Corporate Polyamide Seminar TAIWAN May 2014 Page1
Tailor-made solution for Polyamide by Huntsman
BENVENUTI/WELCOME Stefano Cavestro
Corporate Polyamide Seminar TAIWAN May 2014 Page2 AICTC – Dalmine – 27 Maggio 2016
GENERALITA’
Corporate Polyamide Seminar TAIWAN May 2014 Page3 AICTC – Dalmine – 27 Maggio 2016
POLIAMMIDE 6.6
• BASSA AFFINITA’ • ALTA SOLIDITA’ UMIDO
PIU’ CRISTALLINA
RESISTENTE TRAZIONE
FUSIONE 250°C
TERMOFIX 220°C
TEMP. TINT. 120°C
TENDENZA BARRATURE
ALTA
TAPPETI USI TECNICI
POLIAMMIDE 6 • ALTA AFFINITA’ • BASSE SOLIDITA’
MENO CRISTALLINA
MINOR RESISTENZA
ALLA TRAZIONE
FUSIONE 210°C
TERMOFIX 190°C
TEMP. TINT. 108°C
ECONOMICA
ABBIGLIAMENTO
PA 6 Vs PA6.6
Corporate Polyamide Seminar TAIWAN May 2014 Page4 AICTC – Dalmine – 27 Maggio 2016
• I PARAMETRI FISICI DELLA FIBRA SONO PIU’ IMPORTANTI RISPETTO ALLA CHIMICA DI PRODUZIONE.
• PUNTI CHIAVE − FINEZZA DELLA FIBRA − TERMOFIX PRIMA DELLA TINTURA − CRISTALLINITA’ DELLA FIBRA
• I PARAMETRI FISICI INFLUENZANO MAGGIORMENTE LA TINTURA RISPETTO ALLE DIFFERENZA TRA PA6 e PA66.
• IMPORTANTE PER IL TINTORE (primo test su articoli nuovi): − VELOCITA’ DI ESAURIMENTO. − VALUTAZIONE ESAURIMENTO. − USO DI UN BUON UGUALIZZANTE. − USO DI UN DONATORE DI ACIDO (no per Jigger)
PARAMETRI IMPORTANTI
Corporate Polyamide Seminar TAIWAN May 2014 Page5 AICTC – Dalmine – 27 Maggio 2016
INFLUENZA TiO2
FIBRA LUCIDA NO TiO2 FIBRA OPACA SI TiO2
LA LUCE ATTRAVERSA LA FIBRA SENZA COLPIRE MOLECOLE DI TiO2. COLPENDO SOLO IL COLORANTE.
TONALITA’ PIU’ INTENSA
LA LUCE ATTRAVERSA LA FIBRA COLPENDO MOLECOLE DI TiO2,
VIENE RIFLESSA E TORNA VERSO L’ OSSERVATORE.
TONALITA’ PIU’ CHIARA
OSSERVATORE OSSERVATORE
Corporate Polyamide Seminar TAIWAN May 2014 Page6 AICTC – Dalmine – 27 Maggio 2016
INFLUENZA NUMERO DI BAVE
A PARITA’ DI TITOLO UN ELEVATO NUMERO DI BAVE DETERMINA UNA MAGGIORE RIFRAZIONE DELLA LUCE (EFFETTO SCATTERING) COMPORTANDO UNA PERDITA DI RESA COLORISTICA.
BASSO NUMERO DI FIBRILLE
ALTO NUMERO DI FIBRILLE OSSERVATORE OSSERVATORE
Corporate Polyamide Seminar TAIWAN May 2014 Page7 AICTC – Dalmine – 27 Maggio 2016
TESSUTO PIANO (T.P.)
• PURGA PRIMA DI TERMOFIX. • BUONA PENETRAZIONE
INCROCI TRAMA/ORDITO. • TINTURA A JIGGER PER
TESSUTO A SCARSA PERMEABILITA’ E CON TENDENZA AL MOIRE’.
• TINTURA A SILURO: ELEVATA PRESSIONE DIFFERENZIALE. BASSO NUMERO CICLI INT/EST.
• DIFFICOLTA’ DI ESAURIMENTO SOPRATTUTTO ALTA TENACITA’.
• TANNINI SINTETICI POSSONO INTERFERIRE CON ACCOPPIATURA/SPALMATURA.
