MILD & MEDIUM CARBON STEEL ELECTRODES 1-16 LOW ALLOY … · mild & medium carbon steel electrodes 1-16 17-48 49-79 80-95 96-110 111-119 120-125 low alloy steel electrodes stainless

MILD & MEDIUM CARBON STEEL ELECTRODES 1-16

17-48

49-79

80-95

96-110

111-119

120-125

LOW ALLOY STEEL ELECTRODES

STAINLESS STEEL ELECTRODES

HARD FACING ELECTRODES

NON FERROUS ELECTRODES

CAST IRON & CUTTING ELECTRODES

FLUX CORED WIRE & CO2 WELDING WIRES

Abbreviations and Symbols

Types of Current Codes

Abbreviations

Notes:

Direct current electrode attached to positive pole

Direct current electrode attached to negative pole

Direct current electrode attached to either positive or negative pole

Alternating current

Preferably direct current attached to positive pole, but also alternating current may be used

Preferably direct current attached to negative pole, but also alternating current may be used

Preferably direct current attached to either positive or negative pole, but also alternating current maybe used

tensile strengthyield strengthelongation after rupture (1=5d)impact valueas- weldedstress relieved

(brackets) - Minimum open circuit voltage when welding using an alternating current

Rm [MPa]Rp 0.2 [MPa]A5 [%]Impact (ISO) [J]US

= -

~

= + ~

= +

_

= + ~

_

= - ~

= +

All values listed in this guide are indicative only.All information contained within this guide is based on careful evaluation.Regardless, the manufacturer does not assume any liability for their correctness.Further, the manufacturer reserves the right to change the specifications listed in this guide at any time andwithout prior notice.

Electrode Brand Name - International Standards

Z-610Z-611Z-6Z-9Z-11Z-14Z-15Z-15 (14)

A5. 1: E 6010A5. 1: E 6011A5. 1: E 6013A5. 1: E 6013A5. 1: E 6013A5. 1: E 6013A5. 1: E 6013A5. 1: E 6013

1913: E 43 43 C41913: E 43 43 C41913: E 43 22 RR61913: E 42 22 R(C) 31913: E 43 22 RR61913: E 51 22 RR61913: E 43 22 RR61913: E 51 22 RR61913: E 51 22 R(C)31913: E 51 22 RR(C) 61913: E 51 22 RR11 1401913: E 51 22 RR11 1601913: E 51 22 RR11 1801913: E 51 32 RR11 1601913: E 51 22 RR11 180

1913: E 51 44 B9 H101913: E 51 44 B10 H101913: E 51 44 B10 H101913: E 51 44 B10 H51913: E 51 44 B10 H58529: EY 46 66 Mn BH51913: E 51 43 B(R)12 160 H51913: E 51 44 B(R)9 H10-8575: E Mo B 26-8575: E CrMo1 B 268575: E CrMo1 B 268529: E SY 42 77 2Ni B H58529: E Y 46 76 1Ni B H51913: E 51 33 B10 H58529: E Y 50 76 Mn1Ni B H58529: E SY 50 66 Mn B H58529: E Y 50 32 1NiCu B H58575: E CrMo2 B 268575: E CrMo2 B 268529: E SY 55 65 MnMo B H58529: E SY 50 0 1NiMo B H58529: E Y 55 87 2NiMo B H58529: E Y 62 87 Mn2NiMo B H58529: E Y 69 76 Mn2NiCrMo B H58529: E Y 79 76 Mn2Ni1.5CrMo B H58575: E CrMo5 B 268575: E CrMo9 B 26

639: E 43 43 C 19639: E 43 43 C 16639: E 43 22 RR 22639: E 43 22 R 12639: E 43 22 RR 22639: E 51 22 RR 32639: E 43 22 RR 32639: E 51 22 RR 32639: E 51 22 R 12639: E 51 22 RR 12639: E 51 22 RR 140 35639: E 51 22 RR 160 32639: E 51 22 RR 190 35639: E 51 22 RR 160 32639: E 51 22 RR 190 35

639: E 51 44 B 16 HH639: E 51 44 B 26 HH639: E 51 44 B 26 HH639: E 51 44 B 26 H639: E 51 44 B 26 H639: E 51 55 B 120 16 H639: E 51 43 B 160 36 H639: E 51 44 B 110 54 HH2493: E Mo C2493: E Mo B639: E 51 32 C 102493: E 1CrMo B2493: E 1CrMo L B2493: E 2Ni B H2493: E 1Ni B H639: E 51 33 B 120 26 H639: E 51 54 B 120 26 H639: E 51 55 B 120 16 H-2493: E 2CrMo B2493: E 2CrMo L B2493: E MnMo B H-2493: E MnNi B H2493: E NiMo B H2493: E 2NiMo B H2493: E 2NiCrMo B H2493: E 5CrMo B2493: E 9CrMo B

499: E 42 2 C 41499: E 42 2 C 31499: E 42 0 RR 12499: E 42 0 R 12499: E 42 0 RR 12 499: E 42 0 RR 12499: E 38 0 RR 12499: E 42 0 RR 12

12345678910111213141516

1718192021222324252627282930313233343536373839404142434445464748

499: E 42 0 RC 12499: E 46 0 RR 32499: E 42 0 RR 53499: E 46 0 RR 73499: E 46 0 RR 73499: E 46 0 RR 73499: E 46 0 RR 732560-A: E-5000Z1

499: E 46 3 B 11 H10499: E 42 3 B 12 H10499: E 42 3 B 32 H10499: E 46 3 B 32 H5499: E 42 3 B 32 H15499: E 46 5 B 32 H5499: E 42 3 RB 53 H5499: E 42 3 B 35 H10499: E 42 0 Mo C 411599: E Mo B 32 mod499: E 46 2 1NiMo C 411599: E CrMo1 B 32mod1599: E CrMo1 L B 32 mod499: E 46 6 2Ni B 42 H5-499: E 50 2 B 32 H5503Mo: B 42 H5499: E 50 6 Mn1Ni B 32 H5499: E 50 5 B 32 H5499: E 50 2 B 32 H51599: E CrMo2 B 32mod1599: E CrMo2 L B 32mod499: E 50 5 MnMo B 32 H5499: E 50 A 32 H5499: E 50 A 32 H5499: E 50 5 Z B 32 H5499: E 50 5 Z B 32 H5499: E 50 5 Z B 32 H5499: E 50 5 Z B 32 H51599: E CrMo5 B 32mod1599: E CrMo9 B 32mod

A5. 1: E 6013A5. 1: E 7014A5. 1: E 7024A5. 1: E 7024A5. 1: E 7024A5. 1: E 7024-1A5. 1: E 70245.5 E-9010-G

A5. 1: E 7016A5. 1: E 7016A5. 1: E 7018A5. 1: E 7018A5. 1: E 7018A5. 1: E 7018-1A5. 1: E 7028A5. 1: E 7048A5. 5: E 7010-A1A5. 5: E 7018-1A5. 5: E 8010-GA5. 5: E 8010-B2A5. 5: E 8010-B2LA5. 5: E 8010-C1A5. 5: E 8010-C3A5. 5: E 8010-GA5.5 E-8018-GA5. 5: E 8018-GA5. 5: E 8018-GA5. 5: E 8018-WA5. 5: E 9018-B3A5. 5: E 9018-B3LA5. 5: E 9018-D1A5. 5: E 9018-GA5.5 E-9018-GA5. 5: E 9018-MA5. 5: E 10018-MA5. 5: E 11018-MA5. 5: E 12018-MA5. 4: E 502-15A5. 4: E 505-15A5.5 E-9015-B9

Z-26Z-16Z-17Z-18Z-19Z-20Z-21Z-910

Z-7DIALOGUEZ-2Z-4Z-4 ACZ-55Z-42Z-47Z-710Z-23Z- CELLUPIPEZ-31 SZ-31Z-32Z-34Z-3Z-3PZ-8Z-33Z-3 WZ-41 SZ-41Z-46Z-40 SZ-X70Z-48Z-50Z-52Z-53 MZ-502Z-505Z-91

MILD & MEDIUM CARBON STEEL ELECTRODES

LOW ALLOY STEEL ELECTRODES

ELECTRODE

ELECTRODE

AWS/ASME SFA

AWS/ASME SFA

DIN

DIN

BS

BS

EN

EN

Z-307 BZ-307 RZ-307 HRZ-308 BZ-308 LZ-308 LVDZ-308 LHRZ-308 HZ-309 BZ-309 SZ-309 CbZ-309 MoZ-310Z-312Z-312 SZ-316 BZ-316 LZ-316 LVDZ-316 LHRZ-316 HSZ-317Z-318 BZ-318Z-320Z-347 BZ-347Z-ARM BSZ-Ni ViZ-2209 BZ-2209 RZ-2594 R

A5. 4: E 307-15A5. 4: E 307-16A5. 4: E 307-16A5. 4: E 308L-15A5. 4: E 308L-16A5. 4: E 308L-17A5. 4: E 308L-16A5. 4: E 308-16A5. 4: E 309L-15A5. 4: E 309L-16A5. 4: E 309Cb-16A5. 4: E 309MoL-16A5. 4: E 310-16A5. 4: E 312-16A5. 4: E 312-16A5. 4: E 316L-15A5. 4: E 316L-16A5. 4: E 316L-17A5. 4: E 316L-16A5. 4: E 316-16A5. 4: E 317L-16A5. 4: E 318-15A5. 4: E 318-16A5. 4: E 385-16modA5. 4: E 347-15A5. 4: E 347-16A5. 4: E 308Mo-15 mod A5. 4: E 308Mo-16 modA5. 4: E 2209-15A5. 4: E 2209-16A5. 4: E 2594-16

----------A5. 13: EFe5-B mod A5. 13: EFeMn-AA5. 13: EFeMn-A modA5. 13: ECoCr-AA5. 13: ECoCr-B-

---8556: E 19 9 L B 20+8556: E 19 9 L R 238556: E 19 9 L R 138556: E 19 9 L R 36 1508556: E 19 9 R 238556: E 23 12 L B 20+8556: E 23 12 L R 238556: E 23 12 Nb R 238556: E 23 12 3 R 238556: E 25 20 R 268556: E 29 9 R 238556: E 29 9 R 238556: E 19 123 L B 20+8556: E 19 123 L R 238556: E 19 12 3 L R 138556: E 19 12 3 L R 26 1508556: E 19 12 3 MPR 23 170-8556: E 19 12 3 Nb B 20+8556: E 19 12 3 Nb R 238556: E 20 25 5 L Cu R 38556: E 19 9 Nb B 20+8556: E 19 9 Nb R 23--8556: E 22 9 3 L B 20+8556: E 22 9 3 L R 23

---2926: E 19 9 L B2926: E 19 9 L R2926: E 19 9 L R2926: E 19 9 L R2926: E 19 9 R2926: E 23 12 L B2926: E 23 12 L R2926: E 23 12 Nb R2926: E 23 12 2 R2926: E 25 20 R2926: E 29 9 R2926: E 29 9 R2926: E 19 12 3 L B2926: E 19 12 3 L R2926: E 19 12 3 L R2926: E 19 12 3 L R2926: E 19 12 3 RMP2926: E 19 13 4 L R2926: E 19 12 3 Nb B2926: E 19 12 3 Nb R-2926: E 19 9 Nb B2926: E 19 9 Nb R2926: E 19 9 3 B2926: E 19 9 3 R--

---1600: E 19 9 L B 221600: E 19 9 L R 121600: E 19 9 L R 111600: E 19 9 L R 53 mod1600: E 19 9 R 121600: E 23 12 L B 421600: E 23 12 L R 121600: E 23 12 Nb R 121600: E 23 12 2 L R 121600: E 25 20 R 12 mod1600: E 29 9 R 121600: E 29 9 R 121600: E 19 12 3 L B 221600: E 19 12 3 L R 121600: E 19 12 3 L R 111600: E 19 12 3 L R 53 mod1600: E 19 12 2 R 721600: E 19 13 4 L R 12 mod1600: E 19 12 3 Nb B 221600: E 19 12 3 Nb R 121600: E 20 25 5 Cu L R 121600: E 19 9 Nb B 221600: E 19 9 Nb R 12--1600: E 22 9 3 L B 221600: E 22 9 3 L R 121600: E 2594 NLR Z3

8555: E 1 UM 3008555: E 1 UM 4008555: E 6 UM 55 R8555: E 6 UM 558555: E 6 UM 608555: E 6 UM 608555: E 10 UM 60 Z8555: E 10 UM 60 GR8555: E 10 UM 65 GR8555: E 10 UM 65 GR8555: E 4 UM 60 S8555: E 7 UM 250 KP8555: E 7 UM 250 KP-8555: E 20 UM 45 CTZ8555: E 20 UM 50 CTZ

----------------

----------------

49505152535455565758596061626364656667686970717273747576777879

80818283848586878889909192939495

Z-104Z-105Z-110Z-111Z-113Z-114Z-120Z-120 BZ-123Z-125Z-130Z-151Z-151 NCZ-152Z-STEL 6Z-STEL 12

STAINLESS STEEL ELECTRODESELECTRODE AWS/ASME SFA

HARD FACING ELECTRODESELECTRODE AWS/ASME SFA

DIN BS EN Pg.

DIN BS EN Pg.

Z-Ni 1Z-Ni BZ-Ni A2Z-Ni 182Z-Ni 182R1Z-Ni 112Z-Ni 112RZ-NiCroMo3Z-NiCroMo4Z-Ni CZ-Ni 190Z-Ni 187Z-BRONZE AZ-BRONZEZ-BRONZE M

Z-SuperNiZ-Ni 99Z-Ni 99 NCZ-Ni 55Z-GSMZ-GMZ-71Z-72Z-OXYCUT

Z-71T1Z-71T5

Z-R2Z-R3Z-R6Z-RMo

A5. 11: ENi-1A5. 11: ENiMo-1A5. 11: ENiCrFe-2A5. 11: ENiCrFe-3A5. 11: ENiCrFe-3A5. 11: ENiCrMo-3A5. 11: ENiCrMo-3A5. 11: ENiCrMo-3A5. 11: ENiCrMo-4A5. 11: ENiCrMo-5A5. 11: ENiCu-7A5. 6: ECuNiA5. 6: ECuSn-AA5. 6: ECuSn-CA5. 6: ECuSn-C

A5. 15: ENi-CIA5. 15: ENi-CIA5. 15: ENi-CIA5. 15: ENiFe-CI-A5. 15: ENiCu-B---

A5. 20: E71T-1A5. 20: E71T-5

A5. 18: ER-70S-2A5. 18: ER-70S-3A5. 18: ER-70S-6A5. 28: ER-80S-D2

8573: E Ni-BG-218573: E Ni-BG-238573: E Ni-BG-238573: E NiFe-1-BG-238573: E FeC-G-BG-268573: E NiCu-BG-23---

-8559: SG 18559: SG 28559: SG Mo

--2901: A 182901: A 30/A 31

440: G2 Ti-440: G3 Si 1 mod440: G4 Mo

1736: EL-NiTi 31736: EL-NiMo 291736: EL-NiCr 15 FeNb1736: EL-NiCr 15 FeMn1736: EL-NiCr 15 FeMn1736: EL-NiCr 20 Mo 9 Nb1736: EL-NiCr 20 Mo 9 Nb1736: EL-NiCr 20 Mo 9 Nb1736: EL-NiMo15 Cr 15 W1736: EL-NiMo15 Cr 15 W mod1736: EL-NiCu 30 Mn1733: EL-CuNi 30-1733: EL-CuSn 71733: EL-CuSn 7

---------------

---------

--

--

--

---------------

96979899100101102103104105106107108109110

111112113114115116117118119

120121

122123124125

NON FERROUS ELECTRODESELECTRODE AWS/ASME SFA DIN BS EN Pg.

CAST IRON & CUTTING ELECTRODESELECTRODE AWS/ASME SFA DIN BS EN Pg.

FLUX CORED WIRE

ELECTRODE AWS/ASME SFA DIN BS EN Pg.

SEMI AUTOMATIC SOLD WIREELECTRODE AWS/ASME SFA DIN BS EN Pg.

