Material Specification SheetDISOGRIN 6865

Name: DISOGRIN 6865Material: Premium polyurethane, TODI basedType: Injection moldedColor: Natural

Property Standard Value Units

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens.

Material Spec Sheet 6865 01.08.00

Hardness ASTM D-2240-68 92 Shore A

Tensile Strength ASTM D-412 Die C 5,900 psi

Elongation Set ASTM D-412 Die C 550 %

Elongation Set ASTM D-412 Die C 15 %

300% Modulus ASTM D-412 Die C 1,700 psi

100% Modulus ASTM D-412 Die C 750 psi

Abrasion Loss DIN 53/516 25 mm3

Tear Die C ASTM D-624 660 pli

Tear Nicked ASTM D-624 360 pli

Bayshore Resilence ASTM D-2632-7 51 %

Compression Set B

22 Hrs @ 70C ASTM D-395-69, Method B 9 %

Specific Gravity ASTM D-792, Method A1 1.15

Material Specification SheetDISOGRIN 9250

Property Standard Value Units

Hardness ASTM D-2240-68 92 Shore A

Tensile Strength ASTM D-412 Die C 6,000 psi

Elongation Set ASTM D-412 Die C 400 %

Elongation Set ASTM D-412 Die C 18 %

300% Modulus ASTM D-412 Die C 3,400 psi

100% Modulus ASTM D-412 Die C 1,600 psi

Abrasion Loss DIN 53/516 36 mm3

Tear Die C ASTM D-624 700 pli

Tear Nicked ASTM D-624 480 pli

Bayshore Resilence ASTM D-2632-7 35 %

Compression Set

22 Hrs @ 70C ASTM D-395-69 (Method B) 26 %

Specific Gravity ASTM D-792, Method A1 1.17

Name: DISOGRIN 9250Material: Premium polyurethane, TODI basedType: CastColor: Natural

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens.

Material Spec Sheet 9250 01.08.00

Material Specification SheetDISOGRIN D92S

Name: DISOGRIN D92SMaterial: Premium polyurethane, TODI basedType: Injection moldedColor: Natural

Property Standard Value Units

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens.

Material Spec Sheet D92S 01.08.00

Hardness ASTM D-2240 94 3 Shore A

Hardness ASTM D-2240 43 3 Shore DTear Strength ASTM D-624 45 N/mm, Min.

Tensile Strength ASTM D-412 25 MPa, Min.Modulus @ 300% Enlongation ASTM D-412 15 MPa, Min.

Elongation ASTM D-412 400 % Min.Compression Set

22 Hours @ 70C ASTM D-395 (Method B) 30 % Max.

Heat Age (70 Hours @ 100C)Change in Hardness ASTM D-573 15Change in Tensile Strength ASTM D-573 30 % Max.

Change in Elongation ASTM D-573 -50 % Max.

Water Resistance (70 Hours @ 100C)Change in Hardness, ASTM D-471 10 % Max.

Change in Valume ASTM D-471 15 % Max.

Fluid Resistance, ASTM #1 Oil (70 Hours @ 100C)Change in Hardness ASTM D-471 -5 to +15 % Max

Change in Tensile Strength ASTM D-471 -25 % MaxChange in Elongation ASTM D-471 -45 % Max.

Change in Volume ASTM D-471 -10 to +5 % Max.

Fluid Resistance, ASTM #3 Oil (70 Hours @ 100C)Change in Hardness ASTM D-471 -10 to +5 % Max.

Change in Strength ASTM D-471 -45 % Max.Change in Elongation ASTM D-471 -45 % Max.

Change in Volume ASTM D-471 0 to +25 % Max.

Material Specification SheetDISOGRIN D80S

Hardness ASTM D-2240 85 3 Shore ATear Strength ASTM D-624 67 N/mm, Min.Tensile Strength ASTM D-412 25 MPa, Min.

Modulus @ 300% Enlongation ASTM D-412 9 MPa, Min.Elongation ASTM D-412 400 %, Min.

Compression Set22 Hours @ 70C ASTM D-395 (Method B) 35 %, Max.