TESSUTO ELASTICO (T.E.) • RELAX PRIMA DEL TERMOFIX. • BASSA TENSIONE DURANTE LA
TINTURA PER PRESERVARE L’ELASTICITA’.
• MATERIALI AD ALTO CONTENUTO DI EL DEVONO ESSERE TINTI A SILURO (PREVENZIONE PIEGHE).
• TINTURA A SILURO: BASSA PRESSIONE DIFFERENZIALE. CIRC. EST/INT (PREVENZIONE DISTORSIONE).
• SOLIDITA’ AD UMIDO DIFFICILI DA OTTENERE.
• TANNINI SINTETICI INFLUENZANO LA MANO.
TESS ELASTICO VS PIANO
Corporate Polyamide Seminar TAIWAN May 2014 Page8 AICTC – Dalmine – 27 Maggio 2016
PREPARAZIONE
Corporate Polyamide Seminar TAIWAN May 2014 Page9 AICTC – Dalmine – 27 Maggio 2016
LA VELOCITA’ DEI TELAI ARIA/ACQUA AUMENTA. CONTINUA EVOLUZIONE DELLE BOZZIME. ALTE VELOCITA’ COMPORTANO USO MASSICCIO DI OLII DI FILATURA CON CONSEGUENTI RISCHI DI MACCHIE, TRAME SPORCHE E SPORCHI RESISTENTI.
LA RIDUZIONE DEI TEMPI DI TINTURA RICHIEDE UNA PREPARAZIONE OTTIMALE.
LE BOZZIME PER PA SONO SOLUBILI IN ACQUA. IL pH OTTIMALE (in base al tipo di bozzima) GARANTISCE LA RIMOZIONE DELLA BOZZIMA. IMPORTANTE GARANTIRE BUONE PROPRIETA’ DI BAGNABILITA’, NO SCHIUMA, RIGONFIAMENTO OTTIMALE.
PER RIMUOVERE CERE/OLII OTTIMALE USARE UN BUON DISPERDENTE/TENSIOATTIVO.
USO DI PRODOTTI SEQUESTRANTI AIUTA A RIMUOVERE LE IMPURITA’ E LIMITA IL RISCHIO DI RI-DEPOSIZIONE.
PREPARAZIONE (T.P.) - BACKGROUND
Corporate Polyamide Seminar TAIWAN May 2014 Page10 AICTC – Dalmine – 27 Maggio 2016
DURANTE LA TESSITURA L’ELASTICO VIENE INCORPORATO IN CONDIZIONI DI DIFFERENTE TENSIONI.
LA FASE DI RELAX ESEGUITA PRIMA DI OGNI TRATTAMENTO SERVE PER ELIMINARE TENSIONI E CREA L’ELASTICITA’ DELLA MAGLIA. BARRATURE FISICHE LEGATE ALLA TENSIONE DELL’ELASTICO VENGONO ELIMINATE IN QUESTA FASE.
PREPARAZIONE (T.E.) - BACKGROUND
Corporate Polyamide Seminar TAIWAN May 2014 Page11 AICTC – Dalmine – 27 Maggio 2016
“PRODOTTO SENZA SOLVENTE, TENSIOATTIVO CON PROPRIETA’ EMULSIONANTI/SGRASSANTI DISEGNATO PER RIMUOVERE OLII SILICONICI DALLE MISTE CON ELASTOMERO SIA PER FIBRE SINTETICHE CHE CELLULOSICHE.”
ESIGENZA
Corporate Polyamide Seminar TAIWAN May 2014 Page12 AICTC – Dalmine – 27 Maggio 2016
INNOVAZIONE
SILICON OIL REMOVAL PROBLEM SOLVER PER MISTE CON ELASTOMERO. APPLICABILE IN DIFFERENTI PROCESSI (CONTINUO, DISCONTINUO, SEMI-CONTINUO). UTILIZZABILE IN IMPIANTI AUTOMATICI.
ULTRAVON® SIR LIQ
Corporate Polyamide Seminar TAIWAN May 2014 Page13 AICTC – Dalmine – 27 Maggio 2016
ULTRAVON® SIR LIQ
§ POTERE EMULSIONANTE/SGRASSANTE. § RIMUOVE GLI OLII SILICONICI DALLE MISTE CON ELASTOMERO. § PREVIENE LA RIDEPOSIZIONE DEGLI OLII SILICONICI. § IDONEO PER LA RIMOZIONE DI TUTTI I TIPI DI OLII, SOSTANZE
GRASSE ED IMPUREZZE.
