800 MPA

Built over platinum foil and refractory dies these provide true shading and natural esthetics.

These restorations provide a combination of rich esthetics and added strength and can be stained or layered to resemble natural dentition.

The combination of a CAD/CAM zirconium oxide substructure with veneered porcelain provides a translucent, natural-looking tooth with excellent durability, allowing full porcelain coverage or layered in the esthetic zone to maintain maximum strength.

Full Contour Monolithic ZirconiaPrecision-milled from a shade specific monolithic/full-contour disc using CAD/CAM technology. These restorations provide solid chip-resistant results without porcelain veneering. Ideal for long span cases, bruxing patients, increased bite forces, and a tooth shaded alternative to full-cast crown restorations.

NAME

• Very high strength• Provides solid, chip-resistant results• Minimal prep/adjustment needed

POSTERIOR

ANTERIOR

ANTERIOR

765 MPA

1100 MPA

500 MPA

870 MPA

1100-1250 MPA

ADVANTAGES IDEAL PLACEMENT STRENGTHCEMENTATION

Feldspathic porcelain

Lithium Disilicate

Zirconia with Veneered Porcelain

DSmz™

DSez™

BruxZir®

BruxZir® Esthetic

DSz™

3M ESPE Lava™

IPS e.max®Full Contour

IPS e.max®Layered

Laminate Veneers

TYPE

Guide to All Ceramic Restorations

800.259.3717 � WWW.DENTALSERVICES.NET

160 MPA

70-90 MPA

CONSIDERATIONS

• Esthetics from surface staining• Cementation considerations• Minimal translucency

• Mid strength• Natural looking esthetics• Shade matches for 16 Vita shades

• Stump shade needed • Occlusal clearance minimum 1.5mm

• Popular/well known• Glazed to smooth surface• Resitant to wear

• Glaze degrades at occlusal contacts• Cannot acid etch• Time consuming to remove

• Natural looking translucently• Lifelike zirconia• Minimal preparation

• Low strength due to higher translucency• Limited shade variations

• Highly esthetic • Reliable durability • Layering creates shade variation

• Porcelain compromises strength

• Highly esthetic • Reliable durability • Porcelain compromises strength

• Translucent and esthetic• Long term durability• Acid etches well

• Low strength• Deeper prep needed• Can wear opposing dentition

• Very translucent• Highly esthetic

• Low strength• Porcelain interface

• Extremely esthetic• Very natural looking• Slight preparation

• Very low strength• Tooth substructure dictates outcome• Anterior only

1200 MPA

POSTERIOR

ANTERIOR

ANTERIOR

ANTERIOR

ANTERIOR &POSTERIOR

ANTERIOR &POSTERIOR

Conventional Bonded

METAL FREE | CHAIRSIDE GUIDE

Ideal Placement

All

Cer

amic

Opt

ions

METAL FREE | CHAIRSIDE GUIDE

**

Ideal Placement

Name Product Description Posterior Anterior

DSmz™ CAD/CAM milled monolithic full contour zirconia crown ideal for bruxing patients.

DSez™

to satisfy the esthetic and functional requirements of the anterior region of the mouth. 3 units, with one pontic

DSz™ CAD/CAM zirconia substructure with porcelain overlay, translucent.

CAD/CAM milled monolithic full contour zirconia crown ideal for bruxing patients.

| CHAIRSIDE GUIDE

Ideal Placement

Product Description Posterior Anterior Bridges Inlay / Onlay Veneers Prep Required Strength

CAD/CAM milled monolithic full contour zirconia crown ideal for bruxing patients.

Ideal prep required

Ideal prep, 360° shoulder/chamfer

to satisfy the esthetic and functional requirements of the anterior region of the mouth. 3 units, with one pontic

0.8mm required, 1.25mm is ideal, stump shade needed

Medium

CAD/CAM zirconia substructure with porcelain overlay, translucent. Splinted crowns,

cantilever bridges

Chamfer 1mm axial/1.5mm occlusial Medium

CAD/CAM milled monolithic full contour zirconia crown ideal for bruxing patients.

Ideal prep, 360° shoulder/chamfer

All

Cer

amic

Opt

ions

DSz™ CAD/CAM zirconia substructure with porcelain overlay, translucent. Splinted crowns, cantilever bridges

CAD/CAM milled monolithic full contour zirconia crown ideal for bruxing patients.

Ideal prep required

to satisfy the esthetic and functional requirements of the anterior region of the mouth. 3 units, with one pontic

CAD OR PRESSED

Pressed: and esthetics

CAD: CAD milled lithium discillicate available in high or low translucency

Pressed only - 3 units. Available only through

premolarsPressed only

Leucite-reinforced glass ceramic that provides a highly esthetic solution for single unit restorations that are adhesively bonded.

Lava™CAD/CAM zirconia substructure with porcelain overlay, translucent. Splinted crowns,

cantilever bridges

Laminate Veneers Ultra thin porcelain veneers, stacked or pressed.