Heat Age (70 Hrs @ 100C)

Change in Hardness ASTM D-573 15 Shore A

Change in Tensile Strength ASTM D-573 30 % Max.Change in Elongation ASTM D-573 -50 % Max.

Water Resistance (70 Hrs @ 100C)Change in Hardness, ASTM D-471 10 % Max.Change in Valume ASTM D-471 15 % Max.

Fluid Resistance, ASTM #1 Oil (70 Hrs @ 100C)Change in Hardness ASTM D-471 -5 to +15 % Max

Change in Tensile Strength ASTM D-471 -25 % MaxChange in Elongation ASTM D-471 -45 % Max

Change in Volume ASTM D-471 -10 to +5 % Max

Fluid Resistance, ASTM #3 Oil (70 Hrs @ 100C)Change in Hardness ASTM D-471 -10 to +5 % Max.

Change in Strength ASTM D-471 -45 % Max.Change in Elongation ASTM D-471 -45 % Max.

Name: DISOGRIN D80SMaterial: Premium polyurethane, TODI basedType: Injection moldedColor: Natural

Property Standard Value Units

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens.

Material Spec Sheet D80S 01.08.00

Material Specification SheetDISOGRIN 928

Name: DISOGRIN 928Material: Premium polyurethane, TODI basedColor: Natural

Property Standard Value Units

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens.

Material Spec Sheet D928 01.08.00

Hardness DIN 53505 98 2 Shore A

Hardness DIN 53505 60 5 Shore D

Specific Gravity DIN 53479 1.20 0.02

Resilience DIN 53512 25 %

Tensile Strength DIN 53455 30 N/mm2

Elongation at Break DIN 53455 300 %

300% Modulus DIN 53455 28 N/mm2

Tear Strength DIN 53507 90 N/mm2

Wear DIN 53516 50 mm3

Glass Transition -17 C

Low Temperature Brittleness -50 C

Compression Set

24 Hrs @ 20C DIN 53517 20 %

22 Hrs @ 70C DIN 53517 35 %

70 Hrs @ 100C DIN 53517 65 %

Material Specification SheetSIMRITAN 94 AU 925

Name: SIMRITAN 94 AU 925Material: Premium polyurethane, TODI basedColor: Blue

Property Standard Value Units

Specific gravity DIN 53479 1.18 g/cm3

Hardness DIN 53505 94 Shore A

Rebound resilience DIN 53512 35 %

Modulus at 100% DIN 53504 11.9 N/mm2

Tensile strength DIN 53504 61.0 N/mm2

Ultimate elongation DIN 53504 428 %

Compression Set

22h @ 70C DIN 53517 40 %

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Spec Sheet 94AU925 01.08.00

Property Standard Value Units

Material Spec Sheet Simritan 98 AU 928 01.08.00

Specific gravity DIN 53479 1.20 g/cm3

Hardness DIN 53505 97 Shore A

Modulus at 100 % DIN 53504 21.1 N/mm2

Tensile strength DIN 53504 41.4 N/mm2

Ultimate elongation DIN 53504 389 %

Material Specification SheetSIMRITAN 98 AU 928

Name: SIMRITAN 98 AU 928Material: Premium polyurethane (TODI based)Color: Blue

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Specification SheetNOVATHAN 95 AU V142

Name: NOVATHAN 95 AU V142Material: Premium polyurethane, MDI basedColor: Blue

Property Standard Value Units

Durometer hardness ASTM D-2240 95 2 Shore A

Durometer hardness ASTM D-2240 48 3 Shore D

Density ASTM D-792 1.20 0.01 g/cm3

Tensile strength ASTM D-412 40 N/mm2

Elongation at break ASTM D-412 500 %

Tear strength ASTM D-624 120 N/mm

Rebound resilience DIN 53512 42 %

Abrasion DIN 53516 18 mm3

Compression set

70h/70C, 25% compression ASTM D-395 (Method B) 27 %

Compression set

24h/100C, 25% compression ASTM D-395 (Method B) 24 %

Compression Set

70h/70C, 25% compression ASTM D-395 (Method B) 26 %

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Spec Sheet NOVATHAN 01.08.00

