Supplemental information
Unusual morphologies of poly(vinyl alcohol) thin films adsorbed on polydimethylsiloxane
substrates
Akchheta Karki,§ Lien Nguyen,
§ Bhanushee Sharma, Yan Yan, and Wei Chen*
Chemistry Department, Mount Holyoke College, South Hadley, MA 01075
*To whom correspondence should be addressed
Email: [email protected]
Tel: 413-538-2224
Fax: 413-538-2327
§Both authors contributed equally to this work
Figure 1S. a-x) Optical microscopy time-lapse images of in-situ PVOH99%
adsorption on
PDMS2k taken every hour over a 23-h period. Spots are due to dust particles on the camera lens.
2
Figure 2S. a-x) Optical microscopy time-lapse images of in-situ PVOH99%
adsorption on
PDMS49k
taken every hour over a 23-h period.
3
Figure 3S. TEM images of thicker PVOH regions (PVOH99%
on the left and PVOH88%
on the
right) where electron diffraction patterns were obtained.
4
Figure 4S. a-x) Optical microscopy time-lapse images of in-situ desorption of PVOH99%
-
PDMS49k
taken every hour over a 23-h period.
5
Figure 5S. Advancing and receding water contact angles of PVOH99%
and PVOH88%
thin films
adsorbed on PDMS2k (top) and plasma treated PDMS
49k (bottom) substrates as a function of
time.
0
20
40
60
80
100
120
0 20 40 60 80 100 120 140 160 180
Dynamic Contact angles (°)
Time (h)
Adv,88% Rec,88% Adv,99% Rec,99%
0
20
40
60
80
100
120
0 20 40 60 80 100 120 140 160 180
Dynamic Contact angles (°)
Time (h)
Adv,88% Rec,88% Adv,99% Rec,99%