COMPOZIÞIE CHIMICÃ • STARE
COMPOZIÞIA CHIMICÃ A ALIAJELOR
Si (%)ALIAJ
1050 <=0.25 <=0.4 <=0.05 <=0.05 <=0.05 <=0.07 <=0.05 <=0.03 <=99.5
2007 <=0.8 <=0.8 3.3-4.6 <=0.2 0.8-1.5 0.5-1.0 0.4-1.8 <=0.1 <=0.80 <=0.20 <=0.03 Rest
2011 <=0.4 <=0.7 5.0-6.0 0.2-0.6 0.2-0.6 <=0.30 <=0.05 Rest
2014 0.5-1.2 <=0.7 3.9-5.0 0.4-1.2 0.2-0.8 <=0.1 <=0.25 <=0.15 <=0.05 Rest
2017 0.2-0.8 <=0.7 3.5-4.5 0.4-1.0 0.4-1.0 <=0.1 <=0.25 <=0.25 <=0.05 Rest
2024 <=0.5 <=0.5 3.8-4.9 0.3-0.9 1.2-1.8 <=0.1 <=0.25 <=0.15 <=0.05 Rest
3003 <=0.6 <=0.7 <=0.3 1.0-1.5 <=0.10 <=0.05 Rest
3005 <=0.6 <=0.7 <=0.3 1.0-1.5 0.2-0.6 <=0.1 <=0.25 <=0.1 <=0.05 Rest
5005 <=0.3 <=0.7 <=0.2 <=0.2 0.5-1.1 <=0.1 <=0.25 <=0.05 Rest
5052 <=0.25 <=0.4 <=0.1 <=0.1 2.2-2.8 0.15-0.35 <=0.10 <=0.05 Rest
5083 <=0.4 <=0.4 <=0.1 0.4-1.0 4.0-4.9 0.05-0.25 <=0.25 <=0.15 <=0.05 Rest
5754 <=0.4 <=0.4 <=0.1 <=0.5 2.6-3.6 <=0.3 <=0.2 <=0.15 <=0.05 Rest
6060 0.3-0.6 0.1-0.3 <=0.1 <=0.1 0.35-0.6 <=0.05 <=0.15 <=0.1 <=0.05 Rest
6063 0.2-0.6 <=0.35 <=0.1 0.45-0.9 <=0.1 <=0.10 <=0.1 <=0.05 Rest
6082 0.7-1.3 <=0.5 <=0.10 0.4-1.0 0.6-1.2 <=0.255 <=0.20 <=0.10 <=0.05 Rest
7075 <=0.40 <=0.50 1.2-2.0 <=0.3 2.1-2.9 0.18-0.28 5.1-6.1 <=0.2 <=0.05 Rest
Fe (%) Cu (%) Bi (%) Pb (%) Mn (%) Mg (%) Cr (%) Zn (%) Ti (%) Alte(%) Al(%)
STAREA TABLELOR LAMINATEINDICATOR
STARE
F Forjat. Format prin prelucrare la rece, prelucrare la cald sau turnare fãrã control special al temperaturii sau al cãlirii superficiale.
O Moale. Laminat la cald, tratat termic în vederea obþinerii unui nivel foarte redus al duritãþii.H11 Cãlit superficial pânã la o duritate cuprinsã între 0 ºi 1/4.H111 Cãlit superficial pânã la o duritate cuprinsã între 0 ºi H11.H12 Cãlit superficial pânã la o duritate de 1/4.H14 Cãlit superficial pânã la o duritate de 1/2.H16 Cãlit superficial pânã la o duritate de 3/4.H18 Cãlit superficial pânã la o stare complet durã.H22 Prelucrat la rece, cãlit superficial ºi tratat termic parþial pânã la o duritate de 1/4.H24 Prelucrat la rece, cãlit superficial ºi tratat termic parþial pânã la o duritate de 1/2.H26 Prelucrat la rece, cãlit superficial ºi tratat termic parþial pânã la o duritate de 3/4.H28 Prelucrat la rece, cãlit superficial ºi tratat termic parþial pânã la o stare complet durã.H32 Prelucrat la rece, cãlit superficial ºi stabilizat la o duritate de 1/4.H34 Prelucrat la rece, cãlit superficial ºi stabilizat la o duritate de 1/2.H36 Prelucrat la rece, cãlit superficial ºi stabilizat la o duritate de 3/5.H38 Prelucrat la rece, cãlit superficial ºi stabilizat pânã la o stare complet durã.
STÃRI ALIAJE ALUMINIU
INDICAREA STÃRII ALIAJELOR ÎMBUNÃTÃÞIBILE ªI TRATAMENTUL TERMIC AL ACESTORAINDICATOR
STARE
T1
T2
T3
T4
T5
T6
Rãcit dupã procedeul de prelucrare la temperaturi ridicate ºi imbãtrânit natural pânã la obþinerea unei stãri stabileRãcit dupã procedeul de prelucrare la temperaturi ridicate, deformat la rece ºi imbãtrânit natural pentru obþinerea unei stãri stabilePus în soluþie deformat la rece ºi imbãtrânit natural pentru obþinerea unei stãri stabilePus în solutie ºi imbãtrânit natural pentru obþinerea unei stãri stabileRãcit dupã un procedeu de prelucrare la temperaturi ridicate ºi imbãtrânit artificialPus în solutie ºi apoi imbãtrânit artificial
3
ALIAJ 1050A 2007 2011 2017A 2024 3003 5005 5052 5083 6060 6082 7075
DENSITATE 2.7 2.85 2.82 2.8 2.77 2.73 2.69 2.68 2.66 2.7 2.7 2.8