WWW.TN-EUROPE.COMKNOWLEDGE. EXPERIENCE. CRAFTSMANSHIP.
SELF-ADHESIVE MEMBRANES
VAPORSTOP CA 500 (TECHNOELAST VB 500 SELF)
ULTRAFLEX SA NBS
ULTRAFLEX SA | ULTRAFLEX SA NB
MIDA SELF SA 1.5 mm STRONG P | MIDA SELF SA 1.5 mm STRONG G
SELF-ADHESIVE MEMBRANES
TN-INTERNATIONAL 2
Long operational lifetime, reliability and convenience of installation —
that’s the ideal waterproofing. Any defect, especially when it comes to
foundations, will certainly lead to destruction of the entire system and
huge financial losses to the customer.
Application of self-adhesive materials make possible to install reliable
waterproofing where the standard torch-on application is forbidden,
and high flexibility and elasticity allow the materials to be used on
surfaces of any complexity and in limited space.
APPLICATION AREA:
Waterproofing of underground (below-grade) parts of premises and
engineering structures;
Indoor waterproofing of premises and buildings;
Waterproofing of confined space, where standard technologies
cannot be applied (bathroom floor). Can be used in parquetry and
floor installation;
As an underlay on pitched roofs and as a vapor barrier on the
corrugated steel sheets and precast concrete slabs;
Corrosion protection of steel pipes and junctions.
ADVANTAGES:
APPLICATION ON
SURFACES, WHERE
TORCH-ON APPLICATION
IS PROHIBITED
SIMPLE
INSTALLATION
APPLICATION ON
SURFACES OF ANY
COMPLEXITY
DOES NOT REQUIRE
EXTRA EQUIPMENT
COLD APPLICATION
PREVENTS SMOKE,
ODOURS AND NOISE
QUICK
INSTALLATION
Self-adhesive waterproofing is a type of materials, that combines all the
advantages of torch-on applied materials and non-torch-on installation, which
helps to avoid issues associated with the use of flame.
SELF-ADHESIVE MEMBRANES
TN-INTERNATIONAL 3
Vapor barrier with aluminum foil intended to use as a reliable vapor-
proofing layer in roofing constructions on a corrugated steel decking.
Self-adhesive bottom surface and high tensile strength ensure the
ability of the material to withstand the weight of the person standing
between the corrugations of the profiled metal deck without breaking
or stretching.
Intended use:
Material is used as a vapor barriers in construction of public and
industrial buildings with normal temperature and humidity conditions
(malls, warehouse complexes, sport centers etc.).
VAPORSTOP CA 500 (TECHNOELAST VB 500 SELF)
PROPERTIES VAPORSTOP CA 500
Weight, kg/m2 0.5±0.10
Thickness, mm 0.5±0.10
Flexibility / Flow resistance, °С ≤ -25 / ≥ 90
Tensile strength, N/50 mm 600 / 600±120
Reinforcement type fiberglass mesh
Protective covering type: upper /bottom aluminum foil / protective film
Width х length, m 50 × 1.08
ADVANTAGES:
High workforce productivity —
few installation steps
Easier to install an ideal vapor
barrier
Vapor permeability Sd=1000
Mechanically stable – withstand
the weight of the person
VAPORSTOP CA 500 (TECHNOELAST VB 500 SELF)
TN-INTERNATIONAL 4
SOLUTION EXAMPLES:
VAPORSTOP CA 500 (TECHNOELAST VB 500 SELF)
TN-INTERNATIONAL 5
METHOD OF APPLICATION:
Cut the siliconized anti-adhesion
film at the distance of 30-40 cm
from the beginning of the roll by
means of roofing knife.
1
Remove the protective film from the
edge of the roll and attach the
membrane to the surface.
2
Press the place of the first adhesion
by roller for the whole width of the
membrane.
3
Continue attaching the membrane to
the base. One worker pulls the film
off, while the other smooths the
membrane by brush.
4
Convenience, simplicity and safety of installation of the membrane are due to the special adhesive polymer-bitumen layer, which allows installation of the material
without additional equipment.
