PREPREG TB CARBON Fiber Prepreg
www.tbcarbon.com
TB
CA
RB
ON
1
G eneral Product Information
TB CARBON is the trade mark of TB CARBON for the Impregnated carbon
fiber products with 250◦F(121◦C)Curing Epoxy Resin System.
Special Features
● Prepreg from hot melt process, providing least void composites
● Economical curing temperature
● Easy-to-handle with desireable tack and resin strength
● Uniform thickness and resin content
● Service temperature of up to 80℃
● Long out-time of 30 days at 25℃
TB CARBON
2
G eneral Modulus Prepreg (24Ton) without Scrim
FAW Resin Resin Content Thickness
Wt(g/m²) Wt(g/m²) (%) (mm)
Standard Resin Content
CP 020NS 20 18 47 38 0.026
CP 030NS 30 24 44 54 0.037
CP 050NS 55 37 40 92 0.061
CP 075NS 75 46 38 121 0.080
CP 100NS 100 54 35 154 0.101
CP 125NS 125 62 33 187 0.121
CP 150NS 150 74 33 224 0.145
CP 175NS 175 86 33 261 0.169
CP 200NS 200 99 33 299 0.194
CP 250NS 250 123 33 373 0.241
Low Resin Content (C)
CP 075NS.C 75 32 30 107 0.070
CP 100NS.C 100 43 30 143 0.091
CP 125NS.C 125 54 30 179 0.114
CP 150NS.C 150 64 30 214 0.137
CP 175NS.C 175 75 30 250 0.160
CP 200NS.C 200 86 30 286 0.183
CP 250NS.C 250 107 30 357 0.228
Low Resin Content (D)
CP 125NS.D 125 42 25 167 0.106
CP 150NS.D 150 50 25 200 0.125
CP 175NS.D 175 58 25 233 0.146
CP 200NS.D 200 67 25 267 0.167
CP 250NS.D 250 83 25 333 0.208
TB CARBON
Code NameTotal
Wt(g/m²)
3
G eneral Modulus Prepreg (24Ton) with Scrim
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
Standard Resin Content
CP 0303 30 24 44 35 89 0.067
CP 0503 55 37 40 35 127 0.091
CP 0753 75 46 38 35 156 0.110
CP 1003 100 54 35 35 189 0.131
CP 1253 125 62 33 35 222 0.151
CP 1503 150 74 33 35 259 0.175
CP 1753 175 86 33 35 296 0.199
CP 2003 200 99 33 35 334 0.224
CP 2503 250 123 33 35 408 0.271
Low Resin Content (C)
CP 0753.C 75 32 30 35 142 0.100
CP 1003.C 100 43 30 35 178 0.121
CP 1253.C 125 54 30 35 214 0.144
CP 1503.C 150 64 30 35 249 0.167
CP 1753.C 175 75 30 35 285 0.190
CP 2003.C 200 86 30 35 321 0.213
CP 2503.C 250 107 30 35 392 0.258
Low Resin Content (D)
CP 1003.D 100 33 25 35 168 0.116
CP 1503.D 150 50 25 35 235 0.155
CP 1753.D 175 58 25 35 268 0.176
CP 2003.D 200 67 25 35 302 0.197
CP 2503.D 250 83 25 35 368 0.238
TB CARBON
Code NameScrim
Wt(g/m²)
4
C /C carbon (24 Ton)
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
C2
CP 020NS20 16 44 0 36 0.026
C3
CP 030NS30 24 44 0 54 0.037
MC2
MCP 020NS20 16 44 0 36 0.024
MC3
MCP 030NS30 30 50 0 60 0.042
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Length
(CP 125NS)125 62 33 0 187 0.121
Width
(CP 020NS)20 16 44 0 36 0.026
Total 145 78 35 0 223 0.147
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Length
(CP 150NS)150 74 33 0 224 0.145
Width
(CP 030NS)30 24 44 0 54 0.037
Total 180 98 35 0 278 0.182
TB CARBON
Code Name
Code Name
EX) CP 125C2
Code Name
EX) CP 150C3
5
M edium Modulus Prepreg (30Ton) without Scrim
FAW Resin Resin Content Thickness
Wt(g/m²) Wt(g/m²) (%) (mm)
Standard Resin Content
MCP 020NS 20 18 47 38 0.026
MCP 030NS 30 30 50 60 0.042
MCP 050NS 55 37 40 92 0.061
MCP 075NS 75 44 37 119 0.078
MCP 100NS 100 43 30 143 0.091