ULTRAVON® SIR LIQ competition products
1.0 g/l 1.0 g/l 1.0 g/l 1.0 g/l
2.0 g/l 2.0 g/l 2.0 g/l 2.0 g/l
test method T 2.10 (degreasing power on wool)
Corporate Polyamide Seminar TAIWAN May 2014 Page14 AICTC – Dalmine – 27 Maggio 2016
ULTRAVON® PRE
§ IDONEO PER TRATTAMENTI IN CONTINUO ED IN DISCONTINUO DI FIBRE SINTETICHE.
§ BASSA FORMAZIONE DI SCHIUMA, OTTIMO POTERE RE-IMBIBENTE E DETERGENTE.
§ NON CONTIENE ANTISCHIUMA.
§ BUONA STABILITA’ ALLA RIDUZIONE, OSSIDAZIONE, ALCALI ED ACIDI.
§ FORMULAZIONE LIQUIDA, POMPABILE, ADATTA AI SISTEMI DI DOSAGGIO AUTOMATICO.
Corporate Polyamide Seminar TAIWAN May 2014 Page15 AICTC – Dalmine – 27 Maggio 2016
TINTURA A SILURO
Corporate Polyamide Seminar TAIWAN May 2014 Page16 AICTC – Dalmine – 27 Maggio 2016
SCELTA DEL SILURO
IDEALE PER ARTICOLI: § CON ALTO CONTENUTO DI ELASTOMERO
§ CON SUPERFICIE «SENSIBILE»
§ NO RISCHIO DI PIEGHE PERMANENTI.
§ NO RIPETUTA TENSIONE DURANTE LA TINTURA.
§ NO “GRAFFI” O “LUCIDI” SULLA SUPERFICIE DEL TESSUTO.
ARTICOLI TIPICI: § MAGLIA CON ALTO CONTENUTO ELASTOMERO
§ RETI PER FODERAME
§ TESSUTI RASCHEL
§ TESSUTI PIANI CON SUPERFICIE “SENSIBILE”
Corporate Polyamide Seminar TAIWAN May 2014 Page17 AICTC – Dalmine – 27 Maggio 2016
PREPARAZIONE SUBBIO
MATE
RIA
LE
SUBBIO BEN PREPARATO
FLUSSO CORRETTO
SUBBIO FORATO RISCHIO TINTURA DISUNITA
FLUSSO DISTURBATO • OLII RESIDUI, IMPURITA’ • TENSIONE ARROTOLAMENTO • DIFFERENZE TERMOFIX
PROBLEMI PREPARAZIONE
Corporate Polyamide Seminar TAIWAN May 2014 Page18 AICTC – Dalmine – 27 Maggio 2016
PREPARAZIONE SUBBIO
FASCE
d d = COPERTURA FORI DEL SUBBIO
h
h = ALTEZZA ROTOLO
Corporate Polyamide Seminar TAIWAN May 2014 Page19 AICTC – Dalmine – 27 Maggio 2016
PREPARAZIONE SUBBIO
FLUSSO FUORIESCE DAI FORI SCOPERTI
DISUNIFORMITA’!
Corporate Polyamide Seminar TAIWAN May 2014 Page20 AICTC – Dalmine – 27 Maggio 2016
PREPARAZIONE SUBBIO
FLUSSO UNIFORME
DIMINUZIONE RISCHIO DISUNIFORMITA’
Corporate Polyamide Seminar TAIWAN May 2014 Page21 AICTC – Dalmine – 27 Maggio 2016
TINTURA MISTE EL.
BASSA PRESSIONE = FLUSSO REGOLARE ALTA PRESSIONE = FLUSSO IRREGOLARE
§ SOLO INTERNO ESTERNO § INVERSIONI DI CIRCOLAZIONE POSSONO FAR MUOVERE IL
MATERIALE ALL’INTERNO DEL SILURO. § CIRCOLAZIONE ESTERNO-INTERNO PUO’ INCREMENTARE IL
RISCHIO DI MOIRE’. § BASSA PRESSIONE DIFFERENZIALE (0.1 – 0.2 bar)
§ ALTA PRESSIONE DIFFERENZIALE POTREBBE SOLLEVARE IL MATERIALE E CREARE CANALI PREFERENZIALI. RISULTATO DISUNITEZZE.
