFI crystal has an anisotropic two-dimensionalchannel network consisting of straight channels of ellipticalcross-section (0.51 0.54 nm) along the b-direction andsinusoidal channels of nearly circular cross-section(0.54 nm) along the c-direction, Fig. 3. Due to the aniso-tropic nature of this zeolite, the orientation of the crystalswill have a signicant inuence on the molecular sievingperformance.

Preferred crystal orientation could impact the molecularsieving and permeation of the zeolite lm that are crucialfor their application in membrane reactors. Due to the

soporous Materials 90 (2006) 198220 207attractive features of oriented thin lms, there has beenintense eort during the last 5 years to prepare zeolite

lms with controlled orientation and several approacheshave been developed:

(a) Identifying and controlling conditions to promotegrowth rates along certain crystallographic directions. Pro-

lm could be achieved with in situ crystallization throughsystematic optimization of the synthesis composition. Theyfound that within the synthesis system of TPAOH:NaOH:TEOS:H2O:NaCl, OH

/Si and Na+/TPA+ ratios play acritical role in controlling crystal orientation. Forsodium-free or low sodium syntheses, only random-ori-ented lms are formed at OH/SiP 0.64, (a,b)-orientedlms at 0.64 > OH/Si > 0.5 or at 0.2P OH/Si > 0.1,and b-oriented lms at 0.5P OH/Si > 0.2. For a givenOH/Si ratio, addition of Na+ leads to change of crystalorientation from b-oriented, to (a,b)-oriented, to (a,b,c)-oriented, and eventually to random oriented. Wang et al.explained this by the fact that Na+ tends to cause agglom-eration of silicate precursors leading to large aggregates ofrandom-oriented crystals. Wang et al. also found that thecrystallization temperature and time as well as the chemicalnature and roughness of the support are important for ori-

Fig. 3. MFI crystal with stylistic pore structure and crystallographic axis[66].

208 E.E. McLeary et al. / Microporous and Mesoporous Materials 90 (2006) 198220gress towards the fundamental understanding of the originof shape and habit of zeolite crystals will greatly facilitatethe task of engineering zeolite lm microstructure accord-ing to design. Some degree of preferred orientation couldalways be expected since most of the zeolite structure typeshave anisotropic growth rates. MFI crystals most oftenhave a con shape, elongated along the c-crystallographicdirection, indicative of fast growth along the c-axis. Manyauthors have noted that the growth morphology of zeolitevaries with the composition of the synthesis mixture, i.e.composition of the starting mixture, as well as the synthesistemperature. This means that the growth process for eachcrystal face is strongly dependent on the synthesis condi-tions. Systematic variations of MFI synthetic conditionscan lead to particle shapes ranging from symmetric to elon-gated needle or con. Iwasaki et al. [138] and Wang andYan [95] performed a systematic study on the correlationbetween the crystal orientation in MFI lms on stainlesssteel plates and the composition of the synthesis solution.The goal of their respective studies was to show thatmanipulation of crystal orientation in a continuous thinFig. 4. Molecular sieve membranes with small dierences in microentation and lm continuity.By studying the nucleation and growth rates of MFI

crystals along dierent crystallographic directions, Laiet al. were able to manipulate relative growth rates alongdierent crystallographic directions of MFI, and by doingso, obtained highly selective oriented molecular sieve lms[99,139]. Membranes of the high silica molecular sieve MFIwith c-out-of-plane preferred orientation showed low selec-tivity for p-/o-xylene, Fig. 4, left, due to the presence ofgrain boundary defects. MFI membranes with a smalldierence in preferred orientation (c-axis inclined by about35, (h0h) plane normal to the support) showed noevidence for the presence of similar defects at the grainboundaries. These membranes show excellent selectivityfor p-xylene. The relationship between membrane micro-structure and the transport properties of ZSM-5 mem-branes were also investigated by Au and Yeung [100].Experiments conducted by the authors suggested that grainboundaries form the main non-zeolitic pathway in themembrane diusion and their elimination through graingrowth can result in better membrane performance.structure showing drastically dierent performance [97,100].

(b) The second approach involves starting the mem-brane synthesis with oriented seeds and proceeding withthe seeded growth in the absence of further nucleation. Sev-eral dierent strategies have been used for oriented seedlayer deposition. These include dip coating [131], chargereversal of the support with a cationic polymer followedby seed deposition [101,140], and recently there has beena trend to make use of chemical linkers such as iso-cyanatesto covalently bond the seed crystals to the support [135].

Tsapatsis et al. [141] prepared a silicalite membraneby growing a layer of oriented silicalite-1 crystals on a

LTA seed crystals electrostatically on the support. Filmcrystallization on the seeded substrate was eected byhydrothermal treatment in synthesis solution with the samecomposition that was used for the seed crystal preparation.They obtained an essentially continuous 280 nm LTA lmwith the (100) plane of the crystals primarily oriented par-allel to the substrate surface. In 1998 Mintova et al. [143]reported the synthesis of ZSM-5 lms on quartz substratesfrom template free precursors. The substrates were coveredwith a monolayer of seed crystals. These crystals weregrown into continuous lms with thicknesses in the range

