Recommended Uses

■ Interior or Exterior Applications

■ Previously Painted Concrete or Steel Surfaces

■ Bridge Abutments

■ Commercial and Municipal Buildings

■ Schools

■ Transit Stations

■ Overpasses

■ Railcars

■ Concrete Fences

■ New Construction

Features

■ Graffiti removal with just water

■ Non-Sacrificial

■ Weatherability

■ Single component

■ Elastomeric

■ Low VOC

■ Long service life —10–15+ years

■ Surface tolerant

■ One coat application

Benefits

■ Cost savings of 25% to 40% compared to existing methods of repainting, chemical removal, or abrasive cleaning.

■ Can be cleaned an unlimited amount of times.

■ Preserves its aesthetic appearance throughout lifetime.

■ Ready to brush, roll, or spray. No mixing multiple components.

■ Expands and contracts with the substrate — no adhesion issues.

■ Long term cost savings.

■ Apply over concrete, steel, or previously painted surfaces.

■ Saves labor and time.

Anti-Graffiti Coating®

Anti-Graffiti Coating is a clear, one-component, non-

sacrificial, ready-to-use siloxane coating intended for use over

bare concrete or previously painted concrete or steel surfaces.

It cures with atmospheric moisture and offers excellent graffiti

resistance and cleanability with water power-washing.

PRODUCT INFORMATION

©2015 The Sherwin-Williams Company Protective & Marine Coatings

1.800.524.5979www.sherwin-williams.com/protective

To learn more, visit us atwww.sherwin-williams.com/protective or call 1-800-524-5979 to have a representative contact you.

©2015 The Sherwin-Williams CompanyProtective & Marine Coatings 2005983 1/15 AD0022

Performance Characteristics

Product Characteristics

ANTI-GRAFFITI COATING

B97C150

Protective &

MarineCoatings

9.54Revised: January 24, 2013

www.sherwin-williams.com/protective

PRODUCT DESCRIPTION

ANTI-GRAFFITI COATING is a one-component, non-sacrifi cial, ready-to-use siloxane coating that cures with atmospheric moisture. Intended for use over properly prepared concrete surface.

• Excellent graffi ti resistance• Excellent cleanability with either water power-washing, or solvent

wipe• UV resistance• Excellent adhesion• Low VOC• Fast drying• Outstanding airless spray properties• Single component

PRODUCT CHARACTERISTICS

Finish: Semi-Gloss

Color: Clear

Volume Solids: 72% ± 2%

Weight Solids: 75% ± 2%

VOC (EPA Method 24): <250 g/l; 2.1 lb/gal

Recommended Spreading Rate per coat:Minimum Maximum

Wet mils (microns) 8.0 (200) 12.0 (300)Dry mils (microns) 6.0 (150) 9.0 (225)~Coverage sq ft/gal (m2/L) 128 (3.1) 192 (4.7)Theoretical coverage sq ft/gal (m2/L) @ 1 mil / 25 microns dft 1152 (28.2)

NOTE: Brush or roll application may require multiple coats to achieve maximum fi lm thickness and uniformity of appearance.

Drying Schedule @ 10.0 mils wet (250 microns):@ 40°F/4.5°C @ 77°F/25°C @ 120°F/49°C

50% RHTo touch: 9 hours 1 hour 30 minutesTack free: 12 hours 4 hours 1 hourTo cure: 21 days 7 days 4 daysDrying time is temperature, humidity, and fi lm thickness dependent.

Shelf Life: 12 months, unopenedStore indoors at 40°F (4.5°C) to 100°F (38°C)

Flash Point: >100°F (38°C), TCCReducer/Clean Up: Mineral Spirits - up to 5% as

needed for spray application

Clean Up: Mineral Spirits or Naphtha

continued on back

RECOMMENDED USES

Uses:• Use over interior or exterior concrete surface that needs protec-

tion from graffi ti defacing

• Bridge Abutments• Commercial Buildings• Schools• Transit Stations• Overpasses• Railcars• New Construction

PERFORMANCE CHARACTERISTICS

Performance:Passed 4000 hours of QUV / multi-graffi ti application and removal

Gloss retention = 63% Color change <3 delta E CIE *L a b

No signs of graffi ti left after clean-up; no visible signs of streaking, cracking, pinholing, discoloration or other coating degradation upon casual examination

Graffi ti Removal from Surface Coated:Power wash with 3000-psi pressure washer (25 feet of hose) having a 15-degree tip at 2-3 inches away from the surface.

