This information and our technical advice – whether verbal, in writing or by ways of trial – are given in good faith but without warranty and are subject to change without notice. This also applies where proprietary rights of third parties are involved. The information is provided by Covestro AG without assumption of any liability. Our advice does not release you from the obligation to verify the information provided – especially that contained in our safety data and technical information sheets –, to check for updates of any information provided by us and to test our products as to their suitability for the in-tended processes and uses. The application, use and processing of our products and the products manufactured by you on the basis of our technical advice are beyond our control and, therefore, entirely your own responsibility. Our products are sold in accordance with the current version of our General Conditions of Sale and Delivery.
Covestro Deutschland AG Business Unit Coatings, Adhesives and SpecialtiesD-51365 Leverkusen Germany
[email protected] Edition: 2015 · Order-No.: COV00072994 · Printed in Germany
Dispersions
Bayhydrol® Bayhydur® Bayhytherm® Desmodur®
Impranil® Baybond® Dispercoll® Imprafix®
02 Dispersions Dispersions 03
04 – 05 Our Mission: INVENTING FOR YOU
06 – 07 Aqueous dispersions – an innovative and eco-friendly platform
08 – 09 Building blocks for efficiency, supply security and sustainability
Coatings
10 – 13 Bayhydrol® A Aqueous acrylic polyol dispersions for
waterborne 2K PUR & 1K PUR stoving systems
14 – 17 Bayhydrol® UH Aqueous high molecular weight polyurethane
dispersions
18 – 19 Bayhydrol® U Aqueous polyurethane-polyol dispersions
20 – 21 Bayhydrol® UV Radiation curing polyurethane dispersions
22 – 23 Bayhydur® BL, Imprafix®, Baybond® XL Thermally activated polyurethane hardener for 1K waterborne stoving systems
22 – 23 Bayhytherm® Self-crosslinking urethane resins for
1K waterborne stoving systems
24 – 25 Bayhydur® Waterdispersible polyisocyanates
26 – 27 Desmodur® Low viscous polyisocyanates
26 – 27 Desmodur® Flexibilizing polyisocyanates
28 – 31 Impranil® Aqueous PUR dispersions for textile coatings
30 –31 Baybond® PUR dispersions for glass fiber coatings
Adhesives
32 –35 Dispercoll® U PUR dispersions for adhesive applications
36 –37 Dispercoll® C CR dispersions for adhesive applications
38 –39 Dispercoll® S Additives for Dispercoll® C and Dispercoll® U
40 –41 Dispercoll® BL, Desmodur®, Bayhydur® Crosslinker for PUR dispersions
42 –43 Fast-lane access to polyurethane innovations
Contents
Bayhydrol® Bayhydur® Bayhytherm® Desmodur®
Impranil® Baybond® Dispercoll® Imprafix®
Flexible Packaging 05
INVENTINGVISIONS FOR YOU
04 DispersionsAs your leading partner for polyurethane chemistry, we know you are competing in increasingly challenging environments: Your customers are becoming more and more demanding in their expectations for quality, dura-bility, sustainability and aesthetics of products. And they have more choices. For you this means that cost pressure is rising – while innovation cycles are becoming faster and faster.
Helping you to turn this challenge into your competitive advantage is the goal that drives our daily work. We call it: INVENTING FOR YOU. But what exactly are the basic values underlying this promise? What principles enable us to improve your productivity, drive sustainability, ensure reliability and co-create future-proof businesses? First and foremost, we are curious. Because only if we listen closely to you and ask the right questions, we can respond to your individual needs with new, creative and unexpected solutions that make a real difference to you. That’s why inventing for us always starts with thinking about your unmet business challenges. It requires an indepth understanding of your needs along the whole value chain. To make sure: What we invent stands the test of time. Living up to this aspiration requires more than competencies – it calls for a corporate culture of being courageous. A culture that is defined and lived by dedicated people who cooperate to push the boundaries of invention founded on knowledge and experience. Our courage permeates our entire business – from partnerships to business models. This is also reflected in our colorful business philosophy. We appreciate partnerships that go beyond traditional black-and-white ways of acting and thinking. An attitude of open-ness that invites you to co-create new things – rather enabling you than just providing. We are optimistic and resourceful in finding solutions that inspire our customers and partners.
This set of fundamental values adds up to an unrivaled performance orien-tation to constantly strive for the better, be it through big or small changes. A true sense of business regardless of function. And a deep commitment to delivering our promise everyday. Anywhere. Again and again.
INVENTING FOR YOU.
Flexible Packaging 07
Pioneering polyurethane chemistryEver since the discovery by Otto Bayer of the po-lyisocyanate polyaddition process in 1937, Bayer – now Covestro – has pioneered polyurethane chemistry. 50 years ago, Bayer – now Covestro – developed the first applications using polyiso-cyanates for the coatings and adhesives sectors. We work closely with our customers to systemati-cally advance the state of the art in polyurethane technology. Using market-oriented research and development, we specifically adapt our product portfolio to our customers’ increasingly stringent requirements. Together with you, we want to con-tinue our successful journey along this path.
High-performance waterborne portfolioAs one of the leading producers of coating and adhesive raw materials, we offer a comprehensive range of high-grade raw materials for polyure- thane coatings and adhesives. The demand for ecological technology is steadily growing and has greatly accelerated the shift away from solvent-borne coatings and adhesives to solvent-free and waterborne systems. With our ecological techno-logy platform we offer a wide variety of aqueous dispersions for the coatings and adhesives mar-ket. Our mission is to provide competitive advan-tages for our customers: eco-friendly products with superior quality and performance to enable highly efficient coating and bonding proces-ses. We are continuously developing innovative dispersions to complement our range of water-borne products based on a variety of chemis-tries – polyurethane, polyacrylate, and polyester dispersions. Depending on your requirements and cost-performance demands, we can offer the most attractive formulation option based on a 1K or 2K system.