E.E. McLeary et al. / Microporous and Mesoporous Materials 90 (2006) 198220 209composite precursor nanocrystalline silicalite/aluminaunsupported lm using controlled secondary growth. Theorientation of the crystals was primarily with the c-direc-tion perpendicular to the support, in other words bothstraight and sinusoidal channel networks ran nearly paral-lel to the membrane surface. Although oriented seed crys-tals give rise to a zeolite layer of the same orientationinitially, it was found that as the lm grew thicker duringsecondary growth, randomly oriented lms formed due toanisotropic growth rates of the dierent crystal faces. In1998 Gouzinis and Tsapatsis [97] further studied thegrowth of an oriented zeolite layer. They succeeded inmanipulating the out-of-plane grain orientation by second-ary growth conditions, in such a way that the c-axis ofthe grains range from being oriented perpendicular to thesubstrate to being oriented at and angle of 35 from thedirection normal to the substrate. More recently Laiet al. [99] succeeded in preparing a primarily b-orientedlayer on a-Al2O3 disks, by following a three-step approach.First the supports were coated with a mesoporous silicalayer, masking the support and providing a smooth layerfor membrane growth (see Fig. 5). This was followed bythe deposition of an essentially single layer of seed crystalsthrough the use of chemical linking groups according to themethod of Ha et al. [135]. Finally the seeded supports werehydrothermally treated at 175 C for 24 h in a synthesissolution containing trimer TPA as structure directingagent. Lai et al. obtained superior o-xylene/p-xylene sepa-ration whilst maintaining high permeances with the abovedescribed membrane.

Hedlund et al. [142] treated an alumina support with acationic polymer in order to reverse the charge of the sup-port. They subsequently deposited the negatively chargedFig. 5. Cross-section and top view of the primarily b-oriented silicalite-1 membthe membranes (top trace) [99].2303500 nm by hydrothermal treatment. The preferentialorientation of the crystals constituting the lm was initiallywith the c-axis close to parallel to the substrate surface.During the course of crystallization this orientation chan-ged to one with the most of the crystals having the axisdirected (as in the case of Tsapatsis et al. [97]) approxi-mately 35 from perpendicular to the substrate surface.In 1999 Hedlund et al. [102] investigated certain parametersin the lm formation process. These included the seedcrystal size, amount of adsorbed seed crystals and lmthickness after hydrothermal treatment of the seeded sub-strates. They concluded that the shape and orientation ofthe adsorbed seed crystals and their growth rate in dierentdirections determine the orientation of the nal lm. Bycontrolling the seed size and amount of seed crystals theycould attain some control of the orientation of the crystalsconstituting the lm.

In 2001 Yeung et al. [86] also succeeded in preparing a(101)-oriented MFI zeolite membrane on seeded supportsby tailoring the synthesis conditions and composition.

(c) Changing the direction of the highest nutrient con-centration from the out-of-plane to the in-plane direction.The presence of a precursor gel can be used to provide highnutrient concentrations on the surface of the substrate.Direct hydrothermal synthesis with this approach canlead to a- and/or b-out-of-plane oriented lms since thefastest growing crystallographic plane (along the c-axis) isnow in-plane, conned by nutrient availability. Essentiallyb-oriented MFI lms, prepared according to this approachwere previously reported on silicon wafer and glass sup-ports by Jansen et al. [144], den Exter et al. [112] andKoegler et al. [106]. However, these lms were often non-continuous.rane, and corresponding XRD trace of the seed layers (bottom trace) and

Me3.2. Reproducibility and long-term stability of membranes

Reliability and durability are key criteria in the processindustry and one of the main obstacles for industrial zeolitemembrane reactors. It is well-known that poor reproduc-ibility of zeolite membrane preparations is a commonlyencountered problem [83] due to the large number of fac-tors that play a role in zeolite membrane formation. Vande Graaf et al. for instance reported that only 4 out of 12silicalite-1 membranes had an acceptable quality. Noacket al. [145] also concluded that reproducibility of mem-brane preparation was severely lacking with only 1030%of preparations producing high quality membranes. Byvarying the synthesis composition and conditions, theauthors could however increase the yield of high-qualitymembranes to 70% of their preparations.

One of the key contributing factors to the diculty ofobtaining reproducibility is the lack of attention that hasbeen paid to temperature trajectories within synthesisreactors. Several authors have shown that the synthesistemperature and prole has a signicant inuence on themicrostructure and the overall quality of the membrane[100,146]. Li et al. [147] obtained notably improved resultswhen use was made of a two-stage temperature synthesis,allowing the formation of a larger amount of nuclei anda resultant continuous membrane. Even though tempera-ture proles within reactors clearly have a major inuenceon the nal quality of the membrane, very few authorshave mentioned synthesis reactor characteristics or temper-ature proles within those reactors. This necessitates there-optimization of synthesis procedures whenever theexperimental setup and conditions are slightly altered.