Graffi ti can also be removed by solvent wiping or acceptable graffi ti removers.

Fast DryingNon-Sacrifi cialExcellent Cleanability

Test Name Test Method Results

AcceleratedWeathering

• ASTM D4587, QUV-A, 4,000 hours• Xenon Arch, 2,000 hours

<3.0 DE color change, CIE *L a b; 63% gloss retention

Texas DOT - Graffi ti Removal Testing Pass

Adhesion ASTM D6677 Passes, Rating 8

ANTI-GRAFFITI COATING

B97C150

Protective &

MarineCoatings

9.54Revised: January 24, 2013

www.sherwin-williams.com/protective

PRODUCT DESCRIPTION

ANTI-GRAFFITI COATING is a one-component, non-sacrifi cial, ready-to-use siloxane coating that cures with atmospheric moisture. Intended for use over properly prepared concrete surface.

• Excellent graffi ti resistance• Excellent cleanability with either water power-washing, or solvent

wipe• UV resistance• Excellent adhesion• Low VOC• Fast drying• Outstanding airless spray properties• Single component

PRODUCT CHARACTERISTICS

Finish: Semi-Gloss

Color: Clear

Volume Solids: 72% ± 2%

Weight Solids: 75% ± 2%

VOC (EPA Method 24): <250 g/l; 2.1 lb/gal

Recommended Spreading Rate per coat:Minimum Maximum

Wet mils (microns) 8.0 (200) 12.0 (300)Dry mils (microns) 6.0 (150) 9.0 (225)~Coverage sq ft/gal (m2/L) 128 (3.1) 192 (4.7)Theoretical coverage sq ft/gal (m2/L) @ 1 mil / 25 microns dft 1152 (28.2)

NOTE: Brush or roll application may require multiple coats to achieve maximum fi lm thickness and uniformity of appearance.

Drying Schedule @ 10.0 mils wet (250 microns):@ 40°F/4.5°C @ 77°F/25°C @ 120°F/49°C

50% RHTo touch: 9 hours 1 hour 30 minutesTack free: 12 hours 4 hours 1 hourTo cure: 21 days 7 days 4 daysDrying time is temperature, humidity, and fi lm thickness dependent.

Shelf Life: 12 months, unopenedStore indoors at 40°F (4.5°C) to 100°F (38°C)

Flash Point: >100°F (38°C), TCCReducer/Clean Up: Mineral Spirits - up to 5% as

needed for spray application

Clean Up: Mineral Spirits or Naphtha

continued on back

RECOMMENDED USES

Uses:• Use over interior or exterior concrete surface that needs protec-

tion from graffi ti defacing

• Bridge Abutments• Commercial Buildings• Schools• Transit Stations• Overpasses• Railcars• New Construction

PERFORMANCE CHARACTERISTICS

Performance:Passed 4000 hours of QUV / multi-graffi ti application and removal

Gloss retention = 63% Color change <3 delta E CIE *L a b

No signs of graffi ti left after clean-up; no visible signs of streaking, cracking, pinholing, discoloration or other coating degradation upon casual examination

Graffi ti Removal from Surface Coated:Power wash with 3000-psi pressure washer (25 feet of hose) having a 15-degree tip at 2-3 inches away from the surface.

Graffi ti can also be removed by solvent wiping or acceptable graffi ti removers.