Material Specification SheetMerkel 70 NBR B209

Name: Merkel 70 NBR B209Material: NBR (Acrylonitrile Bunadiene Rubber)Color: Black

Property Standard Value Units

Density 1.20 0.02 g/cm3

Hardness 70 5 SHORE A

Hardness 70 5 IRHD

Tensile Strength 11 N/MM

Ultimate Elongation 250 %

Modulus 100% Elongation* 4.4 N/mm 2

Tear Strength* 11 N/mm

Change In Volume*

ASTM Oil I (168 hr/100C) -5.4 %

ASTM Oil III (168 hr/100C) 13 %

Change In Hardness*

ASTM Oil I (168 hr/100C) 1 Point

ASTM Oil III (168 hr/100C) -8 Point

Compression Set

24 hr/70C DIN 53517 11 %

70 hr/100C DIN 53517 23 %

24 hr/70C ASTMD 395 B 10 %

70 hr/100C ASTM-D 395 B 15 %

*Typical Properties

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Spec Sheet 70 NBR B209 01.08.00

Material Specification SheetMerkel 70 NBR B276

Name: Merkel 70 NBR B276Material: NBR (Acrylonitrile Bunadiene Rubber)Color: Black

Property Standard Value Units

Density DIN 53479 1.23 0.02 g/cm3

Hardness DIN 53505 70 5 Shore A

Hardness DIN 53519 73 5 IRHD

Tensile Strength DIN 53504 14 N/mm2

Ultimate Elongation DIN 53504 280 %

Modulus 100% Elongation DIN 53504 5 N/mm2

Resistance To Tear Propagation DIN 53515 18 N/mm2

Low Temperature Reference Value TR DIN 53520 -22 C

Brittle Point TS DIN 53546 -50 C

Change In Volume

ASTM Oil I (168 hr/100C) -5 %

ASTM Oil III (168 hr/100C) 11 %

Change In Hardness

ASTM Oil I (168 hr/100C) 5 Points

ASTM Oil III (168 hr/100C) -6 Points

Compression Set

24 hr /70C DIN 53517 17 %

70 hr /100C DIN 53517 32 %

24 hr /70C ASTM-D 395 B 12 %

70 hr /100C ASTM-D 395 B 20 %

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Spec Sheet 85 NBR 70 B276 01.08.00

Property Standard Value Units

Material Spec Sheet Simrit 72 NBR 872 01.08.00

Specific gravity DIN 53479 1.21 g/cm2

Hardness DIN 53505 72 Shore A

Rebound resilience DIN 53512 34 %

Modulus at 100 % DIN 53504 6.5 N/mm2

Tensile strength DIN 53504 16.5 N/mm2

Ultimate elongation DIN 53504 270 %

Compression set (22 hr/100C) DIN 53517 20 %

Material Specification SheetMerkel 72 NBR 872

Name: Merkel 72 NBR 872Material: NBR (Acrylonitrile Bunadiene Rubber)Color: Black

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Specification SheetMerkel 79 NBR B246

Name: Merkel 79 NBR B246Material: NBR (Acrylonitrile Bunadiene Rubber)Color: Black

Property Standard Value Units

Density DIN 53479 1.22 0.02 g/cm3

Hardness DIN 53505 78 5 Shore A

Hardness DIN 53519 78 5 IRHD

Tensile Strength DIN 53504 10.5 N/mm2

Ultimate Elongation DIN 53504 250 %

Modulus 100% Elongation* DIN 53504 6.5 N/mm2

Tear Strength* DIN 53515 16 N/mm

Change In Volume*

ASTM Oil I (168 hr/100C) -1.7 %

ASTM Oil III (168 hr/100C) 16 %

Change In Hardness*

ASTM Oil I (168 hr/100C) 2 Points

ASTM Oil III (168 hr/100C) -12 Points

Compression Set

24 hr/70C DIN 53517 15 %

70 hr/100C DIN 53517 40 %

24hr/70C ASTM-D 395 B 14 %

70 hr/100C ASTM-D 395 B 26 %

*Typical Properties

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Spec Sheet 79 NBR B246 01.08.00

