Unit 6: EXTRUSION

Introduction: Extrusion is a metal working process in which cross section of metal is reduced by

forcing the metal through a die orifice under high pressure.

It is used to produce cylindrical bars, tubes and sections of any regular or irregular types.

Forces required to extrude a metal are quite high and hence hot extrusion is most widely

done as deformation resistance of metal is low at high temperature. However, cold

extrusion is also performed for soft metals like Aluminum, lead etc.

Difficult to form metals like stainless steels, nickel based alloys and high temperature

metals can also be extruded.

History; Originally the principle of extrusion was applied to make lead pipe and lead

sheathing of electrical cables.

Types of Extrusion

1) Direct Extrusion

In this process, the metal billet is placed in a container and compressed

and extruded through the die by a ram.

Some features of direct extrusion:

• Both the ram and extrusion move in the same direction.

• A dummy block or pressure plate is in contact with the billet and ram.

2

• The relative motion between billet and container wall develops high friction. Hence

power required is relatively high.

• Brittle metals like Tungsten, Titanium alloys are difficult to extrude because they

fracture during the process. Fractures occur because of rapid growth of micro cracks

due to tensile stresses.

2) Indirect Extrusion

A hollow ram compresses metal through a die in a direction opposite to ram

motion. Either the ram is moved against a stationery billet or the billet (hence container)

is made to move against stationery ram.

Some features of indirect extrusion:

• There is no relative motion between the billet and the wall of the container.

• Hence friction is lower and power required is relatively less.

• Limitation; Due to hollow ram, the load that can be applied is limited and only

small sections can be extruded.

3) Tube extrusion

A mandrel is attached to the end of the ram as shown, which produces a hollow tube.

The clearance between the mandrel and die wall determines the thickness of the tube

3

Fig.Tube Extrusion

To begin with, either a hollow billet is taken or a solid billet is first pierced through

and then extruded.

4) Impact Extrusion

In this process a punch moves into the die and squeezes metal around the die

cavity. It may have either direct or indirect extrusion arrangement.

Fig. Impact Extrusion

It is useful to produce short lengths of hollow shapes like collapsible tooth paste tubes

and thin walled cans.

It is usually a cold working process, but the high speed of deformation develops heating.

The process is limited to soft metals like lead, tin, aluminum, copper.

4

5) Hydrostatic Extrusion

In this process the space between the ram plate and billet is filled with water.

Hence billet is subjected to uniform hydrostatic pressure.

Fig. Hydrostatic Extrusion

Also, there is no direct contact between wall of container and work piece. Hence

there is no container-billet friction. As a result, the curve of extrusion pressure v/s ram

travel is nearly flat. Therefore, large length to diameter ratios are possible. eg coils of

wire.

Advantages:

i) Lubrication is very effective.

ii) Extruded product has good surface finish and dimensional accuracy.

iii) It is possible to use dies with very low semi cone angle ( about 20 degrees)

because friction is less.

iv) This reduces extrusion pressure and improves homogeneity of deformation.

v) Redundant deformation is minimized.

Limitations:

i) Hot working is not possible.

ii) Leakages of liquid are frequent due to high pressures involved ( upto

1.7GPa)

iii) Liquid used should not solidify at high pressure.

iv) Extrusion ratios possible ; 20:1 for mild steel, 200:1 for aluminum.

5

Extrusion Equipment

I) Hydraulic Press

Types based on direction of ram travel:

i) Vertical Press and ii) Horizontal Press

i) Vertical Press ( 3 MN to 20 MN)

The ram acts vertically on the billet and squeezes it through the die.

Advantages:

i) Easier alignment between the press ram and tools.

ii) Hence closer control on tolerances is possible.

iii) High rates of production.

iv) Requires less floor space.

v) Produces uniform cooling of billet in container. Hence symmetrically uniform

deformation of metal occurs.

Limitations:

i) This requires more head room to accommodate vertical motion of ram

ii) Floor pits are needed to accommodate long extrusions.

Applications: Thin walled tubing where uniform wall thickness and concentricity are

required.

6

II) Horizontal Press (15 MN to 50 MN)

Ram moves horizontally and extrudes metal.

Advantages:

i) The head room required is less compared to vertical press.

Limitations:

i) Alignment between press ram and tools is difficult.

ii) The bottom of the billet is more in contact with the container wall and hence it

is cooled faster compared to the top of the billet. Therefore deformation is

non uniform.

iii) To overcome above difficulty, the container walls are internally heated to

avoid differential cooling of the billet.

Ram speed:

Higher ram speeds are required for high temperature extrusion to prevent heat

loss to container walls.

Ram speeds of 0.4n/s to 0.6m/s are used to extrude refractory metals.

Dies and Toolings

They must withstand high stress and thermal shocks/ oxidation. From economics

point of view, another important requirement of the dies is that easy replacement of

damaged parts and reuse of parts after reworking must be possible.