Fast DryingNon-Sacrifi cialExcellent Cleanability

Test Name Test Method Results

AcceleratedWeathering

• ASTM D4587, QUV-A, 4,000 hours• Xenon Arch, 2,000 hours

<3.0 DE color change, CIE *L a b; 63% gloss retention

Texas DOT - Graffi ti Removal Testing Pass

Adhesion ASTM D6677 Passes, Rating 8

ANTI-GRAFFITI COATING

B97C150

Protective &

MarineCoatings

9.54Revised: January 24, 2013

www.sherwin-williams.com/protective

PRODUCT DESCRIPTION

ANTI-GRAFFITI COATING is a one-component, non-sacrifi cial, ready-to-use siloxane coating that cures with atmospheric moisture. Intended for use over properly prepared concrete surface.

• Excellent graffi ti resistance• Excellent cleanability with either water power-washing, or solvent

wipe• UV resistance• Excellent adhesion• Low VOC• Fast drying• Outstanding airless spray properties• Single component

PRODUCT CHARACTERISTICS

Finish: Semi-Gloss

Color: Clear

Volume Solids: 72% ± 2%

Weight Solids: 75% ± 2%

VOC (EPA Method 24): <250 g/l; 2.1 lb/gal

Recommended Spreading Rate per coat:Minimum Maximum

Wet mils (microns) 8.0 (200) 12.0 (300)Dry mils (microns) 6.0 (150) 9.0 (225)~Coverage sq ft/gal (m2/L) 128 (3.1) 192 (4.7)Theoretical coverage sq ft/gal (m2/L) @ 1 mil / 25 microns dft 1152 (28.2)

NOTE: Brush or roll application may require multiple coats to achieve maximum fi lm thickness and uniformity of appearance.

Drying Schedule @ 10.0 mils wet (250 microns):@ 40°F/4.5°C @ 77°F/25°C @ 120°F/49°C

50% RHTo touch: 9 hours 1 hour 30 minutesTack free: 12 hours 4 hours 1 hourTo cure: 21 days 7 days 4 daysDrying time is temperature, humidity, and fi lm thickness dependent.

Shelf Life: 12 months, unopenedStore indoors at 40°F (4.5°C) to 100°F (38°C)

Flash Point: >100°F (38°C), TCCReducer/Clean Up: Mineral Spirits - up to 5% as

needed for spray application

Clean Up: Mineral Spirits or Naphtha

continued on back

RECOMMENDED USES

Uses:• Use over interior or exterior concrete surface that needs protec-

tion from graffi ti defacing

• Bridge Abutments• Commercial Buildings• Schools• Transit Stations• Overpasses• Railcars• New Construction

PERFORMANCE CHARACTERISTICS

Performance:Passed 4000 hours of QUV / multi-graffi ti application and removal

Gloss retention = 63% Color change <3 delta E CIE *L a b

No signs of graffi ti left after clean-up; no visible signs of streaking, cracking, pinholing, discoloration or other coating degradation upon casual examination

Graffi ti Removal from Surface Coated:Power wash with 3000-psi pressure washer (25 feet of hose) having a 15-degree tip at 2-3 inches away from the surface.

Graffi ti can also be removed by solvent wiping or acceptable graffi ti removers.

Fast DryingNon-Sacrifi cialExcellent Cleanability

Test Name Test Method Results

AcceleratedWeathering

• ASTM D4587, QUV-A, 4,000 hours• Xenon Arch, 2,000 hours

<3.0 DE color change, CIE *L a b; 63% gloss retention

Texas DOT - Graffi ti Removal Testing Pass

Adhesion ASTM D6677 Passes, Rating 8A complete line of products. Market expertise. On-time distribution.What else would you expect from a world leader in protective coatings and linings?

It starts with a complete line of time-tested, high-performance products and some of the most innovative technologies in the coatings industry. But we know that it takes more than product alone to be a world leader in protective coatings and linings. And so do the customers that rely on us every day as we help them protect their business.

That’s where nearly 150 years of coatings industry experience comes in. Add to that a NACE-trained workforce with a combined 3,700 years of experience in corrosion control. The market-specific knowledge that our experts provide to evaluate, recommend and deliver the highest-performance coatings and linings that protect our customers’ assets.   It also means that we deliver on time, every time from 4,000 company-owned distribution points worldwide. Leave nothing to chance. Your single source of supply. Sherwin-Williams.