---------

1

Mild & Medium Carbon Steel Electrodes

Z-610

Cellulose electrode for pipe and general weldingDeep penetration and good X-ray qualitySuitable for welding pipes, pressure vessels, storagetanks, ships

Description and Applications:

Welding position

ASME: 1G 2F 2G 3G 3G 4G 5G

ISO 6947 PA PB PC PF PG PE PF/PG

C Mn Si0.10 0.50 0.20

Unalloyed construction steelsBoiler and pressure vessel steelsPipe steels

DIN 17 100DIN 17 155DIN 17 172DIN 17 175DIN 1629API 5LXDIN 17 102

St 33 to St 52.3HI, HIIStE 210.7 to StE 415.7St 35.8 to ST 45.8St 35 to St 52.4X42 to X63StE 255 to StE 355A,B,D

Fine grained steelsShipbuilding steels

Re-drying not necessary.

3/321/85/323/161/4

2.53.254.05.06.0

1414141414

350350350350350

60-9080-125

120-180160-230220-280

1.82.94.36.69.5

5.05.05.05.05.0

15.015.015.015.015.0

Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment430 550 25 80 J @- 20

o-C U

45 J @- 30o-C

Current

Typical all weld metal composition [wt%]

Typical all weld metal mechanical properties

Materials to be welded

Welding parameters and packaging data

AWS/ASME SFA A5.1 : E 6010DIN 1913 : E 43 43 C4BS 639 : E 43 43 C 19EN 499 : E 42 2 X 41

Specifications:

= +

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]


Z-611

Description and Application:

Welding position




Current

Cellulose electrode for pipe and general weldingDeep penetration and good X-ray qualitySuitable for welding pipes, pressure vessels, storagetanks, ships on both AC and DC

ASME:ISO 6947

1GPA

C0.12

Mn0.50

Si0.20

2GPB

2GPC

3GPF

3GPG

4GPE

5GPF/PG

AWS/ASME SFA A5.1 : E 6011DIN 1913 : E 43 43 C4BS 639 : E 43 43 C 16EN 499 : E 42 2 C 31

Rp 0.2[MPa]430


Fine grained steelsShipbuilding steels

Rm [MPa]550

Heat TreatmentU

2

A5 [%]25

Impact [ISO-V]80 J @-20oC45 J @-30oC

Specifications:

= + ~ (Uo : 70 v)


St 33 to St 52.3HI, HIIStE 210.7 to StE 415.7St 35.8 to ST 45.8St 35 to St 52.4X42 to X63StE 255 to StE 355A,B,D


3/321/85/323/161/4

2.53.254.05.06.0

1414141414

350350350350350

60-9080-125

120-180160-230220-280

1.82.94.36.69.5

5.05.05.05.05.0

15.015.015.015.015.0

Welding parameters and packaging dataDia

in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

3


Z-6

Rutile coated electrode for welding on uncleanedsurfaces like paint, oil or galvanized steelUsable for pipes, storage tanks and machine parts


Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

C0.07

Mn0.50

Si0.25

DIN 17 100DIN 17 172DIN 1629API 5LXDIN 1681

St 33 to St 37.2 to St 44.3StE 210.7 to StE 360.7St 35 to St 52.4X42, X46GS 38A,B,C,D

Cast steelsShipbuilding steels


3/321/85/323/16

2.53.254.05.0

14141414

350350350350

70-95100-150140-200180-270

1.93.04.57.0

5.55.55.55.5

16.516.516.516.5


Rp 0.2 [MPa]450

Rm [MPa]550

A5 [%]23

Impact [ISO-V]70 J @ 0oC

Heat TreatmentU


Unalloyed construction steelsPipe steels



AWS/ASME SFA A5.1 : E 6013DIN 1913 : E 43 22 RR6BS 639 : E 43 22 RR 22EN 499 : E 42 0 RR 12

Specifications:

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)

4


Z-9

Rutile coated universal electrode for welding generalstructural steelsSuitable for badly prepared plates of differentthicknesses and bad surface conditionsEasy slag release and arc striking


Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

C0.08

Mn0.50

Si0.30

DIN 17 100DIN 17 172DIN 1629API 5LXDIN 1681

St 33 to St 37.2 to St 44.3StE 210.7 to StE 360.7St 35 to St 52.4X42, X46GS 38A,B,C,D



5/643/321/85/323/16

2.02.53.254.05.0

12141414

14/18

300350350350

350/450

55-8570-100

100-150140-200180-230

1.11.93.04.5

7.0/9.0

4.05.55.55.5

5.5/7.0

12.016.516.516.5

16.5/21


Rp 0.2 [MPa]400

Rm [MPa]520

A5 [%]24


Heat TreatmentU





AWS/ASME SFA A5.1 : E 6013DIN 1913 : E 43 22 R(C)3BS 639 : E 43 22 R 12EN 499 : E 42 0 R 12

Specifications:

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)

5


Z-11

Thickly coated all purpose rutile electrodeSuitable for badly prepared surfaces such asrust and paint and different plate thicknessVery easy slag release and arc striking


Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

C0.08

Mn0.50

Si0.25

DIN 17 100DIN 17 172DIN 17 175DIN 1629DIN 1681

St 33, St 37.2 to St 52.3StE 210.7 to StE 360.7St 35.8, St 45.8St 35 to St 52.4GS 38Cast steels


5/643/321/8

5/323/16

2.02.5

3.254.05.0

1214

14/1814/1814/18

300350

350/450350/450350/450

50-7060-100

100-150140-200180-260

1.12.0

3.3/4.24.9/6.27.7/9.9

4.05.0

5.0/6.05.0/6.05.0/6.0

12.015.0

15.0/18.015.0/18.015.0/18.0


Rp 0.2 [MPa]440

Rm [MPa]520

A5 [%]26


Heat TreatmentU






Specifications:

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)

6


Z-14

Thickly coated electrode for general purposesExceptionally smooth welding seams, low spatterloss and self detaching slag


Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

C0.09

Mn0.55

Si0.30

DIN 17 100DIN 1681DIN 17 172DIN 17 175DIN 1629

St 33, St 37.2 to St 52.3GS 38, GS 45StE 210.7 to StE 360.7St 35.8 to St 45.8St 35 to St 52.4A,B,C,D,EShipbuilding steels


3/321/8

5/323/16

2.53.254.05.0

14181818

350350/450350/450

450

70-110100-160160-200200-270

2.14.87.2

10.3

5.05.0/6.05.0/6.0

6.0

15.015.0/18.015.0/18.0

18.0


Rp 0.2 [MPa]420

Rm [MPa]520

A5 [%]24


Heat TreatmentU


Unalloyed construction steelsCast steelsPipe steels




Specifications:

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)

7


Z-15

Heavy coated rutile electrode for general purposesVery even weld in flat and fillet positions


Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

C0.09

Mn0.60

Si0.50




3/321/8

5/323/16

2.53.254.05.0

14181818

350450450450

70-110100-160160-200200-270

2.14.87.2

10.3

5.06.06.06.0

15.018.018.018.0


Rp 0.2 [MPa]400

Rm [MPa]480

A5 [%]24


Heat TreatmentU






Specifications:

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)

8


Z-15 (14)

Rutile coated electrode for general purposesExceptionally smooth welding seamsSuitable for welding thin metal plates


Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

C0.07

Mn0.55

Si0.50




3/321/8

5/323/16

2.53.254.05.0

14181818

350350/450350/450

450

70-110100-160160-200200-270

2.14.87.2

10.30

5.05.0/6.05.0/6.0

6.0

15.015.0/18.015.0/18.0

18.0


Rp 0.2 [MPa]420

Rm [MPa]520

A5 [%]24


Heat TreatmentU






Specifications:

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)

9


Z-26

Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

C0.07

Mn0.55

Si0.25

DIN 17 100DIN 17 155DIN 17 172DIN 17 175DIN 1629DIN 1681

St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7 to StE 360.7St 35.8, St 45.8St 35 to St 52.4GS 38, GS 45Cast steels


5/643/321/8

5/323/161/4

2.02.5

3.254.05.06.0

121414

14/181414

300350350

350/450350/450

450

55-7070-100

100-150140-200160-230240-340

1.11.93.0

4.5/5.89.0

13.0

4.0/2.05.55.5

5.5/7.05.5/7.0

7.0

12.016.516.5

16.5/21.016.5/21.0

21.0


Rp 0.2 [MPa]470

Rm [MPa]550

A5 [%]25


Heat TreatmentU





AWS/ASME SFA A5.1 : E 6013DIN 1913 : E 51 22 R(c)3BS 639 : E 51 22 R 12EN 499 : E 42 0 RC 12

Specifications:

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)

Rutile Coated all position electrode with a widerange of applications in shipbuilding and structuralworkSuitable for badly prepared plates of differentthicknesses


10


Z-16

Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

C0.08

Mn0.60

Si0.25

DIN 17 100DIN 17 155DIN 17 172DIN 17 175DIN 1629DIN 1681

St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7 to StE 360.7St 35.8, St 45.8St 35 to St 52.4GS 38, GS 45Cast steels


5/643/321/8

5/323/16

2.02.5

3.254.05.0

1214141414

300350350350350

50-7060-100

110-150130-170190-230

1.12.03.64.97.5

4.05.05.05.05.0

12.015.015.015.015.0


Rp 0.2 [MPa]460

Rm [MPa]540

A5 [%]25


Heat TreatmentU





AWS/ASME SFA A5.1 : E 7014DIN 1913 : E 51 22 RR(C)6BS 639 : E 51 22 RR 12EN 499 : E 46 0 RR 32

Specifications:

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Thick rutile electrode for fast deposition rateFocused, stable and penetrating arcSelf detaching slagSuitable for badly prepared plates of differentthicknesses


Current

= + ~ (Uo : 50 V)

11


Z-17

Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

C0.08

Mn0.50

Si0.30

Re-drying: not necessary.

3/321/8

5/323/16

2.53.254.05.0

14181818

350450450450

60-110120-150150-190200-250

2.45.57.8

11.5

5.06.06.06.0

15.018.018.018.0



AWS/ASME SFA A5.1 : E 7024DIN 1913 : E 51 22 RR11 140BS 639 : E 51 22 RR 140 35EN 499 : E 42 0 RR 53

Specifications:

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)

Rutile coated electrode for welding engineeringstructures140% metal recoverySmooth weld appearance and self detaching slag


Rp 0.2 [MPa]430

Rm [MPa]510

A5 [%]25


Heat TreatmentU


DIN 17 100DIN 17 155DIN 17 172DIN 1629DIN 1681

St 33, St 37.2 to St 52.3HI, HII, 17Mn4StE 210.7 to StE 360.7St 35 to St 52.4GS 38A,B,C,D


Unalloyed construction steelsBoilerPlatePipe steels


12


Z-18

Welding position

ASME:

ISO 6947

1G

PA

2F

PB

C0.07

Mn0.70

Si0.25

DIN 17 100DIN 17 155DIN 1681

St 33, St 37.2 to St 52.3HI, HII, 17Mn4GS 38A,B,C,D

Re-drying: not necessary

3/321/8

5/323/161/4

2.53.254.05.06.0

1418181818

350450450450450

85-125130-175150-240210-290290-420

3.06.5

10.015.019.5

4.56.06.06.06.0

13.518.018.018.018.0


Rp 0.2 [MPa]480

Rm [MPa]550

A5 [%]26


Heat TreatmentU


Unalloyed construction steelsBoiler and pressure vessel steelsCast steelShipbuilding steel




Specifications:

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)

Rutile electrode for fillet welds and horizontalV-welds165% metal recovery with high speed weldingSmooth weld appearance and self detaching slag


13


Z-19

Welding position

ASME:

ISO 6947

1G

PA

2F

PB

C0.07

Mn0.70

Si0.25


1/85/323/161/4

3.254.05.06.0

18181818

450450450450

130-170150-230200-350280-480

6.911.215.722.1

6.06.06.06.0

18.018.018.018.0


Rp 0.2 [MPa]460

Rm [MPa]550

A5 [%]27


Heat TreatmentU



in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)


Specifications:Rutile electrode for fillet welds and horizontalV-welds185% metal recovery with high speed weldingSmooth weld appearance and self detaching slag


DIN 17 100DIN 17 155DIN 1681

St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5GS 38A,B,C,D

Cast steels

Unalloyed construction steelsBoiler and pressure vessel steelsCast steelsShipbuilding steels


14


Z-20

Welding position

ASME:

ISO 6947

1G

PA

2F

PB


1/85/323/161/4

3.254.05.06.0

18181818

450450450450

130-170150-230200-350280-480

7.210.616.023.8

6.06.06.06.0

18.018.018.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)

AWS/ASME SFA A5.1 : E 7024-1DIN 1913 : E 51 32 RR11 160BS 639 : E 51 32 RR 160 32EN 499 : E 46 0 RR 73

High speed, high deposit (160% metal recovery),rutile electrodeIdeal for very fast fillet welding and for fillinghorizontal groovesFully controlled molten pool, spatter free and selfdetaching slagSuitable for welding on moderate and thick platesfor buildings, bridges, shipbuilding, etc

Description and Applications: Specifications:

C0.09

Mn0.85

Si0.45


Rp 0.2 [MPa]460

Rm [MPa]550

A5 [%]25


50 J @ -20oC

Heat TreatmentU


DIN 17 100DIN 17 155DIN 1681




15


Z-21

Welding position

ASME:

ISO 6947

1G

PA

2F

PB


1/85/323/161/4

3.254.05.06.0

18181818

450450450450

130-170150-230200-350280-400

7.210.616.024.3

6.06.06.06.0

18.018.018.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 50 V)


Rutile electrode for fillet and horizontal V-welds190% metal recovery with high speed weldingSmooth weld appearance and self detaching slag


C0.07

Mn0.70

Si0.25


Rp 0.2 [MPa]460

Rm [MPa]550

A5 [%]27


Heat TreatmentU


DIN 17 100DIN 17 155DIN 1681




16


Z-910

C0.11

Mn1.1

Si0.55

Ni0.62

Mo0.23


Rp 0.2 [MPa]690

Rm [MPa]616

A5 [%]21



API SPEC5L: X65, X70


AWS/ASME SFA 5.5 : E 9010-GEN ISO 2560-A E50021

Specifications:Cellulose electrode designed for welding in all positionincluding vertical down for high diameter pipelines.

Especially recommended for hot passes, filler and coverlayers.