Main application areasThe most important areas of application for our waterborne coating raw materials are wood and furniture coatings, metal and plastic coatings for industrial applications, high-grade floor coatings, automotive OEMs, transportation vehicle and refinishing coatings and textile coatings. More- over, we offer specialty products for glass fiber sizes and applications in the paper and printing ink industries.
As a fast-growing and highly promising segment for waterborne coatings technology, UV-curing polyurethane dispersions combine fast curing with excellent coating properties. Firmly estab- lished in wood coatings and growing in plastics coatings, we are continuously extending our range to include additional applications.
Our waterborne adhesive raw materials are first choice in heat-activated bonding applications from 3-D film lamination in the furniture industry and heat lamination for car interior trims to bond-ing footwear. Besides the classical foam bonding market, more and more applications are now emerging for our waterborne contact adhesives.
Why not check out our waterborne product lines: Bayhydrol® and Bayhytherm® for coating applica-tions, Dispercoll® for adhesives applications, Impranil® for textile applications, and Baybond® for glass fiber sizes. In combination with our polyisocyanate crosslinkers Desmodur® and Bayhydur® we offer superior system solutions for 2K or 1K stoving applications.
Aqueous dispersions – an innovative and eco-friendly platform
06 Dispersions
08 Dispersions Dispersions 09
SolutionstoenhanceyourprocessefficiencyNowadays, the quality demands made on indust-rial processes are very high. But at the same time, there is a clear need to cut costs. Both goals can be achieved by increasing process efficiency. The complexity of the processes involved in manufac-turing coatings and adhesives offers us various opportunities to enhance process efficiency. Significant process-optimizing and cost-cutting gains are possible, for example through faster curing and shorter process times. At Covestro we have a wide range of solutions designed to enhance your process efficiency. Why not take advantage of our know-how? These solutions will be good for your bottom line.
Outstandingqualityandsupplysecurity–worldwideCovestro, the world’s leading manufacturer of aliphatic and aromatic isocyanates, offers an extensive range of raw materials and services for manufacturers of coatings and adhesives. This allows the very latest technology to be used extremely effectively for a variety of applications. Thanks to its unique setup and worldwide network of state-of-the-art production sites, R&D facilities and customer technical centers, industry-leading supply chain setup, global orientation and local stocks, extremely large product portfolio, highest
health, safety and environmental (HSE) standards, as well as tailored supply chain flexibility with short lead times, Covestro offers the industry unrivaled supply security and assured quality.
Highperformance–enabledbynatureSustainability drives innovation at Covestro. We are committed to optimizing our manufacturing processes, reducing the impact of logistics, and enabling sustainability along the value chains. Renewable feedstocks offer opportunities for developing more sustainable building blocks for coatings and adhesives – with significant po- tential for reducing the carbon footprint of end products while also reducing our overall depend- ence on fossil-based resources. But to make more sustainable solutions not just possible but also economically feasible, the performance of all our feedstocks needs to satisfy high industry standards. To this end, we are evaluating the use of renewable raw materials and will enlarge our product portfolio with new bio-based and mid- to long-term cost-competitive products, provided the raw materials become commercially available. In all these efforts we are committed to focusing on products that perform at least as well as estab- lished products but are at the same time more sustainable.
Building blocks for efficiency, supply security and sustainability
10 Dispersions Dispersions 11
Bayhydrol® ABuilding blocks for high-end & low-VOC coatings systems that match solventborne performance
Bayhydrol®A145 45 DMEA SN 4/BG 4 3.3Suited for high gloss, clear and pigmented topcoats and primers
Bayhydrol® A 242 42 NH3 0 4 Good chemical resistance, solvent-free
Bayhydrol® A2427 42 NH3 0 2 In 1K as well as in 2K formulations, fast drying, good adhesion to plastics, solvent-free
Bayhydrol®A2457 41 NH3 0 2.5 Good chemical resistance, outstanding water resistance, solvent-free
Bayhydrol® A2470 45 DMEA/ Triethanolamine SN 4/PnB 4 3.9
For high performance clear-/topcoats in various applications; excellent gloss, chemical & weathering resistance
Bayhydrol® AXP2770 44.5 DMEA PnB 3.6 3.9Low VOC version of A 2470; faster dry-ing
Bayhydrol® A2542 50 Triethanolamine PnB 1.1 3.8High gloss, good chemical and mechanical resistance, outstanding water resistance
Bayhydrol® A2546 41 NH3 0 4.8Good chemical resistance, outstanding water resistance, solvent-free, suited for fast sanding sealers
Bayhydrol® A 2601 45 DMEA/ Triethanolamine SN 4/PnB 4 3.9
High gloss, high chemical resistance, very fast drying & curing, but with long pot life
Bayhydrol® A 2646 50 Triethanolamine PnB 1.1 3.8 Faster drying version of A 2542 with similar property profile
Bayhydrol® A2651 41 DMEA PnB 3.4 3 Fast drying, high chemical resist-ance. Excellent grain accentuation (Anfeuerung) on wood