For the successfully implementation of zeolite mem-branes in industrial processes, permeances and selectivitiesshould also be maintained over long periods of time.Coronas et al. [85] studied the separation properties as afunction of time on stream for several membranes andobserved a reduction in the n-hexane permeance and n-hexane/2,2-dimethylbutane selectivitiy that increased withincreasing operating temperature. The degraded mem-branes could however be regenerated by calcination at ele-vated temperature to obtain their original permeances andselectivities. Van den Broeke et al. [148] studied the repro-ducibility of permeation results for carbon dioxide and therobustness of silicalite-1 membranes prepared by them witha time span of about a year between runs. During this per-iod a large number of temperature and pressure cycles wereperformed, with various gases. Their results indicated onlyminor changes in performance. Van de Graa et al. [83]investigated the long-term stability of a silicalite-1 mem-brane using the n-butane/i-butane permselectivity at30 C as a standard test and found that there was only aslight decrease in selectivity over a period of two years.Studies on the reliability of membrane syntheses and thereproducibility of membrane performance has also been

210 E.E. McLeary et al. / Microporous andconducted by Gora et al. [149] and Hedlund et al. [150]Current eorts to produce reproducible high quality mem-branes overall indicates that a satisfactory success ratecould be obtained with optimization of conditions andcompositions for zeolite membrane formation.

3.3. Ultramicroporous membranes

Zeolite molecular sieves, having high porosities andwell-dened pore sizes in the range of 312 A, are clearlygood candidates for membrane reactors. The diculty toproduce ultramicroporous zeolite membranes howeverremains and is of dual-nature: rstly zeolite membraneswith pores in the 3 A range to separate small gas mole-cules on the basis of size exclusion should be produced,and secondly a method to produce zeolite membranes with-out non-zeolite pores or defects has to be found.

Until recently the attention of the research communityhad been focused on MFI zeolites due to its suitabilityfor the separation of several industrially important rawmaterials. The development of zeolite membranes withchannel sizes small enough to achieve high separation fac-tors for gas mixtures is however also attractive for theseparation of small gas molecules such as carbon dioxide(CO2) and methane (CH4) which typically have small dif-ferences in adsorption strengths. The small pore size of,for instance, zeolite NaA (0.41 nm) could improve separa-tion of small gas molecules such as nitrogen (0.364 nm) andoxygen (0.346 nm) by exploiting dierences in size betweenthem. Xu et al. [151] made use of this fact in order to sep-arate nitrogen and oxygen and achieved a permselectivityof 1.8 for O2/N2. Further investigation however indicatedthe presence of defects with a larger diameter than the poresize of zeolite NaA. More recently Kazemimoghadam et al.[152] investigated the dehydration of water/1-1-dimethyl-hydrazine mixtures by zeolite NaA and hydroxy sodalitemembranes. Separation factors of >10000 were obtainedfor both NaA and hydroxy sodalite membranes at 25 Cand a pressure of 1.5 mbar on the permeate side. Thehydroxysodalite membrane had a slightly lower ux butalso a higher selectivity due to its smaller pore size. Othersmall pore zeolite membrane that have been investigatedinclude the zeolite P membrane (examined by Dong andLin [75] for the separation of H2/Ar, CH4/Ar and H2/SF6), zeolite T [153] and a DDR type zeolite membrane,examined by Tomita et al. [154]. Tomita et al. concludedthat the prepared DDR membrane had few defectsand worked well as molecular sieving membrane, obtaininga separation factor of 220 for a 1:1 CO2/CH4 mixtureat 28 C and 0.5 MPa total gas feed pressure. Poshustaet al. [76] demonstrated that a SAPO-34 membrane alsohold promise for the separation of light gas molecules.The authors achieved a CO2/CH4 separation factor of 30at 27 C.

The intercrystalline diusion via defects in the structureof the zeolite membrane has a large negative impact on theperformance of the membrane. In Fig. 6, Nelson et al. [155]

soporous Materials 90 (2006) 198220showed that the ux through the imperfect membrane has asimilar functional form to that for the perfect membrane,

Mebut with a maximum ux that is about ten times larger.This increase in ux was attributed to the decrease in theeective thickness of the membrane due to the presenceof voids. Since the eective membrane thickness is muchsmaller than the actual thickness Nelson et al. also predictlower permselectivities for this imperfect, anisotropic mem-brane compared to those for defect-free membranes.

Since defect size and defect density determines the sepa-ration performance of the membrane:

(a) The number and size of defects that form duringmembrane crystallization and post-synthesis thermaltreatment have to be limited to a minimum.

0.005

0.004

0.003

0.002

0.001

0.000

0.05 0.10 0.15 0.20 0.25 0.30 0.35

Perfect membrane

Temperature kBT/Ex

Flux

J(T

)

Anisotropy factor = 10Spacing between adjacentdefects = 50

Fig. 6. Comparison of uxes through an anisotropic imperfect membranewith nanoscopic defects and a perfect membrane as a function oftemperature [153].

E.E. McLeary et al. / Microporous and(b) The defects that do form should be repaired througha suitable technique.

Several groups have shown the deleterious eect of cal-cination on the membrane quality and performance. BothDen Exter et al. [112], Geus et al. [156] and Dong et al.[157] found that compression stresses that developed dur-ing cooling after calcination induced cracks in the sup-ported zeolite lm. In response to the mentioned ndings,endeavors to prepare zeolite membranes in the absence ofan organic template have been reported by for instanceMintova et al. [143] and Hedlund et al. [150] reported thein situ synthesis of a MFI membrane while Lai and Gav-alas [158], Pan and Lin [159] and Lassinanti et al. [160]reported the preparation of a MFI membrane accordingto the secondary growth method. Most authors reportedreduced ux and slightly increased selectivity.