3/321/8

5/32

2.53.254.0

141414

350350350

80-125110-180140-230

555

151515


in mmLength

in mmCurrent[amps]

Weight packet[kg]

Weight carton[kg]

Welding position

17

Low Alloy Steel Electrodes

Z-7

Welding position

AWS/ASME SFA A5.1 : E 7016DIN 1913 : E 51 44 B9 H10BS 639 : E 51 44 B 16 HEN 499 : E 46 3 B 11 H10

Specifications:Basic coated electrode for high quality joiningof general construction steelsVery good X-ray propertiesSuitable for rool pass welding in narrow jointsGood impact toughness at low temperatures


ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

3G

PG

4G

PE

C0.07

Mn1.00

Si0.60

Re-drying: 2h/300oC

3/321/8

5/323/16

2.53.254.05.0

14141418

350350350450

70-80100-120140-160190-210

1.93.14.79.2

5.05.05.06.0

15.015.015.018.0


Rp 0.2 [MPa]490

Rm [MPa]570

A5 [%]26


100 J @ -20oC80 J @ -30oC

Heat TreatmentU


DIN 17 100DIN 17 155DIN 17 172API 5LXDIN 1626-1630DIN 1681

St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7X42, X46, X52, X60St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS 45, GS 52A,B,C,D,E AH, DH, EH


General structure steelsBoiler and pressure vessel steelsPipe steels



in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

18


DIALOGUE

Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

C0.06

Mn1.10

Si0.65

Re-drying: 300oC/2h

3/321/8

5/323/16

2.53.254.05.0

1414/18

1818

350350/450350/450

450

60-9095-150

140-190190-250

2.03.4/4.3

6.710

4.54.55/6

6

13.513.5

15/1818


Rp 0.2 [MPa]420

Rm [MPa]530

A5 [%]30

Impact [ISO-V]110 J @ -20oC100 J @ -30oC

Heat TreatmentU



in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

AWS/ASME SFA A5.1 : E 7016DIN 1913 : E 51 44 B10 H10BS 639 : E 51 44 B 26 HHEN 499 : E 42 3 B 12 H10

Specifications:Double coated basic electrodeSuitable for repair and maintenance workExcellent for root pass and all positional weldingHigh impact toughness at low temperatures


DIN 17 100DIN 17 155DIN 17 172API 5LXDIN 1626-1630DIN 1681DIN 17 175DIN 17 102

St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7X42, X46, X52, X60St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS 45, GS 52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,E AH, DH, EH

Cast steelsElevated temperature steelsFine grained steelShipbuilding steels



19


Z-2

Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

C0.06

Mn1.00

Si0.35

Re-drying: 300oC/2h

3/321/8

5/323/161/4

2.53.254.05.06.0

1414/1814/18

1818

350350/450350/450

450450

60-9090-140

140-190190-240250-320

2.33.6/4.65.3/6.810.1014.20

4.54.5/6.04.5/6.0

6.06.0

13.513.5/18.013.5/18.0

18.018.0



in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

AWS/ASME SFA A5.1 : E 7018DIN 1913 : E 51 44 B10 H10BS 639 : E 51 44 B 26 HHEN 499 : E 42 3 B 32 H10

Basic coated all position welding electrodeGood toughness at low temperaturesSuitable for welding general structural steels


Rp 0.2 [MPa]430

Rm [MPa]510

A5 [%]28


Heat TreatmentU


DIN 17 100DIN 17 155DIN 17 172DIN 1626-1630DIN 1681DIN 17 175DIN 17 102

St 33, St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS 45, GS 52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,E




20


Z-4

Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Re-drying: 300oC/2h

3/321/8

5/323/161/4

2.53.254.05.06.0

1414/1814/18

1818

350350/450350/450

450450

75-100110-140140-190190-240230-330

2.63.8/4.95.6/7.2

10.514.3

4.54.5/6.05.0/6.0

6.06.0

13.513.5/18.015.0/18.0

18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)


Basic coated low hydrogen electrode with highductilitySuitable for welding general construction steelsVery good bead appearranceGood impact toughness at -30oC


C0.08

Mn1.00

Si0.60


Rp 0.2 [MPa]480

Rm [MPa]570

A5 [%]26


Heat TreatmentU







21


Z-4 AC

Re-drying: 300oC/2h

3/321/8

5/323/16

2.53.254.05.0

1414/1814/1814/18

350350/450350/450350/450

75-100110-140130-170180-240

2.53.7/4.95.5/7.1

8.1/10.4

4.54.5/6.05.0/6.05.0/6.0

13.513.5/18.015.0/18.015.0/18.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

C0.09

Mn1.00

Si0.65







Basic coated low hydrogen electrode with highductilitySuitable for welding general construction steelsVery good bead appearranceGood impact toughness at -30oCPreferably welded on AC


Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Current

= + ~ (Uo : 70 V)


Rp 0.2 [MPa]450

Rm [MPa]550

A5 [%]28


Heat TreatmentU


22


Z-55

Welding position

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Current

= + ~ (Uo : 70 V)

C0.06

Mn1.45

Si0.45

API SPEC5L: X65, X70, X70


AWS/ASME SFA A5.1 : E 7018-1DIN 8529 : EY 46 66 MN BH5EN 499 : E 46 5B 32 H5

Low hydrogen basic electrode designed for weldingin all positions.Excellent strength and high toughness down to -46oC. suitable for welding medium and highstrength steels.It can be used in as welded conditions or after heattreatment.



Rp 0.2 [MPa]520

580

Rm [MPa]600

500

A5 [%]25

27

Impact [ISO-V]140 J @ -29oC140 J @ -30oC155 J @ -30oC115J @ -46oC

Heat Treatment

PWHT620oC@8hr


3/321/8

5/323/16

2.53.254.05.0

141418

17.7

350350450450

60-90110-140140-190190-260

5566

15151818


in mmLength

in mmCurrent[amps]

Weight packet[kg]

Weight carton[kg]

23


Z-42

Re-drying: 300oC/2h

1/85/323/161/4

3.254.05.06.0

18181818

450450450450

120-190190-230230-300300-350

6.710.216.023.0

5.55.55.55.5

16.516.516.516.5


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Welding position

ASME:

ISO 6947

1G

PA

2F

PB

Current

= + ~ (Uo : 70 V)

Rp 0.2 [MPa]540

Rm [MPa]550

A5 [%]24


Heat TreatmentU


AWS/ASME SFA A5.1 : E 7028DIN 1913 : E 51 43 B(R)12 160 H5BS 639 : E 51 43 B 160 36 HEN 499 : E 42 3 RB 53 H5

High efficiency basic electrode (160% metalrecovery)Fast deposition rates and high productivityIdeal for steel construction, bridges, ship building,containers and storage tank weldingHigh porosity resistance


C0.05

Mn1.10

Si0.30


DIN 17 100DIN 17 155DIN 17 172DIN 1681DIN 17 102DIN 17 175

St 33 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7GS 38, GS 45, GS 52StE 255 to StE 420St 35.8, St 45.8A,B,C,D,E,AH,DH,EH

Unalloyed construction steelsBoiler and pressure vessel steelsPipe steelsCast steelsElevated temperature steelsFine grained steelsShipbuilding steels


24


Z-47

Welding position

Re-drying: 300oC/2h

3/321/8

5/323/16

2.53.254.05.0

14141418

350350/450

350450

70-9090-140

135-180175-255

1.72.94.48.9

5.05.0/6.05.0/6.0

6.0

15.015.0/18.015.0/18.0

18.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

Rp 0.2 [MPa]430

Rm [MPa]530

A5 [%]26

Impact [ISO-V]100 J @ -29oC

Heat TreatmentU

C0.08

Mn1.00

Si0.60


AWS/ASME SFA A5.1 : E 7048DIN 1913 : E 51 44 B(R)9 H10BS 639 : E 51 44 B 110 54 HHEN 499 : E 42 3 B 35 H10

Vertical down welding basic electrodeRecommended for welding in shipbuildingconstructionVery little slag and spatter lossHigh welding speed


ASME:

ISO 6947

1G

PA

2F

PB

3G

PG

5G

PG



St 33 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7St37.0/4, St44.0/4, St52.0/4GS 38, GS 45, GS 52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,E,AH,DH,EH

General structural steelsBoiler and pressure vessel steelsPipe steelsCast steelsElevated temperature steelsFine grained steelsShipbuilding steels


25


Z-710

Welding position


3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

60-9090-120

120-160160-200

1.62.84.36.6

5.05.05.05.0

15.015.015.015.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= +

Rp 0.2 [MPa]500

Rm [MPa]580

A5 [%]23

Av [ISO-V]70 J @ 0oC

Heat TreatmentS

C0.10

Mn0.50

Si0.20

Mo0.50


AWS A5.5 : E 7010-A1BS 2493 : E MoCEN 499 : E 42 0 Mo C 41

Cellulose coated electrodeVertical down welding of high strength pipesHigh mechanical properties




St 37 to St 52.3HIIStE 210.7 to StE 415.7St 35.8, St 45.8St 35 to St 52.4X42 to X63StE 255 to StE 355


Fine grained steels


ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

3G

PG

4G

PE

5G

PF/PG

26


Z-23

Welding position

Re-drying: 300oC/2h

3/321/8

5/323/16

2.53.254.05.0

1414

14/1814

350350

350/450450

60-9090-130

130-190180-220

2.33.5

5.0/6.06.0

4.55.0

5.0/6.06.0

13.515.0

15.0/18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]410

Rm [MPa]540

A5 [%]28


Heat TreatmentS

C0.05

Mn0.70

Si0.40

Mo0.50


AWS/ASME SFA A5.5 : E 7018-A1DIN 8575 : E Mo B 26BS 2493 : E Mo BEN 1599 : E Mo B 32 mod

Basic coated electrodeFor welding creep resistant Mo containing low-alloy steelsWithstands service temperatures up to 525oC



DIN 17 155

DIN 17 245DIN 17 175DIN 17 102

14Mn4, 19Mn5, 15Mo3St 45.8, 15Mo3GS C25, GS 22 Mo415Mo3, 16Mo5StE 285 to StE 420

Boiler and pressure vessel steelsPipe steel for elevated temperaturesCast steelsElevated temperature steelsFine grained steels


27


Z-CELLUPIPE

Welding position


3/321/8

5/323/16

2.53.254.05.0

14141818

350350450450

60-9080-125

120-180160-230

1.82.95.68.6

5.05.05.05.0

15.015.015.015.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= +

Rp 0.2 [MPa]550

Rm [MPa]600

A5 [%]23


50 J @ -20oC

Heat TreatmentU

C0.10

Mn0.80

Si0.25

Ni0.45

Mo0.45



DIN 17 172API 5LXDIN 17 102

StE 290.7 to StE 415.7, StE 290.7 TM to StE 445.7 TMX42 to X70StE 255 to StE 355

Pipe steels

Fine grained steels


ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

3G

PG

4G

PE

5G

PF/PG

AWS/ASME SFA A5.5 : E 8010-GBS 639 : E 51 32 C 10EN 499 : E 46 2 1NiMo C 41

Cellulosic electrode for vertical down pipe weldingEasy peentration due to forceful arcSuitable for hot passes in the root, filler andcapping passesLow suscptability to wagon tracks, windowsand pinholesGood X-ray quality


28


Z-31 S

Welding position

Re-drying: 300o C/2h

3/321/8

5/323/16

2.53.254.05.0

1414

14/1818

350350

350/450450

60-10090-130

130-180180-250

2.23.4

5.0/6.410.0

4.55.0

5.0/6.06.0

13.515.0

15.0/18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

AWS/ASME SFA A5.5 : E 8018-B2DIN 8575 : E CrMo1 B 26BS 2493 : E 1 CrMo BEN 1599 : E CrMo 1 B 32 mod

Basic coated electrode for welding creep resistingsteels containing 1% Cr and 0.5% MoService temperatures of maximum 550oC


Rp 0.2 [MPa]540

Rm [MPa]690

A5 [%]20

Import [ISO-V]120 J @ 20oC

Heat TreatmentS

C0.08

Mn0.80

Si0.35

Cr1.10

Mo0.50



DIN 17 155

DIN 17 200DIN 17 210DIN 17 245

13CrMo44, 16CrMo44, 15CrMo5, 24CrMo5,22CrMo4425CrMo415Cr3, 16MnCr5, 20MnCr5GS 17CrMo55, GS 22CrMo54, GS 17CrMo55

Elevated temperature steels

Quenched and tempered steelsCase hardening steelsCast steels


29


Z-31

Welding position


3/321/8

5/323/16

2.53.254.05.0

1414

14/1818

350350

350/450450

60-10090-130

130-180180-250

2.23.4

5.0/6.410.0

4.55.0

5.0/6.06.0

13.515.0

15.0/18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

AWS/ASME SFA A5.5 : E 8018-B2 LDIN 8575 : E CrMo1 B 26BS 2493 : E 1 CrMo L BEN 1599 : E CrMo 1 L B 32 mod

Basic coated electrode for welding creep resistingsteels containing 1% Cr and 0.5% MoService temperatures of maximum 550oC

Specifications:Description and Applications:

Rp 0.2 [MPa]540

Rm [MPa]690

A5 [%]20

Import [ISO-V]120 J @ 20oC

Heat TreatmentS

C0.05

Mn0.90

Si0.50

Cr1.15

Mo0.55



DIN 17 155DIN 17 200DIN 17 210DIN 17 245

13CrMo44, 16CrMo44, 15CrMo5, 24CrMo5, 22CrMo4425CrMo415Cr3, 16MnCr5, 20MnCr5GS 17CrMo55, GS 22CrMo54, GS 17CrMo55

Elevated temperature steelsQuenched and tempered steelsCase hardening steelsCast steels


30


Z-32

Welding position


3/321/8

5/323/161/4

2.53.254.05.06.0

1414/1814/18

1818

350350/450350/450

450450

80-100100-140130-185190-250240-320

2.23.6/4.

5.4/6.910.815.0

4.55.0/6.05.0/6.0

6.06.0

13.515.0/18.015.0/18.0

18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]520

Rm [MPa]590

A5 [%]27

Import [ISO-V]110 J @ -59oC

Heat TreatmentS

AWS/ASME SFA A5.5 : E 8018-C1DIN 8529 : E SY 42 77 2Ni B H5BS 2493 : E 2Ni B HEN 499 : 46 6 2Ni B 42 H5

Basic coated electrode for welding low alloystructures subjected to service down to -60oCGood corrosion resistance to chloric and sulphuricacid


C0.05

Mn0.90

Si0.40

Ni2.15



DIN 17 102DIN 17 280

StE315 to StE46011MnNi53, 13MnNi63, 14NiMn6, 10Ni14

Fine grained steelsLow temperature steels


31


Z-34

Welding position


3/321/8

5/323/16

2.53.254.05.0

1414/1814/18

18

350350/450350/450

450

75-110100-140130-200200-275

2.33.8/4.95.5/7.0

11.0

4.55.0/6.05.0/6.0

6.0

13.515.0/18.015.0/18.0

18.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]490

Rm [MPa]580

A5 [%]28

Import [ISO-V]70 J @ -40oC40 J @ -60oC

Heat TreatmentU

AWS/ASME SFA A5.5 : E 8018-C3DIN 8529 : E Y 46 76 1Ni B H5BS 2493 : E 1Ni B H

Low hydrogen basic coated electrodeSuitable for welding of low alloyed, fined grained,high tensile strength steels


C0.05

Mn0.90

Si0.35

Ni0.90

Mo0.25



DIN 17 102DIN 17 280

StE255 to StE50011MnNi53, 13MnNi63, 14NiMn6, 10Ni14

Fine grained steelsLow temperature steels


32


Z-3

Welding position


3/321/8

5/323/161/4

2.53.254.05.06.0

1414/1814/1814/18

18

350350/450350/450

450450

75-110110-140140-180190-260240-330

2.53.6/4.65.1/6.6

8.0/10.315.0

4.55.0/6.05.0/6.0

6.06.0

13.515.0/18.015.0/18.0

18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]500

Rm [MPa]580

A5 [%]26


Heat TreatmentU

AWS/ASME SFA A5.5 : E 8018-GDIN 1913 : E 51 33 B10 H5BS 639 : E 51 33 B 120 26 HEN 499 : E 50 2 B 32 H5

Basic coated low hydrogen electrodeSuitable for maintenance repairing of agriculturalequipmentElectrode produces crack free and tough weldedjoints


C0.06

Mn1.30

Si0.25

Mo0.20



DIN 17 100DIN 1681DIN 17 175DIN 17 102

St 52.3GS 52St45.8StE 315 to StE 500

General structural steelsCast steelsElevated temperature steelsFine grained steels


33


Z-3P

Welding position


3/321/8

5/32

2.53.254.0

1414/18

18

350350/450

450

60-9090-140

110-190

4.55.0/6.0

6.0

13.513.5/18.0

18.0


in mmLength

in mmCurrent[amps]

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]620

Rm [MPa]540

A5 [%]26


AWS/ASME SFA A5.5 : E 8018-GEN ISO 2500-A2005 E503MoB42H5

Low hydrogen welding electrode with basic coating.Designed for all position welding except vertical down.Especially recommended for filler and cover layers ofpipeline.