MCP 125NS 125 54 30 179 0.114
MCP 150NS 150 64 30 214 0.137
MCP 175NS 175 75 30 250 0.160
MCP 200NS 200 86 30 286 0.183
MCP 250NS 250 107 30 357 0.228
Low Resin Content(C)
MCP 075NS.C 75 32 30 107 0.070
Low Resin Content (D)
MCP 100NS.D 100 33 25 133 0.086
MCP 125NS.D 125 42 25 167 0.106
MCP 150NS.D 150 50 25 200 0.125
MCP 175NS.D 175 58 25 233 0.146
MCP 250NS.D 250 83 25 333 0.208
TB CARBON
Code NameTotal
Wt(g/m²)
6
M edium Modulus Prepreg (30Ton) with Scrim
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
Low Resin Content
MCP 0303 30 30 50 95 0.072
MCP 0503 55 37 40 127 0.091
MCP 0753 75 44 37 154 0.108
MCP 1003 100 43 30 178 0.121
MCP 1253 125 54 30 214 0.144
MCP 1503 150 64 30 249 0.167
MCP 1753 175 75 30 285 0.190
MCP 2003 200 86 30 321 0.213
MCP 2503 250 107 30 392 0.258
Low Resin Content(C)
MCP 0753.C 75 32 30 142 0.100
Low Resin Content (D)
MCP 1003.D 100 33 25 168 0.116
MCP 1253.D 125 42 25 202 0.136
MCP 1503.D 150 50 25 235 0.155
MCP 1753.D 175 58 25 268 0.176
MCP 2003.D 200 67 25 302 0.197
TB CARBON
Code NameScrim
Wt(g/m²)
35
35
35
35
35
35
35
35
35
35
35
35
35
35
35
7
C /C Carbon (30Ton)
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
C2
CP 020NS20 16 44 0 36 0.026
C3
CP 030NS30 24 44 0 54 0.037
MC2
MCP 020NS20 16 44 0 36 0.024
MC3
MCP 030NS30 30 50 0 60 0.042
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Length
(MCP 100NS)100 43 33 0 143 0.091
Width
(CP 020NS)20 16 44 0 36 0.026
Total 120 59 33 0 179 0.117
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Length
(MCP 150NS)150 64 30 0 214 0.137
Width
(CP 030NS)30 24 44 0 54 0.037
Total 180 88 33 0 268 0.174
TB CARBON
Code Name
Code Name
EX) MCP 100C2
Code Name
EX) MCP 150C3
8
H igh Modulus Prepreg (36Ton) without Scrim
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
Low Resin Content
HCP 050NS 55 37 40 92 0.061
HCP 069NS 69 36 34 105 0.068
HCP 075NS 75 39 34 114 0.074
HCP 092NS 92 39 30 131 0.084
HCP 100NS 100 43 30 143 0.091
HCP 116NS 116 50 30 166 0.106
HCP 125NS 125 54 30 179 0.114
HCP 139NS 139 60 30 199 0.127
HCP 150NS 150 64 30 214 0.137
HCP 160NS 160 69 30 229 0.146
HCP 175NS 175 75 30 250 0.160
HCP 184NS 184 79 30 263 0.168
HCP 200NS 200 86 30 286 0.183
Low Resin Content (D)
HCP 092NS.D 92 34 27 126 0.079
HCP 100NS.D 100 37 27 137 0.086
HCP 116NS.D 116 41 26 157 0.099
HCP 125NS.D 125 44 26 169 0.106
HCP 139NS.D 139 46 25 185 0.116
HCP 150NS.D 150 50 25 200 0.125
HCP 160NS.D 160 53 25 213 0.133
HCP 175NS.D 175 58 25 233 0.146
HCP 200NS.D 200 67 25 267 0.167
TB CARBON
Code Name
9
H igh Modulus Prepreg (36Ton) with Scrim
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Low Resin Content
HCP 0503 55 37 40 35 127 0.091
HCP 0693 69 36 34 35 140 0.098
HCP 0753 75 39 34 35 149 0.104
HCP 0923 92 39 30 35 166 0.114
HCP 1003 100 43 30 35 178 0.121
HCP 1163 116 50 30 35 201 0.136
HCP 1253 125 54 30 35 214 0.144
HCP 1393 139 60 30 35 234 0.157
HCP 1503 150 64 30 35 249 0.167
HCP 1603 160 69 30 35 264 0.176
HCP 1753 175 75 30 35 285 0.190
HCP 1843 184 79 30 35 298 0.198
HCP 2003 200 86 30 35 321 0.213
Low Resin Content (D)
HCP 0923.D 92 34 27 35 161 0.109
HCP 1003.D 100 37 27 35 172 0.116