7

Fig. Typical tooling arrangement

Typical arrangement of extrusion tooling:

• The die is supported in a die (6) holder(5) and bolster (7).

• The die head (2) all the above parts 5,6 and7.

• The wedge (1) applies pressure and seals the entire assembly.

• The liner(4) is shrunk into container(3) to produce compressive pre stress in the

inside surface of liner ( Liner needs periodic replacements)

Types of extrusion dies

1) Flat Faced Dies

Fig. Flat Die

Some important features:

• It is used when metal entering the die forms a dead zone and shears internally to

form its own die angle.

8

• A parallel land on the exit side of the die strengthens the die.

• It also allows reworking of the flat face on the entrance side without increasing

the exit diameter.

2) Conical Dies

Fig. Conical Die

Some important features:

• The entrance side has conical shape and taper.

• They are used in extrusion with good lubrication.

• Die angle is decreased and this increases homogeneity of deformation and also

reduces extrusion pressure.

• If the angle is too small, it leads too high friction in die surface. Hence an optimal

angle is necessary.

Other supporting systems required in extrusion equipment:

a) Provision for heating extrusion container

b) Billet heating facilities

c) Automatic transfer equipment for placing the heated billet in the container

d) Hot saw to cut off extrusion product

e) Run out table to catch the extrusion

f) Straightener to correct minor warpage of the extruded product.

9

Extrusion Variables

They affect the extrusion process considerably. They are:

1) Type of extrusion (direct or indirect)

In direct extrusion process, metal begins to flow through the die at the maximum

value of the pressure called “break through pressure”.

As billet extrudes, the pressure required progressively decreases with decreasing

length of the billet in the container (because, the friction between the billet and container

decreases).

• In indirect extrusion, there is no relative motion between billet and wall. Therefore

extrusion pressure is almost constant with increase in ram travel.

• It represents the stress required to deform the metal through the die.

• Limited in application by the need of hollow ram, which limits the size of extrusion

& pressure.

• Hence most of the hot extrusion is done by direct extrusion.

• At the end of the ram stroke, there is a rapid pressure build up & therefore a

small “ discard ’’ is left behind in the container, without extruding it.

2. Extrusion Ratio : (R)

R= Initial cross area of the billet / final cross section area after extrusion R = Ao / Af Up to = 40 : 1 for hot extrusion of steel Up to = 400 : 1 for Aluminium � A small change in the fractional reduction results in large increase in extrusion

ratio

Velocity of extruded product = ram velocity x R Therefore high sliding velocities exist along the die land. Extrusion Pr. = P = K Ao ln ( Ao / Af )

10

K = extrusion constant, which accounts for flow stress, friction ,and inhomogeneous deformation. 3. Temperature : Hot extrusion decreases flow stress of metal, but increases oxidation of billet &

extrusion tools. Other features are:

• Softens die & tools

• Difficult to provide lubrication

• Therefore it is advantageous to use the min. temp. which provides required

plasticity to metal.

• The upper hot working temp. of metal is the temp. at which “ Hot shortness ”

occurs.

• Higher plastic deformations involved also lead to internal heating of the metal.

• Therefore max. working temp. must be safely below the melting point.

• Typical Values steel billets heated to 11000 C to 12000 C

• Toolings : preheated to 350 0 C.

4. Extrusion pressures – range : 800 MPa to 1200 MPa

5. Lubrication : ( Glass )

• To be maintained at high temperature & under high pressure.

• Low strength alloy (Al) does not require lubrication.

• Metal deformation is non – uniform and therefore wide variation in heat treatment response is observed

• Effect of temperature, pressure & strain rate on the allowable working range or interdependence of extrusion speed & temperature:

• For a given working pressure & temperature there will be a maximum amount of deformation possible on the work piece.

• As pre heat temperature of billet increases, the flow stress falls & therefore amount of possible deformation increases

11

• As strain rate of deformation increases, more heat is retained in the work & therefore work temperature will have to be reduced so that final temperature is below hot shortness temperature.

6. Ram speed :

Increase in ram speed increases the extrusion pressure.

Whereas, low ram speeds leads to cooling of the billet and because of billet cooling, flow stress is increased.

• The higher the temperature of billet, the greater the effect of low extrusion speed on the cooling of the billet.

• Therefore high extrusion speeds are required with high strength alloys which need high extrusion temperatures.

• At the same time at high extrusion speeds, temperature rise due to deformation is greater.

• The selection of proper extrusion speed & temperature is best determined by trial & error for each alloy and billet size.

• For a given extrusion pressure the extrusion ratio which can be obtained increases with increasing temperature.

• For a given temperature a large extrusion ratio can be obtained with high pressure.

• Maximum billet temperature is determined by the temperature at which melting is about to occur.

• The temperature rise of extrusion is determined by the speed of extrusion & extrusion ratio.

Deformation , Lubrication and Defects in Extrusion : Pressure required in extrusion depends on the way the metal flows in the container &

extrusion die. The metal flow is mainly determined by conditions of lubrication.