Taper between4° & 8°

Occlusal reduction of at least 2.0 mm in contact area

360° Shoulder preparation of at least 1.0 mm proximal reduction

Coronal Length at least 4.0 mm

Butt joint margin

Rounded internalline angles

Football-shapedfinishing bur

Butt joint margin 1.0 mm reductionat gingival margin

1.0 mm to 1.5 mm facial reduction

1.5 mm lingualcontact clearance

1.5 mm to 2.0 mm incisal reduction

Rounded internalline angles

1.0 mm reductionat gingival margin

1.5 mm to 2.0 mm occlusal reduction

1.5 mm axial reduction

diamond bur is utilized to A flat-ended tapered

establish a butt-joint margin

Depth cuts of 0.6 mm to 0.8 mm

Incisal 1.0-1.5 mm

Taper between4° & 8°

Occlusal reduction of at least 2.0 mm in contact area

360° Shoulder preparation of at least 1.0 mm proximal reduction

Coronal Length at least 4.0 mm

Butt joint margin

Rounded internalline angels

Football-shapedfinishing bur

Butt joint margin 1.0 mm reductionat gingival margin

1.0 mm to 1.5 mm facial reduction

1.5 mm lingualcontact clearance

1.5 mm to 2.0 mm incisal reduction

Rounded internalline angels

1.0 mm reductionat gingival margin

1.5 mm to 2.0 mm occlusal reduction

1.5 mm axial reduction

diamond bur is utilized to A flat-ended tapered

establish a butt joint margin

Depth cuts of 0.6 mm to 0.8 mm

Incisal 1.0-1.5 mm

ANTERIOR CROWN PREPARATION POSTERIOR CROWN PREPARATION LAMINATE VENEER PREP

esthetic solution for single unit restorations that are adhesively bonded.

Lava™CAD/CAM zirconia substructure with porcelain overlay, translucent.

Laminate Veneers Ultra thin porcelain veneers, stacked or pressed.

Taper between4° & 8°

Occlusal reduction of at least 2.0 mm in contact area

360° Shoulder preparation of at least 1.0 mm proximal reduction

Coronal Length at least 4.0 mm

Butt joint margin

Rounded internalline angels

Football-shapedfinishing bur

Butt joint margin 1.0 mm reductionat gingival margin

1.0 mm to 1.5 mm facial reduction

1.5 mm lingualcontact clearance

1.5 mm to 2.0 mm incisal reduction

Rounded internalline angles

1.0 mm reductionat gingival margin

1.5 mm to 2.0 mm occlusal reduction

1.5 mm axial reduction

diamond bur is utilized toA flat-ended tapered

establish a butt joint margin

360° Shoulder preparation of at least 1.0 mm proximal reduction

Coronal Length at least 4.0 mm

Rounded internalline angels

Football-shapedfinishing bur

1.0 mm to 1.5 mm facial reduction

1.5 mm lingualcontact clearance

1.5 mm to 2.0 mm incisal reduction

1.0 mm reductionat gingival margin

1.5 mm axial reduction

diamond bur is utilized toA flat-ended tapered

establish a butt joint margin

ANTERIOR CROWN PREPARATION POSTERIOR CROWN PREPARATIONCEMENTATION REQUIREMENTSVeneers, IPS Empress® must be adhesively bonded (light cure or dual cure). e.max® Pressed adhesive bonding suggested. All other products on this list may utilize conventional cementations or adhesive bond.

esthetic solution for single unit restorations that are adhesively bonded.

chamfer, stump shade needed

CAD/CAM zirconia substructure with porcelain overlay, translucent. Splinted crowns,

cantilever bridges

Chamfer 1mm axial/1.5mm occlusial Medium

Ultra thin porcelain veneers, stacked or pressed.Min. prep and ideal esthetics, stump shade needed

Butt joint margin

Rounded internalline angels

Football-shapedfinishing bur

Butt joint margin 1.0 mm reductionat gingival margin

1.0 mm to 1.5 mm facial reduction

1.5 mm lingualcontact clearance

1.5 mm to 2.0 mm incisal reduction

Rounded internalline angles

1.0 mm reductionat gingival margin

1.5 mm to 2.0 mm occlusal reduction

1.5 mm axial reduction

diamond bur is utilized to A flat-ended tapered

establish a butt joint margin

Depth cuts of 0.6 mm to 0.8 mm

Incisal 1.0-1.5 mm

Rounded internalline angels

Football-shapedfinishing bur

1.0 mm to 1.5 mm facial reduction

1.5 mm lingualcontact clearance

1.5 mm to 2.0 mm incisal reduction

1.0 mm reductionat gingival margin

1.5 mm axial reduction

diamond bur is utilized to A flat-ended tapered

establish a butt joint margin

Depth cuts of 0.6 mm to 0.8 mm

ANTERIOR CROWN PREPARATION POSTERIOR CROWN PREPARATION LAMINATE VENEER PREP

ALL CERAMIC PREPARATION

Ceramic Restorations Prep Guides

800.259.3717 � WWW.DENTALSERVICES.NET

PREP SPECIFICATIONS