Eorts that have been made to eliminate defects that didform during synthesis, include post-synthetic coke treat-ment [161], chemical vapor deposition of silica by reactionwith silicon alkoxide or silylation agents and treatmentwith a silane coupling reagent [162]. In a study performedby Nomura et al., the separation selectivity for a n/i-C4H10 mixture increased from 9.1 to 87.8 after modi-cation of the membrane pore structure by a TEOS-O3counter-diusion chemical vapor deposition technique[163,164]. Van den Broeke et al also demonstrated thatthe permeation behaviour of a silicalite-1 membrane canbe modied selectively by the reaction of a silane (CH3)3-ClSi (TMCS), with accessible zeolitic OH-groups [148].Xomeritakes et al. [165,166] selectively sealed cracks thatformed during the calcination of MFI membranes by dip-coating the membranes in a surfactant-templated silica.After drying, the mesostructured surfactant-silica layerthat formed on top of the MFI membrane exhibited exten-sive cracking and could be easily peeled o by blowing themembrane surface with compressed air. However, the solinltrated inside large cracks during dip-coating, perma-nently plugged the cracks after transformation to an imper-vious surfactant-silica composite and improved themembrane selectivity. Although this method is successfulin increasing the selectivity, it could lead to pore blockingand is therefore done at the cost of the ux. Van den Bro-eke et al. reported a reduction in n-butane ux by a factor17 after silanation.

Lai et al. [99] recently made a large contribution to theart of membrane synthesis when the authors showed thatit is possible to prepare highly selective zeolite membraneswith a very low defect density. They were the rst to reporta zeolite membrane showing excellent separation with highpermeance that relies on discrimination between moleculeson the basis of dierences in size and shape. The orientedlm of the siliceous zeolite ZSM-5 prepared, showed p-xylene/o-xylene selectivities of 200800 whilst maintain-ing high ux.

3.4. Addressing the problem of sealing

The property of inorganic zeolite membranes that setthem apart from polymeric and amorphous membranes istheir thermostability, which allows operation under severeconditions as well as the ability to be reactivated whichin turn gives rise to increased life expectancies for thesemembranes. It is however, generally acknowledged thatthe high-temperature application of zeolitic membranes isstrongly limited by high-temperature resistant sealing ofthe module by which feed and permeate are separated fromeach other [167]. Despite the technical importance of high-temperature seals for zeolite membrane research, studieswith emphasis on high-temperature seals themselves areseldom reported in literature.

One possibility is the parting of the locations of sealingand separation in order to be able to apply already knowntechnology for sealing at low temperature. This howevernecessitates a much more complex membrane module inwhich a large temperature gradient exists over the dierentsections (that for separation and that for sealing) of theequipment. This has been achieved by providing a cooling

soporous Materials 90 (2006) 198220 211system (e.g. water cooling) in a fully heated apparatus[168].

3.5. Up-scaling

Up-scaling is faced with a number of challenges; such asthe synthesis of large continuous membranes. Althoughseeded synthesis may improve nucleation density andtherefore increase the ease of synthesizing a large continu-ous membrane, the two-step synthesis procedure also posesproblems and decreased ease of synthesis when one consid-ers for instance the application of the seed layer in a uni-form and continuous way on a large scale.

Temperature control in large synthesis reactors isanother subject that needs more thorough investigation.Larger volumes would lead to the existence of a large tem-perature trajectory within the reactor, which means thatsynthesis conditions will have to be optimized for largervolume preparations. Obtaining a clear picture of the eectof synthesis temperature as a parameter on the nucleation

MeOf the many joining processes available, brazing is oneof the most established techniques for ceramic to metaljoining. In its simplest form, a brazing alloy that wetceramics is applied to the support surface and subsequentlyheated in a controlled atmosphere such as nitrogen orargon [26]. Due to large dierences in thermal expansioncoecients between the brazing material and the ceramic,this process often generates high residual stresses in theceramic with resultant cracking and an inability to formgas impermeable seals. Another innovation has a ceramicincorporated in the braze alloy, to both increase itsstrength and reduce its coecient of thermal expansion[169].

Ceramic glazes can also be used to seal the porous sur-face around the ends of a ceramic membrane. Ceramicglazes will limit the dierence in thermal expansion coe-cients between the seal and the membrane and reduce thedevelopment of thermal stresses. However some ceramicglazes have a lower chemical resistance and could dissolvein the high pH zeolite synthesis solution. Reed et al. [170]addressed the dilemma in their patent for a gas imperme-able, glass-based glaze that can withstand high tempera-tures, for sealing the ends of a porous tubular aluminasupport containing a microporous separation membraneon the inside.

Geus et al. [113] solved the problem by preparing MFImembranes on porous, sintered stainless steel supportswithin stainless steel membrane modules in order to per-form (high temperature) permeation experiments whilstavoiding high-temperature sealing by the formation ofthe zeolite layer on both porous and non-porous stainlesssteel parts. Although the as-synthesized layers were foundto be gas-tight, even for small molecules such as neon, thismethod severely complicates the synthesis procedure. LaterGora et al. [149] obtained a gas-tight seal by preparing zeo-lite A and MFI membranes on porous stainless steel sup-ports to which swagelok connections had been welded.