Deformation in Extrusion Process

The defects in extrusion are related to the way in which metal deforms during extrusion.

(1) Homogeneous Deformation: (with less friction)

Fig a) indicates homogeneous deformation in direct extrusion.

12

Fig d) shows homogeneous deformation in indirect extrusion.

The following conditions are favorable for homogeneous deformation:

i) Low container friction

ii) Well lubricated billet

iii) Hydrostatic extrusion conditions

iv) Indirect extrusion process.

Fig. Different Grid Patterns During Deformation in Extrusion

Characteristics of homogeneous deformation:

The deformation is more uniform until close to the die entrance where metal flow is

restricted.

(2) Deformation with more friction between billet and container wall

Fig (b) above indicates increased container wall friction.

• This is indicated by severe distortion of grid pattern at the corners of the die due

to a “dead zone.”

13

• The dead zone consists of stagnant metal which does not undergo any

deformation.

• The grid elements at the centre of the billet undergo pure elongation into the

extruded rod.

• The grid elements near the sides of the billet undergo shear deformation

• The shear deformation requires additional energy called “redundant work”. This

work is not related to metal working from billet to extruded product.

(3) Deformation with very high friction

Fig (c) above indicates the condition of high friction at the container – billet interface.

• The metal flow is concentrated towards the centre.

• An internal shear plane develops due to high friction.

• This situation also exists when the billet surface is chilled by a cold container.

This is because, at low temperature of the billet at the sides, the flow stress

increases compared to the flow stress at the central portion of the billet

• Under such sticking conditions between the billet and container, a shear zone is

formed along which the metal separates internally.

• In this condition, extruded product contains clean new metal and outer surface of

billet remains in the container.

Lubrication in Extrusion Process

The following are the requirements of a lubricant in hot extrusion:

• It must have a low shear strength

• It must be stable enough without breaking down at high working temperatures.

• The most widely used lubricant for steels and nickel based alloys is “molten

glass”.

The process using molten glass as lubricant is called “Ugine-Sejournet Process”.

The steps involved are:

• The billet is heated in inert atmosphere.

14

• It is coated with glass powder before it enters the extrusion container.

• The glass coating serves as a lubricant and also as a thermal insulator, thereby

reducing heat loss from billet to container wall and other tools.

• The thickness of glass film between extrusion and die is about 25 microns.

Interaction between optimal lubricant, temperature and ram speed:

• If ram speed is too low, the lubricant is thick because of low initial extrusion

pressure. This exhausts the glass reservoir rapidly. This increases cost of

lubricant.

• If the ram speed is too high, the glass film becomes too thin and friction

increases.

•

Important requirements of lubrication:

• The lubricant film must be complete and continuous to be successful.

• Any gaps in film develops shear zones in metal which eventually develop into

surface cracks.

Defects in Extrusion

1) Laminations of glass/ oxide into the interior of extrusion.

Cause: Improper lubrication method

Remedy: To provide optimum lubrication on the outside of billet and to use

optimal ram speed.

2) Extrusion defect:

The last 1/3rd of extrusion may have oxides and other impurities in it rendering it

unfit for use because of poor mechanical properties. This leads to the formation

of “annular ring of oxide” in the extruded product.

15

Cause: The metal in the middle (2/3rd) is first extruded as it moves faster than

the periphery of billet due to friction. This tendency of extrusion defect increases

with friction between billet and container wall.

Remedy: The last 1/3rd of billet is left out without extruding it. But this is

economically not feasible. Instead a ”follower block” is widely used. This block is

slightly smaller diameter than the container and it scalps or scrapes the billet,

leaving behind the oxide layers in the container.

3) Axial Hole/ Funnel:

It is an axial hole in the back end of extrusion.

Cause: Rapid radial flow of metal during extrusion of last 1/4th of billet.

Remedy: Inclining the face of the ram at an angle to the ram axis.

4) Surface Cracking:

It is in the form of rough surface or fir-tree cracking.

Cause: i) Longitudinal tensile stresses generated as extrusion passes through

the die.

ii) Very high ram speed for the given temperature.

Remedy: Use of optimal ram speed and billet temperature and heating the

container.

5) Center Burst (or Chevron Cracking):

Cause: Low extrusion ratios and low friction in the deformation zone at the die.

Remedy: Increasing the friction at tool-billet interface to obtain a sound product.

6) Variation in hot worked structure and properties:

This is the non-uniform properties of the extruded product, having variation in

properties from front to back end.

16

Extrusion of Tubes

By piercing and extruding in one step:

This method is better compared to the one using a mandrel.

The piercing mandrel and the ram are operated by two separate hydraulic

systems. This requires a double action extrusion press. Steps:

i) First the piercing mandrel is withdrawn and the billet is pressed with the

ram.

ii) Next, the billet is pierced with the sharp mandrel, ejecting a metal plug

through the die.

iii) Then the ram advances and extrudes the billet over the mandrel to

produce the tube.