Artisan 02 Ceramic 2%

Near IR

780~2500nm

Visible Light

380~780nm

UV

300~380nm

IR Cut Hard-Coating

Silicone Release Film(23㎛)

UV-Cut PSA

Optical Grade PET Film (23±1㎛)

Adhesive

Optical Grade PET Film (12±1㎛)

Thickness 1.5Mil/2Ply

Shading Coefficient 0.48 KS L 2016

Solar Heat Gain Coefficient (SHGC)

0.42 KS L 2514

Scratch Resistant >2H ASTM D3363

Adhesion of Hard-Coated Surface

5B (0% peel-off)

ASTM D3359

Visible Light Transmitted 6% KS L 2514

Visible Light

Reflected

External 4.6% KS L 2514

Internal 4.7%

Solar Heat

Transmitted 12.2%

KS L 2514 Reflected 4.4%

Absorbed 83.3%

IR Rejected 900~1000nm 79%

780~2500nm 83%

UV Rejected 99%↑ KS L 2514

Total Solar Energy Rejected (TSER) 58% KS L 2514

Artisan 05 Ceramic 5%

Near IR

780~2500nm

Visible Light

380~780nm

UV

300~380nm

IR Cut Hard-Coating

Silicone Release Film(23㎛)

UV-Cut PSA

Optical Grade PET Film (23±1㎛)

Adhesive

Optical Grade PET Film (12±1㎛)

Thickness 1.5Mil/2Ply

Shading Coefficient 0.48 KS L 2016

Solar Heat Gain Coefficient (SHGC)

0.42 KS L 2514

Scratch Resistant >2H ASTM D3363

Adhesion of Hard-Coated Surface

5B (0% peel-off)

ASTM D3359

Visible Light Transmitted 10% KS L 2514

Visible Light

Reflected

External 4.6% KS L 2514

Internal 4.8%

Solar Heat

Transmitted 16.5%

KS L 2514 Reflected 4.5%

Absorbed 79%

IR Rejected 900~1000nm 74%

780~2500nm 79%

UV Rejected 99%↑ KS L 2514

Total Solar Energy Rejected (TSER) 58% KS L 2514

Artisan 20 Ceramic 20%

Near IR

780~2500nm

Visible Light

380~780nm

UV

300~380nm

IR Cut Hard-Coating

Silicone Release Film(23㎛)

UV-Cut PSA

Optical Grade PET Film (23±1㎛)

Adhesive

Optical Grade PET Film (12±1㎛)

Thickness 1.5Mil/2Ply

Shading Coefficient 0.51 KS L 2016

Solar Heat Gain Coefficient (SHGC)

0.45 KS L 2514

Scratch Resistant >2H ASTM D3363

Adhesion of Hard-Coated Surface

5B (0% peel-off)

ASTM D3359

Visible Light Transmitted 16% KS L 2514

Visible Light

Reflected

External 4.7% KS L 2514

Internal 4.9%

Solar Heat

Transmitted 21.3%

KS L 2514 Reflected 4.5%

Absorbed 74.1%

IR Rejected 900~1000nm 68%

780~2500nm 75%

UV Rejected 99%↑ KS L 2514

Total Solar Energy Rejected (TSER) 55% KS L 2514

Artisan 25 Ceramic 25%

Near IR

780~2500nm

Visible Light

380~780nm

UV

300~380nm

IR Cut Hard-Coating

Silicone Release Film(23㎛)

UV-Cut PSA

Optical Grade PET Film (23±1㎛)

Adhesive

Optical Grade PET Film (12±1㎛)

Thickness 1.5Mil/2Ply

Shading Coefficient 0.57 KS L 2016

Solar Heat Gain Coefficient (SHGC)

0.49 KS L 2514

Scratch Resistant >2H ASTM D3363

Adhesion of Hard-Coated Surface

5B (0% peel-off)

ASTM D3359

Visible Light Transmitted 26% KS L 2514

Visible Light

Reflected

External 5.1% KS L 2514

Internal 5.4%

Solar Heat

Transmitted 28.3%

KS L 2514 Reflected 5%

Absorbed 66.7%

IR Rejected 900~1000nm 61%

780~2500nm 71%

UV Rejected 99%↑ KS L 2514

Total Solar Energy Rejected (TSER) 51% KS L 2514

Artisan 35 Ceramic 35%

Near IR

780~2500nm

Visible Light

380~780nm

UV

300~380nm

IR Cut Hard-Coating

Silicone Release Film(23㎛)