C0.050

Mn1.03

Si0.38

Mo0.36



API SPEC 5L: X46, X52, X56, X60


34


Z-8

Welding position


3/321/8

5/323/161/4

2.53.254.05.06.0

1414/1814/18

1818

350350/450350/450

450450

60-9090-135

140-180180-240260-310

2.13.5/4.56.8/8.7

10.615.1

4.55.0/6.05.0/6.0

6.06.0

13.515.0/18.015.0/18.0

18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]500

Rm [MPa]590

A5 [%]30

Impact [ISO-V]100 J @ -20oC90 J @ -40oC60 J @ -60oC

Heat TreatmentU

AWS/ASME SFA A5.5 : E 8018-GDIN 8529 : E Y 50 76 Mn 1Ni B H5BS 639 : E 51 54 B 120 26 HEN 499 : E 50 6 Mn 1Ni B 32 H5

Basic coated electrode with maximum 1% NiExcellent impact toughness at very lowtemperatures


C0.06

Mn1.60

Si0.30

Mo0.60



DIN 17 100DIN 1681DIN 17 175DIN 17 102DIN 17 280

St 52.3GS 52St45.8StE 315 to StE 50011MnNi53, 13MnNi63, 14MnNi6

General structural steelsCast steelsElevated temperature steelsFine grained steelsLow temperature steels


35


Z-33

Welding position


5/643/321/8

5/323/161/4

2.02.5

3.254.05.06.0

1214

14/1814/18

1818

300350

350/450350/450

450450

50-7575-95

90-140135-185175-255250-330

1.22.3

3.7/4.85.8/7.5

11.416.5

4.04.5

4.5/6.05.0/6.0

6.06.0

1213.5

13.5/18.015.0/18.0

18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]530

Rm [MPa]600

A5 [%]25


Heat TreatmentS

AWS/ASME SFA A5.5 : E 8018-GDIN 8529 : E SY 50 66 Mn B H5BS 639 : E 51 55 B 120 16 HEN 499 : E 50 5 B 32 H5

Basic coated low hydrogen electrodeDesigned for all position weldingSuited for welding high strength fine grainedstructural steelsHigh impact toughness at -46oC


C0.08

Mn1.50

Si0.35



DIN 17 100DIN 1681DIN 17 175DIN 17 102DIN 17 280

St 52.3GS 52St45.8StE 315 to StE 50011MnNi53, 13MnNi63, 14MnNi6

General structural steelsCast steelsElevated temperature steelsFine grained steelsLow temperature steels


36


Z-3 W

Welding position


3/321/8

5/323/16

2.53.254.05.0

1414/1814/1814/18

350350/450350/450

450

75-110110-140150-200190-260

2.53.7/4.85.5/7.1

8.2/10.5

4.54.5/6.05.0/6.0

6.0

13.513.5/18.015.0/18.0

18.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]500

Rm [MPa]600

A5 [%]25


Heat TreatmentU

AWS/ASME SFA A5.5 : E 8018-WDIN 8529 : E Y 50 32 1NiCu B H5EN 499 : E 50 2 B 32 H5

Basic coated electrode for welding thick structural“weathering” steels of similar compositionresistant to atmospheric corrosionHigh mechanical properties


C0.05

Mn1.20

Si0.35

Cr0.50

Ni0.60

Cu0.50



DIN 17 100DIN 17 175API 5LXDIN 17 102

St 37.2 to St 52.3HI, HII, 17Mn4, 19Mn5X42, X52, X60StE 255 to StE 420A,B,C,D,E, AH, DH, EHWTSt 37, WTSt 52.3

Unalloyed construction steelsBoiler and pressure vessel steelsPipe steels Fine grained steelsShipbuilding steelsWeather resistant structural steels


37


Z-41 S

Welding position


3/321/8

5/323/16

2.53.254.05.0

1414

14/1818

350350

350/450450

70-11090-130

130-180180-250

2.23.5

5.1/6.610.0

4.55.0

5.0/6.06.0

13.515.0

15.0/18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]580

Rm [MPa]720

A5 [%]18


Heat TreatmentS

AWS/ASME SFA A5.5 : E 9018-B3DIN 8575: E CrMo2 B 26BS 2493 : E 2CrMo BEN 1599 : E CrMo2 B 32 mod

Basic coated electrode for welding creep resistingsteels containing 2% Cr and 1% MoService temperatures of maximum 600oC


C0.09

Mn0.75

Si0.40

Cr2.25

Mo1.05



DIN 17 175

DIN 17 245

10CrMo9 10, 12CrMo9 10, 10CrSiMo V7, 24CrMo10GS 12CrMo9 10, GS 18CrMo9 10GS 19CrMo9 10

Creep and hydrogenresisting steelsCast steels


38


Z-41

Welding position


3/321/8

5/323/16

2.53.254.05.0

1414

14/1818

350350

350/450450

70-11090-130

130-180180-250

2.23.5

5.1/6.610.0

4.55.0

5.0/6.06.0

13.515.0

15.0/18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]580

Rm [MPa]720

A5 [%]18


Heat TreatmentS

AWS/ASME SFA A5.5 : E 9018-B3 LDIN 8575: E CrMo2 B 26BS 2493 : E 2CrMo L BEN 1599 : E CrMo2 L B 32 mod

Basic coated electrode for welding creep resistingsteels containing 2% Cr and 1% MoService temperatures of maximum 600oC


C0.05

Mn0.80

Si0.40

Cr2.00

Mo1.00



DIN 17 175

DIN 17 245

10CrMo9 10, 12CrMo9 10, 10CrSiMo V7, 24CrMo10GS 12CrMo9 10, GS 18CrMo9 10GS 19CrMo9 10

Creep and hydrogenresisting steelsCast steels


39


Z-46

Welding position


3/321/8

5/323/16

2.53.254.05.0

14141418

350350/450350/450

450

75-100110-140150-190190-260

2.13.66.0

11.2

5.05.0/6.05.0/6.0

6.0

15.015.0/18.015.0/18.0

18.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]600

Rm [MPa]650

A5 [%]23


Heat TreatmentS

AWS/ASME SFA A5.5 : E 9018-D1DIN 8529: E SY 55 65 MnMo B H5BS 2493 : E MnMo B HEN 499 : E 50 5 MnMo B 32 H5

Basic coated electrode suited for welding hightensile structural steels, working at very lowtemperaturesExtremely low diffusible hydrogen content


C0.07

Mn1.45

Si0.40

Mo0.35



DIN 17 100

DIN 17 155

St 33, St 37.2 to St 52.3DOMEX 400TE, 450, 480HI, HII, 17Mn4, 19Mn5USS-T

General structural steels

Boiler and pressure vessel steelsFine grained steels


40


Z-40 S

Welding position


3/321/8

5/323/16

2.53.254.05.0

14141418

350350350450

75-100110-140150-190190-260

2.13.65.2

10.3

4.55.05.06.0

13.515.015.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= +

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]500

Rm [MPa]600

A5 [%]25

Impact [ISO-V]-

Heat TreatmentS

AWS/ASME SFA A5.5 : E 9018-GDIN 8529: E SY 50 0 1NiMo B H5EN 499 : E 50 A 32 H5

Basic coated electrode for welding steels suchas 4130 and 8630 subjected to heat treatingWelded joints are crack free and tough


C0.05

Mn1.25

Si0.40

Cr0.60

Mo0.35

Ni1.20



API 5LXDIN 17 102DIN 17 102

X70, X 75, X80StE420, StE460, StE50022NiMoCr37, 17MnMoV64, 15NiCuMoNb5,20MnMoNi45, 20MnMoNi55

Pipe steelsFine grained steelsHigh temperature fine grained steels


41


Z-X70

Welding position


3/321/8

5/32

2.53.254.0

1414

14/18

350350

350/450

60-9090-140

110-190

2.252.52.5

13.51515


in mmLength

in mmCurrent[amps]

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70 V)

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]690

Rm [MPa]605

A5 [%]25


AWS/ASME SFA A5.5 : E 9018-GEN 757 E552MnMoB

Low hydrogen basic electrode designed for weldingin al positions except vertical down.Especially recommended for filler and cover layers of high diameter pipelines.


C0.05

Mn1.5

Si0.32

Mo0.50



API SPEC5L: X65, X70,X70


42


Z-48

Welding position


3/321/8

5/323/161/4

2.53.254.05.06.0

1414141818

350350

350/450450450

70-10090-140

140-190180-250240-320

2.13.65.2

10.414.9

4.55.0

5.0/6.06.06.0

13.515.0

15.0/18.018.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= ~ (Uo : 70 V)+

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]580

Rm [MPa]640

A5 [%]24


Heat TreatmentU

AWS/ASME SFA A5.5 : E 9018-MDIN 8529 : E Y 55 87 2NiMo B H5BS 2493 : E MnNi B HEN 499 : E 50 5 Z B 32 H5

Basic coated electrode for welding of lowtemperature, high strength, fine grained structuralsteelsGood impact toughness at low temperatures


C0.05

Mn0.90

Si0.25

Ni1.75

Mo0.30



DIN 17 100DIN 17 155DIN 17 172 DIN 1681DIN 17 175DIN 17 102DIN 17 102

St 50.2, St 60.215Mo3StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE 360.7GS 6010Mo3, 16Mo5TStE420 to TStE50022NiMoCr37, 17MnMoV64, 15 NiCuMoNb5,20MnMoNi45, 20MnMoNi55

General structural steelsBoiler and pressure vessel steelsPipe steelsCast steelsElevated temperature steelsFine grained steelsHigh temperature fine grained steels


43


Z-50

Welding position


3/321/8

5/323/161/4

2.53.254.05.06.0

1414141818

350350/450350/450

450450

70-9590-140

135-185175-255250-330

2.33.75.6

11.216.2

4.55.0/6.05.0/6.0

6.06.0

13.515.0/18.015.0/18.0

18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= ~ (Uo : 70 V)+

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]630

Rm [MPa]790

A5 [%]22


Heat TreatmentU

AWS/ASME SFA A5.5 : E 10018-MDIN 8529 : E Y 62 87 2Mn2NiMo B H5BS 2493 : E NiMo B HEN 499 : E 50 5 Z B 32 H5

Basic coated electrode for welding of lowtemperature, high strength, fine grained structuralsteels such as navel crafts and submarines.Particularly low diffusible hydrogen content.


C0.05

Mn1.65

Si0.40

Ni2.00

Cr0.20

Mo0.40







44


Z-52

Welding position


3/321/8

5/323/161/4

2.53.254.05.06.0

1414141818

350350/450350/450

450450

70-9590-140

135-185175-255250-330

2.33.75.6

11.216.2

4.55.0/6.05.0/6.0

6.06.0

13.515.0/18.015.0/18.0

18.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= ~ (Uo : 70 V)+

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]700

Rm [MPa]780

A5 [%]22


Heat TreatmentU

AWS/ASME SFA A5.5 : E 11018-MDIN 8529 : E Y 69 76 Mn2NiCrMo B H5BS 2493 : E 2NiMo B HEN 499 : E 50 5 Z B 32 H5

Basic coated electrode for welding high strengthsteels for military applicationsExcellent X-ray quality


C0.05

Mn1.60

Si0.30

Cr0.25

Ni2.25

Mo0.40







45


Z-53 M

Welding position


3/321/8

5/323/161/4

2.53.254.05.06.0

1414/1814/18

1818

350350/450350/450

450450

65-9590-135

140-185180-240240-320

2.13.6

5.2/6.810.414.9

4.55.0

5.0/6.06.06.0

13.515.0

15.0/18.018.018.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= ~ (Uo : 70 V)+

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]800

Rm [MPa]940

A5 [%]20


Heat TreatmentU

AWS/ASME SFA A5.5 : E 12018-MDIN 8529 : E Y 79 76 Mn2Ni1.5CrMo B H5BS 2493 : E 2NiCrMo B HEN 499 : E 50 5 Z B 32 H5

Basic coated electrode for welding very highstrength steels for military applications


C0.06

Mn1.90

Si0.30

Cr2.20

Ni1.20

Mo0.50







46


Z-502

Welding position


3/321/8

5/323/16

2.53.254.05.0

12141414

300350350350

65-9590-130

125-180180-240

2.03.65.48.5

4.05.05.05.0

12.015.015.015.0


in mmLength

in mmCurrent[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= ~ (Uo : 70 V)+

ASME:

ISO 6947

1G

PA

2F

PB

2G

PC

3G

PF

4G

PE

Rp 0.2 [MPa]490

Rm [MPa]620

A5 [%]20


Heat TreatmentS

AWS/ASME SFA A5.4 : E 502-15DIN 8575 : E CrMo5 B 26BS 2493 : E 5CrMo BEN 1599 : E CrMo5 B 32 mod

Basic coated 5% Cr - 0.5% Mo electrodeService temperature of maximum 600oCWelding of Cr-Mo alloys of similar compositionSuitable for critical thick joints


C0.06

Mn0.60

Si0.35

Cr5.20

Mo0.60



DIN 17 155DIN 17 245

12CrMo19 5 GS 12CrMo19 5

Boiler and pressure vessel steelsCast steels


47


Z-505

Basic coated 9% Cr- 1% Mo electrodeService temperatures of maximum 6500C


Current

Specifications:

= + ~ (Uo : 70V)

AWS/ASME SFA A5.4 : E 505-15DIN 8575: E CrMo9 B 26BS 2493 : E 9CrMO BEN 1599 : E CrMo9 B 32 mod

Welding position

ASME: 1G 2F 2G 3G 4G

ISO 6947 PA PB PC PF PE

DIN 17 176DIN 17 245

Boiler and pressure vessel steelsCast steels





X12 CrMO91GX 12CrMo 10 1

C Mn Si Cr Mo0.08 0.75 0.65 9.50 1.00

Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment550 700 22 80 J @ 20oC S

Re-drying : 3000C/2h

3/321/8

5/323/16

2.53.254.05.0

12141414

300350350350

65-105110-140150-190180-230

1.93.65.48.4

4.05.05.05.0

12.015.015.015.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

48


Z-91

Low hydrogen electrode suitable for welding9%Cr-1%Mo steels, also known as GRADE 91designed to provide excellent endurance in creep,fatigue, oxidation and corrosion resistance on hightemperatures.

ASTMA213 T91A335 P91A369 FP91EN1.4903 (X10CrMoVNb 91)

A387 G91A217 C12A

A182/A336 F91A234 P91


Rp 0.2 [MPa] Rm[MPa] A5 [%] Impact [ISO-V]570 700 18 121J@20oC

Current





AWS/ASME SFA 5.5: E9015-B9

Specifications:

C Mn* Si Cr Ni* Mo v0.1 1 0.25 9 0.3 1 0.2*Mn+Ni<1.5

= + ~ (Uo : 70V)

Welding position



3/321/85/32

2.53.254.0

141414

350350350

75-10090-140

110-190

4.566

13.51818

Diain mm

Lengthin mm

Current[amps]

Weight packet[kg]

Weight carton[kg]

49

Stainless Steel Electrodes

Z-307 B

Basic coated stainless steel electrodeFor welding 14% Mn steels, armour plate, steelswith unknown composition and hardening steelsUsed for buffer layers in hardfacing applications


Various steel grades such as: Non-magnetic austenitic steelsWork hardening austenitic manganese steelsDissimilar steel grades (CMn-steels to stainless steel)

Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]520 620 35 70 J @ 20oC

Current





AWS/ASME SFA A5.4 : E 307-15Specifications:

C Mn Si Cr Ni Mo0.06 4.30 0.40 20.50 9.50 0.80

= +

Welding position



Re-drying : 3000C2h

3/321/8

5/323/16

2.53.254.05.0

12141414

300300300300

65-8095-120

110-160150-190

1.73.14.76.5

1.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

50


Z-307 R

Rutile coated stainless steel electrodeFor welding 14% Mn steels, armour plate, steelswith unknown composition and hardening steelsUsed for buffer layers in hardfacing applications








AWS/ASME SFA A5.4 : E 307-16

Specifications:

C Mn Si Cr Ni Mo0.09 4.00 0.80 19.00 10.00 0.90

Re-drying : 3000C2h

Current

= + ~ (Uo : 70V)

Welding position



3/321/8

5/323/16

2.53.254.05.0

12141414

300350350350

65-8095-120

110-160150-190

1.73.14.76.5

1.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

51


Z-307 HR

Rutile coated high recovery stainless steelelectrodeFor welding 14% Mn steels, mixed joints betweenhigh alloyed steel, stainless steels and unalloyedbase materialsUsed for hard to weld steel joints and bufferlayers in hardfacing applications



Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] - 620 35 100 J @ 20oC





AWS/ASME SFA A5.4 : E 307-16Specifications:

C Mn Si Cr Ni Mo0.08 4.00 0.80 19.50 9.50 1.10


Current

= + ~ (Uo : 70V)