Property Standard Value Units

Material Spec Sheet Simrit 80 NBR 709 01.08.00

Specific gravity DIN 53479 1.27 g/cm2

Hardness DIN 53505 82 Shore A

Rebound resilience DIN 53512 29 %

Modulus at 100 % DIN 53504 10.2 N/mm2

Tensile strength DIN 53504 16.9 N/mm2

Ultimate elongation DIN 53504 290 %

Compression set (22 hr/100C) DIN 53517 25 %

Material Specification SheetMerkel 80 NBR 709

Name: Merkel 80 NBR 709Material: NBR (Acrylonitrile Bunadiene Rubber)Color: Black

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Property Standard Value Units

Material Spec Sheet Simrit 80 NBR 878 01.08.00

Specific gravity DIN 53479 1.30 g/cm2

Hardness DIN 53505 83 Shore A

Rebound resilience DIN 53512 26 %

Modulus at 100 % DIN 53504 10.5 N/mm2

Tensile strength DIN 53504 15.5 N/mm2

Ultimate elongation DIN 53504 170 %

Compression set (22 hr/100C) DIN 53517 20 %

Material Specification SheetMerkel 80 NBR 878

Name: Merkel 80 NBR 878Material: NBR (Acrylonitrile Bunadiene Rubber)Color: Black

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Specification SheetMerkel 85 NBR B248

Name: Merkel 85 NBR B248Material: NBR (Acrylonitrile Bunadiene Rubber)Color: Black

Property Standard Value Units

Density DIN 53479 1.37 0.02 g/cm3

Hardness DIN 53505 84 5 Shore A

Hardness DIN 53519 86 5 IRHD

Tensile Strength DIN 53504 14 N/mm2

Ultimate Elongation DIN 53504 200 %

Modulus 100 % Elongation* DIN 53504 5.8 N/mm2

Tear Strength* DIN 53515 30 N/mm

Change In Volume*

ASTM Oil I 168hr/100C -3.5 %

ASTM Oil III 168hr/100C 11 %

Change In Hardness*

ASTM Oil I 168hr/100C 8 Points

ASTM Oil III 168hr/100C -7 Points

Compression Set

24 hr/70C DIN 53517 35 %

70 hr/100C DIN 53517 55 %

24 hr/70C ASTM-D 395 B 30 %

70 hr/100C ASTM-D 395 B 55 %

*Typical Properties

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Spec Sheet 85 NBR BI B248 01.08.00

Material Specification SheetMerkel 87 NBR B247

Name: Merkel 87 NBR B247Material: NBR (Acrylonitrile Bunadiene Rubber)Color: Black

Property Standard Value Units

Density DIN 53479 1.25 0.02 g/cm3

Hardness DIN 53505 86 5 Shore A

Hardness DIN 53519 87 5 IRHD

Tensile Strength DIN 53504 17.5 N/mm2

Ultimate Elongation DIN 53504 200 %

Modulus (100% Elongation*) DIN 53504 8.8 N/mm2

Tear Strength* DIN 53515 21 N/mm

Change In Volume*

ASTM Oil I (168 hr/100C) -2.5 %

ASTM Oil III (168 hr/100C) 12.6 %

Change In Hardness*

168hr/100C 2 Point

168hr/100C -10 Point

Compression Set

24 hr/70C DIN 53517 20 %

70 hr/100C DIN 53517 35 %

24 hr/70C ASTM-D 395 B 20 %

70 hr/100C ASTM-D 395 B 33 %

*Typical Properties

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Spec Sheet 87 NBR B247 01.08.00

Property Standard Value Units

Material Spec Sheet Simrit 88 NBR 101 01.08.00

Specific gravity DIN 53479 1.41 g/cm2

Hardness DIN 53505 90 Shore A

Rebound resilience DIN 53512 18 %

Modulus at 100 % DIN 53504 8.0 N/mm2

Tensile strength DIN 53504 13.5 N/mm2

Ultimate elongation DIN 53504 230 %

Compression set (22 hr/100C) DIN 53517 43 %

Material Specification SheetMerkel 88 NBR 101

Name: Merkel 88 NBR 101Material: NBR (Acrylonitrile Bunadiene Rubber)Color: Black