Corporate Polyamide Seminar TAIWAN May 2014 Page22 AICTC – Dalmine – 27 Maggio 2016
AUSILIARI DI TINTURA
1.5 g/l 1.0 g/l 0.5 g/l 0.25 g/l 0.1 g/l ALBATEX®
PS-35
―- 0.5 % 1.0 % 1.5 % 2.0 % UNIVADINE®
MC
0.5 g/l 0.5 g/l 0.5 g/l 0.5 g/l 0.5 g/l ALBAFLOW® UNI-01
> 4.0 % NERI
MARINI 1.5 – 4 % 0.5– 1.5% 0.1–0.5 % < 0.1 % % COLORANTE
Raccomandazioni generali, basate su esperienza. In base ad articoli/macchinari le quantità possono variare.
Corporate Polyamide Seminar TAIWAN May 2014 Page23 AICTC – Dalmine – 27 Maggio 2016
UNIVADINE® MC
§ UGUALIZZANTE § SOLUZIONE SPECIFICA PER COLORANTI LANASET E COLORANTI ACIDI. § OTTIMA COPERTURA BARRATURE E SUPPORTO ALLA MIGRAZIONE. § MIGLIORA L’UNITEZZA DI QUALSIASI TIPO DI POLIAMMIDE. § BILANCIATO POTERE RITARDANTE: OTTIMA RIPRODUCIBILITA’.
§ PREVIENE LA PRECIPITAZIONE DEI COLORANTI METALLO-COMPLESSI.
1 % UNIVADINE MC senza
Migrazione con 1 % UNIVADINE MC
Migrazione senza
Corporate Polyamide Seminar TAIWAN May 2014 Page24 AICTC – Dalmine – 27 Maggio 2016
UNIVADINE® MC
1%
2%
SENZA UGUALIZZANTE
UNIVADINE® MC
COPERTURA BARRATURE CON COLORANTI LANASET® PA
Corporate Polyamide Seminar TAIWAN May 2014 Page25 AICTC – Dalmine – 27 Maggio 2016
ALBATEX® PS-35
§ RIDUCE GRADUALMENTE IL pH ALL’AUMENTARE DELLA TEMPERATURA.
§ STABILE AL MAGAZZINAGGIO ED IN FASE ALLESTIMENTO BAGNO.
§ PERMETTE UN ESAURIMENTO UNIFORME ED UNA UGUALIZZAZIONE DEI COLORANTI.
§ PERMETTE IL TOTALE E CONTROLLATO ESAURIMENTO GARANTENDO RIPRODUCIBILITA’ BAGNO SU BAGNO.
§ pH INIZIALE PUO’ ESSERE REGOLATO A PIACERE ALL’INIZIO DEL CICLO DI TINTURA (ANCHE PARTENDO DA pH ALCALINO).
§ ALBATEX PS-35 PERMETTE DI CONTROLLARE LE DIFFERENZE INT/EST A SILURO GRAZIE AL pH DOSATO.
§ IL PERICOLO DI DISUNITEZZA NEI TONI CHIARI E’ MINIMIZZATO.
Corporate Polyamide Seminar TAIWAN May 2014 Page26 AICTC – Dalmine – 27 Maggio 2016
COLORANTI
Corporate Polyamide Seminar TAIWAN May 2014 Page27 AICTC – Dalmine – 27 Maggio 2016
COLORANTI
Cutting-edge economic tailor-made dyes for polyamide
make a splash with ERIOFAST®
Corporate Polyamide Seminar TAIWAN May 2014 Page28 AICTC – Dalmine – 27 Maggio 2016
COLORANTI
LANASET®
§ SVILUPPATI 30 ANNI FA. § SOLUZIONE SPECIFICA NATA
PER LANA. § TINTURA A pH 4.5 (PUNTO ISO-
ELETTRICO. PRESERVANO LA LANA).
§ NO LANA PICCHIETTATA. § AMPIO RANGE DI ELEMENTI. § IL RANGE DI MAGGIOR
SUCCESSO NELLA STORIA DEI COLORANTI PER WO/PA.