Welding position

ASME: 1G 2F 3G

ISO 6947 PA PB PF

3/321/8

5/323/16

2.53.254.05.0

14181818

350450450450

65-8095-120

110-160150-190

3.26.6

10.215.0

5.06.06.06.0

5.018.018.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

52


Z-308 B

Description and Applications:Basic coated electrode for welding austeniticstainless Cr-Ni steelsSuited for positional welding of thick plates andhighly restrained jointsExcellent resistance to cold crackingGood mechanical properties

DIN 17 440/17 445

DIN 17 440/17 445

DIN 17 440/17 445

Extra loiw carbon C<0.035%

Medium carbon C>0.03%

Ti-, Nb Stabilized

Current





AWS/ASME SFA A5.4 : E 308L-15DIN 8556 : E 19 9 L B 20 +BS 2926 : E 19 9 L BEN 1600 : 19 9 L B 22

Specifications:

X2 CrNi 19 11X2 CrNiN 18 10X5 CrNi 18 10G-X6 CrNi 18 9X6 CrNiTi 18 10X6 CrNiNb 18 10G-X5 CrNiNb 18 9

1.43061.43111.43011.43081.45411.45501.4552

C Mn Si Cr Ni0.03 1.00 0.50 19.00 10.00



= +Welding position



5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141418

300300350350450

40-5555-80

75-110110-150140-180

1.21.83.65.6

10.4

1.5/2.01.5/2.02.0/2.52.0/2.5

6.0

9.0/12.09.0/12.0

12.0/15.012.0/15.0

18.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

53


Z-308 L

Description and Applications:Rutile-basic coated electrode for welding nonstabilized and stabilized corrosion resistantaustenitic Cr-Ni steels up to 3500 CSmooth metal transfer with both AC and DCWeld metal beads exhibit fine ripple formationFocused and stable arc with low spatter lossSelf detachin slagMoisture resistant formulation producing weldsfree from porosity

DIN 17 440/17 445

DIN 17 440/17 445

DIN 17 440/17 445



Ti-, Nb Stabilized





AWS/ASME SFA A5.4 : E 308L-16DIN 8556 : E 19 9 L R 23BS 2926 : E 19 9 L REN 1600 : E 19 9 L R 12

Specifications:


1.43061.43111.43011.43081.45411.45501.4552

C Mn Si Cr Ni0.020 0.75 0.80 19.00 10.00



Current

= + ~ (Uo : 50V)

Welding position



5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350450

30-5050-75

75-110110-150140-190

1.11.73.34.97.1

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

54


Z-308 LVD

Description and Applications:Ruitle-acid austenitic stainless Cr-Ni steel electrodefor welding 304L or equivalent steels in thevertical down positionDesigned for welding root passes in grooveswith root openingHigh corrosion resistance in oxidizing envionments

DIN 17 440/17 445

DIN 17 440/17 445

DIN 17 440/17 445



Ti-, Nb Stabilized






Specifications:


1.43061.43111.43011.43081.45411.45501.4552

C Mn Si Cr Ni0.025 0.70 0.70 19.50 10.00



Current

= + ~ (Uo : 50V)

Welding position

ASME: 1G 2F 2G 3G 3G 4G

ISO 6947 PA PB PC PF PG PE

3/321/8

2.53.25

1212

300300

60-7080-100

1.42.4

2.02.0

12.012.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

55


Z-308 LHR


Rutile coated high recovery (145%) electrodees.Used whenever a high deposition rate is required.Easy slag realease, smooth and finely rippled deposit.Excellent for fillet and downhand welding.

for welding austenitic Cr- Ni steels.

Welding position


Specifications:

AWS/ASME SFA A5.4 : E-308L -16EN 1600: E 19 9 LR 53 mod

Current

= + ~ (Uo : 70V)



ASME: 1G 2F

ISO 6947 PA PB

C Mn Si Cr Ni0.025 0.80 0.80 19.50 10.3


Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]450 580 40 35J@- 105c

Extra low carbon C<0.03%Medium carbon C>0.03%Ti-, Nb Stabilezed

DIN 17 440/17 445DIN 17 440/17 445DIN 17 440/ 17 445


1.43061.43111.43011.43081.45411.45501.4552

Re-drying: 3000 C/2h

3/321/8

5/323/16

2.53.254.05.0

1214/18

1818

300350/450

450450

75-95110-130135-155180-210

2.55.0/6.40

9.314.3

4.05.0/6.0

6.06.0

12.015.0/18.0

18.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

56


Z-308 H

Rutile-basic all position stainless steel electrodeUsed for welding low-carbon stainless steels ofthe type AISI 304 in cases where maximumresistance to intergranular corrosion is requiredFor welding Titanium and Niobium stabilizedstainless steelsWeldable on both AC and DC


Welding position



DIN 17 440/17 445

DIN 17 440/17 445

Medium carbon steels

Ti-: Nb stabilized steels



Current





AWS/ASME SFA A5.4 : E 308-16DIN 8556 : E 19 9 R 23BS 2926 : E 19 9 REN 1600 : E 19 9 R 12

Specifications:

C Mn Si Cr Ni0.05 1.00 0.80 20.00 10.00

X5 CrNi 18 10G-X6 CrNi 18 9X6 CrNiTi 18 10X6 CrNiNb 18 10

1.43011.43081.45411.4550

= + ~ (Uo : 50V)

1/165/643/321/85/323/16

1.62.02.53.254.05.0

121212141414

300300300350350350

25-4030-5050-75

75-110110-150140-190

0.51.11.73.34.97.1

1.5/2.01.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

57


Z-309 B

Description and Applications:Basic coated stainless electrode for welding rootruns in acid resisting parts of clad steelUsed when overlaying on mild steel or low alloysteelsJoining dissimilar steels (austenitic steels to mildand low alloy steels)Suitable for welding similar metal joints andaustenitic-martensitic steels of the 13% Cr-6% Ni typeUsed for buffer layers in hardfacing applicaions

Welding position



DIN 17 440/17 465Corrosion resistingClad steel

Dissimilar metals (mild and low alloyed steel to stainless steel)Build-up welding on mild and low alloyed steel

Current





AWS/ASME SFA A5.4 : E 309L-15DIN 8556 : E 23 12 L B 20+BS 2926 : E 23 12 L BEN 1600 : E 23 12 L B 42

Specifications:

X2 CrNiN 18 10X2 CrNi 19 11X5 CrNi 18 10

1.43111.43061.4301

= +

C Mn Si Cr Ni0.02 0.90 0.40 24.00 12.00


3/321/8

5/323/16

2.53.254.05.0

12141414

300350350350

50-8080-110

100-150160-220

1.93.45.47.8

1.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]


58


Z-309 S

Rutile coated low carbon electrode for joiningof dissimilar steels (austenitic steels to mild andlow alloy steels)Suitable for welding similar metal joints (23% Cr-12% Ni) and austenitic - martenistic steels of 13% Cr - 6% Ni typeUsed for buffer layers in hardfacing applicationsFocued and stable arcEasy slag release


Welding position

DIN 17 440/17 465


Current






Specifications:

= + ~ (Uo : 50V)



C Mn Si Cr Ni0.025 0.80 0.80 22.00 12.00


Corrosion resistingClad steel

X2 CrNiN 18 10X2 CrNi 19 11X5 CrNi 18 10

1.43111.43061.4301

Dissimilar metals (mild and low alloyed steel to stainless steel)Build-up welding on mild and low alloyed steel

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

30-6040-70

70-110110-140140-180

1.21.83.45.17.3

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

59


Z-309 Cb

High CrNiNb alloyed rutile-basic all positionbuffer electrodeDesigned for buffering mild and low alloyedsteels for nuclear applicationsUsed as a buffer electrode in AISI 312 and AISI347 claddingsUsed for the first run when welding 321 or 347clad steels, prior to completion with 347 typeweld metalFocused and stable arcEasy slag release


Welding position

DIN 17 440

DIN 17 440

DIN 17 440

Re-drying: 150o- 2000C/1-2h

Current





AWS/ASME SFA A5.4 : E 309Cb-16DIN 8556 : E 23 12 Nb R 23BS 2926 : E 23 12 Nb REN 1600 : E 23 12 Nb R 12

Specifications:

= + ~ (Uo : 50V)



C Mn Si Cr Ni Nb0.04 0.90 0.80 23.50 13.50 0.80


Extra low carbon steels C<0.03%

Medium carbon steels C>0.03%

Ti-, Nb stabilized steels

1.43061.43111.43011.43081.45411.4550

X2 CrNi 19 11X2 CrNiN 18 10X5 CrNi 18 10G-X6 CrNi 19 9X6 CrNiTi 18 10X6 CrNiNb 18 10

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

30-6040-70

70-110110-140140-180

1.21.83.45.17.3

4.04.05.05.05.0

12.012.015.015.015.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

60


Z-309 Mo


Welding position

DIN 17 440

Re-drying: 3000C/2h

Current





AWS/ASME SFA A5.4 : E 309MoL-16DIN 8556 : E 23 13 2 R 23BS 2926 : E 23 12 2 REN 1600 : E 23 12 2 L R 12

Specifications:

= + ~ (Uo : 50V)



C Mn Si Cr Ni Mo0.025 0.90 0.80 22.50 12.50 2.80


CrNiMo - claddings

Welsing dissimilar metals: mild steel or low alloyed steel to stainless CrNiMo steel up to max thickness of 12mmBuild up welding on mild or low alloyed steel

1.44041.44351.44061.44291.44011.44361.45711.45731.45801.4583

X2 CrNiMo 17 13 2X2 CrNiMo 18 14 3X2 CrNiMoN 17 12 2X2 CrNiMoN 17 13 3X5 CrNiMo 17 12 2X5 CrNiMo 17 13 3X6 CrNiMoTi17 12 2X10 CrNiMoTi18 12X6 CrNiMoNb 17 12 2X10 CrNiMoNb 18 12

Rutile-basic coated low carbon all positionstainless steel electrodeSuitable for welding high alloyed corrosionresistant Cr-Ni-Mo steels, dissimilar steels(austenitic to ferritic steels)Depositon of austenitic cladding root runsFocused and stable arcEasy slag release

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

30-6040-70

70-110110-140140-180

1.21.83.55.27.5

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

61


Z-310

Description and Applications:Basic-rutile coated, fully austenitic all positionelectrodeSuitable for welding heat resistant Cr and Cr-Ni steelsOxidation and scalig resistance up to 12000C

Welding position



DIN 17 465/43 720Heat resisting stels

Current





AWS/ASME SFA A5.4 : E 310-16DIN 8556 : E 25 20 R 26BS 2926 : E 25 20 REN 1600 : E 25 20 R 12 mod

Specifications:

X10 CrAI 24G-X25 CrNiSi 18 9G-X40 CrNiSi 22 9X15 CrNiSi 20 12G-X25 CrNiSi 20 12G-X40 CrNiSi 25 12X15 CrNiSi 25 20G-X15 CrNi 25 20X12 CrNi 25 21G-X40 CrNiSi 25 20

1.47621.48251.48261.48281.48321.48371.48411.48401.48451.4848

C Mn Si Cr Ni0.13 2.10 0.40 26.00 20.00



= + ~ (Uo : 70V)

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

30-6060-90

90-120130-160150-180

1.21.83.75.98.5

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

62


Z-312


Welding position



Various steel grades such as: Hardenable steels including difficult to weld steelsNon-magnetic austenitic steelsWork hardening austenitic manganese steels

Current






Specifications:

C Mn Si Cr Ni0.02 0.90 0.80 29.00 9.00

Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]500 760 24 -

Re-drying :3000C/2h

= + ~ (Uo : 50V)

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

30-6060-80

70-11090-150

150-220

1.21.93.75.68.3

4.04.05.05.05.0

12.012.015.015.015.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Rutile-basic coated all position electrode forjoining dissimilar steels and surfacing applicationsSuitable for welding difficult to weld steels suchas: Mn-steel, armour platesExcellent weldability on both AC and DC

63


Z-312 S


Welding position



Various steel grades such as: Hardenable steels including difficult to weld steelsNon-magnetic austenitic steelsWork hardening austenitic manganese steels

Current






Specifications:

C Mn Si Cr Ni0.11 0.90 0.85 29.00 9.00

Re-drying :3000C/2h

= + ~ (Uo : 50V)

Rutile-basic coated all position electrode forjoining dissimilar steels and surfacing applicationsSuitable for welding difficult to weld steels suchas: Mn-steel, armour platesExcellent weldability on both AC and DC


5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

30-6060-80

70-11090-150

150-220

1.11.73.34.97.0

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

64


Z-316 B


Welding position



Current





AWS/ASME SFA A5.4 : E 316L-15DIN 8556 : E 19 12 3 L B 20+BS 2926 : E 19 12 3 L BEN 1600 : E 19 12 3 L B 22

Specifications:

C Mn Si Cr Ni Mo0.035 1.00 0.40 18.50 12.00 2.60

Re-drying :3000C/2h

= +

Basic coated low carbon electrode for weldingaustenitic stainless Cr-Ni-Mo steelsGood mechnical propertiesEXcellent position welding properties andpenetration


X2 CrNiMo 17 13 2X2 CrNiMo 18 14 3X2 CrNiMoN 17 12 2X2 CrNiMoN 17 13 3X5 CrNiMo 17 12 2X5 CrNiMo 17 13 3G-X6 CrNiMo 18 12G-X10 CrNiMo 18 9G-X6 CrNiMo 18 10X6 CrNiMoTi 17 12 2X6 CrNiNb 18 10G-X5 CrNiNb 18 9G-X5 CrNiMoNb 18 10X10 CrNiMoNb 18 12

1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583

DIN 17 440/17 445

DIN 17 440/17 445

DIN 17 440/17 445

Extra low carbonC<0.03%

Medium carbonC>0.03%

Ti-, Nb Stabilized

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

40-5555-80

75-110110-150140-180

1.21.83.65.6

10.4

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

65


Z-316 L


Welding position



Current





AWS/ASME SFA A5.4 : E 316L-16DIN 8556 : E 19 12 3 L R 23BS 2926 : E 19 12 3 L REN 1600 : E 19 12 3 L R 12

Specifications:

C Mn Si Cr Ni Mo0.025 0.80 0.80 18.00 11.50 2.80

Re-drying :3000C/2h

Rutile coated electrode for welding on stabilizedcorrosion resistant Cr-Ni-Mo steelsSmooth metal transter with both AC and DCWeld metal beads exhibit fine ripple formatinFocused and stable arc with low spatter lossEasy slag releaseMoisture resistant formula producing welds freefrom porosity



1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583

DIN 17 440/17 445

DIN 17 440/17 445

DIN 17 440/17 445



Ti-, Nb Stabilized

= + ~ (Uo : 50V)

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

30-5050-75

75-110110-150140-190

1.11.83.45.17.3

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

66


Z-316 LVD


Welding position

ASME: 1G 2F 2G 3G 3G 4G

ISO 6947 PA PB PC PF PG PE

Current





AWS/ASME SFA A5.4 : E 316L-17DIN 8556 : E 19 12 3 L R 13BS 2926 : E 19 12 3 L REN 1600 : E 19 12 3 L R 11

Specifications:

C Mn Si Cr Ni Mo0.025 0.80 0.70 18.00 11.50 2.70

Re-drying :3000C/2h

Rutile-acid austenitic stainless Cr-Ni-Mo steelelectrode for welding 316L or equivalent steelsin the vertical down positionDesigned for welding root passes in grooveswith root openingHigh corrosion resistance in oxidizing environments



1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583

DIN 17 440/17 445

DIN 17 440/17 445

DIN 17 440/17 445



Ti-, Nb Stabilized

= + ~ (Uo : 50V)

3/321/8

2.53.25

1212

300300

60-7080-100

1.42.4

1.51.5

9.09.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

67


Z-316 LHR


Welding position

ASME: 1G 2F

ISO 6947 PA PB

Current





AWS/ASME SFA A5.4 : E 316L-16DIN 8556 : E 19 12 3 L R 26 150BS 2926 : E 19 12 3 L REN 1600 : E 19 12 3 L R 53 mod

Specifications:

C Mn Si Cr Ni Mo0.025 0.80 0.80 18.00 11.50 2.70

Re-drying :3000C/2h

Rutile coated high recovery (145%) electrodefor welding austenitic stainless Cr-Ni-Mo steelsUsed whenever a high deposition rate is requiredEasy slag rlease, smooth and finely rippleddepositExcellent for fillet and downhand welding



