Investigation of Organic Coatings Durability on Concrete Reinforcement Corrosion
Protection with the Synergistic Influence of Corrosion Inhibitors
S.Kalogeropoulou1, P.Pantazopoulou1, Th.Zafeiropoulou2, K. Sideris3
1. Electrical Engineering Department, Technological Educational Institute of Piraeus, Athens, Greece2. Faculty of Chemical Engineering, National Technical University of Athens, Greece
3. Democritus University of Thrace, Dept. of Civil Engineering, Xanthi, Greece
eRA – 9, T.E.I. of Piraeus, 22-24 September 2014
In this work the results obtained until now in the framework of an ARCHIMEDES III research project entitled "Investigation of Organic Coatings Durability on Concrete Reinforcement Corrosion Protection with the Synergistic Influence of Corrosion Inhibitors” are presented.
eRA-9 222/9/2014
Aim of the study
The action of various organic coatings and corrosion inhibitors in the protection of steel reinforcement in highly corrosive conditions is investigated. Five different types of organic protective coatings have been chosen to be studied: a two-pack epoxy paint, a two-pack polyurethane paint, a nanotechnology paint and two acrylic dispersions. A classification of the protective action of the organic coatings against corrosion, based on the results of various experimental methods, is presented.
eRA-9 322/9/2014
Reinforcement corrosion – Protection methods
Reinforcement corrosion: main cause of reduction of a structure’s life
coatings on the surface of concrete
corrosion inhibitors
cathodic protection
stainless steel reinforcement
coating of reinforcement
22/9/2014 eRA-9 4
available
protection
methods
Organic coatings
Surface coatings on concrete:prevent the deterioration by creating a
physical barrier between the concrete structure and the harmful substances from the environment
improve or maintain the appearance offer an effective and reliable solution for the
protection both of the concrete and the embedded steel
22/9/2014 eRA-9 5
Desired properties of organic coatings
Good adhesion to concrete even when wet Resistance to high alkalinity of concrete Ability to penetrate into the pores and cracks of concrete Good resistance to ultraviolet (UV) radiation and
weathering Good mechanical strength Prevent entry of water but allow water vapor permeation High resistance to the permeation of sulfur dioxide and
carbon dioxide and to the penetration of chloride ions in the pores and cracks (less than 0,3 mm) of the concrete
22/9/2014 eRA-9 6
Corrosion inhibitors
Corrosion inhibitors have been successfully used as admixtures to concrete to reduce the risk of reinforcement corrosion.
Alkanolamine-based corrosion inhibitors move through the pore structure of concrete to reach the
surface of reinforcing steel, where they form a protective filmreduce chloride ion ingress into concreteare classified as mixed inhibitors, because they influence
both the cathodic and the anodic process of corrosion
22/9/2014 eRA-9 7
Degradation of coatings
Μain factors influencing the durability of coatings:
sunlight (ultraviolet radiation)
moisture
heat
Τhe result of the combination of these factors is much
more serious than each factor individually.
Degradation can vary from mere surface discoloration
affecting the aesthetic appeal of a product to substantial
loss of mechanical properties.
22/9/2014 eRA-9 8
Properties studied and methods used
Reinforcement’s corrosion behavior
Effect of UV-radiation to coatings
Liquid water and water vapor transmission rates
Carbonation depth
22/9/2014 eRA-9 9
Reinforcement’s corrosion behaviorUse of the Strain Gauge (SG) technique, which is based on
the appearance of swelling strain near the steel reinforcement in the concrete and is measured by embedded SG sensors in mortar specimens. The cause of the swelling tension is the formation of corrosion products (iron oxides, Fe3O4, Fe2O3, FeO(OH)) having greater specific volume than iron.
Determination of the gravimetric mass loss of reinforcing steel bars after a certain period of exposure in the corrosive environment. Mass loss (according to ISO/DIS 8407) is estimated as the difference between the initial and the final mass of the bars, as determined by removing the corrosion products from the bars.
22/9/2014 eRA-9 10
Effect of UltraViolet-radiation to coatingsDry Film Thickness was measured according to ASTM
D4138 “Standard Practices for Measurement of Dry Film Thickness of Protective Coating Systems by Destructive, Cross-Sectioning Means”.
Cross cut test was performed according to ISO 2409:1992(E) “Paints and varnishes – Cross cut test” and ASTM D3330 / D3330M - 04(2010) “Standard Test Method for Peel Adhesion of Pressure-Sensitive Tape”.
In coated specimens coatings’ adhesion was measured according to BS EN 24624:1993/ BS EN ISO 4624:2003 “Paints and varnishes - Pull off test for adhesion” and ASTM D4541 - 09e1 “Standard Test Method for Pull-Off Strength of Coatings Using Portable Adhesion Testers”.
22/9/2014 eRA-9 11
Liquid water and water vapor transmission rates
Liquid water transmission rate of each coating is determined according to standard DIN EN 1062-3:2008-04 “Paints and varnishes - Coating materials and coating systems for exterior masonry and concrete - Part 3: Determination of liquid water permeability”.
Water vapor transmission rate is determined according to standard DIN EN ISO 7783-2 “Coating materials and coating systems for exterior masonry and concrete - Part 2: Determination and classification of water-vapor transmission rate (permeability)”.