Another approach, often used for lab-scale reaction sys-tems, involves the lamination of the ends of the membranescombined with the use of graphite O-ring seals. The high-temperature enamel (Aremco 617) that can tolerate tem-peratures up to 1100 K was for instance used by Wonget al. to coat the tube ends while viton or graphite O-ringswere used along with modied compression ttings to pro-vide leak-free sealing [146]. The major problem of this tech-nique is that, if not properly designed, the system canexperience substantial thermally induced stress due to thedierences in the thermal expansion coecients betweenthe seal, the ceramic support and the zeolite membraneand this could cause the membrane to crack during heatingor cooling.

Recently Min et al. [171] reported a new approach tomembrane module design using a porous metal supportand a tapered sealing technique. To perform the perme-ation measurements of single gases and xylene isomers at

212 E.E. McLeary et al. / Microporous andtemperatures of up to 723 K, Min et al. developed an all-stainless steel module in which the membrane modulewas constructed by tightly mounting the sintered metalsupport into a tapered hole to fasten the metal support inthe module as shown in Fig. 7. Afterwards the membranemodule and support was placed in a stainless steel auto-clave and a hydrothermal synthesis repeatedly carried outat 180 C until the zeolite membrane was rendered imper-meable to N2. By following the tapered sealing method,no special sealant was needed to seal the metal supportand membrane module in order to perform the permeationexperiments above 473 K.

It does seem as if some progress has been made in thehigh-temperature sealing of zeolite/ceramic membranes,especially at laboratory scale. The gas-tight, high-tempera-ture resistant sealing of tubular zeolite membranes in anindustrial scale module, where each individual tube in atube bundle has to be sealed and xed to metal tube sheetsin the module, with dierences in thermal expansion, whilststill preserving the integrity of the membrane lm on theceramic support, remains problematic and a possible bot-tleneck for this technology.

He

Back pressureregulator

Zeolite synthesized on a porous stainless steel tube Tapered sealingtechnique

Permeate + He

FeedP

Fig. 7. Schematic cross-sectional view of the membrane module [171].

soporous Materials 90 (2006) 198220and crystal growth rate of zeolites on a support is very dif-culty due to insucient/incomplete information that are

Megiven regarding the subject in reports of membrane synthe-ses. Microwave heating could provide better control overthe temperature-time prole. Compared to conventionalhydrothermal synthesis, microwave synthesis of zeolitemembranes provide fast homogeneous heating throughouta reaction vessel and more simultaneous nucleation on thesupport surface, uniform small zeolite crystals and a result-ing thin membrane, as well as a reduction in processingtime and energy cost compared to conventional heating[172].

Membrane reactor modules will have to be designed inorder support large surface area membranes, especiallywhen dealing with potentially fragile ceramic units. Easeand eectiveness of sealing inside the module will also needattention.

3.6. Cost considerations

The estimation of the feasibility of a membrane reactorprocess is not merely as straightforward as the comparisonof yield and selectivity with that of a xed bed process(although this is the approach generally used) and actuallyrequires a full economic assessment. However, due to thefact that zeolite membrane technology is relatively newand very few long-term commercial processes exist, an eco-nomic evaluation of a zeolite membrane reactor process isvery dicult and reports of such evaluations in literatureare scarce.

An initial study of the limited number of cost assess-ments of zeolite membranes and zeolite membrane reactorsthat have been reported in literature, paints a rathergloomy picture for the future of zeolite membrane reactortechnology. Costs of about US$3000/m2 for zeolite mod-ules of which 1015% is contributed to the membrane itselfhas been reported by Caro et al. [66]. Meindersma and deHaan [173] concluded in a feasibility study done by themfor the separation of aromatics from Naphtha feedstocks,that unless membrane module costs were reduced by afactor of 10 and the ux were increased by a factor of 25the investments would be uneconomical. Tennison alsoreported that due to selectivity limitations of zeolite mem-branes, membrane processes are uneconomical and a con-siderable reduction in membrane costs is required tomake such processes feasible [174]. Tennison emphasizedthat very few processes would be able to tolerate costs ofmore than 1000/m2 and operation would also occur underfar more demanding conditions than were generally used inmodelling studies [175].

Besides variable and xed costs in processes, increasingconsideration will have to be paid in future to the costs forminimizing the environmental damages of manufacturing.The disposal of toxic or dangerous waste, such as spent cat-alysts and chemicals, easily amounts to US$250US$750per ton [176]. It is therefore critical to minimize waste pro-duction and emission, both from a conservation responsi-

E.E. McLeary et al. / Microporous andbility as well as a cost perspective. Zeolites and zeolitemembrane reactors are ideally suited for environmentallyfriendly operation and their respective properties suggestthat they will have a key role to play in sustainable processtechnology in the new millennium.

The economics of a plant could be improved by improv-ing the overall selectivity and the productivity of the plant.Zeolite membrane reactors are known to be benecial forproduct selectivity and using zeolite membranes/catalysts,which have an improved resistance to deactivation andcould already separate species that could lead to deactiva-tion, before reaching the catalyst, could limit plant down-timethereby increasing productivity. The losses andtransfers of energy, which dictate the investment costs,can be potentially minimized by zeolite membrane reactortechnology by maximizing the reaction selectivity and theconcentration of the various streams, and by minimizingchanges in temperature.