1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583

DIN 17 440/17 445

DIN 17 440/17 445

DIN 17 440/17 445



Ti-, Nb Stabilized

= + ~ (Uo : 70V)

3/321/8

5/323/16

2.53.254.05.0

1214/18

1818

300350/450

450450

75-95110-130135-155180-210

2.54.8/6.2

9.615.1

4.05.0/6.0

6.06.0

12.015.0/18.0

18.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

68


Z-316 HS


Welding position Current





AWS/ASME SFA A5.4 : E 316-16DIN 8556 : E 19 12 3 MPR 23 170BS 2926 : E 19 12 3 RMPEN 1600 : E 19 12 2 R 72

Specifications:

C Mn Si Cr Ni Mo0.025 0.90 0.70 19.60 11.70 2.80

Re-drying :3000C/2h

High recovery (170%) rutile coated electrodefor welding austenitic stainless Cr-Ni-Mo steelsUsed whenever easy welding, smooth weldingsurfaces and a high deposition rate are required



1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583

DIN 17 440/17 445

DIN 17 440/17 445

DIN 17 440/17 445



Ti-, Nb Stabilized

= + ~ (Uo : 50V)

ASME: 1G 2F 3G

ISO 6947 PA PB PF

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1214

14/181818

300350

350/450450450

30-6065-10590-145

145-215180-270

1.83.3

5.6/7.210.917.2

4.05.0

5.0/6.06.06.0

12.015.0

15.0/18.018.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

69


Z-317







AWS/ASME SFA A5.4 : E 317L-16BS 2926 : E 19 13 4 L REN 1600 : E 19 13 4 L R 12 mod

Specifications:

C Mn Si Cr Ni Mo0.025 0.90 0.75 19.00 13.00 3.50


Rutile coated electrode for dissimilar weldingSuitable for difficult to weld steelsEnhanced corrosion resistance applications


X2 CrNiMoN 18 18 3X2 CrNiMoN 17 13 3X2 CrNiMo 18 14 3X2 CrNiMo 18 16 4

1.44281.44291.44351.4438

DIN 17 440/17 445Extra low carbonC<0.03%

= + ~ (Uo : 50V)



5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

35-5540-80

80-110110-150150-220

1.21.83.45.27.4

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

70


Z-318 B


Welding position



Current





AWS/ASME SFA A5.4 : E 318-15DIN 8556 : E 19 12 3 Nb B 20+BS 2926 : E 19 12 3 Nb BEN 1600 : E 19 12 3 Nb B 22

Specifications:

C Mn Si Cr Ni Mo Cb0.035 1.05 0.35 18.50 11.50 2.75 0.35

Re-drying :3000C/2h

Basic coated all position electrode for weldingTi, Nb stabilized austenitic stainless Cr-Ni-MosteelsHigh reistance to intergranular corrosion upto 4000CExcellent weldability and easy slag release



1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583

DIN 17 440/17 445

DIN 17 440/17 445

DIN 17 440/17 445



Ti-, Nb Stabilized

= +

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

30-5050-70

80-100110-140140-180

1.21.83.65.6

10.4

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

71


Z-318







AWS/ASME SFA A5.4 : E 318-16DIN 8556 : E 19 12 3 Nb R 23BS 2926 : E 19 12 3 Nb REN 1600 : E 19 12 3 Nb R 12

Specifications:

C Mn Si Cr Ni Mo Nb0.025 0.90 0.80 18.00 11.50 1.60 0.40

Re-drying :3000C/2h

Rutile-basic coated all position electrode forwelding Ti, Nb stabilized austenitic stainlessCr-Ni-Mo steelsHigh resistance to intergranular corrosion upto 4000CExcellent weldability and easy slag release an both AC and DC



1.44041.44351.44061.44291.44011.44361.44371.44101.44081.45711.45501.45521.45811.4583

DIN 17 440/17 445

DIN 17 440/17 445

DIN 17 440/17 445



Ti-, Nb Stabilized

= + ~ (Uo : 50V)



5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

40-5550-80

80-110110-150150-180

1.11.73.34.97.2

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

72


Z-320







AWS/ASME SFA A5.4 : E 385-16 modDIN 8556 : E 20 25 5 L Cu R 26EN 1600 : E 20 25 5 Cu L R 12

Specifications:

C Mn Si Cr Ni Mo Cu0.025 1.30 0.85 20.00 25.50 4.70 1.70

Re-drying :3000C/2h

Rutie-basic fully austenitic stainless steel electrodeHigh resistance in phosphoric and sulphuricacid applicatonsSmooht metal trasfer on both AC and DC


G-X7 NiCrMoCuNb 25 20X5 NiCrMoCu Ti 20 18G-X2 NiCrMoCuN 20 18G-X2 NiCrMoCuN 25 20X1 NiCrMoCuN 25 20 5G-X7 CrNiMoCuNb18 18X5 NiCrMoCuNb 22 18

1.45001.45061.45311.45361.45391.45851.4586

DIN/SEW 400/410Fully austenitic NiCrMoCu andCrNiMoCu steel

= + ~ (Uo : 50V)



3/321/8

5/32

2.53.254.0

121414

300350350

40-7560-10580-140

1.83.14.6

1.5/2.02.0/2.52.0/2.5

9.0/12.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

73


Z-347 B







AWS/ASME SFA A5.4 : E 347-15DIN 8556 : E 19 9 Nb B 20+BS 2926 : E 19 9 Nb BEN 1600 : E 19 9 Nb B 22

Specifications:

C Mn Si Cr Ni Nb0.03 1.00 0.50 19.00 10.00 0.35

Re-drying :3000C/2h

Basic coated all position electrode for weldingTi, or Nb stabilized austenitic Cr-Ni steelsHigh reistance to intergranular corrosion upto 4000CExcellent weldability and easy slag release


X6 CrNiTi 18 10X6 CrNiNb 18 10G-X5 CrNiNb 18 9X5 CrNi 18 10X2 CrNi 19 11G-X6 CrNi 18 9G-10 CrNi 18 8

1.45411.45501.45521.43011.43061.43081.4312

DIN 17 440/17 445

DIN 17 440/17 445

Ti-, Nb Stabilized

Non Stabilized

= +



5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

30-5050-70

80-100110-140140-180

1.21.83.65.6

10.4

1.5/2.01.5/2.02.0/2.52.0/2.5

6.0

9.0/12.09.0/12.0

12.0/15.012.0/15.0

18.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

74


Z-347







AWS/ASME SFA A5.4 : E 347-16DIN 8556 : E 19 9 Nb R 23BS 2926 : E 19 9 Nb REN 1600 : E 19 9 Nb R 12

Specifications:

C Mn Si Cr Ni No0.03 0.80 0.80 19.00 10.00 0.40

Re-drying :3000C/2h

Rutile-basic coated all position electrode forwelding Ti or Nb stabilized austenitic Cr-NisteelsHigh resistance to intergranular corrosion upto 4000CExcellent weldability and slag release an bothAC and DC


DIN 17 440/17 445

DIN 17 440/17 445

= + ~ (Uo : 50V)

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

35-5550-80

80-110120-150150-180

1.11.73.34.97.1

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]



Ti-, Nb Stabilized

Non Stabilized

X6 CrNiTi 18 10X6 CrNiNb 18 10G-X5 CrNiNb 18 9X5 CrNi 18 10X2 CrNi 19 11G-X6 CrNi 18 9G-10 CrNi 18 8

1.45411.45501.45521.43011.43061.43081.4312

75


Z-ARM BS

Description and Applications:Basic coated austenitic stainless steel electrodeespecially designed for welding armour plateand other difficult to weld steelsAll position welding on DC currentNeat weld appearanceExcelent slag release

Welding position



Forged and cast armour steels, alloyed steels, high carbon steels, Mn steel, high strength steels, spring steels andstainless steelsJoining dissimilar steels and steels having different chemical composition

Current





AWS/ASME SFA A5.4 : E 308Mo-15 modBS 2926 : E 19 9 3 B

Specifications:

= +

C Mn Si Cr Ni Mo0.05 1.90 0.30 20.50 9.80 2.90



1/85/323/16

3.254.05.0

141414

350350350

90-120135-185175-255

3.24.76.9

2.0/2.52.0/2.55.0/6.0

12.0/15.012.0/15.012.0/18.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

76


Z-Ni Vi


Current




C Mn Si Cr Ni Mo0.03 0.85 0.75 19.50 9.80 2.60

Rutile coated austenitic stainless steel electrodeespecially designed for welding armour platesand other difficult to weld steelsAll position welding on both AC and DCNeat weld appearanceExcellent slag release

Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]

= + ~ (Uo : 70V)

Forged and cast armour steels, alloyed steels, high carbon steels, Mn steel, high strength steels, spring steels andstainless steelsJoining dissimilar steels and steels having different chemical composition

AWS/ASME SFA A5.4 : E 308Mo-16 modBS 2926 : E 19 9 3 R

Specifications:

500 680 35 90 J @ 20oC

Welding position




Re-drying :3000C/2h

5/643/321/8

5/323/16

2.02.5

3.254.05.0

1212141414

300300350350350

35-6050-80

90-120130-170160-220

1.21.83.35.07.5

1.5/2.01.5/2.02.0/2.52.0/2.52.0/2.5

9.0/12.09.0/12.0

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

77


Z-2209 B






AWS/ASME SFA A5.4 : E 2209-15DIN 8556 : E 22 9 3 L B 20+EN 1600 : E 22 9 3 L B 22

Specifications:

C Mn Si Cr Ni Mo N<0.04 1.00 0.40 25.50 9.00 3.00 0.14

Basic coated electrode for welding stainlessferritic-austenitic Cr-Ni-Mo Steels (Duplex steels)Highly resistant to pitting and stess corrosioncrakingRecommended for sub-zero toughness, positionalwelding applicationsMaximum temperature of use +2500C


X2 CrNiMoN 22 5 3 1.4462DIN/SEW 400Duplex Stainless-Steels

= +




Re-drying :3000C/2h

3/321/8

5/32

2.53.254.0

141818

350450450

50-7070-100

100-150

1.63.55.3

1.52.02.0

9.012.012.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

78


Z-2209 R


Welding position




AWS/ASME SFA A5.4 : E 2209-16DIN 8556 : E 22 9 3 L R 23EN 1600 : E 22 9 3 L R 12

Specifications:

C Mn Si Cr Ni Mo N0.03 0.90 0.80 25.50 9.00 3.00 0.14


X2 CrNiMoN 22 5 3 1.4462DIN/SEW 400Duplex Stainless-Steels




Re-drying :3000C/2h

3/321/8

5/32

2.53.254.0

141818

350450450

60-7070-10090-140

1.63.55.3

1.52.02.0

9.012.012.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Rutile-basic coated electrode for welding stainlessferritic-austenitic Cr-Ni-Mo Steels (Duplex steels)Highly resistant to pitting and stress corrosioncrakingSuited for all-position welding applications onboth AC and DCMaximum temperature of use +2500C

Current

= + ~ (Uo : 50V)

79


Z-2594 R


Welding position



AWS/ASME SFA 5.4 : E 2594-16

EN 1600 2594 NLR 2 3

Specifications:

C Mn Si Cr Ni Mo Cu N FN0.03 0.9 0.9 25.25 9.8 4.0 0.75 0.25 30-50

Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]

700 850 26 60 J@20oC



Rutile electrode designed for welding ferritic- austenitic steels of

Super Duplex types.

Its chemical composition allows high resistance to pitting and

intergranular corrosion combined to excellent mechanical

properties.

Well suited for condition in the off-shore field.

Current

= + ~ (Uo : 50V)

40J@-40oC


1.4462

Super Duplex Stainless-Steel

SAFZERON100

ASTM EN1.44102507 S32750

S32760


3/321/8

5/32

2.53.254.0

141414

350450450

50-7570-12090-160

222

121212

Diain mm

Lengthin mm

Current[amps]

Weight packet[kg]

Weight carton[kg]

80

Hard Facing Electrodes

Z-104





DIN 8555: E 1 UM 300Specifications:

C Mn Si Cr Fe0.10 0.50 0.80 3.40 Bal.

Basic coated abrasion resistant electrodeMachinable weld depositModerate impact toughnessApplicable for gear teeth, brake drums, sprockets,bushings and rail crossings

Hardness28-33 Rc 275-325 HB

= + ~ (Uo : 70V)




Re-drying :3000C/2h

3/321/8

5/323/16

2.53.254.05.0

14181818

350350/450

450450

60-80110-130140-180190-240

2.14.56.7

11.2

5.05.0/6.0

6.06.0

15.015.0/18.0

18.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

81


Z-105






C Mn Si Cr Fe0.30 0.30 0.70 3.20 Bal.

Basic coated electrode for surfacing parts subjectedto medium abrasion and high compressionApplicable for runners, caterpillar track links,gear wheels and dredging machinery

Hardness37-42Rc 350-400 HB

= + ~ (Uo : 70V)




Re-drying :3000C/2h

3/321/8

5/323/161/4

2.53.254.05.06.0

1414/18

181818

350350/450

450450450

70-100105-115120-160180-240250-290

2.23.5/4.5

6.610.315.0

5.05.0/6.0

6.06.06.0

15.015.0/18.0

18.018.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

82


Z-110





DIN 8555: E 6 UM 55 RSpecifications:

C Mn Si Cr Mo Fe0.30 0.40 0.70 11.90 0.90 Bal.

Rutile coated electrode for corrosion resistanthard surfacing up to 5000CApplicable for shafts, rails, mixer arms, valveseats of cast steel leading buckets


= + ~ (Uo : 70V)

ASME: 1G 2F 2G 3G

ISO 6947 PA PB PC PF


Re-drying :1200C/1h

1/85/323/16

3.254.05.0

1414/18

18

350350450

85-120120-150160-210

3.04.5/5.8

9.1

5.05.06.0

15.015.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

83


Z-111






C Mn Si Cr Mo Fe0.50 1.10 0.40 7.20 0.90 Bal.

Rutile coated electrode for hard surfacing of earth moving machinesLow open current voltageHeat resistant up to 6000CApplicable for buldozer blades, crusher jaws,excavator teeth and mixersNon machinable weld deposit

Hardness55-58Rc 560-615 HB

= + ~ (Uo : 50V)

ASME: 1G 2F 2G 3G




3/321/8

5/323/161/4

2.53.254.05.06.0

1414/1814/18

1818

350350/450350/450

450450

70-10090-110

140-180180-250220-280

2.13.5/4.65.3/6.8

10.615.0

5.05.0/6.05.0/6.0

6.06.0

15.015.0/18.015.0/18.0

18.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

84


Z-113






C Mn Si Cr Mo V Fe0.50 0.40 0.80 7.50 0.50 0.60 Bal.

Basic coated electrode for surfacing parts subjectedto impact, high compression stresses and severeabrasionApplicable for tracctor and crane parts, shovelteeth, crusher hammers and scraper blades

Hardness57-62 Rc

= + ~ (Uo : 70V)

ASME: 1G 2F 2G 3G




3/321/8

5/323/161/4

2.53.254.05.06.0

1414/1814/18

1818

350350/450350/450

450450

60-80100-130120-160180-210220-280

2.13.5/4.45.3/6.7

10.615.0

5.05.0/6.05.0/6.0

6.06.0

15.015.0/18.015.0/18.0

18.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

85


Z-114






C Mn Si Cr Mo0.60 0.90 0.70 4.70 1.80

Rutile coated electrode for surfacing partssubjected to abrasion and impactApplicable for rails truck wheels, worms, couplingshafts and spindlesNon machinable weld deposit


= + ~ (Uo : 70V)

ASME: 1G 2F 2G 3G




3/321/8

5/323/16

2.53.254.05.0

1414

14/1818

350350

350/450450

75-110110-140150-190190-260

2.43.9

6.1/7.812.3

5.05.0

5.0/6.06.0

15.015.0

15.0/18.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

86


Z-120





DIN 8555: E 10 UM 60 ZSpecifications:

C Mn Si Cr Fe3.00 0.20 0.90 29.00 Bal.