LANASET® PA • TRICROMIA PIU’ ELEMENTI
ADDIZIONALI. § SPECIFICI PER POLIAMMIDE,
PIU’ ECONOMICI RISPETTO LANASET®
§ TRICROMIA STUDIATA PER MINIMIZZARE LE DIFFERENZE DI AFFINITA‘ DELLA PA.
§ ACCUMULO ECCELLENTE SU MICROFIBRA.
§ COMPRENDE ELEMENTI BRILLANTI.
Corporate Polyamide Seminar TAIWAN May 2014 Page29 AICTC – Dalmine – 27 Maggio 2016
LANASET ® PA
§ ECONOMICITA’ DI SISTEMA PER POLIAMMIDE.
§ ECCELLENTE SATURAZIONE. PERMETTONO TONI SCURI E PROFONDI ANCHE SU MICROFIBRA CON UN METODO TINTORIALE SEMPLICE ED EFFICIENTE.
§ OTTIME SOLIDITA’ AD UMIDO SU MOLTI ARTICOLI.
§ ALTE SOLIDITA’ LUCE. UTILIZZABILI SIA PER OUTDOOR CHE PER SPORTSWEAR.
§ ASSORTIMENTO COMPATTO. UN’ECCELLENTE TRICROMIA CON PERFETTA SALITA TONO IN TONO SU POLIAMMIDE.
§ ELEVATA FLESSIBILITA’ DI SISTEMA.
§ LANASET® PA SONO PERFETTAMENTE COMPATIBILI CON GLI ORIGINALI LANASET®.
Corporate Polyamide Seminar TAIWAN May 2014 Page30 AICTC – Dalmine – 27 Maggio 2016
LANASET ® PA (TONI DI COMBINAZIONE)
ERIOFAST® Navy M Economical dull navy & royal blue shades with
outstanding wet fastness properties
make a splash with ERIOFAST®
Corporate Polyamide Seminar TAIWAN May 2014 Page32 AICTC – Dalmine – 27 Maggio 2016
ERIOFAST® NAVY M
SOLIDITA’ AD UMIDO
IMBATTIBILI.
PERMETTE DI REALIZZARE TONI ROYAL INTENSI IN COMBINAZIONE CON
ERIOFAST® Blue 3R
TONI MARINO BRILLANTI
TONI SCURI MARINO IN COMBINAZIONE CON
ERIOFAST® Black M
Corporate Polyamide Seminar TAIWAN May 2014 Page33 AICTC – Dalmine – 27 Maggio 2016
ERIOFAST® NAVY M
Properties § NUOVO STANDARD NELLE SOLIDITA’ AD UMIDO SU
POLIAMMIDE E MISTE CON ELASTOMERO NEI TONI MARINI E NERI. ANCHE SU MICROFIBRA.
§ PROCESSO TINTORIALE SEMPLICE E CORTO.
§ NESSUN IMPATTO SULLA MANO DEL MATERIALE.
§ NESSUN IMPATTO SULLE SOLIDITA’ DURANTE LA PREFORMATURA.
§ SCARSO STINGIMENTO SU ELASTICO.
§ PERMETTE DI REALIZZARE TONI ROYAL BLEU ECONOMICI.
§ EFFETTO COLOR BLOCKING ECCELLENTE.
§ COMPATIBILITA’ CON LA GAMMA ERIOFAST®.
Corporate Polyamide Seminar TAIWAN May 2014 Page34 AICTC – Dalmine – 27 Maggio 2016
ERIOFAST® NAVY M
ECCELLENZA OPERATIVA ED ECONOMICITA’
§ AMPLIA LA GAMMA COLORI NELL’AREA ROYAL, NAVY E NERO.
§ TONI ROYAL INTENSI POSSONO ESSERE REALIZZATI. § PRIMA RICHIEDEVANO GRANDI
QUANTITA’ DI ERIOFAST® Blue 3R
§ MARINO ECONOMICO § FINO AD ORA TONI INTENSI NAVY
POSSIBILE SOLO COMBINANDO ERIOFAST® Black M
ERIOFAST® Blue 3R § A SECONDA DELLE RICETTA
VIENE RIDOTTO IL QUANTITATIVO DI ERIOFAST® Blue 3R SENZA COMPROMETTERE LA RIPRODUCIBILITA’.