Bayhydrol® A2809XP 48 DMEA PnB 2.0 3.3Suitable for high gloss, clear and pig-mented topcoats and primers; low VOC
Bayhydrol® A2845XP 40 DMEA PnB 3.2 4.5High gloss, good chemical and weather resistance, low thermoyellowing; low VOC
Bayhydrol® A 2846 XP 40 NH3 — 1.5Self crosslinking resin for 1K and 2K, fast drying, good chemical resistance, high hardness and early sandability
= especially suitable
= suitable
NON-VOLAT. CONTENT
APPROX. [%]
CO-SOLVENT CONTENT [%]
IN SUPPLY FORM
1K AIR- DRYING
NEUTRAL AGENT OH CONTENT [%]ON SOLIDS
2K
AUTOOEM
WOOD,FURNITURE
PARQUETTRADE
CORROSION PROTECTION
1K STOVING
INDUSTRIAL METAL
PLASTIC COATINGS
FLOOR WALL
PROPERTIES
Aqueous acrylic polyol dispersions for waterborne 2K PUR & 1K PUR stoving systems
AUTO-REFINISH
LARGE VEHICLES
12 Dispersions Dispersions 13
Bayhydrol® ABuilding blocks for high-end & low-VOC coatings systems that match solventborne performance
NON-VOLAT. CONTENT
APPROX. [%]
CO-SOLVENT CONTENT [%]
IN SUPPLY FORM
NEUTRAL. AGENT
OH CONTENT [%]
ON SOLIDS2K
WOOD,FURNITURE
PARQUETTRADE
CORROSION PROTECTION
Bayhydrol® A2058 42 DMEA BG 2 4.8 Elastic, good adhesion to plastics, low VOC content
Bayhydrol® A2139/2 47 DMEA BDG 2.5 3.8 Fatty acid modified, high gloss
Bayhydrol® A2227/1 42 DMEA BG 8 3.8For topcoats and primers with low co-solvent content (< 5 %) and very good overbaking resistance
Bayhydrol® AXP2469 45 DMEA PnB 7.9 2.5 High gloss, cost effective
Bayhydrol® A2695 41 DMEA/Triethanolamine PnB 7.2 5
For clear-/topcoats with high hardness, very high chemical and weather resistance. For primers and fillers with excellent corrosion protection properties
Bayhydrol® A 2861 XP 53 DMEA PnB 1.2 3.5 Mainly for air- and forced drying coating systems with a very high flexibility
= especially suitable
= suitable
1K STOVING
AUTO-REFINISH
LARGE VEHICLES
INDUSTRIAL METAL
PLASTIC COATINGS
PROPERTIES
Aqueous acrylic polyol dispersions for waterborne 2K PUR & 1K PUR stoving systems
AMP = Aminomethyl propanolBA = Butyl acetateBDG = Butyl diglycolBG = Butyl glycolDMEA = Dimethyl ethanol amineDPGDA = Dipropylene glycol diacrylateEA = EthylacetateEDIPA = Ethyl diisopropyl amineIB = IsobutanolMPA = MethoxypropylacetateNH3 = Ammonia
NMP = N-Methyl pyrrolidone SN = Solvent naphtha TEA = Triethyl aminePAC = PolyacrylatePES = Polyester PGDME = Dipropylenglycol dimethyl etherPnB = Propylenglycol-n-bulyletherPUR = PolyurethaneVP LS ... XP ... = TrialproductsX = Xylene
LEGEND
14 Dispersions Dispersions 15
Bayhydrol® UHFast-drying polyurethanes for tough, durable and elastic coatings. Excellent for 1K and 2K formulations.
Bayhydrol® UH 240 40 Na salt 0 For soft-feel coatings and flexibilization of 1K & 2K industrial coatings
Bayhydrol® UH340/1 40 Na salt 0Highly elastic for the flexibilization of hard PAC and PUR dispersions and 1K industrial coatings; for soft-feel coatings with excellent soft-touch effect
Bayhydrol® UH650 50 Na salt 0Air- and forced-drying basecoats for two-layer plastic coatings; combination resin for soft-feel coatings
Bayhydrol® UH2305 50 Na salt 0Highly elastic dispersion for primers and soft-feel coatings
Bayhydrol® UH2342 35 TEA NMP < 5Self-crosslinking, fatty acid modified, high black heel mar resistance and abrasion resistance, solvent-free alternative (Bayhydrol® UH 2557) available
Bayhydrol® UH2557 35 TEA 0Solvent-free alternative to Bayhydrol® UH 2342; reduced solvent demand in formulation
Bayhydrol® UH2558 37 TEA 0High hardness and abrasion resistance, tough and elastic; well suited for 2K applications
Bayhydrol® UH2593/1 35 TEA 0Self-crosslinking, fatty acid modified, high black heel mar resistance and high hardness, improves drying speed as co-binder
Bayhydrol® UH 2606 35 EDIPA 0 Broad adhesion profile, very high hardness and tough, well suited for 2K formulation
Bayhydrol® UH2952/1 40 DMEA 0For metallic basecoats and primers; excellent stability against hydrolysis
Bayhydrol® UA2856XP 35 DMEA 0For air- and forced-drying metallic basecoats, highly flexible stone chip primers
= especially suitable
= suitable
Aqueous high molecular weight polyurethane dispersions
CO-SOLVENT CONTENT [%]
IN SUPPLY FORM
NON-VOLAT. CONTENT
APPROX. [%]
NEUTRAL. AGENT
AUTOOEM
WOOD,FURNITURE
PARQUETTRADE
AUTO-REFINISHLARGE VEHICLES
INDUSTRIAL METAL
PLASTIC COATINGS
FLOOR WALL
PROPERTIES
16 Dispersions Dispersions 17
Bayhydrol® UHFast-drying polyurethanes for tough, durable and elastic coatings. Excellent for 1K and 2K formulations.
= especially suitable
= suitableBayhydrol® UHXP2592 45 EDIPA 0
Oxidatively drying; free of solvent, drier and anti-skin agent; wood exterior, industrial coatings with low VOC, excellent corrosion protection, primers and high gloss topcoats, crosslinkable e.g. with polyisocyanates, calculated OH-content: 2.1 % (on solids)
Bayhydrol® UH2648/1 35 DMEA 0 Elastic even at low temperatures, broad adhesion profile, especially suitable as co-binder in crosslinking systems
Bayhydrol® UH XP 2660 40 Na salt 0 Combination resin for soft-feel coatings, improved stabili-ty against hydrolysis, solvents and suntan lotions
Bayhydrol® UHXP2719 40 TEA 0 Fast build up of high blocking resistance, good chemical resistance, fast drying, adhesion to aluminium
Aqueous high molecular weight polyurethane dispersions
NON-VOLAT. CONTENT
APPROX. [%]
CO-SOLVENT CONTENT [%]
IN SUPPLY FORM
NEUTRAL. AGENT
AUTOOEM
WOOD,FURNITURE
CORROSION PROTECTION
AUTO-REFINISHLARGE
VEHICLES
INDUSTRIAL METAL
PARQUETTRADE
PLASTIC COATINGS
PROPERTIES
18 Dispersions Dispersions 19
Bayhydrol® UElastic and durable polyurethane dispersions for waterborne 2K & 1K PUR stoving systems.