Rutile coated electrode for high abrasion withoutimpact applications160% weld metal recoveryCan be used both for buildups and rebuildingSuitable for crushing mills, rock drills, mixersand plough shares

Hardness60 Rc 60-650 HB

= + ~ (Uo : 70V)

ASME: 1G 2F

ISO 6947 PA PB


Re-drying : 3000C/1-2h

1/85/323/16

3.254.05.0

141414

350350350

100-130120-160150-240

5.68.3

13.3

4.04.04.0

12.012.012.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

87


Z-120 B





DIN 8555: E 10 UM 60 GRSpecifications:

C Mn Si Cr Fe3.90 0.30 1.00 24.90 Bal.

Basic coated electrode for surfacing parts subjectedto severe abrasionApplicable for crusher parts, conveyer screwsand bucket teeth

Hardness60 Rc 650 HB

= +

ASME: 1G 2F

ISO 6947 PA PB



1/85/323/16

3.254.05.0

141818

350450450

110-140140-180185-230

5.310.616.3

4.56.06.0

13.518.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

88


Z-123


Welding position




C Mn Si Cr Nb Fe6.50 0.80 0.60 22.70 7.00 Bal.

Basic coated electrode for hardsurfacing partssubjected to severe abrasion without impactUse up to 4500CApplicable for screws of refractory materialpresses, brick presses and cement presses


ASME: 1G 2F

ISO 6947 PA PB



1/85/323/16

3.254.05.0

141818

350450450

115-150135-200195-255

5.711.517.6

4.56.06.0

13.518.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70V)

89


Z-125


Current




C Mn Si Cr Mo Nb V W Fe4.30 0.70 0.80 17.70 4.90 2.00 0.60 3.00 Bal.


= +



Welding position

ASME: 1G 2F

ISO 6947 PA PB

Basic coated electrode for hardsurfacing partssubjected to severe abrasion without impactUse up to 6500CApplicable for sinter crushers, scraper wires inzinc industries, scrap collectors and mechanicalstokers

1/85/323/16

3.254.05.0

141818

350450450

125-160150-200220-300

6.312.519.7

4.56.06.0

13.518.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

90


Z-130


Current



Specifications:

C Mn Si Cr Mo W V Fe0.70 0.70 0.80 3.70 8.00 2.70 0.60 Bal.


= +



Welding position

Basic coated electrode for high speed tool surfacingModerate resistance to impactHeat resistant up to 6000CApplicable for cutting tools, drills, knives, shears,punches and dies

AWS/ASME SFA A5. 13 : EFe5-B modDIN 8555 : E 4 UM 60 S

ASME: 1G 2F 2G

ISO 6947 PA PB PC

3/321/8

5/32

2.53.254.0

141414

350350350

80-100110-130130-160

2.74.36.7

4.54.5/5.04.5/5.0

13.513.5/15.013.5/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

91


Z-151


Current



Specifications:

C Mn Si Cr Ni Fe0.60 12.20 0.60 0.10 4.60 Bal.

Hardness

230 HBAs welded

500 HBAfter work hardening

= +



Welding position

Basic coated cold work hardening Mn austeniticelectrodeHigh resistance to impact and shockUsed for rebuilding and joining between Mnsteel and Carbon steelApplicable for crusher plates, dredger teeth andhammers

AWS/ASME SFA A5. 13 : EFeMn-ADIN 8555 : E 7 UM 250 KP

ASME: 1G 2F 2G 3G


1/85/323/161/4

3.254.05.06.0

14/1814/18

1818

350/450350/450

450450

100-130150-180200-250240-290

3.76.0

11.116.2

5.0/6.05.0/6.0

6.06.0

15.0/18.015.0/18.0

18.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

92


Z-151 NC


Current



Specifications:

C Mn Si Cr Ni Fe1.00 13.20 0.25 4.60 5.00 Bal.

Hardness

200 HBAs welded


= +



Welding position

Basic coated cold work hardening Mnaustenitic electrodeHigh resistance to impact and shockUsed for rebuilding and joining betweenMn steel and Carbon steelApplicable for crusher plates, dredger teethand hammersNon conductive coating

AWS/ASME SFA A5. 13 : EFeMn-A modDIN 8555 : E 7 UM 250 KP

ASME: 1G 2F 2G 3G


1/85/323/161/4

3.254.05.06.0

14141818

350350450450

95-130130-180190-250240-280

3.96.3

11.217.0

5.05.06.06.0

15.015.018.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

93


Z-152




C Mn Si Cr Fe0.60 12.90 0.30 14.70 Bal.

Hardness

200 HBAs welded




Welding position

Rutile coated electrode for surfacing partssubjected to high impact and cavitationJoining and surfacing Mn steels and hard toweld steelsApplicable for dredge pumps, hydraulic presspistons, crushing equipment and rails

1/85/323/161/4

3.254.05.06.0

18181818

450450450450

110-140165-175190-220260-290

6.49.6

13.519.5

6.06.06.06.0

18.018.018.018.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70V)



94


Z-STEL 6


Current



Specifications:

C Cr W Co1.10 28.00 4.50 Bal.

Hardness44 Rc

= +



Welding position

Cobalt base hard facing electrodeUsed for high temperature high impact applications(up to 9000C)Corrosion resistant in organic and anorganicmedia

AWS/ASME SFA A5. 13 : ECo Cr-ADIN 8555 : E 20 UM 45 CTZ

ASME: 1G 2F

ISO 6947 PA PB

1/85/323/16

3.254.05.0

141818

350350350

90-120120-155150-190

3.75.98.5

2.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

95


Z-STEL 12


Current



Specifications:

C Cr W Co1.40 29.00 8.00 Bal.

Hardness47 Rc

= +



Welding position

Cobalt base hard facing electrodeUsed for high temperature moderate impact applications (up to 9000C)Corrosion resistant in organic and anorganicmedia

AWS/ASME SFA A5. 13 : ECo Cr-BDIN 8555 : E 20 UM 50 CTZ

ASME: 1G 2F

ISO 6947 PA PB

1/85/323/16

3.254.05.0

141818

350350350

90-120120-155150-190

3.95.97.3

2.0/2.52.0/2.52.0/2.5

12.012.012.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

96

Non Ferrous Electrodes

Z-Ni 1




Specifications:

C Mn Si Ti Fe Ni0.025 0.40 0.50 2.30 0.30 Bal.

Basic coated pure nickel electrodeEspecially for welding nickel and nickel alloysand joining to unalloyed and low alloyed steelsSuitable for welding NiCu and NiCu alloys tocarbon, stainless and nickel base alloys

= +

ASME: 1G 2F 2G 3G


AWS/ASME SFA A5. 11 : ENi-1DIN 1736 : EL-NiTi 3




ASTMAlloy 200Alloy 201Alloy 205--------

UNSN02200N02201N02205--------

DINNi99.2LC Ni99LC Ni99.6Ni99.6Ni99.8Ni99.4FeNiMn1NiMn2NiMn3AlNiMn5NiA14Ti

W.Nr2.40662.40682.40612.40602.40502.40622.41061.42102.41222.41162.4128


Re-drying :2500C/1-2h

3/321/8

5/32

2.53.254.0

141414

350350350

50-8075-120

100-140

2.03.35.1

2.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.0

12.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

97


Z-Ni B


Welding position


Specifications:

C Mn Si Fe Mo V Ni0.05 0.60 0.60 5.00 27.00 0.25 Bal.

Basic coated thick electrode for depositingNiMo-1 alloy and welding NiMo alloysCan be used at very high temperatures inreducing gases environmentExcellent resistance to acetic, phosphoric,sulphuric and hydrochloric acids

ASME: 1G 2F 2G 3G


AWS/ASME SFA A5. 11 : ENiMo-1DIN 1736 : EL-NiMo 29




ASTMAlloy B2

UNSN10665

DINNiMo29

W.Nr2.4616


Re-drying :2500C/2h

3/321/8

5/32

2.53.254.0

141414

350350350

90-110130-150180-200

3.66.39.3

2.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70V)

98


Z-Ni A2

Description and Applications: Specifications:Basic coated electrode designed for joining Nickel base alloys andfor joining dissimilar steels. The welding designed to endure widerange of temp from cryogenic up to 9800C

ASME: 1G 2F 2G 3G


AWS/ASME SFA A5. 11 : ENiCrFe-2DIN 1736 : EL-NiCr 15 FeNb



Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]410 650 32 50 J @ -196

0C

ASTMAlloy 800Alloy 600Alloy BAlloy C-Alloy 75Alloy 80AAlloy 9%Ni

UNSN08800N06600N06004N06003-N06075N07080K81340

DINX10 NiCrAlTi32 20NiCr 15FeNiCr60 15NiCr80 20NiCr10NiCr20TiNiCr20TiAlX8 Ni9

W.Nr1.48762.46402.48672.48692.48702.49512.49521.5662


Typical all weld metal composition [wt%]C Mn Si Cr Mo Nb Fe Ni

0.07 3.40 0.40 16.10 1.80 2.10 6.60 Bal.


3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

70-90100-135130-180190-220

2.64.36.5

10.2

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Current

= + ~ (Uo : 70V)

99


Z-NI 182

Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrFe-3DIN 1736 : EL-NiCr 15 FeMn




0C

ASTMAlloy 600Alloy 601Alloy 800Alloy 800HAlloy 75Alloy 80AAlloy 90Alloy 9%Ni

UNSN06600N06601N08800N08810N06075N07080N07090K81340

DINNiCr15FeNiCr23FeX10 NiCrAlTi32 20X10 NiCrAlTi32 20NiCr20TiNiCr20TiAlNiCr20Co18TiX8 Ni9

W.Nr2.46402.48511.48761.48582.49512.49522.49691.5662


Typical all weld metal composition [wt%]C Mn Si Cr Nb Fe Ni

0.02 7.50 0.40 13.80 1.80 4.40 Bal.


3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

75-100100-140140-180170-210

2.64.67.0

10.0

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Synthetic basic coated NiCr electrodeFor welding Ni-base alloys, claddings anddissimilar metalsHigh creep resistant and high resistance toembrittlement

Current

= +

Welding position

ASME: 1G 2F 2G 3G


100

Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrFe-3DIN 1736 : EL-NiCr 15 FeMn




0C

ASTMAlloy 600Alloy 601Alloy 800Alloy 800HAlloy 75Alloy 80AAlloy 90Alloy 9%Ni

UNSN06600N06601N08800N08810N06075N07080N07090K81340

DIN NiCr15FeNiCr23Fe X10 NiCrAlTi32 20X10 NiCrAlTi32 20NiCr20TiNiCr20TiAlNiCr20Co18Ti X8 Ni9

W.Nr2.46402.48511.48761.48582.49512.49522.49691.5662


Typical all weld metal composition [wt%]C Mn Si Cr Nb Fe Ni

0.02 6.70 0.70 13.50 1.60 5.00 Bal.


3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

105-145140-180175-215225-265

2.84.87.3

11.2

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Rutile basic coated NiCr electrode For welding Ni-base alloys, claddings anddissimilar metals High creep resistant and high resistance toembrittlement

Welding position

ASME: 1G 2F 2G 3G


Current

= + ~ (Uo : 70V)


Z-NI 182

101


Z-Ni 112

Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrMo-3DIN 1736 : EL-NiCr 20 Mo 9 Nb




0C

ASTMAlloy 625Alloy 825Alloy 600Alloy 800Alloy 75Alloy 80AAlloy 9%NiAlloy 6%Mo

UNSN06625N08825N06600N08800N06075N07080K81340S31254

DINNiCr22Mo9NbNiCr21MoNiCr15FeX10 NiCrAlTi32 20NiCr20TiNiCr20TiAlX8 Ni9

W.Nr2.48562.48582.46401.48762.49512.49521.5662


Typical all weld metal composition [wt%]C Mn Si Cr Nb Mo Fe Ni

0.05 0.90 0.60 21.0 3.4 9.5 3.4 Bal.


Current

= + ~ (Uo : 70V)

Synthetic basic coated NiCrMo electrodeSuitable for welding alloy 625, alloy 825 orsimilar gradesJoining 9%Ni for high toughness at cryogenictemperaturesExtreme high rsistance to general andintergranular corrosion, pitting, crevice andstess corrosion crackingResistant to high temperature oxidaton andcarburization

Welding position

ASME: 1G 2F 2G 3G


3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

90-130120-160150-190190-230

2.74.67.0

10.7

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

102


Z-Ni 112R





0C


UNSN06625N08825N06600N08800N06075N07080K81340S31254


W.Nr2.48562.48582.46401.48762.49512.49521.5662


Typical all weld metal composition [wt%]C Mn Si Cr Nb Mo Fe Ni

0.04 0.70 0.70 20.00 3.30 9.50 3.50 Bal.


Current

= + ~ (Uo : 70V)

Synthetic rutile coated NiCrMo electrodeSuitable for welding alloy 625, alloy 825 orsimilar gradesJoining 9%Ni for high toughness at cryogenictemperaturesExtreme high rsistance to general andintergranular corrosion, pitting, crevice andstess corrosion crackingResistant to high temperature oxidaton andcarburization

Welding position

ASME: 1G 2F 2G 3G


3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

90-130120-160150-190190-230

4.45.97.38.8

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

103


Z-NiCroMo3





0C


UNSN06625N08825N06600N08800N06075N07080K81340S31254


W.Nr2.48562.48582.46401.48762.49512.49521.5662


Typical all weld metal composition [wt%]C Mn Si Cr Mo Nb Fe Ni

0.03 0.40 0.50 21.50 9.50 3.50 3.00 Bal.


Current

= +

All position electrode depositing austenitic Ni-base high CrMoNb weldMatching core wireEspecially designed to match th compositionans properties of alloy 625Extremely high resistance to general andintergranular corrosion, pitting and crevicecorrosion and strees corrosion crackingResistant to stress corrosion cracking in sulphuricacid solutions and chloride containingenvironmentsResistant to hot cracking and high temperatureoxidation and carburiztionHigh toughness at cryogenic temperatures

Welding position



3/321/8

5/32

2.53.254.0

101212

250300300

40-7070-10090-140

1.92.93.7

2.02.02.0

12.012.012.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

104


Z-NiCroMo4

Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrMo-4DIN 1736 : EL-NiMo 15 Cr 15 W




0C

ASTMAlloy C276Alloy C4Alloy 625Alloy GAlloy G3

UNSN10276N06455N06625N06007N06985

DINNiMo16Cr15WNiMo16Cr15TiNiCr22Mo9NbNiCr22Mo6CuNiCr22Mo7Cu

W.Nr2.48192.46102.48562.46182.4619


Typical all weld metal composition [wt%]C Mn Si Cr Mo W Fe Ni

0.015 0.30 0.10 16.00 16.50 3.50 6.00 Bal.


Current

= +

All position electrode depositing austenitic Ni-base high CrMoNb weldMatching core wireEspecially designed to match th compositionans properties of alloy C276Extremely high resistance to general andintergranular corrosion, pitting and crevicecorrosion and strees corrosion crackingResistant to stress corrosion cracking in sulphuricacid solutions and chloride containingenvironmentsResistant to hot cracking and high temperatureoxidation and carburiztionHigh toughness at cryogenic temperatures

3/321/8

5/32

2.53.254.0

101212

250300300

40-7070-10090-140

1.92.93.7

2.02.02.0

12.012.012.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

Welding position



105


Z-Ni C

Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCrMo-5DIN 1736 : EL-NiMo 15 Cr 15 W mod



Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]- 720 28 -

ASTMAlloy C276Alloy C4Alloy C625

UNSN10276N06455N06625

DINNi Mo 16Cr 15WNi Mo 16Cr 15TiNi Cr 22Mo 9NbNi Cr 22Mo 6CuNi Cr 22Mo 7Cu

W.Nr2.48192.46102.48562.46182.4619


Typical all weld metal composition [wt%]C Mn Si Cr Mo Fe W Ni

0.04 0.30 0.90 14.50 16.80 4.00 3.70 Bal.