Therefore, although at rst glance economic feasibilityof zeolite membrane reactors seems unattainable, thereare a lot of possible benets that should be taken intocareful consideration and which will play an increasinglyimportant role in future developments. In light of theabove as well as the recent reports of submicron, highlyselective, high ux [99,103,142], reproducible, and reducedcost membranes [177], economic feasibility might well bereached.

3.7. Multicomponent transport and separation behaviour

Transport in zeolite membranes is a complex processthat is governed by adsorption and diusion. The irregularnature of the zeolite membrane with intercrystalline pores[155], and the further contribution of a support layer tothe permeation resistance [178] add to the complexity ofthe process. In order to employ zeolite membranes on alarge scale, improved experimental methods for the mea-surement of intracrystalline diusion has to be developedand our understanding of the mass transport properties,the factors governing separation behaviour and our abilityto predict the permeation of molecules through these mem-branes have to be increased.

The diusivity in zeolites depends strongly on the porediameter, the structure of the pore wall, the interactionsbetween the surface atoms and the diusing molecules,the shape of the diusing molecules and the way the chan-nels are connected as well as, most important in mixtures,adsorbateadsorbate interactions [179]. The quantitativeprediction of diusion rates inside zeolites with modellingtechniques is often hard to relate to the aforementionedproperties and the underlying microscopic mechanisms[180,181]. A contributing factor to the diculty of diusionprediction is the large discrepancies that often existbetween diusivities determined from dierent experimen-tal techniques [182184].

When used as a catalyst or molecular sieve, at least two,and often more, species are present inside the zeolite pore

soporous Materials 90 (2006) 198220 213structure. A number of studies have indicated that mixtureseparation selectivities could not be predicted from the

utarm

Mepermeances of single components alone since competitiveadsorption, pore mouth blocking and/or single le diu-sion may govern the molecular transport through thezeolite channels, Fig. 8 [178,185187]. However despite itspractical importance, mixture transport through zeolitesand zeolite membranes has only recently received moresubstantial attention. This can be contributed to the di-culty of experimentation with mixtures as well as the expo-nential increase in complexity of simulations with anincreasing number of components.

Currently two classes of experiments to measure intra-crystalline diusion through zeolites can be distinguished;macroscopic techniques, or visible uptake measurements(gravimetry, volumetry, Fourier transfrom infrared (FTIR)spectroscopy), including the frequency response techniqueand zero-length-column chromatography and secondlymicroscopic techniques such as pulsed eld gradientNMR (PFG NMR) [188,189] and quasi-electron neutronscattering (QENS) [190]. Unlike macroscopic techniques,

0 50 100 1500

5

10

15

20

25

hydrogen

n-butane

Time [s]

Flux

[m

mol m

-2 s

-1 ]

Fig. 8. Breakthrough curves of the (a) single components hydrogen and n-bthe dierence in uxes of components in single component and mixture pe

214 E.E. McLeary et al. / Microporous andthe microscopic techniques take place under equilibriumconditions. The dierence in diusivities obtained by thesetwo classes of techniques has sparked further developmentof experimental techniques to measure diusion such as thefast pulse technique for the simultaneous determination ofboth the pore diusion coecients in, and the rate con-stants for adsorption and desorption at zeolitic materialsreported by Nijhuis et al. [191], Schumacher et al. [192]reported tracer-exchange experiments with positron emis-sion proling (TEX-PEP) which allowed the measurementof self-diusion coecients of adsorbates in zeolites on amacroscopic time-scale and at elevated temperature; whileZhu et al. [193] used the novel tapered element oscillatingmicrobalance (TEOM) technique to determine the intra-crystalline diusivities of n-hexane, 2-methylpentane, 3-methylpentane and 2,3-dimethylpentane in silicalyte-1and obtained good agreement with ZLC results.

A number of simulation techniques have been used andsometimes combined to describe mixture transport throughzeolites and zeolite membranes such as Monte-Carlo [194],molecular dynamics (MD), transition-state theory (TST),Fick and Onsager formulations and the MaxwellStefanmodel to name a few. Among these it is generally acceptedthat the generalized MaxwellStefan formulation oers themost convenient and the nearest quantitative prediction ofmulticomponent diusion through zeolite membranes[61,181]. This model is based on the principle that frictionalinteractions (characterized by MaxwellStefan diusivities)experienced between dierent molecules in a mixture aswell as with a solid matrix, balances the driving force (oftenthe chemical potential gradient in the case of membranes)exerted on each molecule and gives rise to the dierentvelocities of molecules. The strength of this model lies inthe fact that it intrinsically encompasses intra-crystallinediusion phenomena as well as sorption processes, allow-ing it to predict multicomponent diusion based on purecomponent MaxwellStefan diusivities and mixtureadsorption isotherms. Congurational-bias Monte-Carlo(CBMC) simulations demonstrated that due to the ine-

Time [s]0 50 100 150 200 250 300

0

1

2

3

Flux

[mmo

l m-2 s

-1 ]

hydrogen

n-butane

ne and a hydrogen/n-butane mixture (95 kPa/5 kPa, T = 295 K) indicatingeation [178,185].