UV-Cut PSA

Optical Grade PET Film (23±1㎛)

Adhesive

Optical Grade PET Film (12±1㎛)

Thickness 1.5Mil/2Ply

Shading Coefficient 0.63 KS L 2016

Solar Heat Gain Coefficient (SHGC)

0.54 KS L 2514

Scratch Resistant >2H ASTM D3363

Adhesion of Hard-Coated Surface

5B (0% peel-off)

ASTM D3359

Visible Light Transmitted 37% KS L 2514

Visible Light

Reflected

External 5.4% KS L 2514

Internal 5.7%

Solar Heat

Transmitted 37.3%

KS L 2514 Reflected 5.2%

Absorbed 57.5%

IR Rejected 900~1000nm 53%

780~2500nm 64%

UV Rejected 99%↑ KS L 2514

Total Solar Energy Rejected (TSER) 46% KS L 2514

Artisan 40 Ceramic 40%

Near IR

780~2500nm

Visible Light

380~780nm

UV

300~380nm

IR Cut Hard-Coating

Silicone Release Film(23㎛)

UV-Cut PSA

Optical Grade PET Film (23±1㎛)

Adhesive

Optical Grade PET Film (12±1㎛)

Thickness 1.5Mil/2Ply

Shading Coefficient 0.66 KS L 2016

Solar Heat Gain Coefficient (SHGC)

0.56 KS L 2514

Scratch Resistant >2H ASTM D3363

Adhesion of Hard-Coated Surface

5B (0% peel-off)

ASTM D3359

Visible Light Transmitted 43% KS L 2514

Visible Light

Reflected

External 5.8% KS L 2514

Internal 6%

Solar Heat

Transmitted 39.7%

KS L 2514 Reflected 5.4%

Absorbed 54.9%

IR Rejected 900~1000nm 52%

780~2500nm 64%

UV Rejected 99%↑ KS L 2514

Total Solar Energy Rejected (TSER) 44% KS L 2514

Artisan 42 Ceramic 42%

Near IR

780~2500nm

Visible Light

380~780nm

UV

300~380nm

IR Cut Hard-Coating

Silicone Release Film(23㎛)

UV-Cut PSA

Optical Grade PET Film (23±1㎛)

Adhesive

Optical Grade PET Film (12±1㎛)

Thickness 1.5Mil/2Ply

Shading Coefficient 0.66 KS L 2016

Solar Heat Gain Coefficient (SHGC)

0.56 KS L 2514

Scratch Resistant >2H ASTM D3363

Adhesion of Hard-Coated Surface

5B (0% peel-off)

ASTM D3359

Visible Light Transmitted 46% KS L 2514

Visible Light

Reflected

External 6% KS L 2514

Internal 6.1%

Solar Heat

Transmitted 42.7%

KS L 2514 Reflected 5.7%

Absorbed 51.6%

IR Rejected 900~1000nm 49%

780~2500nm 62%

UV Rejected 99%↑ KS L 2514

Total Solar Energy Rejected (TSER) 44% KS L 2514

Artisan 50 Ceramic 50%

Near IR

780~2500nm

Visible Light

380~780nm

UV

300~380nm

IR Cut Hard-Coating

Silicone Release Film(23㎛)

UV-Cut PSA

Optical Grade PET Film (23±1㎛)

Adhesive

Optical Grade PET Film (12±1㎛)

Thickness 1.5Mil/2Ply

Shading Coefficient 0.69 KS L 2016

Solar Heat Gain Coefficient (SHGC)

0.59 KS L 2514

Scratch Resistant >2H ASTM D3363

Adhesion of Hard-Coated Surface

5B (0% peel-off)

ASTM D3359

Visible Light Transmitted 53% KS L 2514

Visible Light

Reflected

External 6.3% KS L 2514

Internal 6.5%

Solar Heat

Transmitted 47.9%

KS L 2514 Reflected 5.9%

Absorbed 46.1%

IR Rejected 900~1000nm 45%

780~2500nm 58%

UV Rejected 99%↑ KS L 2514

Total Solar Energy Rejected (TSER) 41% KS L 2514