Compozitie Chimica Stare Aluminiu

COMPOZIÞIE CHIMICÃ • STARE

COMPOZIÞIA CHIMICÃ A ALIAJELOR

Si (%)ALIAJ

1050 <=0.25 <=0.4 <=0.05 <=0.05 <=0.05 <=0.07 <=0.05 <=0.03 <=99.5

2007 <=0.8 <=0.8 3.3-4.6 <=0.2 0.8-1.5 0.5-1.0 0.4-1.8 <=0.1 <=0.80 <=0.20 <=0.03 Rest

2011 <=0.4 <=0.7 5.0-6.0 0.2-0.6 0.2-0.6 <=0.30 <=0.05 Rest

2014 0.5-1.2 <=0.7 3.9-5.0 0.4-1.2 0.2-0.8 <=0.1 <=0.25 <=0.15 <=0.05 Rest

2017 0.2-0.8 <=0.7 3.5-4.5 0.4-1.0 0.4-1.0 <=0.1 <=0.25 <=0.25 <=0.05 Rest

2024 <=0.5 <=0.5 3.8-4.9 0.3-0.9 1.2-1.8 <=0.1 <=0.25 <=0.15 <=0.05 Rest

3003 <=0.6 <=0.7 <=0.3 1.0-1.5 <=0.10 <=0.05 Rest

3005 <=0.6 <=0.7 <=0.3 1.0-1.5 0.2-0.6 <=0.1 <=0.25 <=0.1 <=0.05 Rest

5005 <=0.3 <=0.7 <=0.2 <=0.2 0.5-1.1 <=0.1 <=0.25 <=0.05 Rest

5052 <=0.25 <=0.4 <=0.1 <=0.1 2.2-2.8 0.15-0.35 <=0.10 <=0.05 Rest

5083 <=0.4 <=0.4 <=0.1 0.4-1.0 4.0-4.9 0.05-0.25 <=0.25 <=0.15 <=0.05 Rest

5754 <=0.4 <=0.4 <=0.1 <=0.5 2.6-3.6 <=0.3 <=0.2 <=0.15 <=0.05 Rest

6060 0.3-0.6 0.1-0.3 <=0.1 <=0.1 0.35-0.6 <=0.05 <=0.15 <=0.1 <=0.05 Rest

6063 0.2-0.6 <=0.35 <=0.1 0.45-0.9 <=0.1 <=0.10 <=0.1 <=0.05 Rest

6082 0.7-1.3 <=0.5 <=0.10 0.4-1.0 0.6-1.2 <=0.255 <=0.20 <=0.10 <=0.05 Rest

7075 <=0.40 <=0.50 1.2-2.0 <=0.3 2.1-2.9 0.18-0.28 5.1-6.1 <=0.2 <=0.05 Rest

Fe (%) Cu (%) Bi (%) Pb (%) Mn (%) Mg (%) Cr (%) Zn (%) Ti (%) Alte(%) Al(%)

STAREA TABLELOR LAMINATEINDICATOR

STARE

F Forjat. Format prin prelucrare la rece, prelucrare la cald sau turnare fãrã control special al temperaturii sau al cãlirii superficiale.

O Moale. Laminat la cald, tratat termic în vederea obþinerii unui nivel foarte redus al duritãþii.H11 Cãlit superficial pânã la o duritate cuprinsã între 0 ºi 1/4.H111 Cãlit superficial pânã la o duritate cuprinsã între 0 ºi H11.H12 Cãlit superficial pânã la o duritate de 1/4.H14 Cãlit superficial pânã la o duritate de 1/2.H16 Cãlit superficial pânã la o duritate de 3/4.H18 Cãlit superficial pânã la o stare complet durã.H22 Prelucrat la rece, cãlit superficial ºi tratat termic parþial pânã la o duritate de 1/4.H24 Prelucrat la rece, cãlit superficial ºi tratat termic parþial pânã la o duritate de 1/2.H26 Prelucrat la rece, cãlit superficial ºi tratat termic parþial pânã la o duritate de 3/4.H28 Prelucrat la rece, cãlit superficial ºi tratat termic parþial pânã la o stare complet durã.H32 Prelucrat la rece, cãlit superficial ºi stabilizat la o duritate de 1/4.H34 Prelucrat la rece, cãlit superficial ºi stabilizat la o duritate de 1/2.H36 Prelucrat la rece, cãlit superficial ºi stabilizat la o duritate de 3/5.H38 Prelucrat la rece, cãlit superficial ºi stabilizat pânã la o stare complet durã.

STÃRI ALIAJE ALUMINIU

INDICAREA STÃRII ALIAJELOR ÎMBUNÃTÃÞIBILE ªI TRATAMENTUL TERMIC AL ACESTORAINDICATOR

STARE

T1

T2

T3

T4

T5

T6

Rãcit dupã procedeul de prelucrare la temperaturi ridicate ºi imbãtrânit natural pânã la obþinerea unei stãri stabileRãcit dupã procedeul de prelucrare la temperaturi ridicate, deformat la rece ºi imbãtrânit natural pentru obþinerea unei stãri stabilePus în soluþie deformat la rece ºi imbãtrânit natural pentru obþinerea unei stãri stabilePus în solutie ºi imbãtrânit natural pentru obþinerea unei stãri stabileRãcit dupã un procedeu de prelucrare la temperaturi ridicate ºi imbãtrânit artificialPus în solutie ºi apoi imbãtrânit artificial

3

ALIAJ 1050A 2007 2011 2017A 2024 3003 5005 5052 5083 6060 6082 7075

DENSITATE 2.7 2.85 2.82 2.8 2.77 2.73 2.69 2.68 2.66 2.7 2.7 2.8