soporous Materials 90 (2006) 198220cient packing of higher branched alkanes and aromaticmolecules, their saturation loadings will be lower than thatof linear short alkanes and these molecules might even beexpelled from the zeolite, as a result of congurationalentropy eects [195]. Adsorption isotherms of mixturesconsisting of components with widely dierent saturationloadings would therefore show an inection, which is notdescribed by multicomponent Langmuir isotherms in athermodynamically consistent way. Kapteijn et al. [196]extended the generalized MaxwellStefan equations formulti-component diusion to also account for moleculeswith dierent saturation loadings by using the idealadsorbed solution theory (IAST) of Myers and Prausnitz[197] which shows good agreement with adsorption iso-therms predicted from CBMC simulations [198]. Krishnaand Paschek [199] made use of CBMC simulations todevelop the required mixture isotherms and followed theapproach of Kapteijn et al. [196] using the MaxwellStefantheory for describing hydrocarbon mixture diusion acrossa silicalite-1 membrane. Both authors emphasized the inu-

Meence of mixture non-ideality eects on separation selectivi-ties and recommended the use of the IAST in the MaxwellStefan formulation in order to account for size and cong-urational entropy eects.

4. Catalytic activity of zeolites in membrane reactors

The high internal surface area of zeolites, coupled withthe ability to control the number and strength of acid sitesand shape and size selective eects, allow the application ofzeolites as versatile heterogeneous catalysts and catalystsupports. The intrinsic catalytic activity of zeolites coupledwith the possibility to tune adsorptive properties makesthem good candidates for bringing about simultaneousreaction and separation. The symbiosis that exists betweenthe catalyst and membrane in the membrane reactorhowever also limits the degrees of freedom of both themembrane and the catalyst. Besides an appropriate mem-brane, membrane reactors will therefore also require thedesign of a customized catalyst, owing to the dierent con-ditions that catalysts are exposed to in membrane reactorscompared to conventional reactors.

One of the main aspects that received attention is thecorrelation of the membrane throughput with the catalystactivity. Van Dyk et al. [200] did a comparative study ofthe dehydrogenation of isobutane in an extractor-typeCMR tted rstly with a MFI membrane and secondlywith a Pd-membrane, which showed superior performancecompared to the zeolite membrane, and found that thereactor performance was in fact limited by the catalyst.The authors concluded that in order to draw the full benetof the separationreaction synergism, very active catalyststhat were able to comply with the high extraction abilityof the membrane had to be developed. Also Miachonet al. [201] highlighted that although a catalyst could beactive enough to achieve equilibrium in a conventionalreactor this was not necessarily the case in an extractortype membrane reactor. Membrane reactors might alsorequire catalysts with improved stability. Such is the casefor catalysts used for dehydrogenation reactions in anextractor-type membrane reactor, where selective hydrogenremoval might in fact promote coke formation due to adecrease in the H/C ratio and result in a decrease in cata-lytic activity. Larachi et al. [202] for instance reported thatan increase in conversion during methane aromatizationdue to hydrogen removal from the reaction zone was osetby a drop-o ascribed to a carbon build-up on catalyticactive sites. The authors were however able to regeneratethe catalytic sites by an interruption in permeation witheither autogeneous hydrogen or an external source ofhydrogen to reduce the deposited carbon.

The presence of a membrane however does not alwaysadversely aect the catalyst function. It could also protectthe catalyst from poisons and increase selectivity by sup-pressing undesirable side reactions from taking place. Lai

E.E. McLeary et al. / Microporous andet al. [203] reported one such case when they investigatedthe Knoevenagel condensation reaction of benzaldehydeand ethyl cyanoacetate to produce ethyl 2-cyano-3-phenyl-acrylate. Here, the presence of a ZSM-5 membrane in aPBMR and microreactor enabled the continuous and selec-tive removal of water during the reaction, protecting theCesium-exchanged NaX faujasite catalyst from deactiva-tion by the water which is formed as byproduct duringthe reaction. Espinoza et al. [204] applied the same princi-ple to the FischerTropsch process, protecting the cobaltand iron-based catalysts from deactivation by water pro-duced during the reaction. An increase in the contact timeor eective reactor volume due to product extraction fromthe reactive zone and a resultant improvement in conver-sion and yield could also be eected by the presence of amembrane. The dimerization of i-butene into branched oct-enes not only produces i-octenes, but also undesired C12 oreven C16 species. Piera et al. [19] reported that by removingthe C8 intermediate product from the reaction environmentthrough a silicalite-1 membrane further reaction to giveundesired C12 and C16 compounds was prevented, and anincreased residence time of the reactants eected, conse-quently, increasing both the i-butene conversion and i-octene reaction selectivity considerably with respect to aconventional FBR.

Although inert membranes simply function as a distrib-utor of reactants or a separator of products, inorganicmembranes with catalytic activity are able to simulta-neously function as a distributor, a separator and a cata-lytic reactor. The benet most often reported by authorsis the improved selectivity and resistance to deactivationof catalytic membranes as compared to the same catalyst,employed in a packed bed conguration. In a study byYeung et al. [82] the eect of catalyst location in membranereactors was investigated. The authors demonstrated thatfor a PBMR, a CMR and a xed bed reactor (FBR), fora rst-order reversible reaction, a non-uniform distributionof catalyst, located on the feed/external side in either themembrane (CMR) or the pellet (PBMR and FBR) gavesuperior performance compared to uniformly distributedcatalyst. In addition it was found that the performance ofthe CMR and PBMR was identical when the catalyst loca-tion is at the feed side of the membrane (for the CMR) orat the external surface of the pellet (for the PBMR), due tothe absence of mass transfer resistance. These two mem-brane congurations exceeded the performance of theFBR conguration over the full range of residence times.