1
2
3
4 5
6
7 8
9
-60
-40
-20
0
20
40
60
80
100
-40 -20 0 20 40 60 80
b*
a*
Gamut (CIELAB D65/10)
1: ERIOFAST YELLOW 5G 2: ERIOFAST YELLOW R 3: ERIOFAST ORANGE 4R
4: ERIOFAST RED B 5: ERIOFAST RED 2B 6: ERIOFAST BLUE 3R
7: ERIOFAST BLUE 3G 8: ERIOFAST Navy M 9: ERIOFAST BLACK M
Reference Depth = 1.00
Corporate Polyamide Seminar TAIWAN May 2014 Page35 AICTC – Dalmine – 27 Maggio 2016
ERIOFAST® NAVY M
ERIOFAST® NAVY M
depth Ch PA Ch PA Ch PA Ch PA Ch PA Xenon Light Fastness
ISO 105 B02
N/L
N/Dk
6–7
7
>4
>4
-
>4
-
>4
-
Washing 40°C ISO 105 C06-B2S
N/L
N/Dk
5 4–5
5 5
4 -5
4
-
-
>4-5
>4
>4
>3 -4
Washing 50°C ISO 105 C06-B2S
N/L
N/Dk
5 4–5
5 5
4 -5
4
-
-
-
-
-
-
Washing 60°C ISO 105-C06-C2S
N/L
N/Dk
5 4–5
4–5 4–5
4 -5
4
-
-
-
-
-
-
Washing 49°C AATCC 61 2A
N/L
N/Dk
4–5 4–5
4–5 4–5
4
4
-
-
-
-
Water ISO 105 E-01
N/L
N/Dk
4–5 5
5 5
4
4
4
4
>4-5
>4
>4
>4
Sea water ISO 105 E-02
N/L
N/Dk
5 5
5 5
-
-
-
-
>4
>4
>4
>4
Perspiration alkaline ISO 105 E-04
N/L
N/Dk
4–5 4–5
5 5
4
4
3
3
>4-5
>4
>3
>3
Perspiration acid ISO 105 E-04
N/L
N/Dk
5 5
5 5
4
4
3
3
>4-5
>4
>3
>3
Chlorinated water ISO 105-E03 (50 ppm Cl)
4 -5
3 -4
-
-
-
>4
-
>4
-
Rubbing ISO 105-X12 N/Dk
dry
wet
4–5
4–5
4 3
4 3
>4 >3
-
>4 >3
-
N/L – standard depth “light navy”
N/Dk – standard depth “dark navy”
2.6%
3.9%
Corporate Polyamide Seminar TAIWAN May 2014 Page36 AICTC – Dalmine – 27 Maggio 2016
ERIOFAST® NAVY M
LA SCELTA AMBIENTALE
• SODDISFA OEKO-Tex 100 (COMPRESA CLASSE I) • SODDISFA STANDARD EUROPEI • BLUESIGN® • SODDISFA LISTE DEI MARCHI RSL’s (Restricted Substance Lists) • RESPONSIBLE CARE
Corporate Polyamide Seminar TAIWAN May 2014 Page37 AICTC – Dalmine – 27 Maggio 2016
NUOVO RANGE ERIOFAST®
ERIOFAST® Yellow 5G Bright lemon yellow dye with highest light and wet fastness properties. For bright yellow and green shades in combination with ERIOFAST® Blue 3G. Can be used as a non-photochromic yellow trichromatic element.
2.0% 4.0%
ERIOFAST® Yellow R Neutral yellow component, basis for brilliant yellow and orange shades. Very good compatibility with all the other dyes of the range. Main trichromatic yellow element. 1.0% 2.0%
ERIOFAST® Orange 4R Very bright non-photochromic orange dye with excellent wet fastness properties. In combination with ERIOFAST® Red B and ERIOFAST® Yellow R to match all shades from very bright orange to intense scarlet. 2.0% 4.0%
ERIOFAST® Red B Most brilliant red component of the ERIOFAST® range. Basis for all brilliant red and scarlet shades, especially in combinations with ERIOFAST® Orange 4R. 3.4% 6.8%
ERIOFAST® Red 2B Red component with highest light fastness, similar to metal complex dyes, but much higher brilliancy. Best build-up, excellent compatibility with all other elements of the range.