= especially suitable
= suitable
NON-VOLAT. CONTENT
APPROX. [%]
CO-SOLVENT CONTENT [%] IN
SUPPLY FORM
NEUTRAL. AGENT
WOOD,FURNITURE
PARQUETTRADE
OH CONTENT [%]ON SOLIDS
2K
AUTOOEM
Bayhydrol® U 241 41 DMEA NMP 4.5 2.5 Elastic polyurethane-polyol, suited for primers and topcoats
Bayhydrol® U355 55 DMEA NMP 2 1.5 Very elastic, for soft-feel coatings
Bayhydrol® UXP2698 52 DMEA 0 1.5 NMP- and solvent-free version of Bayhydrol® U 355
Bayhydrol® UXP2750 41 DMEA 0 3.6
For high gloss, clear and pigmented topcoats and primers, outstanding weather resistance, solvent-free marked self-healing effect after scratching
Bayhydrol® U2757 52 DMEA 0 1.8
For plastic coatings incl. soft-feel, universal adhesion profile on plas-tics, solvent-free, good hydrolysis resistance, long pot life. NMP- and solvent-free version of U 241
Bayhydrol® UXP2766 37 DMEA 0 4.0
Very high gloss, especially for pigmented topcoats. Fast drying, chemical resistance and hardness development, low thermoyellowing, solvent-free
1K STOVING
AUTO-REFINISHLARGE VEHICLES
INDUSTRIAL METAL
PLASTIC COATINGS
PROPERTIESAqueous poly-urethane-polyol dispersions
20 Dispersions Dispersions 21
Bayhydrol® UVBayhydrol® UV waterborne UV-curing resins: The most promising technology among the various environmentally friendly wood and plastic coating systems are UV-curing PU dispersions, and coatings based on them are growing fastest in the wood market. Their key property is their similarity to conventional PU coatings so that similar goals can be achieved using similar application methods at similar or faster drying times.
* Flow time (AFAM 2008/105 03) –4 mm cup
= especially suitable
= suitable
TYPE FLOW TIME AT 23 °C (S)*
NON-VOLAT. CONTENT APPROX. [%]
CORK PVC
Bayhydrol® UV 2282 PUR dispersion 39 ≤ 50High chemical resistance, good grain wetting, physical drying. For all-around use (multicoat)
Bayhydrol® UV 2317 PUR dispersion 37 15–80High wet film transparency, good grain wetting, physical drying
Bayhydrol® UV 2280 PUR dispersion 39 12–70 Outstanding physical drying, good standard product for pigmented coatings
Bayhydrol® UV XP2687 PUR emulsion 49 50–500 mPa • sGrain wetting, high solids, good adhesion; especially as primer on wood
Bayhydrol® UV 2689/1 PUR dispersion 42 15–50Highest crosslink density, low physical drying. Especially for clear coats or single layer metallic coats
Bayhydrol® UV XP2690 PUR dispersion 39 20–500 mPa • s Weather-stable, tough; especially suited for wood exterior applications, very fast water release
Bayhydrol® UV 2720/1 PUR dispersion 40 < 200 mPa • sCombines physical drying and highest crosslink density; especially for pigmented systems; thermoformable before UV
Bayhydrol® UV XP2775 PUR dispersion 40 < 300 mPa • s Excellent chemical and stain resistance, in white pigmented topcoats or matte clearcoats
Bayhydrol® UV 2792XP Cationic PUR emulsion 39 < 50 Excellent grain wetting and tannin blocking, good adhesion; especially suitable as primer for wood
FURNITURE
PLASTICS PARQUET PROPERTIESRadiation curing polyurethane dispersions
22 Dispersions Dispersions 23
Bayhydur® BLImprafix®Baybond® XLBayhytherm®The key to high coatings performance in 1K applications.
Thermally activated polyurethane hardener for 1K waterborne stoving systems
Self-crosslinkingurethane resins for 1K water-borne stoving systems
TYPE NEUTRAL. AGENT
NON-VOLAT. CONTENT APPROX. [%]
CO-SOLVENTCONTENT [%] IN
AUTO OEM
GLASSCOATINGS
Bayhydur®BL5335 W-based 35 — MPA 4.5/X 4.5 7.1 For glass and can coatings with good alkali resistance
Bayhydur®BLXP2706 HDI/IPDI-based 40 DMEA 0 8.2 High reactivity (DMP blocked), excellent thermostability (yellowing) and better chemical resistance
Imprafix® 2794XP HDI-based 38 — 0 12.7 High reactivity (DMP blocked), very good thermostability (yellowing), good caustic restistance
Baybond® XL6366 HDI-based 45 — 0 12.5 Medium reactivity (MEKO blocked)
Baybond® XL825 HDI-based 30 — 0 10.0 Low reactivity (CPL blocked) thermostability (yellowing)
Baybond® XL7270 HDI-based 30 — 0 13.1 Low reactivity (CPL blocked) thermostability (yellowing)
Baybond® XL3674XP HDI-based 30 — 0 10.7 Food contact acc. EC 2011/10
BLOCKED NCO CONTENT [%]
ON SOLIDSINDUSTRIAL
METALPROPERTIES
= especially suitable
= suitable
Bayhytherm®3146 Aliphatic, self-crosslinking baking urethane resin 46 DMEA NMP 1, SN/MPA 3 For OEM primer surfacers with high solids content; also
for general industrial coatings
Bayhytherm®3246XP Aliphatic, self-crosslinking baking urethane resin 46 DMEA MPA 2.6/SN 2.4 Further development of Baythytherm® 3146 without NMP
24 Dispersions Dispersions 25
Bayhydur®Easy mixing and high performance: surfactant-free hydrophilized poly isocyanates.