SELF-ADHESIVE MEMBRANES
TN-INTERNATIONAL 6
Used for indoor waterproofing with the direct installation of ceramic
tiles onto the material without the need of protective sand cement
screed. Can be used on bases, where the standard torch-on
application is forbidden (wood, XPS, etc.)
MATERIAL STRUCTURE:
1. Polypropylene (Spunbond)
Protects waterproofing layer from mechanical damage. Provides
strong sticking to the tile adhesive.
2. Self-adhesive polymer-bitumen compound
High elasticity index of this layer allows installation of waterproofing
on surfaces of any complicated shape
3. Easy-removable protective film
Used for underside surface protection from sticking in the roll.
ULTRAFLEX SA NBS
PROPERTIES ULTRAFLEX SA NBS
Weight, kg/m2 1.5±0.25
Thickness, mm 1.5±0.10
Flexibility / Flow resistance, °С ≤ -15 / ≥ 85
Tensile strength, N/50 mm NPD
Reinforcement type -
Protective covering type: upper /bottom Spunbond / protective film
Width х length, m 20 × 1
ADVANTAGES:
Material is installed in one layer
unlike cement based waterproofing,
which requires several layers.
No need to wait for the screed to dry
Tile is installed directly on the
material.
ULTRAFLEX SA NBS
TN-INTERNATIONAL 7
SOLUTION EXAMPLES:
SELF-ADHESIVE MEMBRANES
TN-INTERNATIONAL 8
Self-adhesive polyester reinforced SBS-modified bitumen membrane
ULTRAFLEX SA is designed to complete secure application. It is used
as an underlay on pitched roofs and as a vapor barrier.
Could also be used for waterproofing of foundations and engineering
structures Non-skid upper layer from fine-grained sand provide safe
movement on the roof during installation.
MATERIAL STRUCTURE:
1. PE film or sand
Protects waterproofing layer from mechanical damage and
prevents adhesion of the material in the roll.
2. Polymer-bitumen compound
Provides reliable waterproofing
3. Polyester
Provides excellent elongation and grants optimal strength to the
material.
4. Self-adhesive polymer-bitumen compound
Self-adhesive layer allows to install the material on combustible
surfaces.
5. Easy-removable protective film
Used for underside surface protection from sticking in the roll.
ULTRAFLEX SA
PROPERTIES ULTRAFLEX SA
Weight, kg/m2 1.8±0.20
Thickness, mm 1.5±0.20
Flexibility / Flow resistance, °С ≤ -20 / ≥ 90
Tensile strength, N/50 mm ≥ 90
Reinforcement type polyester
Protective covering type: upper /bottom film or sand / protective film
Width х length, m 20 × 1
ADVANTAGES:
Self-adhesive
Simple and quick installation
High speed of application
Dimensional stability
Safety at work
ULTRAFLEX SA
TN-INTERNATIONAL 9
SOLUTION EXAMPLES:
SELF-ADHESIVE MEMBRANES
TN-INTERNATIONAL 10
Self-adhesive carrier less SBS-modified bitumen membrane
ULTRAFLEX SA NB is designed for waterproofing of foundations and
engineering structures, indoor waterproofing. Thanks to the special
adhesive bitumen compound, the material can be used on surfaces,
where the standard torch-on application is forbidden (expanded /
extruded polystyrene or wooden base). The absence of a carrier is a
key feature of this material that makes it very elastic and flexible.
MATERIAL STRUCTURE:
1. Thick PE film for mechanical protection
Protects waterproofing layer from mechanical damage and impacts
of chemically aggressive media
2. Self-adhesive polymer-bitumen compound
High elasticity of this layer preserves waterproofing undamaged
when cracks and splits occur in the foundation
3. Easy-removable protective film
Used for underside surface protection from sticking in the roll.