2.2% 4.4%
ERIOFAST® Blue 3R Brilliant royal blue, offers by far better wet fastness properties compared to acid dyes with similar shades. Highest light fastness, very well compatible with the other dyes of the range.
3.0% 6.0%
ERIOFAST® Blue 3G Greenish blue dye with highest light and wet fastness properties. For matching all greenish shades in combination with ERIOFAST® Yellow 5G. In trichromatic combinations with ERIOFAST® Yellow R or Yellow 5G and Red 2B to correct metamerism.
3.5% 7.0%
ERIOFAST® Navy M Innovative navy with outstanding fastness properties, particularly fastness to chlorinated water. Basis for all navies, can be shaded with all ERIOFAST® dyes. Together with ERIOFAST® Blue 3R for intensive economic royal blue shades. 2.6% 3.9%
ERIOFAST® Black B Innovative black with outstanding wetfastness properties. Basis for all black and dull deep navy shades. On some polyamide types a dyeing temperature of 105 to 110oC gives improved build-up.
4.3%
Corporate Polyamide Seminar TAIWAN May 2014 Page38 AICTC – Dalmine – 27 Maggio 2016
FINISSAGGIO
Corporate Polyamide Seminar TAIWAN May 2014 Page39 AICTC – Dalmine – 27 Maggio 2016
CARATTERISTICHE DEL CAPO
CARATTERISTICHE IMPORTANTI DI UN CAPO PER LO SPORTIVO.
TENDENZIALMENTE LE DONNE PREDILIGONO CONFORT E FLESSIBILITA’.
TENDENZIALMENTE GLI UOMINI PREDILIGONO LE PERFORMANCE.
Corporate Polyamide Seminar TAIWAN May 2014 Page40 AICTC – Dalmine – 27 Maggio 2016
COMFORT ULTRATEX ® STS-D “STABLE SILICONE SOFTENER” MICRO EMULSIONE SILICONICA. ECCELLENTE STABILITA’ ALLE FORZE DI TAGLIO. ECCELLENTE STABILITA’ ALLO STOCCAGGIO. STABILE A TEMPERATURE COMPRESE TRA 60-80°C. STABILE DA pH 1-2 FINO A 12. STABILE AI SALI COMUNI.
ULTRAPHIL® PA MOISTURE MANAGEMENT PER PA E MISTE PA/EL EFFETTO IDROFILICO COMBINATO CON MANO E PROPRIETA’ ANTISTATICHE. PROPRIETA’ SOIL RELEASE. APPLICABILE PER IMPREGNAZIONE E SU CAPO.
EVERGLIDE MINIMIZZA LA FRIZIONE TRA TESSUTO E PELLE. EVERGLIDE ASSICURA LA RESILIENZA DEI TESSILI E LORO DURABILITA’. EVERGLIDE RIDUCE IL RISCHIO DI ARROSSAMENTO ED IRRITAZIONE DELLA PELLE GRAZIE ALLE SUE CARATTERISTICHE DI “LUBRIFICAZIONE”.
Corporate Polyamide Seminar TAIWAN May 2014 Page41 AICTC – Dalmine – 27 Maggio 2016
PERFORMANCE
ZELAN ® R3 FLUORINE FREE. CONTIENE IL 63% DI MATERIA PRIMA PROVENIENTE DA FONTI RINNOVABILI (TEST ASTM method 6866) REPELLENTE ALL’ACQUA ED AI PIU’ COMUNI LIQUIDI BASE ACQUOSA. RESISTENTE FINO A 30 LAVAGGI. IDONEO PER TUTTE LE FIBRE TESSILI.
ERIONAL ® PCL FISSATORE ESENTE DA FORMALDEIDE PER INCREMENTARE SOLIDITA’ AL CLORO SU PA E MISTE APPLICABILE IN CONTINUO O PAD-DRY-THERMOFIX NON RACCOMANDATO PER BIANCO OTTICO. NO IMPATTO SU SOLIDITA’ ALLA LUCE
PHOBOTEX ® RANGE RAIN PROTECTION (OUTERWEAR) STAIN MANAGEMENT (ACTIVEWEAR) STAIN MANAGEMENT (PANTS) STAIN MANAGEMENT (CAREERWEAR)
Corporate Polyamide Seminar TAIWAN May 2014 Page42
GRAZIE/THANK YOU Stefano Cavestro