Basic coated electrode giving a Ni-base weldmetal equivalent in composition of Hastelloy CIdeal for use as build ups in high temperaturesoxidation, corrosion and mechanical stressapplications

Current

= +

Welding position

ASME: 1G 2F 2G 3G


3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

70-90100-110130-160160-200

3.66.39.3

14.5

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

106


Z-Ni 190

Description and Applications: Specifications:AWS/ASME SFA A5. 11 : ENiCu-7DIN 1736 : EL-NiCu 30 Mn

Materials to be weldedASTMMonel 400Monel K500

UNSN04400N65500

DIN 17 743NiCu 30 FeLC NiCu 30 FeG Ni Cu 30 NbNiCu30 AlNiCu 14 FeMo

W.Nr2.43602.43612.43652.43752.4400


Typical all weld metal composition [wt%]C Mn Si Cu Ti Fe Ni

0.03 2.60 0.60 33.00 0.30 1.30 Bal.


Basic coated Ni-Cu electrode for welding Ni-Cu alloy to mild and low alloy steelsHigh resistance to sea water corrosionExcellent resistance to stress corrosion cracking

Current

= +

Welding position

ASME: 1G 2F 2G 3G


Typical all weld metal mechanical propertiesRp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V]

320 510 35 120 J @ -200C

3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

70-9090-125

110-160155-185

1.93.24.97.5

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

107


Z-Ni 187

Description and Applications: Specifications:AWS/ASME SFA A5. 6 : ECuNiDIN 1733 : EL-CuNi 30 Mn

Materials to be weldedUNSC71500C71300C70600

DINCuNi 30Mn1FeCuNi 25CuNi 10Fe

W.Nr2.08822.08302.0872

Typical all weld metal composition [wt%]Mn Si Ni Fe Cu1.70 0.70 30.00 0.60 Bal.

Basic coated electrode for welding wrought ironor cast copper nickel alloys (max 30% Ni)Can be used for cladding steelsWeld metal Resistant to Corrosion, erosion andcavitation in sea-water

Typical all weld metal mechanical propertiesRp 0.2 [MPa] Rm [MPa] A5 [%] Hardness

220 370 30 105 HB

Current

= + ~

Welding position

ASME: 1G 2F 2G 4G

ISO 6947 PA PB PC PE



3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

50-7575-110

110-145145-185

2.23.45.07.9

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

108


Z-BRONZE A

Description and Applications: Specifications:AWS/ASME SFA A5. 6 : ECuSn-A

Materials to be weldedUNSC50700C51100

DINCuSn2CuSn4

W.Nr2.10102.1016

Typical all weld metal composition [wt%]Sn P Cu5.00 0.30 Bal.

Basic coated electrode for joining phosphor-bronze platesApplicable for electrial conductorsUsed for surfacing bronze, cast steel and copperplates

Typical all weld metal mechanical propertiesRp 0.2 [MPa] Rm [MPa] Hardness

190 250 100 HB

Current= +



Welding position

ASME: 1G 2F

ISO 6947 PA PB

3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

40-6570-100

120-160160-200

1.93.14.86.8

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

109


Z-BRONZE


Materials to be weldedUNSC50700C51100C51900C52100

DINCuSn2CuSn4CuSn6CuSn8

W.Nr2.10102.10162.10202.1030


Basic coated electrode for assembly and surfacingwelds on copper alloysIdeal for surfacing on steel, cast steel and castiron


140 300 105 HB

Current= +

Specifications:AWS/ASME SFA A5. 6 : ECuSn-CDIN 1733 : EL-CuSn 7

Welding position

ASME: 1G 2F

ISO 6947 PA PB



3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

40-6570-100

120-160160-200

1.93.14.86.8

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

110


Z-BRONZE M


Materials to be weldedUNSC50700C51100C51900C52100

DINCuSn2CuSn4CuSn6CuSn8

W.Nr2.10102.10162.10202.1030


Basic coated electrode for assembly and surfacingwelds on copper alloysIdeal for surfacing on steel, cast steel and castiron


140 300 105 HB

Specifications:AWS/ASME SFA A5. 6 : ECuSn-CDIN 1733 : EL-CuSn 7

Welding position

ASME: 1G 2F

ISO 6947 PA PB

Current

= + ~ (Uo : 70V)



3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

40-6570-100

120-160160-200

1.93.35.07.0

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

111

Cast Iron & Cutting Electrodes

Z-SuperNi

Description and Applications: Specifications:AWSASME SFA A5. 15 : ENi-ClDIN 8573 : E Ni-BG-21



Rp 0.2 [MPa] Rm [MPa] A5 [%] Hardness- 300 5 170HB

Castings, pump bodies, machine bases, engine blocks, gears, cylinders and valvesLamellar grey cast ironMalleable cast ironNodular cast iron

DIN 1691DIN 1692DIN 1693

GG 10 to GG 35GTS 35 10 to GTS 55 4, GTW 35 04 to GTW 45 07, GTW S 38 12GGG 40 to GGG 60

Typical all weld metal composition [wt%]C Si Fe Ni

1.50 3.00 4.00 Bal.

Current

= + ~ (Uo : 50V) _

Special nickel cored electrode for depositingsoft, machinable metal on grey cast ironSuitable for reclamation and repair of grey castiron and for joining these to mild and C-MnsteelsCan be used with low welding currentsWelding both positive direct current and negativeand alternating currents

Welding position




Re-drying : 100-1500C/1-2hr

3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

50-8080-110

110-150150-190

2.03.35.17.4

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

112


Z-Ni 99

Description and Applications: Specifications:AWSASME SFA A5. 15 : ENi-ClDIN 8573 : E Ni-BG-23





DIN 1691DIN 1692DIN 1693



0.80 0.10 4.50 Bal.

Special electrode for depositing soft machinablemetal on grey cast ironExcellent for repairing casting defects in greycast ironCan join cast irons to steels, monels etc.



Current

= + ~ (Uo : 50V)

Welding position

ASME: 1G 2F 2G 4G


3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

50-8080-110

110-150150-190

2.03.45.27.4

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

113


Z-Ni 99NC

Description and Applications: Specifications:AWS/ASME SFA A5. 15 : ENi-ClDIN 8573 : E Ni-BG-23





DIN 1691DIN 1692DIN 1693



0.75 0.20 5.30 Bal.

Electrode for welding cast iron or malleable castironNon conductive coatingMachinable weld deposit

Current

= + ~ (Uo : 50V)

Welding position

ASME: 1G 2F 2G 4G



Re-drying : 1200C/1hr

3/321/8

5/32

2.53.254.0

141414

350350350

60-9090-110

110-170

2.13.35.2

2.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

114


Z-Ni 55

Description and Applications: Specifications:AWS A5. 15 : E NiFe-ClDIN 8573 : E NiFe-1-BG-23





DIN 1691DIN 1692DIN 1693


Typical all weld metal composition [wt%]C Ni Fe

1.20 55.0 Bal.

Basic coated electrode which deposits a machinablenickel iron alloy weldDesigned for strength welding of high duty castiron such as mechanite, malleable and spheroidalgraphite and nodular ironsWelds high phosphorus castingsTypical components to be welded are machinebases, pump bodies, engine blocks, gears andtransmission housings

Current

= + ~ (Uo : 50V)

Welding position




Re-drying : 100-1500C/1-2hr

3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

50-8080-110

110-150150-190

2.03.35.17.4

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

115


Z-GSM

Description and Applications: Specifications:DIN 8573 : E FeC-G-BG-26




Malleable cast ironNodular cast iron

DIN 1692DIN 1693

GTS 35, GTS 45GGG 40 to GGG 50

Basic coated electrode for hot welding of nodularcast ironSuitable for welding malleable black and greycast ironNon machinable weld deposit

Current

= + ~ (Uo : 70V)



Welding position

ASME: 1G 2F 2G 3G


Typical all weld metal composition [wt%]C Si Fe Mn Ni

1.00 0.80 3.60 1.30 Bal.

3/321/8

5/32

2.53.254.0

141414

350350350

60-9090-120

130-180

1.72.74.1

5.05.05.0

15.015.015.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

116


Z-GM

Description and Applications: Specifications:AWS/ASME SFA A5. 15 : ENiCu-BDIN 8573 : E NiCu-BG-23




Lamellar grey cast ironMalleable cast ironNodular cast iron

DIN 1691DIN 1692DIN 1693

GG 10GTS 35GGG 40

Typical all weld metal composition [wt%]C Fe Cu Ni

0.40 2.60 33.00 Bal.

Monel type core wired electrode for weldinglamellar grey, nodular and malleable cast ironSuitable also for welding of cast iron to mildsteelMachinable weld deposit



Current

= + ~ (Uo : 50V)

Welding position

ASME: 1G 2F 2G 3G


3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

50-8080-110

110-150150-190

1.83.24.97.4

2.0/2.52.0/2.52.0/2.52.0/2.5

12.0/15.012.0/15.012.0/15.012.0/15.0

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

117


Z-71


Working position Current

Electrode for scrapping and gougingUsable in all positions on mild and low alloysteels, stainless steels, cast iron, nickel basedalloys and aluminium alloys


All welding positions

3/321/8

5/323/161/4

2.53.254.05.06.0

1414141414

350350350350350

120 Min170 Min190 Mn275 Min350 Min

1.93.34.97.79.8

3.53.53.53.53.5

10.510.510.510.510.5

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

= + ~ (Uo : 50V)

118


Z-72



Electrode for cutting and piercingUsable in all positions on mild and low alloysteels, stainless steels, cast iron, nickel basedalloys and aluminium alloys


All welding positions= + ~ (Uo : 50V)

3/321/8

5/323/16

2.53.254.05.0

14141414

350350350350

120 Min170 Min190 Min 275 Min

1.63.75.47.8

4.54.54.54.5

13.513.513.513.5

Diain mm

Lengthin mm

Current[amps]

Weightkg/100 pcs

Weight packet[kg]

Weight carton[kg]

119


Z-OXYCUT



Flux coated tubular electrode for cutting anymaterial by means of oxygen pressure


All welding positions = +

3/169/32

5.07.0

1818/39.3

450450/1000

200-250250-300

Diain mm

Lengthin mm

Current[amps]

120

Flux Cored Wire

Z-71T1


Approvals

Current




AWS/ASME SFA A5.20 : E71T-1Specifications:

C Mn Si0.06 1.45 0.45

Rutile Flux cored wire suitable for all-positionalweldingStable and penetrative arc with little spatterformationHigh impact toughness at sub-zero temperatures

Rp 0.2 [MPa] Rm [MPa] A5 [%] Impact [ISO-V] Heat Treatment540 580 26 110 J @ -20oC U

Non alloyed sturctural steelsBoiler platesPipe steels

DIN 17 100DIN 17 155DIN 1626/1629DIN 1628/1630DIN 17 175DIN 17 172DIN 17 172API 5LX

St 33, St 37.2, St 44.2, St 52.3Hl, Hll, 17 Mn 4St 37.0 to St 52.0St 37.4 to St 52.4St 35.8, St 45.8St E 210.7 to St E 415.7St E 290.7 TM to St E 480.7 TMX42 to X46St E 255 to St E 460A, B, D, E

Fine grained structural steelsShipbuilding steels

ABS3YSH5

Shielding gas: CO2

LR3YSH5

= +

Welding position



Packaging data

0.0450.063

1.21.6

15 .015.0

Diain mm

Weight/reel 300 DOutside Dia

121

Flux Cored Wire

Z-71T5


Approvals

Current




AWS/ASME SFA A5.20 : E71T-5Specifications:

C Mn Si0.06 1.30 0.38

Low hydrogen basic flux cored wire suitable forall-positional weldingStable and penetrative arc with little spatterformationExtra high impact toughness at sub-zerotemperatures


Non alloyed sturctural steelsBoiler platesPipe steels

DIN 17 100DIN 17 155DIN 1626/1629

DIN 17 102

St 33, St 37, St 44, St 52, St 50, St 60, St 70Hl, Hll, 17 Mn 4, 19 Mn 5St 37.0, St 37.4, St 44.0, St 44.4 St 52.0, St 52.4, St 35.8, St45.8, St E 210.7, ST E 240.7, St E 290.7, St E 320.7, St E 360.7including thermo-mechanical gradesSt E 255 to St E 355, W St E 255 to W St E 355,T St E 255 to T St E 255A, B, D, EGS 38, GS 52, GS 60

Fine grained structural steels

Shielding gas: CO2

LR3YSH5

= +

Packaging data

Welding position



Shipbuilding steelsCast steels

0.0450.063

1.21.6

15 .015.0

Diain mm


122

S MI AUTOMATIC SOLID WIRE

Z-R2


Current




AWS/ASME SFA A5.18 : ER-70S-2 EN 440 : G2 Ti

Specifications:Double de-oxide mild steel mig solid wire for welding of unalloyed steels and fine grained C-Mn steels Capable of producing high quality welds where the steel is rusty


Unalloyed construction steels Boiler plates Pipe steels Shipbuilding steels

DIN 17 100 DIN 17 155 DIN 1629

St 33 to St52.3 Hl, Hll , 17 Mn 4 St35 to St52.4 A, B, D, E

Shielding gas: Argon CO2 (M21)

= +

Packaging data

Welding position



C Mn Si Ti Zr Al0.06 1.10 0.50 0.10 0.09 0.10

0.0240.0300.0350.0390.0450.063

0.60.80.91.01.21.6

15 Kgs15 Kgs15 Kgs15 Kgs15 Kgs15 Kgs

5Kgs 5Kgs 5Kgs 5Kgs 5Kgs5Kgs

Dia in mm

Weight/reel 300 D Outside Dia

Weight/reel 200 D Outside Dia

123

Z-R3


Current




AWS/ASME SFA A5.18 : ER-70S-3DIN 8575 : SG 1 EN 440 : G2 Si

Specifications:Double de-oxide mild steel mig solid wire forwelding of unalloyed steels and fine grainedC-Mn steels


Unalloyed construction steelsBoiler plates Pipe steels

Shipbuilding steels

DIN 17 100DIN 17 155DIN 17 172DIN 1629

St 33 to St52.3 Hl, Hll , 17 Mn 4 StE 210.7 to StE 310.7St35 to St52.4 A, B, D, E


= +

Packaging data

C Mn Si0.07 1.20 0.60

Welding position



0.0240.0300.0350.0390.0450.063

0.60.80.91.01.21.6


5Kgs5Kgs5Kgs5Kgs5Kgs5Kgs

Diain mm




124

Z-R6





AWS/ASME SFA A5.18 : ER-70S-6DIN 8559 : SG 2 BS 2901 : A18 EN 440 : G3 Si 1 mod

Specifications:Double de-oxide mild steel mig solid wire forwelding of unalloyed steels and fine grained C-Mn steels Produces a quality weld with excellent radiographicand mechanical properties


Unalloyed construction steelsBoiler plates Pipe steels

Shipbuilding steels

DIN 17 100DIN 17 155DIN 17 172DIN 1629

St 33 to St52.3 Hl, Hll , 17 Mn 4 StE 210.7 to StE 360.7St35 to St52.4 A, B, D, E


Packaging data

C Mn Si0.08 1.50 0.90

Welding position



ApprovalsLR

3YSH15

0.0240.0300.0350.0390.0450.063

0.60.80.91.01.21.6


5Kgs5Kgs5Kgs5Kgs5Kgs5Kgs

Diain mm




125

Z-RMo


Current




Specifications:Molybdenum mild steel wire Recommended for welding mild steels or 0.5% Moalloyed steels for high temperatures serviceIdeal for avoiding porosity and cracks


Cast ironBoiler plate

DIN 17 245DIN 17 155

GS 22 Mo 415 Mo 4


= +

Packaging data

C Mn Si Mo0.08 1.90 0.70 0.50

AWS/ASME SFA A5.28 : ER-80S-D2DIN 8559 : SG Mo BS 2901 : A 30/A31 EN 440 : G4 Mo

Welding position



0.0300.0350.0390.0450.063

0.80.91.01.21.6

15 Kgs15 Kgs15 Kgs15 Kgs15 Kgs

10.510.510.510.510.5

Diain mm




Documents

MILD & MEDIUM CARBON STEEL ELECTRODES 1-16 LOW ALLOY … · mild & medium carbon steel electrodes 1-16 17-48 49-79 80-95 96-110 111-119 120-125 low alloy steel electrodes stainless