ULTRAFLEX SA NB
PROPERTIES ULTRAFLEX SA NB
Weight, kg/m2 1.5±0.25
Thickness, mm 1.5±0.20
Flexibility / Flow resistance, °С ≤ -15 / ≥ 85
Tensile strength, N/50 mm NPD
Reinforcement type -
Protective covering type: upper /bottom thick film / protective film
Width х length, m 20 × 1
ADVANTAGES:
Self-adhesive
Simple and quick installation
High speed of application
High elasticity
ULTRAFLEX SA NB
TN-INTERNATIONAL 11
SOLUTION EXAMPLES:
SELF-ADHESIVE MEMBRANES
TN-INTERNATIONAL 12
Self-adhesive polyester / glass fiber reinforced SBS-modified bitumen
membrane MIDA SELF SA 1.5 mm STRONG is designed for
waterproofing of foundations and engineering structures.
On the top side, the material is covered with a special thick PE film
that grants additional tensile properties and elongation. The other side
of the material is covered with a removable protective film.
MATERIAL STRUCTURE:
1. Thick PE film for mechanical protection
Protects waterproofing layer from mechanical damage and impacts
of chemically aggressive media
2. Polymer-bitumen compound
Provides reliable waterproofing
3. Polyester (P) / Glass fiber (G)
Reinforced carrier makes the material stable to tension and
deformation.
4. Self-adhesive polymer-bitumen compound
High speed of materials application without any additional
equipment and skills.
5. Easy-removable protective film
Used for underside surface protection from sticking in the roll.
MIDA SELF SA 1.5 mm STRONG
PROPERTIES P G
Weight, kg/m2 1.7±0.20
Thickness, mm 1.5±0.20
Flexibility / Flow resistance, °С ≤ -20 / ≥ 85
Tensile strength, N/50 mm 400 / 300±100 350 / 200±100
Reinforcement type polyester glass fiber
Protective covering type: upper /bottom thick film / protective film
Width х length, m 20 × 1
ADVANTAGES:
Self-adhesive
Simple and quick installation
High speed of application
Dimensional stability
MIDA SELF SA 1.5 mm STRONG
TN-INTERNATIONAL 13
SOLUTION EXAMPLES:
METHOD OF APPLICATION
TN-INTERNATIONAL 14
FLAT ROOF OR INDOOR WATERPROOFING
Clean and treat the surface with
bitumen primer.
1
Fit and straighten the membrane to
the area of application.
2
Re-roll the membrane to the center,
pre-cut the protective film.
3
Remove the protective film and
smooth the membrane.
4
METHOD OF APPLICATION
TN-INTERNATIONAL 15
FLAT ROOF OR INDOOR WATERPROOFING
Longitudinal overlaps – 80-100 mm.
End overlaps – 150 mm.
Overlaps to be glued with bitumen
mastic of 1 mm thickness.
5
On a vertical surface the material to
be placed on a height, sufficient
according to the thickness of the
floor and decoration.
6 ! Self-adhesive materials to be installed at the temperaturesabove +10 °С.
! Surface must be smooth, dry, clean and with no oil stains.
METHOD OF APPLICATION
TN-INTERNATIONAL 16
FOUNDATION WATERPROOFING
Surface must be smooth, dry, clean
and with no oil stains. For better
adhesion, treat the surface with
primer.
1
Measure the depth of the
foundation and cut the material to
the required length.
2
Apply the material from top
downward by gradual removing the
protective film, unrolling the
membrane and smoothing it to the
surface.
3
The material to be installed to the
height of 30-50 cm above the
ground level. Longitudinal overlaps
should be 100 mm, sheet end
overlaps - 150 mm.
4
METHOD OF APPLICATION
TN-INTERNATIONAL 17
FOUNDATION WATERPROOFING
The top end of the waterproofing
membrane to be fixed at basement
level by profiled metal edge strip and
sealed.
5
Protect the membrane from
mechanical damage by means of
thermal insulation or protective
slabs.
!
As a layer protection from mechanical
impacts PLANTER profiled HDPE
membrane is recommended.
!
WWW.TN-EUROPE.COM
THANK YOU FOR ATTENTION!
Name
Position