= especially suitable
= suitable
TYPE VISCOSITY AT 23 °C APPROX. [mPa • s]
NON-VOLAT. CONTENTAPPROX. [%]
CO-SOLVENT CONTENT [%] IN SUPPLY FORM
WOOD,FURNITURE
PARQUETTRADE
CORROSION PROTECTION
AUTOOEM
Bayhydur® 3100 HDI-based 100 2,800 0 17.4 Versatile and economic
Bayhydur® 304 HDI-based 100 4,000 0 18.2Versatile use, improved chemical resistance and mixing
Bayhydur® 305 HDI-based 100 6,500 0 16.2 Easy mixing, high gloss
Bayhydur® 401-70 IPDI-based 70 600 30 MPA/X 13.4 Improved hardness, fast drying
Bayhydur® XP2451/1 HDI-based 100 800 0 20.3Low viscous, suited for solvent-free formulations
Bayhydur® XP2487/1 HDI-based 100 5,400 0 20.6 Highest chemical resistance
Bayhydur® XP2547 HDI-based 100 650 0 22.5 High chemical resistance, low viscous, suited for solvent-free formulations
Bayhydur® XP2655 HDI-based 100 3,500 0 20.8Highest chemical resistance, easy mixing, high gloss
Bayhydur® XP2700 HDI-based 65 77 35 PGDME 16.2Ready-to-use supply form of Bayhydur® 305
Bayhydur® XP2759 IPDI-based 70 6,500 30 MPA 15.7Fast drying, easy mixing, high chemical resistance
Bayhydur® 2858XP HDI-/IPDI-based 70 500 30 PGDA 19.0
Fast drying, easy mixing, high chemical resistance
NCO CONTENT [%] ON SOLIDS
AUTO-REFINISHLARGE VEHICLES
INDUSTRIAL METAL
PLASTIC COATINGS
FLOOR WALL
PROPERTIESWaterdispersible polyisocyanates
26 Dispersions Dispersions 27
Desmodur®Best in class: lowest viscosity polyisocyanate crosslinkers.
= especially suitable
= suitable
Low viscous polyisocyanates
VISCOSITY AT 23 °C APPROX. [mPa • s]
TYPE
NON-VOLAT. CONTENTAPPROX. [%]
CO-SOLVENT CONTENT [%]
IN SUPPLY FORMINDUSTRIAL
METALAUTO OEM
AUTO-REFINISHLARGE VEHICLES
PROPERTIES
Desmodur®N3400 HDI uretdione 100 150 0 21.8 Low viscous HDI uretdione
Desmodur® N3600 HDI trimer 100 1,200 0 23.0 Low viscous HDI isocyanurate
Desmodur® N3900 HDI trimer 100 730 0 23.5 HDI iminooxadiazindione, “asymmetric trimer”
Desmodur® XP2565 IPDI allophanate 80 2,800 BA 20 15.0 IPDI-based, low functionality, improves hardness and pot life
Desmodur® XP 2860 HDI allophanate 100 500 0 20.0 Low viscous, medium functionality
Desmodur® XP 2840 HDI uretdione/trimer 100 500 0 23.0 HDI uretdione, in combination with other Desmodur® or Bayhydur® types
NCO CONTENT [%] ON SOLIDS
PLASTIC COATINGS
FLOOR WALL
WOOD,FURNITURE
PARQUETTRADE
CORROSION PROTECTION
Flexibilizingpolyisocyanates
Desmodur® N3800 HDI trimer 100 6,000 0 11.0 For highly flexible coatings; excellent weather resistance. As a flexibilization partner to combine with Bayhydur® or other Desmodur® polyisocyanates
28 Dispersions Dispersions 29
Impranil®Waterborne, anionic/nonionic aliphatic and aromatic poly-urethane dispersions for coating textiles resolvent-free and environmentally friendly. Suitable for all common textile coating processes in the fields of sports, clothing, fashion articles, technical items, and general protective equipment.
Aqueous PUR dispersions fortextilecoatings
0 = moderate0/+ = satisfactory+ = good++ = excellent
TYPE 1K APPLICATION
NON-VOLAT.CONTENT APPROX. [%]
LIGHTFASTNESSDIN 75202
ELONGATION AT BREAK DIN 53504 [%]
TENSILE STRENGTH
DIN 53504 [MPa]
100 % MODULUS DIN 53504 [MPa]
PROPERTIES
Impranil®DLP/DLP-R Polyester 50 7 + 1.3 10 1,600 200–220 Good resistance to hydrolysis, good adhesion, high solids con-tent, good stirring stability, soft handle
Impranil® DLN-SD Polyester 40 7 0 2 35 1,500 175–200 High flexibility, good washing resistance
Impranil® DLNW50 Polyester 50 7 0 2 35 1,500 175–200 High flexibility, suitable for mechanical foaming
Impranil® DLS Polyester 50 7 0 2.5 30 1,000 170–180 High flexibility, suitable for mechanical foaming
Impranil® DLV/1 Polyether/Polycarbonate 40 7 ++ 2 25 1,200 200–220 Outstanding resistance to hydrolysis, crosslinkable
Impranil® DLU Polyether/Polycarbonate 60 7 ++ 2 30 900 200–230 High solids content, outstanding resistance to hydrolysis,
excellent mechanical foaming, high scratch resistance
Impranil® DLH Polyester 40 7 0/+ 5 50 1,100 165–175 Free from organic solvents and emulsifiers, high flexibility, high lightfastness
Impranil® DLC-F/1 Polycarbonate 40 7 ++ 5 50 600 215–225 Excellent resistance to hydrolysis, good resistance to aging, high scratch resistance
Impranil® DL2611/1 Polyester 40 7 + 13 40 400 200–220 Dry and transparent finish
Impranil® DL1380 Polyester 60 7 0 1.4 25 1,400 210–220 High flexibility, suitable for mechanical foaming, high solids content
Impranil® DL1554 Polyester 60 7 0 2.5 26 1,000 200–220 Free from organic solvents and emulsifiers, high flexibility, excellent mechanical foaming
Impranil® DL1537 Polyester 60 7 + 1.3 15 1,200 200–210 Good resistance to hydrolysis, good adhesion, high solids content, soft handle
Impranil® LPRSC3040 Polyester 40 7 0 2 40 1,200 175–200 Flexible, semi-crystalline
Impranil® XP2772 Polyester 40 7 0 2 40 1,600 175–200 High flexibility, semi-crystalline
Impranil® DLE Polyether 50 7 + 1.5 25 1,600 215–225 Very elastic, good wet adhesion and outstanding washing resistance
Impranil® DLC-T Polyester/Polycarbonate 35 7 ++ 5 6 400 150–160 Good printability, very good hydrolysis resistance, for matt finish
RESISTANCE TO HYDROLYSIS
DIN EN 12280-3MELTING
RANGE [°C]
30 Dispersions Dispersions 31
Baybond®Generally used in manufacturing glass fiber sizes, Baybond® grades display good compatibility with the following additives: adhesion promoters, slip agents, antistatic agents, and flexibilizers.