22/9/2014 eRA-9 12
Carbonation depth
Measurements of carbonation depth are performed
according to BS EN 13295:2004 "Products and systems for
the protection and repair of concrete structures - Test
methods - Determination of resistance to carbonation" and
BS EN 14630:2006 "Products and systems for the protection
and repair of concrete structures - Test methods -
Determination of carbonation depth in hardened concrete
by the phenolphthalein method".
22/9/2014 eRA-9 13
Materials
eRA-9 14
Quarry sand Quarry sand
Reinforcement B500C
1 : 3 : 0.51 : 3 : 0.5
standard proportionscement : sand : water
Inhibitor
Chemical composition of Portland cement (%wt)
eRA-9 15
SiO2 Al2O3 Fe2O3 CaO MgO K2O Na2O SO3 CaO(f) LOI
CEM II 32.5 20.67 4.99 3.18 63.60 2.73 0.37 0.29 2.41 2.41 2.52
Chemical composition of steel (%wt)
C Mn S P Si Ni Cr Cu V Mo
0.22 1.24 0.044 0.032 0.28 0.09 0.10 0.52 0.075 0.028
22/9/2014
Organic Coatings Categories
Two-pack epoxy coating (E)
Two-pack polyurethane coating (P)
Nanotechnology coating (N)
Acrylic emulsion (A)
Elastomeric acrylic dispersion (R)
Uncoated specimens were used as reference (O)
eRA-9 1622/9/2014
Coating procedure
The coating procedure for all coatings involves three layers:The appropriate for each coating primer is applied on the
dried surface of the specimen, to achieve the best adhesion between coating and mortar.
24 hours The first layer of the organic coating is applied by brush. 24 hours The second layer of the organic coating is applied by
brush perpendicularly to the first one.Coated mortar specimens are stored in the laboratory for
at least 7 days, so as coatings are dried and all quantity of solvents has evaporated.
eRA-9 1722/9/2014
Organic coatings - technical characteristics
S/N Code Product Color Characteristics
1 Ε Epoxy Grey Two-pack epoxy paint with amine hardener, density 1,55 kg/Lt, spreading rate 6 m²/kg (100
μm), solids 95% w/v.2 P Polyurethane Grey Two-pack polyurethane with aliphatic isocyanic
hardener, density 1,20-1,40 kg/Lt, spreading rate 9-11 m²/ Lt (50μm).
3 N Paint for exterior use
White Siloxane paint, density 1,60 kg/Lt, solids 50% w/v, spreading rate 8,6 m²/Lt.
4 A Acrylic emulsion paint for
exterior use
White Acrylic dispersion, density 1.46±0.05 g/ml, solids 61±2.5% w/w, pH 8.4±1, spreading rate 9±1
m²/Lt (2 coats).
5 R Elastomeric insulating
acrylic paint
White Acrylic dispersion, undiluted for final coat, density 1.35 g/ml, solids 60±2% w/w, spreading
rate 2±1 m²/Lt.eRA-9 1822/9/2014
Primers – technical characteristics
S/N Code Product Color Characteristics1 ΕΑ Epoxy primer
(coatings 1-2)Colorless Two-pack epoxy primer, Α:Β-2:1 w/v
with hardener, solids 58% w/v, density 0,99 kg/Lt, spreading rate 10 m²/Lt.
2 ΑΑ Acrylic water-based primer
(coating 3)
Colorless Density 1kg/Lt, solids 25,9% w/v, dilution up to 1:4 with water, spreading
rate 8-32 m²/Lt.3 SΑ Styrene-
acrylic primer (coatings 4-5)
Colorless Copolymers of styrene and acrylic resins, density 0.85 g/ml, solids 26±2% w/w,
spreading rate 7.5-8.5 m²/Lt.
eRA-9 1922/9/2014
Conclusions A: Corrosion evaluation The protective action of all organic coatings against
corrosion of the embedded reinforcement is confirmed. Epoxy and polyurethane coatings present an exceptional
performance. The nanotechnology coating presents reduced protective
ability in accelerated corrosion conditions. For the system “corrosion inhibitor – organic coating” the
results have shown that their action is not added. However there is an improvement of the protection given by the coatings with the inhibitor presence, especially in the case of the less effective coatings.
eRA-9 2022/9/2014
Conclusions B: UV radiation & Water/Water vapor permeabilities
Polyurethane coatings present excellent resistance to ultra violet radiation as compared to epoxy coatings that suffer from yellowing. Both coatings present very low water vapor transmission rate and liquid water permeability.
Radiation causes mild degradation to the acrylic and elastomeric emulsions. Both coatings present fairly good behavior towards moisture.
The nanotechnology coating resists very well to radiation and presents an improved behavior compared to all other coatings systems regarding water vapor transmission rate and liquid water permeability.
eRA-9 2122/9/2014
Conclusions C: Carbonation
The two-component industrial coatings with organic solvent (epoxy and polyurethane coatings) provide the best protection.
Aqueous dispersions conventional coatings (elastomeric and acrylic dispersions) offer a satisfying level of protection.
The nanotechnology coating provides a low and negligible protection rate.
eRA-9 2222/9/2014
Acknowledgements
This research has been co-financed by the European Union
(European Social Fund – ESF) and Greek national funds through
the Operational Program "Education and Lifelong Learning" of
the National Strategic Reference Framework (NSRF) - Research
Funding Program: ARCHIMEDES III. Investing in knowledge
society through the European Social Fund.
eRA-9 2322/9/2014
eRA-9 2422/9/2014
Thank you for your attention!