HCP 1163.D 116 41 26 35 192 0.129
HCP 1253.D 125 44 26 35 204 0.136
HCP 1393.D 139 46 25 35 220 0.146
HCP 1503.D 150 50 25 35 235 0.155
HCP 1603.D 160 53 25 35 248 0.163
HCP 1753.D 175 58 25 35 268 0.176
HCP 2003.D 200 67 25 35 302 0.197
TB CARBON
Code Name
10
C /C carbon (36Ton)
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
C2
CP 020NS20 16 44 0 36 0.026
C3
CP 030NS30 24 44 0 54 0.037
MC2
MCP 020NS20 16 44 0 36 0.024
MC3
MCP 030NS30 30 50 0 60 0.042
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Length
(HCP 139NS)139 60 30 0 199 0.127
Width
(CP 020NS)20 16 44 0 36 0.026
Total 159 76 32 0 235 0.153
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Length
(HCP 150NS)150 64 30 0 214 0.137
Width
(CP 030NS)30 24 44 0 54 0.037
Total 180 88 33 0 268 0.174
TB CARBON
Code Name
Code Name
EX) HCP 139C2
Code Name
EX) HCP 150C3
11
H igh Modulus Prepreg (40Ton) without Scrim
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
Standard Resin Content
40H 030NS 30 30 50 60 0.042
40H 050NS 55 37 40 92 0.061
40H 069NS 69 36 34 105 0.068
40H 075NS 75 39 34 114 0.074
40H 092NS 92 39 30 131 0.084
40H 100NS 100 43 30 143 0.091
40H 116NS 116 50 30 166 0.106
40H 125NS 125 54 30 179 0.114
40H 139NS 139 60 30 199 0.127
40H 150NS 150 64 30 214 0.137
40H 160NS 160 69 30 229 0.146
40H 175NS 175 75 30 250 0.160
40H 184NS 184 79 30 263 0.168
40H 200NS 200 86 30 286 0.183
Low Resin Content (D)
40H 092NS.D 92 34 27 126 0.079
40H 100NS.D 100 37 27 137 0.086
40H 116NS.D 116 41 26 157 0.099
40H 125NS.D 125 44 26 169 0.106
40H 139NS.D 139 46 25 185 0.116
40H 150NS.D 150 50 25 200 0.125
40H 160NS.D 160 53 25 213 0.133
40H 184NS.D 184 61 25 245 0.153
40H 200NS.D 200 67 25 267 0.167
TB CARBON
Code Name
12
H igh Modulus Prepreg (40Ton) with Scrim
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Low Resin Content
40H 0503 55 37 40 35 127 0.091
40H 0693 69 36 34 35 140 0.098
40H 0753 75 39 34 35 149 0.104
40H 0923 92 39 30 35 166 0.114
40H 1003 100 43 30 35 178 0.121
40H 1163 116 50 30 35 201 0.136
40H 1253 125 54 30 35 214 0.144
40H 1393 139 60 30 35 234 0.157
40H 1503 150 64 30 35 249 0.167
40H 1603 160 69 30 35 264 0.176
40H 1753 175 75 30 35 285 0.190
40H 1843 184 79 30 35 298 0.198
40H 2003 200 86 30 35 321 0.213
Low Resin Content (D)
40H 0923.D 92 34 27 35 161 0.109
40H 1003.D 100 37 27 35 172 0.116
40H 1163.D 116 41 26 35 192 0.129
40H 1253.D 125 44 26 35 204 0.136
40H 1393.D 139 46 25 35 220 0.146
40H 1503.D 150 50 25 35 235 0.155
40H 1603.D 160 53 25 35 248 0.163
40H 1753.D 175 58 25 35 268 0.176
40H 2003.D 200 67 25 35 302 0.197
TB CARBON
Code Name
13
C /C carbon (40Ton)
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
C2
CP 020NS20 16 44 0 36 0.026
C3
CP 030NS30 24 44 0 54 0.037
MC2
MCP 020NS20 16 44 0 36 0.024
MC3
MCP 030NS30 30 50 0 60 0.042
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Length
(40H 092NS)92 39 30 0 131 0.084
Width
(CP 020NS)20 16 44 0 36 0.026
Total 112 55 32 0 167 0.110
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Length
(40H 116NS)116 50 30 0 166 0.106
Width
(CP 030NS)30 24 44 0 54 0.037
Total 146 74 33 0 220 0.143