Aqueous PUR dispersions for textilecoatings
1K APPLICATION
TYPE
NON-VOLAT.CONTENT APPROX. [%]
LIGHTFASTNESSDIN 75202
ELONGATION AT BREAK DIN 53504 [%]
TENSILE STRENGTH DIN 53504 [MPa]
100 % MODULUS DIN 53504 [MPa]
PROPERTIES
Impranil® DL519 Polyester 40 7 0 9 40 500 180–200 Flexible, dry touch, alcohol resistance
Impranil® LPDSB1069 Polyether 50 7 + 2 20 1,200 220–240 High elasticity
Impranil® DL2077 Polycarbonate 35 7 ++ 20–25 25–30 150–200 220 –230 Excellent hydrolysis resistance
Impranil® DAH Polyether 35 4 + 2 10 700 150–170 Very good adhesion properties on different kinds of substrates, aromatic PUD
Impranil® DAA Polyether 40 3 + 0.5 1 > 3,000 140–160 Very soft aromatic PUD for dry Lamination
MELTING RANGE [°C]
* = crosslinkable** = Food contact acc. EC 2011/10
+ = average++ = good+++ = very good++++ = excellent
NON-VOLAT. CONTENT [%]
CHEMICAL BASE
HYDROPHILIC CHARACTER
VISCOSITY, FLOW TIME (4 mm) s
TENSILE STRENGHTN/mm2
100 % MODULUSN/mm2
COMPATIBLE WITH AMINOSILANE
HYDROLYTIC RESISTANCE
Baybond® PU330 Polyester ionic/nonionic 29–31 30 – 140 6.5–8.0 + 0.5 1.0 2,000 yes thermosets
Baybond® PU403* Polyester ionic/nonionic 38–40 11 – 18 6.0–8.0 +++ 3.4 38.2 1,000 yes thermoplastics
Baybond® PU404XP** Polyester nonionic 48–52 < 500 mPa • s 5.5–7.5 ++ 2.1 37.0 1,300 yes thermoplastics
Baybond® PU 405* Polyether ionic/nonionic 32–35 11 – 18 6.0–8.0 ++++ 4.5 11.0 400 yes thermoplastics
Baybond® PU 406 Polyether nonionic 33–36 10 – 22 5.5–7.5 +++ 3.7 20.0 700 yes thermoplastics
Baybond® PU571XP** Polyether nonionic 33–36 10 – 30 5.5–7.5 +++ 3.7 20.0 700 yes thermoplastics
Baybond® PU407 Polyester ionic/nonionic 39–41 11 – 18 6.3–7.7 ++ 2.7 39.8 1,200 yes thermoplastics
Baybond® PU409XP Polyester ionic/nonionic 48–52 < 90 6.5–8.5 ++ approx. 2.0 approx. 10 approx. 1,000 yes thermoplastics and thermosets
Baybond® VPLS2277 Polyester ionic/nonionic 39–42 10 – 20 6.5–8.5 ++ 2.1 28.1 1,250 yes thermoplastics
Baybond® XP2728 Polyether/Polycarbonate ionic/nonionic 58–62 < 90 7.0–9.0 ++++ 3.1 24.5 910 yes thermoplastics
Baybond® PU 401-A Polyester ionic/nonionic 48–52 ≤ 70 6.5–8.5 ++ 3.0 51 1,200 yes thermoplastics
Baybond® PU 411 XP Polyester ionic/nonionic 38–42 < 500 mPa • s 6.0–8.0 ++ 3.0 20 1,000 yes thermoplastics
Baybond® PU7269 Polyether ionic/nonionic 29–31 < 50 7.5–9.5 +++ 1.0 4 700 yes thermoplastics
Baybond® PU1810** Polyester nonionic 58–62 100 – 1000 mPa • s 5.0–7.0 +++ 2.6 17 900 yes thermoplastics
RESISTANCE TO HYDROLYSIS DIN EN 12280-3
pH ELONGATION AT BREAK [%]
REINFORCEMENT OFPUR dispersions forglassfibercoatings
32 Dispersions Dispersions 33
Dispercoll® UAs aqueous, anionic dispersions of high molecular weight polyurethanes, Dispercoll® U grades are especially suitable for manufacturing heat-activated adhesives. These high- performance adhesive raw materials deliver outstanding bonding properties on most synthetic and natural materials.