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Specification SheetMerkel 90 NBR B283

Name: Merkel 90 NBR B283Material: NBR (Acrylonitrile Bunadiene Rubber)Color: Black

Property Standard Value Units

Density DIN 53479 1.30 0.02 g/cm3

Hardness DIN 53505 93 5 Shore A

Hardness DIN 53519 93 5 IRHD

Tensile Strength DIN 53504 14 N/mm2

Ultimate Elongation DIN 53504 100 %

Tear Strength* DIN 53515 19 N/mm

Change in Volume

ASTM Oil I 168hr / 100 C -3.5 %

ASTM Oil III 168hr / 100 C 8 %

Change in Hardness*

ASTM Oil I 168hr / 100 C 4 Points

ASTM Oil III 168hr / 100 C -5 Points

Compression Set

24 hr / 70 C DIN 53517 18 %

70 hr / 100 C DIN 53517 32 %

24 hr / 70 C ASTM-D 395 B 16 %

70 hr / 100 C ASTM-D 395 B 26 %

*Typical Properties

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Spec Sheet 90 NBR B283 01.08.00

Material Specification SheetMerkel 70 FPM K682

Name: Merkel 70 FPM K682Material: FPM (Fluoroelastomer)

Property Standard Value Units

Density DIN 53479 1.85 0.02 g/cm3

Hardness DIN 53505 70 5 Shore A

Hardness DIN 53519 69 5 IRHD

Tensile Strength DIN 53504 10 N/mm2

Ultimate Elongation DIN 53504 150 %

Modulus 100% Elongation DIN 53504 5.7 N/mm2

Resistance To Tear Propagation DIN 53515 10 N/mm2

Change In Volume

ASTM Oil III (70 hr/150C) 1.8 %

Service Fluid No. (101 70hr/200C) 10 %

Change In Hardness

ASTM Oil III (70 hr/150C) 0 Points

Service Fluid No.101 -6 Points

Compression Set

70 hr/100C DIN 53517 14 %

70 hr/200C DIN 53517 28 %

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Spec Sheet 70 FPM K682 01.08.00

Material Specification SheetMerkel 70 FPM K655

Name: Merkel 70 FPM K655Material: FPM (Fluoroelastomer)Color: Black

Property Standard Value Units

Density DIN 53479 1.90 0.02 g/cm3

Hardness DIN 53505 76 5 Shore A

Hardness DIN 53519 76 5 IRHD

Tensile Strength DIN 53504 12 N/mm 2

Ultimate Elongation DIN 53504 140 %

Modulus %100 Elongation DIN 53504 8 M/mm2

Resistance To Tear Propagation DIN 53515 13.5 N/mm2

Change In Volume

ASTM III (70 hr/150C) 1 %

Service Fluid No. 101 9.5 %

Change In Hardness

ASTM Oil III (70 hr/150C) -2 Points

Service Fluid No. 101 -7 Points

Compression Set

70 hr/100C DIN 53517 13 %

70 hr/200C DIN 53517 25 %

70 hr/100C ASTM-D 395 B 10 %

70 hr/200C ASTM-D 395 B 20 %

Important Notes:Not to be used for specification purposes. These values serve only as a guide for engineering design. Values aremedian values obtained from laboratory specimens. The given values are based on a limited number of tests onstandard test pieces (2mm sheets) produced in the laboratory. The data of finished parts can deviate from abovevalues depending on the manufacturing process and the component geometry.

Material Spec Sheet 70 FPM K655 01.08.00

Material Specification SheetMerkel HGW HG600

Name: HGW HG600Material: Fabric Reinforced ResinColor: Blue

Property Standard Value Units

Compression Strength DIN 53454 340 N/mm2

Flexural Strength DIN 53452 100 N/mm2

Ball impression hardness at 23C DIN 53456 110 N/mm2

Specific gravity DIN 53479 1.25-1.48 g/cm3

Water absorption after 24h at 23C DIN 53495