Santamaria and co-workers [205] also compared threereactor congurations for the catalytic esterication ofethanol with acetic acid, loaded with the same amount ofcatalyst, namely: (i) packed bed reactor, with the H-ZSM-5 catalyst packed as powder inside an impervioustube, (ii) packed bed membrane reactor (PBMR), withthe H-ZSM-5 catalyst packed as powder inside a tubularNa-ZSM-5 membrane which acted as an extractor of prod-uct, (iii) a catalytic membrane reactor (CMR), where therewas no catalyst other than the H-ZSM-5 membrane itself

soporous Materials 90 (2006) 198220 215resulting in the ecient integration of product extractionand reaction. As a result the conversion obtained at the

Mesame feed rate and catalyst loading was greater than inconventional xed bed reactors, or even in reactors wherethe zeolite membrane was kept separated from the catalyst.

When Liu et al. [52] applied a La2NiO4/NaA zeolitecomposite membrane to CH4/CO2 reforming, the conver-sions of CH4 and CO2 in a catalytic membrane reactor(CMR) were remarkably higher than those over a xed-bed reactor, while coke deposition was lower. Here themembrane also acted as an extractor of the products COand H2 resulting in a decrease of carbon depositionalthough the separation selectivity was quite low. Masudaet al. [206] applied a ZSM-5 type zeolite membrane to thecatalytic dehydrogenation of methanol to olens. In thisinstance the membrane served as a contactor, allowingthe control of the residence time of species inside the reac-tive zone. Optimising the reaction rate and the diusionrate in the membrane could minimize further dehydrogena-tion of the olens to aromatics. A selectivity of 8090% forhigh methanol conversions of 6098% was obtained. Tor-res et al. [207] made use of a zeolite-b membrane for theoligomerization of isobutene, which is an acid catalysedreaction. Also in this application, the membrane did notfunction as a separator, but was used as a contact medium,with which the residence time could be controlled, limitingsecondary reactions and improving selectivity. Comparedto a conventional xed-bed zeolite catalyst, here too, thebeta membrane reactor showed improved performanceand resistance to deactivation.

The development of mesoporous molecular sieve lms,such as MCM-41 and UTD-1 in the past decade has madethe encapsulation of nanometer size guest compounds orclusters possible. Furthermore, the reactive hydroxylgroups on the internal surface of these mesoporous hostscould be easily modied by covalently anchoring of orga-nometallic complexes or grafted by silane coupling agents.These mesoporous membranes expand the range of reac-tions that can be catalyzed by zeolite membranes and thepossible applications in membrane reactors.

5. Applications of zeolite membrane reactors

In the majority of zeolite-based membrane reactor appli-cations, the zeolite membrane used, is only applied to sep-aration and is not catalytically active. An example of this isthe dehydrogenation of isobutane to isobutene reported byCasanave et al. [208]. They applied a MFI zeolite mem-brane supported on a mesoporous alumina tube to thedehydrogenation reaction of isobutane to isobutene withmodest gains in yield; in 1999 Casanave et al. [209,210]resumed their study on the dehydrogenation of isobutenethis time making use of two sweeping modes: co-currentand countercurrent and varying the sweep and ow rates.The lower the feed and the higher the sweep ow, thehigher the conversion. High sweep ows is however eco-nomically unfavourable for industrial applications and

216 E.E. McLeary et al. / Microporous andtherefore not recommended. Their studies indicated thatthe limiting parameter could be either the membrane orthe catalyst depending on the sweeping conguration thatis used. Although Dalmon and coworkers obtained a cer-tain degree of success applying MFI membranes (10-mem-bered oxygen ring zeolite with 0.56 nm pore diameter) tothe dehydrogenation of alkanes, it seems dicult to gethigh enough hydrogen separation factors to make the pro-cess industrially viable. Since the zeolite membrane mem-branes have pore diameters larger than the sizes of thecomponents to be separated, separation will not be basedon molecular exclusion but on the combination of compet-itive adsorption and the dierent mobilities of molecules,arising from dierences in molecular shape, within the zeo-lite pore [61,196]. Small pore, defect-free zeolite mem-branes with pore sizes between the size of hydrogen(0.29 nm) and n-alkanes (0.45 nm) have yet to be developedto a satisfactory extent. Possible candidates, in addition toLTA, include the 8 membered ring zeolites such as GIS,CHA and SOD.

Van de Graaf et al. applied an inert stainless steel sup-ported, silicalite-1 membrane in a packed bed membranereactor to study the eect of selective product removal inthe equilibrium limited metathesis of propene to etheneand 2-butene and of cis-2-butene to trans-2-butene[211,212]. Depending on the operating conditions that wereused, the propene conversion was 13% higher than the ther-modynamic equilibrium conversion obtained in a conven-tional packed bed reactor. Van de Graaf et al. showed intheir study, that when the separation selectivity of themembrane is not absolute, the performance of the mem-brane reactor is a balance between reactant loss and su-cient removal of the products. They compared the uxthrough the reactor wall (areal time yield, ATY) to the pro-ductivity per unit volume (space time yield, STY) for thesilicalite-1 membrane reactor and found the values to bebetween 20