PUR dispersions for adhesive applications
NON-VOLAT.CONTENT [%]
VISCOSITY[mPa • s]
pH FURNITURE LAMINATION
AUTOMOTIVE INTERIOR
PACKAGINGSHOE BONDING
Dispercoll® U 42 50 +/– 2 150–800 7.5 +/– 1.5 approx. 80–100
Aqueous anionic dispersion of a high molecular weight amorphous polyure-thane. Because of the softness and flexibility of the polymer film especially suitable for wet-bonding of textile substrates
Dispercoll® U53 40 +/– 1 50–600 7.5 +/– 1.5 approx. 60–70
Aqueous anionic dispersion of a high molecular weight crystallizing polyure-thane. Raw material for the formulation of heat-activated adhesives for use in, for example, the furniture and automotive industries
Dispercoll® U54 50 +/– 1 40–600 7.5 +/– 1.5 approx. 60–70
Aqueous anionic dispersion of a high molecular weight crystallizing polyure-thane. Raw material for the formulation of heat-activated adhesives for use in, for example, the furniture, automotive and especially the footwear industries
Dispercoll® U56 50 +/– 1 50–900 7.5 +/– 1.5 approx. 55–65
Aqueous anionic dispersion of a high molecular weight crystallizing polyure-thane. Especially suitable for applications at low heat activation temperatures in the furniture and automotive industries
Dispercoll® U8755 45 +/– 1 < 1,000 7.5 +/– 1.5 approx. 80–100
Aqueous anionic dispersion of a high molecular weight crystallizing polyurethane. Especially suitable for heat activation above 80 °C. Gives high heat resistance also when used without crosslinker
RECOMMENDED MIN. BONDLINE TEMP. [°C]
TEXTILE BONDING
PROPERTIES
= especially suitable
= suitable
34 Dispersions Dispersions 35
Dispercoll® UAs aqueous, anionic dispersions of high molecular weight polyurethanes, Dispercoll® U grades are especially suitable for manufacturing heat-activated adhesives. These high- performance adhesive raw materials deliver outstanding bonding properties on most synthetic and natural materials.
NON-VOLAT.CONTENT [%]
VISCOSITY[mPa • s]
pH SHOE BONDING
PACKAGING
AUTOMOTIVE INTERIOR
FURNITURE LAMINATION
Dispercoll® UXP2643 40 +/– 1 < 1,000 7.5 +/– 1.5 > RT
Aqueous anionic dispersion of a high mole-cular weight non- crystallizing polyurethane. Especially suitable for bonds at low to moderate temperatures, even at room temperature
Dispercoll® UXP2815 35 +/– 1 < 1,000 7.5 +/– 1.5 > RT
Aqueous anionic dispersion of a high mole-cular weight slowly crystallizing polyure-thane. Especially suitable for bonds at low to moderate temperatures or even at room temperature
Dispercoll® U XP 2682 50 +/– 1 < 1,000 7.5 +/– 1.5 approx. 50–60
Aqueous anionic dispersion of a lower molecular weight crystallizing polyurethane. Especially suitable for applications at low heat activation temperatures in the furniture and automotive industries. Good wetting properties due to low melt viscosity
Dispercoll® UXP2702 47 +/– 1 < 1,000 7.5 +/– 1.5 approx. 55–65
Aqueous anionic dispersion of a high molecular weight polyurethane. Especially suitable for latent-reactive adhesives in conjunction with deactivated Desmodur® LP BUEJ 471 formulation
Dispercoll® UXP2710 45 +/– 1 < 1,000 7.5 +/– 1.5 approx. 65–75
Aqueous anionic dispersion of a high molecular weight crystallizing polyurethane. Especially suitable for heat activation bonding applications with high initial heat resistance
Dispercoll® U 2824 XP 38 – 41 50 – 400 7.5 +/– 1.5 approx. 50–60
Aqueous anionic dispersion of a high mole-cular weight crystallizing polyurethane. The polymer contains carbolyl groups in the poly- mer chain that can be crosslinked with the polycarbodimide from Desmodur® XP 2802 to produce high-qualtiy adhesive bonds
Dispercoll® U2849XP 50 +/– 1 < 2,000 7.5 +/– 1.5 approx. 80–100
Aqueous anionic dispersion of a high mole cular weight amorphous polyurethane. Due to the characteristic polymer proper-ties Dispercoll® U 2849 XP is suitable for adhesive applications with improved climate resistance
RECOMMENDED MIN. BONDLINE
TEMP. [°C]TEXTILE
BONDINGPROPERTIES
= especially suitable
= suitable
PUR dispersions for adhesive applications
36 Dispersions Dispersions 37
Dispercoll® CThe unique property profile of Dispercoll® C waterborne contact adhesives makes these products indispensable for a large number of applications, e.g. as adhesives and sealants for shoes, in the transportation, automotive and construction in-dustries, in packaging, furniture, foamed materials, leather and rubber bonding. When properly formulated, Dispercoll® C can be used to substitute solventborne adhesives in a wide range of applications with no loss of performance, while at the same time bringing great improvements with respect to environmen-tal, handling, and workplace safety issues.
NON-VOLAT.CONTENT [%]
pH
CRYSTALLIZATION SHOE BONDING (CAPS, INNER SOLE)
BUILDING/ CONSTRUCTION
FOAM BONDING
FURNITURE LAMINATION
Dispercoll® C74 58 +/– 0.5 13.0 +/– 0.5 medium medium
Aqueous anionic dispersion of a 2-chlorobutadiene polymer with a medium rate of crystallization, good heat resistance and long open time. Dispercoll® C 74 is suitable for the formulation of aqueous con-tact adhesives
Dispercoll® C 84 55 +/– 0.5 13.0 +/– 0.5 fast very low
Aqueous anionic dispersion of a 2-chlorobutadiene polymer with a high rate of crystallization, fast bond formation, good contactibility and high bond strength. Dispercoll® C 84 is suitable for the formulation of aqueous contact adhesives
Dispercoll® C2325 55 +/– 1.0 12.0 +/– 1.0 fast low
Aqueous anionic dispersion of a 2-chlorobutadiene polymer with a high rate of crystallization, fast bond formation, good contactibility and high bond strength in combination with excellent storage stability and high crosslinking density with iso- cyanates. Dispercoll® C 2325 is suitable for the formulation of aqueous contact adhesives
Dispercoll® CVPLS2372/1 58 +/– 1.0 13.0 +/– 0.5 slow low
Aqueous anionic dispersion of a 2-chlorobutadiene polymer with a very low rate of crystallization, good contactibility and good wet tack in combination with excellent storage stability and high crosslink-ing density with isocyanates. Dispercoll® C VP LS 2372/1 is suitable for the formulation of aqueous contact adhesives. Dispercoll® C VP LS 2372/1 is typically used as blend component to improve wet tack
Dispercoll® CXP 2694 29 +/– 1.0 9.0 +/– 0.5 very fast very low
Aqueous anionic dispersion of a 2-chlorobutadiene polymer with a very high rate of crystallization, very fast bond formation and good contactibility. Can be used without further formulation as contact adhesive or adhesive primer
GEL CONTENT
TEXTILE BONDING
PROPERTIES
= especially suitable
= suitable
CR dispersions for adhesive applications
38 Dispersions Dispersions 39
Dispercoll® SThe new Covestro Dispercoll® S nano silica dispersions display some unique synergistic properties if used in combination with Dispercoll® C or U. Formulated with a Dispercoll® C grade in combination with ZnO, the Dispercoll® S grades can act as thickeners, yield high reinforcement, and deliver high heat resistance.