TB CARBON
Code Name
Code Name
EX) 40H 092C2
Code Name
EX) 40H 116C3
14
H igh Modulus Prepreg (46Ton) without Scrim
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
Standard Resin Content
46H 050NS 55 37 40 92 0.061
46H 069NS 69 36 34 105 0.068
46H 092NS 92 39 30 131 0.084
46H 116NS 116 50 30 166 0.106
46H 139NS 139 60 30 199 0.127
46H 160NS 160 69 30 229 0.146
46H 184NS 184 79 30 263 0.168
Low Resin Content(D)
46H 092NS.D 92 32 26 124 0.078
46H 116NS.D 116 39 25 155 0.097
46H 139NS.D 139 46 25 185 0.116
46H 160NS.D 160 53 25 213 0.133
46H 184NS.D 184 61 25 245 0.153
TB CARBON
Code Name
15
H igh Modulus Prepreg (46Ton) with Scrim
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Low Resin Content
46H 0503 55 37 40 35 127 0.091
46H 0693 69 36 34 35 140 0.098
46H 0923 92 39 30 35 166 0.114
46H 1163 116 50 30 35 201 0.136
46H 1393 139 60 30 35 234 0.157
46H 1603 160 69 30 35 264 0.176
46H 1843 184 79 30 35 298 0.198
Low Resin Content (D)
46H 0923.D 92 34 26 35 159 0.108
46H 1163.D 116 39 25 35 190 0.127
46H 1393.D 139 46 25 35 220 0.146
46H 1603.D 160 53 25 35 248 0.163
46H 1843.D 184 61 25 35 280 0.183
TB CARBON
Code Name
16
C /C carbon (46Ton)
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
C2
CP 020NS20 16 44 0 36 0.026
C3
CP 030NS30 24 44 0 54 0.037
MC2
MCP 020NS20 16 44 0 36 0.024
MC3
MCP 030NS30 30 50 0 60 0.042
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Length
(46H 139NS)139 60 30 0 199 0.127
Width
(CP 020NS)20 16 44 0 36 0.026
Total 159 76 32 0 235 0.153
FAW Resin Resin Content Scrim Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
Length
(46H 160NS)160 69 30 0 229 0.146
Width
(CP 030NS)30 24 43 0 54 0.037
Total 190 93 33 0 283 0.183
TB CARBON
Code Name
Code Name
EX) 46H 139C2
Code Name
EX) 46H 160C3
17
Golf Type Prepreg
24 Ton
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
CP 100NS 100 49 33 149 0.102
CP 125NS 125 62 33 187 0.121
CP 150NS 150 74 33 224 0.145
CP 175NS 175 86 33 261 0.169
30 Ton
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
MCP 100NS 100 49 33 149 0.102
MCP 125NS 125 62 33 187 0.121
MCP 150NS 150 74 33 224 0.145
40 Ton
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
40H 092NS 92 45 33 137 0.086
40H 100NS 100 49 33 149 0.093
40H 116NS 116 57 33 173 0.108
40H 139NS 139 68 33 207 0.129
and high strenth carbon fiber for the use of golf.
TB CARBON
Code Name
※ This prepreg is made of the resin blended specially
Code Name
Code Name
18
Bicycle Type Prepreg
24 Ton
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
CP 050NS.A 55 37 40 92 0.061
CP 075NS.A 75 44 37 119 0.078
CP 100NS.A 100 59 37 159 0.105
CP 125NS.A 125 73 37 198 0.130
CP 150NS.A 150 88 37 238 0.157
30 Ton
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
MCP 075NS.A 75 44 37 119 0.078
MCP 100NS.A 100 59 37 159 0.105
MCP 125NS.A 125 73 37 198 0.130
40 Ton
FAW Resin Resin Content Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) (mm)
40H 075NS.A 75 44 37 119 0.078
40H 100NS.A 100 59 37 159 0.105
TB CARBON
Code Name
※ 자전거용으로 특별하게 조합된 Epoxy 수지를 사용함
※ This prepreg is made of the resin blended specially for the use of bicycle.
