(TR11683)
Automotive Engineered Attachment Systems Technical Data Sheet
Acrylic Foam Tape GT7100 Series
GT7198 General Information : The Acrylic Foam Tape GT7100 Series, which is made by a special process, has a superior adhesion
performance and high flexibility. This tape is specially designed for exterior and interior parts attachments of
automobiles. GT7100 series provides equivalent adhesion properties to conventional Acrylic Foam Tape and
comparable initial adhesion performance at low ambient temperature with Hi-Tack Acrylic Foam Tape designed for
an improvement of low temperature workability.
Features : a) Excellent adhesive performance at low temperatures in comparison with those of the conventional Acrylic
Foam Tape.
b) Follows the shrinkage and elongation of the plastic part caused by the temperature change, and has good
stress relaxation properties which are very important for the automotive parts attachments.
c) Has a high final adhesion and peel strength.
d) Excels in a variety of weather, solvent and high temperature resistance.
e) Shows excellent workability and die cutting properties.
Configuration :
Pressure sensitive Acrylic adhesive
Pressure sensitive Acrylic adhesiveAcrylic foam
Non-woven cloth
Acrylic foamPressure sensitive Acrylic adhesive
Pressure sensitive Acrylic adhesiveAcrylic foam
Non-woven cloth
Acrylic foam
Tape Liner
Tape No. Thickness (mm) Color Color Material
GT7198 0.8 gray translucent red polyethylene
Usage : Emblem attachment, etc.
Test results : Items Substrates GT7198 #5313 Thickness (mm) - 0.8 0.8 Initial state Painted panel 10.0 9.0 Chromium- plated panel 4.7 4.3 180 degree Normal state Painted panel 13.3 13.3 Peeling Chromium- plated panel 5.1 5.1 Strength At high temperature Painted panel 5.3 5.5 (N/cm) Chromium- plated panel 1.9 2.0 Heat aging Painted panel 18.8 19.0 Chromium- plated panel 7.2 7.3 Warm water immersion Painted panel 16.3 16.5 Chromium- plated panel 6.3 6.3 Initial state 0.64 0.63 Shear Normal state Painted panel 0.76 0.78 strength At high temperature and 0.22 0.23 (MPa) Warm water immersion Chromium- plated panel 0.68 0.70 Gasoline immersion 0.70 0.72 Wax-remover immersion 0.63 0.65
Painted panel : Conventional painted panel
Test methods : (1) Thickness : Measured by a dial thickness gauge (in accordance with JIS Z0237)
(2) 180゚peel strength : Peel off the tape in 180゚ direction and measure the adhesion to the substrate with
a tensile test machine after the exposure in the following conditions.
a) Initial state : 23℃ x 20min.
b) Normal state : 23℃ x 24hrs.
c) At high temperature : b) at 80℃
d) Heat aging : b) 80℃ x 336hrs. b)
e) Warm water immersion: b) 40℃ water x 336hrs. b)
* Tape size : 25mm width, * Rolling pressure : 5kg roller one-way, * Peeling speed : 50mm/min.
(3) Shear strength : Measure the strength needed to shear after the exposure in the following conditions.
a),b),c) : as same as the conditions of the 180゚peel strength
e) Warm water immersion : b) 40℃ water x 336hrs. b)
f) Gasoline immersion : b) gasoline x 1hr. b)
g) Wax-remover immersion: b) wax-remover x 1hr. b)
* Tape size : 25mm x 25mm, * Rolling pressure : 5kg roller one-way, * Tensile speed : 50mm/min.