TYPE PARTICLE SIZE[nm]
NON-VOLAT.CONTENT [%]
SHOE BONDING (CAPS, INNER SOLE)
BUILDING/ CONSTRUCTION
PROPERTIESSPEC. SURFACE [m2/mg]
FURNITURE LAMINATION
SPRAY ADHESIVE FOR FOAM TO FOAM
Dispercoll® S5005 Nano SiO2 dispersion 50 +/– 1 55 50 1.390
Nano SiO2 dispersion with small particle size. Formulated in combination with Dispercoll® C and ZnO dispersion, a medium viscosity spray-able adhesive with improved inital tack and bonding strength is obtained
Dispercoll® S4510 Nano SiO2 dispersion 45 +/– 1 30 100 1.340
Nano SiO2 dispersion with small particle size. Formulated in combination with Dispercoll® C and ZnO dispersion, viscosities can be adjusted in a broad range simultaneously improving sta-bility, inital tack and bonding strength
Dispercoll® S 4020 Nano SiO2 dispersion 40 +– 1 15 200 1.295
Nano SiO2 dispersion with very small par-ticle size. Formulated in combination with Dispercoll® C and ZnO dispersion, highly thixo-tropic adhesive formulations can be obtained simultaneously improving initial tack, bonding strength and heat resistance
Dispercoll® S3030 Nano SiO2 dispersion 30 +/– 1 9 300 1.208
Nano SiO2 dispersion with very small par-ticle size. Formulated in com bination with Dispercoll® C and ZnO dispersion, up to paste-like adhesive formulations can be obtained simultaneously improving initial tack, bon ding strength and delivering oustanding heat resistance
Dispercoll® S 2020 XP Nano SiO2 dispersion 20 +/– 1 15 200 1.13
Nano SiO2 dispersion with very small par-ticle size. Formulated in combination with Dispercoll® C for 1K sprayable formulations with low pH, medium viscosity, and improved initial tack
DENSITY[g/m3]
TEXTILE BONDING
= especially suitable
= suitable
Additives for Dispercoll® C and Dispercoll® U
40 Dispersions Dispersions 41
Dispercoll®Desmodur®Bayhydur®Polyisocyanate crosslinkers for adhesives applications.
= especially suitable
= suitable
Crosslinker for latent reactive polyurethane dispersions
NCO-CONTENT[%]
TYPE NON-VOLAT. CONTENTAPPROX. [%]
PROPERTIES
Dispercoll®BLXP2514 TDI-dimer suspension 7.5–10.0 40 ./. Crosslinker for latent-reactive PUD
Desmodur®LPBUEJ471 Micronized IPDI-isocyanurate 16.3–17.7 100 ./. Micronized crosslinker for latent-reactive PUD
VISCOSITY AT23 °C [mPa • s]
Crosslinker for adhesive dispersions
Desmodur® DN Hydrophilic modified isocyanate 21.8 100 1,250 Low hydrophilicity
Desmodur® DA-L Hydrophilic modified isocyanate 20.0 100 3,000 Low hydrophilicity
Bayhydur®3100 Hydrophilic modified isocyanate 17.4 100 2,800 High hydrophilicity
Bayhydur®304 Hydrophilic modified isocyanate 18.2 100 4,000 In compliance with U.S. FDA’s guideline “Title 21 CFR:” Section 175.105 “Adhesives”
Desmodur® XP 2802 Dispersion of hydrophilic polycarbodiimid
approx. 1 mmol – N = C = N –/g 40 30 Crosslinker for carboxylate functionalized dispersions, suitable for 2K formulations with
long pot life
Crosslinker for CR dispersions
TYPE VISCOSITY AT 23 °C[mPa • s] APPROX.
NON-VOLAT.CONTENT [%]
SPRAY ADHESIVE FOR FOAM TO FOAM
TEXTILE BONDING (CAPS, INNER SOLE)
PROPERTIES
SHOE BONDING
NCO-CONTENTON SOLIDS [%]
Bayhydur®401-70 IPDI-based hydrophilic polyisocyanate 70 in MPA/X 600 13.4
Used in CR-dispersion formulations, yields a high chemical crosslinking density to achieve excellent heat resistance. Featuring very long pot life and excellent storage stability
FURNITURE LAMINATION
BUILDING/ CONSTRUCTION
42 Dispersions Dispersions 43
At Covestro innovation is in our DNA. Ever since Otto Bayer discovered polyurethanes in 1937, we have been driving polyurethane innovations in coatings and adhesives as well as in other application areas. As our partner you enjoy fast-lane access to polyurethane innovations, and can help us in developing the next generation of polyurethanes to meet the industry’s upcoming challenges and needs. What can we offer you?
• Powerful know-how on both established and new polyisocya-nates, as well as on new poly-urethane hybrid technologies.
• The prospect of new application technologies to enable efficient processes.
• More sustainable, biomass- or CO2-based materials that do not sacrifice high performance.