Code Name
Code Name
19
H ybrid Prepreg (Carbon/Glass)
FAW Resin Resin Content Glass Cloth Total Thickness
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²) (mm)
CPG 5009 55 37 40 123 215 0.131
CPG 5010 55 37 40 173 265 0.161
CPG 5013 55 37 40 257 312 0.201
CPG 7009 75 46 38 123 244 0.150
CPG 7010 75 46 38 173 294 0.180
CPG 7013 75 46 38 257 378 0.220
CPG 7015 75 46 38 285 406 0.235
CPG 1009 100 54 35 123 277 0.171
CPG 1010 100 54 35 173 327 0.201
CPG 1013 100 54 35 257 411 0.241
CPG 1015 100 54 35 285 439 0.256
CPG 1209 125 62 33 123 310 0.191
CPG 1210 125 62 33 173 360 0.221
C arbon Prepreg Tape
FAW Resin Resin Content Scrim Total
Wt(g/m²) Wt(g/m²) (%) Wt(g/m²) Wt(g/m²)
CPT 0303 0.09 0.07 44 0 0.162
CPT 0305 0.15 0.12 44 0 0.270
CPT 0307 0.21 0.17 44 0 0.378
CPT 0310 0.30 0.24 44 0 0.540
CPT 0503 0.17 0.11 40 0 0.276
CPT 0505 0.28 0.18 40 0 0.460
CPT 0507 0.39 0.26 40 0 0.644
CPT 0510 0.55 0.37 40 0 0.920
CPT 0705 0.38 0.23 38 0 0.605
CPT 0707 0.53 0.32 38 0 0.847
CPT 0710 0.75 0.46 38 0 1.210
MCPT 0305 0.15 0.15 50 0 0.300
MCPT 0307 0.21 0.21 50 0 0.420
MCPT 0310 0.30 0.30 50 0 0.600
TB CARBON
Code Name
Code Name Remark
20
C arbon Fabric Prepreg
FAW Resin Content
Wt(g/m²) (%)
CPF-1115EPC 117 85 0 202 Carbon1K
CPF-3327EPC 205 148 0 353 Carbon3K
CPF-3326EPC 252 182 0 434 Carbon3K
CPF-6638EPC 331 212 0 543 Carbon6K
Glass Fabric Prepreg
Resin Content Thickness
(%) (mm)
EN 303 25 10 35 0.030
EN 108 75 50 125 0.075
EN 110 105 70 175 0.095
EN 118 190 127 317 0.170
EB 209 76 47 123 0.090
EB 210 108 65 173 0.100
EB 215 183 94 277 0.150
EB 218 207 106 313 0.180
EB 224 305 157 462 0.240
C arbon , Kevlar , Glass. Yarn EPC
TB CARBON
0.200
Resin Content
(%)
10~30
10~30
10~30
10~30
10~30
10~30
(g/m)
0.200
0.200
Wt(g/m²)
GPY 200BA EPC
GPY 200R EPC
34
28
Wt(g/m²)
WT
10~30
10~30
Code Name
GPY 067BA EPC
GPY 067G EPC
GPY 067R EPC
0.067
0.067
0.067
GPY 200Y EPC
10~30
WT
10~30
10~30
0.201
0.402
0.042
0.020
0.160
KPY 1420EPC
FAW
Wt(g/m²)
Resin
Wt(g/m²)
Resin Content
KPY 195EPC
(%)
KPY 380EPC
34
34
Code Name
CPY1K EPC 10~30
(g/m)
0.067
CPY3K EPC
CPY6K EPC
40
40
40
38
38
RemarkScrim Total
Wt(g/m²)
Total
Code Name
Code Name
42
42
42
39
Resin
Wt(g/m²)
21
temp.(℃)
100
50
15 30 45 60 70 90 105 120 135 150 165 180
temp.(℃)
100
50
15 30 45 60 70 90 105 120 135 150 165 180
● Information contained in this catalog is ofered in good faith and to the best of our knowledge as
a guide for use at your discretion and risk.
Because we have no control over the conditions under which you may elect to use our product,
we assume no liability in connection with their use.
TB CARBON
Time(min)
Recommended Cure Cycle
Cure Cycle 2
Cure Cycle 1
80
150
150
125
Time(min)
125
80
22
621-881
NO.920, DAMAN-RI, JILLYE-MYEON,
GIMHAE-SI, GYEONGSANGNAM-DO, KOREA
TEL : 82-55-345-2137~9
FAX : 82-55-345-2180